Title of Invention	A PROCESS FOR PRODUCING LUBE OIL
Abstract	The invention relates to a processfor producing (67) Abstract: lube oil comprising isomerizlrig a waxy feed having a wax content of greatherthan 50% and/or having a pour point above 9°C and having greater than 70% paraffinic carbon ever a silicoaluminophesphate catalyst comprising (a) nonzeolltic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minoraxis between 4,2A and 4.8A and a major axis between 5.4A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig, PRICE : THIRTY RUPEES

Title of Invention

A PROCESS FOR PRODUCING LUBE OIL

Abstract

The invention relates to a processfor producing (67) Abstract: lube oil comprising isomerizlrig a waxy feed having a wax content of greatherthan 50% and/or having a pour point above 9°C and having greater than 70% paraffinic carbon ever a silicoaluminophesphate catalyst comprising (a) nonzeolltic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minoraxis between 4,2A and 4.8A and a major axis between 5.4A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig, PRICE : THIRTY RUPEES

Full Text	The present invention relates to a process for producing lube oil by isomerizing a waxy feed, including petroleum waxes, over a catalyst having a particular pore geometry and including at least one Group VIII metal the said lube oil has a low pour point and excellent viscosity and viscosity index properties. High-quality hubricating oils are critical for the operation of modem machinery and automobiles. Unfortunately, the supply of natural crude oils having good tubricating properties is not adequate for present dernands. Due to uncortainties in world crude oil supplies, high-quality hibricating oils must be produced from ordinary crude feedstocks and can even be produced from paraffinic synthetic polymers. Numerous processes have been proposed for producmg lubricating oils that can be converted into other products by upgrading the ordinary and low quality stocks. It is desirable to upgrade a crude fraction otherwise unsuitable for lubricant manufacture into one from which good yields of lube oils can be obtained. Dewaxing is required when highly paraffinic oils are to be used in products which need to remain mobile at low temperatures;, e.g-, lubricating oils, heating oils and jet fiielH. The higher molecular weight straight chain normal and slightly branched paraffins which are prtssent in oils of this kind are waxes which cause high pour points and high cloud points in the oils. If adequately low pour points are to be obtained, these waxes must be wholly or partly removed. In the past, various solvent removal technicfues were used such as propane dewaxing and MEK dev?axing but these techniques are costly and timo consuming. Catalytic dewaxing processes are more economical and achieve this end by selectively crac):ing the longer chain n-paraffins to produce lower molecular weight products, some of which may be removed by distillation. Because of their selectivity, prior art dewaxing catalysts generally comprise an aluminosilicate zeolite having a pore si:;e v/hich admits the straight chain n-paraffins either alone or with only slightly branched chain paraffins (sometimes referred to herein as waxes), but which excludes more highly branched materials, cycloaliphatics and aromatics. Zeolites such as ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35 anc. ZSM-3.3 have been proposed for this purpose in d^iwaxing processes and are described in U.S. Patents Nos. 3,894,938; 4,176,050; 4,181,598; 4,222,8S5; 4,229,282 and 4,247,388. Such processes as are set forth in the above-mentioned patents are used to accomplish dewaxing on feeds which cortain relatively low amounts of waxes, generally veil below 50%, and they operate by selectively cracking the waxes. These processes are not readily adapted for treating high wax coatent feeds since, due to the large amount of cracking which occurs, such waxes would tend to ba cracked to provide very low molecular weight protiucts. Since dewaxing processes of this kind function by means of cracking reactions, a number of useful products become degraded to lower molecular weight materials. For example, waxy paraffins may be cracked to butane, prop.ane, ethane and methane as may the lighter n-:?araffins which do not contribute to the waxy nature of the oil. Because these lighter products are generally of lower value than the higher molecular weight materials, it would obviously be desirable to limit the degree of cracking which takes place during a catalytic dewaxing process. Although U.S. Patents Nos. 3,700,585; 3,894,938; 4,176,050; 4,181,598; 4,222,8:55; 4,222,282; 4,247,388 and 4,859,311 teach dewaxing of waxy feeds, the processes disclosed tJierein do not disclose a process for producing high yields of a lube oil having a very low pour point and high viscosity index from feeds containing a very high wax content, i.e., greater than 80% wax, such as slack wax, deoiled wax or synthetic liquid polymers such as low molecular weight polyethylene. Also, the prior art does not disclose.a lube oil characterized by having both a low pour point (below about -24'C) and a viscosity index greater than 125. It is believed that tl^e closest that the prior art comes to accomplishimj this is set forth in one or more of U.S. Patents 3,365,390 (pour point -23C, viscosity index 124); 3,658,689 (pour point -54'C, viscosity index 92 as calculated from Table III of the patent); 3,764,516 (same as 3,658,689); 3,487,005 (pour point -29C, viscosity index 121 and 125 and pour point -46'C, viscosity index 122) and 4,547,283 pour point not specified but probably above O'C as made by solvent dewaxing, viscosity index 154-156). Since processes which remove wax vrill give a low yield with very waxy feeds, isomeri.zation processes are preferred. U.S. Patent No. 4,734,539 discloses a method for isomerij-.ing a naphtha feed using an intermediate pore s'.ize zeolite catalyst, such as an H-offretite catalyst. U.S. Patent No. 4,518,485 discloses a proceas for dewaxing a hydrocarbon feedstock containi.ng paraffins by a hydrotreating and isomerij;ation process. U.S. Patent No. 4,689,138 disclosess an isomerization process for reducing the nc>rmal paraffin content of a hydrocarbon oil feeidstock using a catalyst comprising an intermediate pore size silicoaluminophosphate molecular si€!ve containing a Group VIII metal component vhich is occluded in the crystals during grovrth. Lube oils may also be prepared from feeds having a high wax content such as slack v'ax by an isomerization process. In prior art wax isomerization processes, however, either the yield is low and thus the process is uneconomical, or the feed is not completely dewaxed. When the feed is not completely dewaxed it must be recycled to a dewaxing process, e.g., a solvent dewaxer, which limits the throughput and increases cost. U.S. Patent No. 4,547,283 discloses converting wax to lube. However, the MEK dewaxing following isomerization disclosed therein severely limits pour reduction and thus, very low pour points cannot be achieved. Further, the catalyst disclosed therein is much less selective than the catalysts used in the present invention. The present invention overcomes the problems and disadvantages of the prior art by providing a process for preparing a lube oil comprising isomerizing a waxy feed over a catalyst comprising an inorganic oxide molecular sieve having generally oval 1-D pores having a minor axis between about 4.2A and about 4.sA and a major axis between about 5.4A and about 7.OA as determined by X-ray crystallography and at le&st one Group VIII metal. It is an object of the invention to produce a lube oil having excellent viscosity and viscosity index properties and a very low pour point. It is a further object of the invention to provide a lube oil having low frictional resistance. It is an additional object of the invention to provide a lube oil which causes less engine wear than prior art mineral oils. It is an additional object of the invention to provide a lube oil which provides increased fuel efficiency. It is yet a further object of the invention to provide a lube oil having improved oxidation resistance compared to conventional mineral oils. The term "oxidation resistance" refers to the resistance of the oil to oxygen addition, i.e., how rapidly oxygen is picked up and added to molecular species within the oil. Oxidation resistance is indicated by the oxidator BN measured in hours. Oxidator BN measures the time required for 100 grams of oil to absorb one liter of oxygen and is described in U.S. Pater.t No. 3,852,207 at column 6, lines 15-30 which is incorporated herein by reference. Additional objects and advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention will be realized and attained by means of the instrumentalities and combinations, particularly pointed out in the appended claims. In accordance with one embodiment the invention provides a process for producing a lube oil having excellent viscosity and viscosity index properties and a low pour point comprising isomerizing a waxy feed over a catalyst comprising an intermediate pore size silicoaluminophosphate molecular sieve and at least one Group VIII metal. In accordance with another embodiment of the invention the catalyst in the process comprises an intermediate pore size ZSM-22, ZSM-23 or ZSM-35 zeolite. The lube oil of the invention has a high paraffinic content which provides a low viscosity for its boiling range. Such properties result in less frictional resistance, less engine wear and increased fuel efficiency. The low viscosity and low pour point of the lube oil result in easier cold engine starting than prior art mineral oils. The lube oil has a high viscosity index ranging from about 125 to about 180 and a very low pour point, ranging from less than about -63C to about -24C, Since little or no viscosity index improver compositions or pour point depressant compositions are necessary for use with the lube oil of the invention, fewer performance-decreasing deposits are formed. The high paraffinic nature of the oil gives it improved oxidation resistance compared to conventional mineral oils. Accordingly, the present invention provides a for producing lube oil comprising isomerizing a waxy feed having a wax content of greater than 50% and/or having a pour point above OC and having greater than 70% paraffinic carbon over a silicoaluminophosphate catalyst comprising (a) nonzeolitic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minor axis between 4,2 A and 4.8 A and a major axis between 5.4 A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig. The invention will be better understood with reference to the accompanying figures of the drawings wherein like numbers denote like parts throughout and wherein: Figure 1 is a ternary diagram showing the compositional parameters of the silicoalumino phosphates of U.S. Patent No. 4,440, 871 in terms of mole fractions of silicon, aluminum and phosphorus. Figure 2 is a ternary diagram showing the preferred compositional parameters of the silicoaluminophosphates of mole fractions of silicon, aluminum and phosphorus. Figure 3 is a plot of 700 F + lube yield versus pour point for the process set forth in Example 3. Figure 4 is a plot of viscosity index versus pour point for the process set forth in Example 3. Reference will now be made in deteiil to the present preferred embodiments of the invemtion. As used herein, the term "waxy feed" includes petroleum waxes. The feedstock employed in the process of the invention preferably contains greater than about 50% wax, mores preferably greater than about 80% wax, most preferably greater than about 90% wax. However, a highly paraffinic feed having a high pour point, generally above about O'C, more usually cibove about lO'C, but containing less than 50% wax is also suitable for use in the process of the invention. Such a feed should preferably contain greater than about 70% paraffinic carbon, more preferably greater than about 80% paraffj.nic carbon, most preferably greater than aboxit 90% paraffinic carbon. Exemplary additional suitable feeqls for use in the process of the invention include vraxy distillate stocks such as gas oils, lubricating oil stocks, synthetic oils such as those by Fischer-Tropsch synthesis, high pour point polyalphaolef ins, foots oils, synthetic vi^axes such as normal alphaolefin waxes, slack waxes, deoiled waxes and microcrystalline waxes. Foots oil is prepared by separating oil from the wax. The isolated oil is referred to as foots oil. Feeds also suitable for use in the process of the invention are partially dewaxed oils wherein dewaxing to an intermediate pour point has been carried out by a process other than that claimed herein, for example, conventional catalytic dewaxing processes and solvent dewaxing processes. Exemplary suitable solvent dtiwaxing processes are set forth in U.S. Patent No. 4,547,287. The process of the invention may cilso be employed in combination with conventional dewaxing processes to achieve a lube oil having particular desired properties. For example, the process of the invention can be used to reduce the pour point of a lube oil to a desired degree. Further reduction of the pour point can then be achieved using a conventional dewaxing process. Under such circumstances, immediately following the isomerization process of the invention, the lube oil may have a pour point greater than about 15F. Further, the pour point of the lube oil produced by the process of the invention can be reduced by adding pour point depressant compositions! thereto. The feedstock will normally be a C20+ feedstock generally boiling above about (iOO'F. However, the process of the invention is particularly useful with waxy distillate stocks such as gas oils, lubricating oil stocks, heating oils and other distillate fractions whos n-paraffins. The feedstock of the present process . will normally be a C20+ feedstock contain:.ng paraffins, olefins, naphthenes, aromaticti and heterocyclic compounds and a substantial proportion of higher molecular weight n-paraffins and slightly branched paraffins which contribute to the waxy nature of the feedstock. During processing, the n-paraffins and the slightly branched paraffins undergo some cracking or hydrocracking to form liquid range materials which contribute to a low viscosity product. The degree of cracking which occurs is, however, limited so that the yield of low boiling products is reduced, thereby preserving the econonic value of the feedstock. Slack wax can be obtained from either a hydrocracked lube oil or a solvent refined lube oil. Hydrocracking is preferred because that process can also reduce the nitrogen content to low values. With slack wax derived from solvent refined oils, deoiling can be used to reduce the nitrogen content. Optionally, hydrotreating of the slack wax can be carried out to lower the nitrogen content thereof. Slack waxes possess a very high viscosity index, normally in the range of from 140 to 200, depending on the oil content and the starting material from which the wax has been prepared. Slack waxes are therefore eminently suitable for the preparation OJ: lubricating oils having very high viscosity indices, i.e., from about 120 to about HJO. The present invention provides a unique lube oil product as characterized by its combination of low pour point and high viscosity index. The lube oil is characterized by a pour point below -24C (generally between -24C and -63'C) and a viscosity index between 125 and 180, suitably greater than about 130. Preferably the pour point is below -30C, more preferably below 40'C, and the viscosity index is greater than about 140. While the process of the invention can be practiced with utility when the feed contains organic (nitrogen containing impurities), it is preferred that the organic nitrogen content of the feed be less than about 50 ppmw (parts per million by weight), more preferably less than about 10 ppmw. Particularly good results, in terir.s of activity and length of catalyst cycle (period between successive regenerations or start-up and first regeneration) are experienced when the feed contains less than about 10 ppmw of organic nitrogen. The phrase "intermediate pore size", as used herein means an effective pore aperture in the range of from about 5.3 to about 6.5 A when the porous inorganic oxide is in the calcined form. Molecular sieves having pore apertures in this range tend to have unicjue molecular sieving characteristics. Unlike small pore zeolites such as erionite and chabazite, they will allow hydrocarbons having some branching into the molecular sieve void spaces. Unlike larger pore zeolites such as the faujasites and mordenites, they can differentiate between n-alkanes and slightly branched alkanes, and larger branched alkanes having, for example, ' quaternary carbon atoms. The effective pore size of the molecular sieves can be measured using standard adsorption techniques and hydrocarbonaceous compounds of known minimum kinetic diameters. See Breck, Zeolite Molecular Sieves. 1974 (especially Chapter 8); Anderson, et al,, J. Catalysis 55./ 114 (1979); and U.S. Patent No. 4,440,871, the pertinent portions of which are incorporated herein by ? reference. In performing adsorption measurements to determine pore size, standard techniques are vsed. It is convenient to consider a particular molecule as excluded if it does not reach at least 95% of its equilibrium adsorption value on the ir.olecular sieve in less than about 10 minutes (p/pc = 0.5; 25-C). Intermediate pore size molecular sieves will typically admit molecules having kir.etic diameters of 5.3 to 6.5 A with little hir.drance. Examples of such compounds (and their kinetic diameters in A) are: n-hexane (4.3), 3-methylpentane (5.5), benzene (5.85), and toluene (5.8). Compounds having kinetic diameters of about 6 to 6.5 A can be admitted into the pores, depending on the particular sieve, but do not penetrate as quickly and in some cases are effectively excluded. Compounds having liiinetic diameters in the range of 6 to 6.5 A include: cyclohexane (6.0), 2,3-dimethylbutane (6.1), and m-xylene (6.1). Generally, compounds having , kinetic diameters of greater than about 6.5 A do not penetrate the pore apertures and thus are not absorbed into the interior of the molecular sieve lattice. Examples of such larger compour.ds include: o-xylene (6.8), 1, 3 , 5-trimethylbeiizene (7.5), and tributylamine (8.1). The preferred effective pore size range is from about 5.5 to about 6.2 A. While the effective pore size as discussed above is important to the practice of the invention not all intermediate pore size molecular sieves having such effective pore sizes are advantageously usable in the practice of the present invention. Indeed, it is essential that the intermediate pore size molecular sieve catalysts used in the practice of the present invention have a very specific pore shape and size as measured by X-ray crystallography. First, the intracrystalline channels must be parallel and must not be interconnected. Such channels are conventionally referred to as 1-D diffusion types or more shortly as 1-D pores. The classification of intrazeolite channels as 1-D, 2-D and 3-D is set forth by R. M. Barrer in Zeolites, Science and Technology, edited by F. R. Rodrigues, L. D. Rollman and C. Naccache, NATO ASI Seiries, 1984 which classification is incorporated in its entirety by reference (see particularly page 75). Known 1-D zeolites include cancrinite hydrate, laumontite, mazzite, mordenite and zeolite L. None of the above listed 1-D pore zeolites, however, satisfies the second essential criterion for catalysts useful in the practice of the present invention. This second essential criterion is that the pores must be generally oval in shape, by which is meant the pores must exhibit two unequal axes referred to herein as a minor axis and a major axis. The term oval as used herein is not meant to require a specific: oval or elliptical shape but rather to refer to the pores exhibiting two unequal axes. In particular, the 1-D pores of the catalysts useful in the practice of the present invention must have a minor axis between about 4.2 A and about 4.8 A and a major axis between about 5.4 A and about 7.0 A as determined by conventional X-ray crystallography measurements. The catalyst used in the isomerization process of the invention has an acidic component and a platinum and/or palladium hydrogenation component. In accordance with one embod;Lment of the invention the acidic component can suitably comprise an intermediate pore size silicoaluminophosphate molecular sieve whicli is described in U.S. Patent No. 4,440,871, the pertinent disclosure of which is incorporated herein by reference. ' The most preferred intermediate pore size silicoaluminophosphate molecular sieve for use in the process of the invention is SAPO-11. SAPO-11 comprises a molecular framework of corner-sharing iSiOg) tetrahedra, lAlOj] tetrahedra and {POj] tetrahedra, [i.e., (Si^lyPJOj tetrahedra:. units]. When combined with a platinum or palladium hydrogenation component, the SAPO-11 com^erts the waxy components to produce a lubricating oil having excellent yield, very low pour poi.nt, low viscosity and high viscosity index. SAPO-11 comprises a silicoaluminophosphate material having a three-dimensional microporous crystal framework structure of [POj], [AlOj] and (SiOj) tetrahedral units whose uni": empirical formula on an anhydrous basis is: mR: (Si^lyPJOj (I) wherein "R" represents at least one organic templating agent present in the intracryistalline pore system; "m" represents the moles of "R" present per mole of (Si^lyP^)02 and has a value of from zero to about 0.3, "x", "y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounded by points A, B, C, D and E on the ternary diagram of Figure 1 or preferably within the are bounded by points a, b, c, d and e on the ternary diagram of Figure 2. The silicoaluminophosphate ha;3 a characteristic X-ray powder diffraction pattern which contains at least the d-spacings (as-synthesized and calcined) set forth below in Table I. When SAPO-11 is in the as-synthesized form "m" preferably has a value of from 0.02 to 0. 3. All of the as-synthesized SAPO-11 compositions for which X-ray powder diffraction data have been obtained to date have patterns which are within the generalized pattern of Table II belov. These values were determined by standard techniques. The radiation was the K-alpha doublet of copper and a diffractometer equipped with a scintillation counter and an associated computer was used. The peak heights, I, and the positions as a function of 2 9, where 9 is the Bragg angle, were determined using algorithms on the computer associated with the spectrometer. From these, the relative intensities, 100 I/Ij,, where I, Ls the intensity of the strongest line or peak, and d (obs.) the interplanar spacing in Angstroms, corresponding to the recorded lines, were determined. In the Tables, the relative intensities are given in terms of the symbols vs = very strong, s = strong, m = medium, w = weak, etc. Another intermediate pore size silicoaluminophosphate molecular sieve preferably used in the process of the invention is SAPO-31. SAPO-31 comprises a silicoaluminophosphate having a three-dimensional microporous crystal framework of [POj], jAlOg] and (SiOjl tetrahedral units whose unit empirical formula on an anhydrous basis is: mR: (Si^lyPJOj wherein R represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Si^lyPj,)02 and has a value of from zero to 0.3; "x", "y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounced by points A, B, C, D and E on the ternary diagram of Figure 1, or preferably within the area bounded by points a, b, c, d and e on the ternary diagram of Figure 2. The silicoaluminophosphate has a characteristic X-ray powder diffraction pattern (as-synthesized and calcined) which contains at least the d-spacings set forth below in Table III. When SAPO-31 is in the as-synthesized form, "m" preferably has a value of from 0.02 to 0.3. All of the as-synthesized SAPO-31 compositions for which X-ray powder diffraction data have presently been obtained have patterns whxch are within the generalized pattern of Table IV below. * Possibly contains peak from a minor impurity. SAPO-4 1, also suitable for use in the process of the invention, comprises a silicoaluminophosphate having a three-dimensional microporous crystal framework structure cif (PO2], [AlOjl and (SiOjl tetrahedral units, and vrhose unit empirical formula on an anhydrous basis is: mR: (SiAlyP2)02 wherein R represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Si^lyP^jOj and has a value of from zero to 0.3; "x", "y" and "z" repreisent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounded by points A, B, C, D and E on the ternary d;.agram of Figure 1, or preferably within the area hounded by points a, b, c, d and e on the ternary d^.agram of Figure 2, and said silicoaluminophosphatt'. having a characteristic X-ray powder diffraction jiattern (as-synthesized and calcined) which contcins at least the d-spacings set forth belov; in Table V. When SAPO-41 is in the as-synthesized form "m" preferably has a value of from 0.02 to 0.03. All of the as-synthesized SAPO-'U composizions for which X-ray powder diffraction data have jsrosently been obtained have patterns which are witliin the generalized pattern of Table VI below. The process of the invention may also be carried out using a catalyst comprising an intermediate pore size nonzeolitic molecular sieve containing AlOg and POj tetrahedral oxide units, and at least one Group VIII metal. Exemjilary suitable intermediate pore size nonzeolitic molecular sieves are set forth in European patent Application No. 158,977 which is incorpojrated herein by reference. The group of intermediate pore si:'.e zeolites of the present invention include, ZSM-22, ZSM-23 and ZSM-35. These catalysts are generally considered to be intermediate pore size catalysts based on the measure of their internal structure as represented by their Constraint Index. Zeolites which provide highly restricted access to and egress from their internal structure have a high value for the Constraint Index, whil.e zeolites which provide relatively free ficcess to the internal zeolite structure have a low value for their Constraint Index, The method for determining Constraint Index is describe-d fully in U.S. Patent No. 4,016,218 which is incorporated herein by reference. Those zeolites exhibiting a Constraint Index value within the range of from about 1 to about 12 are considered to be intermediate pore size zeolites. Zeolites which are considered to be in this range include ZSM-5, ZSM-11, etc. Upon careful examination of the intermediate pore size zeolites, however, it has been found that not all of them are efficient as a catalyst for isomerization of a paraffin-containing feedstock which are high in C20+ paraffins, and preferably which are high in C22+ paraffins. In particular, it has been found that the group including ZSM-22, ZSM-23 and ZSM-35 used in combination with Group VIII metals can provide a means whereby a hydrocarbon feedstock having a paraffinic content with molecules of 20 carbon atoms or more undergoes unexpectedly efficient isomerization without destroying the ultimate yield of the feedstock. It is known to use prior art techniques for formation of a great variety of synthetic aluminosilicates. These aluminosilicates have come to be designated by letter or other convenient symbols. One of the zeolites of the present invention, ZSM-22, is a highly siliceous material which includes crystalline thre-a-dimensional continuous framework silicon containing structures or crystals which result when all the oxygen atoms in the tetrahedra are mutually shared between tetrahedral atoms of silicon or aluminum, and which can exist with a network of mostly SiO2, i.e., exclusive of any intracrystalline cations. The description of ZSM-22 is set forth in full in U.S. Patent No. 4,556,477, U.S. Patent No. 4,481,177 and European Patent Application No. 102,716 the contents of which are incorporated herein by referencie. As indicated in U.S. Patent No. 4,566,477 the crystalline material ZSM-22 has been designated with a characteristic X-ray di.ffraction pattern as set forth in Table VII. It should be understood that the X-ray di.ffraction , pattern of Table VII is characteristic of a].l the species of ZSM-22 zeolite compositions. Ion exchange of the alkali metal cations with, other ions results in a zeolite which reveals substantially the same X-ray diffraction pattern with some minor shifts in interplanar spacing and variation in relative intensity. Furthermore, the original cations of the as-synthesized ZSM-22 can be replaced at least in part by other ions using conventional ion exchange techniques. It may be necessary to precalcine the ZSM-22 zeolite crystals prior to ion exchange. In accordance with the present invention, the replacement ions are those taken from Group VIII of the Periodic Table, especially platinum, palladium, iridium, osmium, rhodium and ruthenium. ZSM-22 freely sorbs normal hexane and has a pore dimension greater than about 4 A. In addition, the structure of the zeolite provides constrained access to larger molecules. The Constraint Index as determined by the procedure set forth in U.S. Patent No. 4,016,246 foe 2SM-22 has been determined to be from about 2.5 to about 3.0. Another zeolite which can be used with the present invention is the synthetic crystalline aluminosilicate referred to as ZSM-23, disclosed in U.S. Patent No. 4,076,842, the contents of which are incorporated herein by reference. The ZSM-23 composition has a characteristic X-ray diffraction pattern as set forth herein in Table VIII. Other molecular sieves which can ba used with the present invention include, for example, Theta-1, as described in U.S. Patents 4,5 33,649 and 4,836,910, both of which are incorporated in their entireties by reference, Nu-10, as described in European Patent Application 065,400 which is incorporated in its entirety by reference and SSZ- 20 as described in U.S. Patent 4,483,835 which is incorporated in its entirety by reference. The ZSM-23 composition can also be defined in terms of mole ratios of oxides in the anhydrous state as follows: (0.58 - 3.4)M2/nO: Al2O3. (40 -250)SiO2 wherein M is at least 1 cation and n is the valence thereof. As in the ZSM-22, the original cations of as-synthesized ZSM-23 can be replaced in accordance with techniques well-known in the art, at. least in part by ionic exchange with other cations. In the present invention these cations include the Group VIII metals as set forth hereinbefore. The third intermediate pore size zeolite which has been found to be successful in the present invention is ZSM-35, which is disclosed in U.S. Patent No. 4,016,245, the contents of which are incorporated herein by reference. The synthetic crystalline aluminosilicate knovn as ZSM-35, has a characteristic X-ray diffraction pattern which is set forth in U.S. Patent No. 4,016,245. ZSM-35 has a composition which can be defined in terms of mole ratio of oxides in the anhydrous state as follows: (0.3-2.5) R2jO: (0-0.8) M20:Al203:>8 SiO2 wherein R is organic nitrogen-containing cation derived from ethylenediamine or pyrrolidine and M is an alkali metal cation. The original cations of the as-synthesized ZSM-35 can be removed using techniques well known in the art which includes ion exchange with other cations. In the present invention the cation exchange is used to leplace the as-synthesized cations with the Group VIII metals set forth herein. It has been observed that the X-ray diffraction pattern os ZSM-35 is similar to that of natural ferrierite with, a notable exception being that natural ferrierite patterns exhibit a significant line at 1.33 A. X-ray crystallography of SAPO-ll, SAPO-31, SAPO-41, ZSM-22, ZSM-23 and ZSM-35 shows these molecular sieves to have the following major and minor axes: SAPO-ll, major 6.7 A, minor 4.4 A; (Benett, J. M., et al, Zeolites, 1, 160(87)), SAPO-31 and SAPO-41, believed to be slightly large than SAPO-ll, ZSM-22, major 5.5 A, minor 4.5 A (Kokotailo, G. T. , et al. Zeolites, i., 349(85)); ZSM-23, major 5.6 A, minor 4.5 A; ZSM-35, major 5.4 A, minor 4.2 A (Meier, W. M. and Olson, D. H., Atlas of Zeolite Structure Types, Butten^orths, 1987) . The intermediate pore size molecular sieve is used in admixture with at least one Giroup VIII metal. Preferably the Group VIII metal is selected from the group consisting of at least one of platinum and palladium and optionally, other catalyticaliy active metals such as molybdenum, nickel, vanadium, cobalt, tungsten, zinc and mixtures thereof. Most preferably, the The term "metal" or "active metal" as .used herein means one or more metals in the elemental state or in some form such as sulfide, oxide and mixtures thereof. Regardless of the state in which the metallic component actually exj.sts, the concentrations are computed as if they existed in the elemental state. The catalyst may also contain metals which reduce the number of strong acid sites on the catalyst and thereby lower the selectivity for cracking versus isomerization. Especially preferred are the Group IIA metals such as magnesium and calcium. It is preferred that relatively small crystal size catalyst be utilized in practicing the invention. Suitably, the average crystal size is no greater than about 10/ii, preferably no more than about 5/i, more preferably no more than about 1/x and still more preferably no more thai about 0.5M. Strong acidity may also be reduced by introducing nitrogen compounds, e.g., NH., or organic nitrogen compounds, into the feed; however, the total nitrogen content should be less than 50 ppm, preferably less than 10 ppm. The physical form of the catalyst depends on the type of catalytic reactor being employed and may be in the form of a granule or powder, and is desirably compacted into a more readily usable form (e.g., larger agglomerates), usually with a silica or alumina binder for fluidized bed reaction, or pills, prills, spheres, extrudates, or o;her shapes of controlled size to accord adequate catalyst-reactant contact. The catalyst may be employed either as a fluidized catalyst, or in a fixed or moving bed, and in one or more reaction stages. The catalytic isomerization step of che invention may be conducted by contacting the feed with a fixed stationary bed of catalyst, with a fixed fluidized bed, or with a transport bed. A simple and therefore preferred configuration is a trickle-bed operation in which the feed is allowed to trickle through a stationary fixed bed, preferably in the presence of hydrogen. The catalytic isomerization conditions employed depend on the feed used and the desired pour point. Generally, the temperature is from about 200C to about 475C, preferably from about 250C and to about 450C. The pressure is typically from about 15 psig and to about 2000 psig, preferably from about 50 to about 1000 psig, more preferably from about 100 psig to about 600 psig. The process of the invention is preferably carried out at low pressure. The liquid hourly space velocity (LHSV) is preferably from about 0.1 to about 20, more preferably from about 0.1 to about 5, and most preferably from about 0.1 to about 1.0. Low pressure and low liquid hourly space velocity provide enhanced isomerization selectivity which results in more isomerization and less cracking of the feed thus producing an increased yield. Hydrogen is preferably present in the reaction zone during the catalytic isomeriz The intermediate pore size molecular sieve used in the isomerization step provides selective conversion of the waxy components to non-waxy components. During processing, isomerizeition of the paraffins occurs to reduce the pour point of the oil below that of the feed and form lube oil boiling range materials which contribute to a low pour point product having excellent viscosity index properties. Because of the selectivity of the intermediate pore size molecular sieve used in the invention, the yield of low boiling products is reduced, thereby preserving the economic value of the feedstock. The intermediate pore size molecular sieve catalyst can be manufactured into a wide variety of physical forms. The molecular sieves can be in the form of a powder, a granule, or a molded product, such as an extrudate having a particle size sufficient to pass through a 2-mesh (Tyler) screen and be retained on a 40-mesh (Tylttr) screen. In cases wherein the catalyst is: molded, such as by extrusion with a binder, the silicoaluminophosphate can be extruded before drying, or, dried or partially dried and then extruded. The molecular sieve can be composited with other materials resistant to temperatures; and other conditions employed in the isomeri2:ation process. Such matrix materials include a.ctive and inactive materials and synthetic or natuially occurring zeolites as well as inorganic materials such as clays, silica and metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Inactive materials suitably serve as diluents to control the amount of conversion in the isomerization process so that products can be obtained economically without employing other means for controlling the rate of reaction. The molecular sieve may be incorporated into naturally occurring clays, e.g., bentonite and kaolin. These materials, i.e., clays, oxides, eti:. , function, in part, as binders for the catalyst. It is desirable to provide a catalyst having,good crush strength because in petroleum refining, the catalyst is oft.en subjected to rough handling. This tends to break the catalyst down into powder¬like materials which cause problems in processing. Naturally occurring clays which can be composited with the molecular sieve include the montmorillonite and kaolin families, which families include the sub-bentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Fibrous clays such as halloysite, sepiolite and attapulgite can also be use as supports. Such clays can be uised in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the molecular sieve can be composited with porous matrix materials and mixtures of matrix naterials such as silica, alumina, titania, magnes;.a, silica-alumina, silica-magnesia, silica-irconia, silica-thoria, silica-beryllia, silica-titania, titania-zirconia as well as ternary compositions such as silica-alumina-thoria, silica-alumina-titania, silica-alumina-magnesia and stl:.ca-magnesia-zirconia. The matrix can be in the form of a cogel. The catalyst used in the process of this invention can also be composited with other zeolites such as synthetic and natural fe.ujasites, (e.g., X and Y) erionites, and mordenites. It can also be composited with purely synthetic zeolites such as those of the ZSM series. The coirbination of zeolites can also be composited in a porous inorganic matrix. It is often desirable to use mild hydrogenation referred to as hydrofinishing after isomerization to produce more stable lubricating oils. Hydrofinishing is typically conducted at temperatures ranging from about 190'C to about 340'C, at pressures from about 400 psig to about 3000 psig, at space velocities (LHSV) from about 0.1 to about 20, and hydrogen recycle ratiss of from about 400 to about 1500 SCF/bbl. The hydrogenation catalyst employed must be active enough not only to hydrogenate the olefins;, diolefins and color bodies within the lubt; oil fractions, but also to reduce the aromatic; • content. The hydrofinishing step is beneficial in preparing an acceptably stable lubricatinc oil. Suitable hydrogenation catalysts ir.clude conventional metallic hydrogenation catalysts, particularly the Group VIII metals such as cobalt, nickel, palladium and platinum. The metals are typically associated with carriers such as bauxite, alumina, silica gel, silica-alumina composites, and crystalline aluminosilicate zeolites. Palladium is a particularly preferred hydrogenation metal. If desired, non-noble Group VIII metals can be used with molybdates. Metal oxides or sulfides can be used. Suitable catalysts are disclosed in U.S. Patent Nos. 3,852,207; 4,157,294; 3,904,513 and 4,673,487, which are incorporated herein by reference. The high viscosity index lube oil produced by the process of the present invention can be used as a blending component to raise the: viscosity index of lube oils to a higher value. Since yield decreases with increasing viscosity index in either hydrocracking or solvent refining, the use of an isomerized wax to increase the viscosity index improves yield. The invention will be further clamified by the following examples, which are intendsid to be purely exemplary of the invention. The wax content of the oil set forth in the . following Examples was determined as follows: 300 g of oil was diluted 50/50 with a 4:1 mixture of methyl ethyl ketone and toluene which was cooled to -20C in a refrigerator. The mixture was filtered through a Coors funnel at -15'C using Whatman No. 3 filter paper. The wax was removed from the filter and placed in a tared 2 liter flask. The solvent was removed cin a hot plate and the wax weighed. Example 1 SAPO-11 was prepared as follows: 472.4 g of 85% H3PO4 were added to 1208 g of distilled HgO in a Teflon beaker in an ice bath. 816.8 g of aluminum isopropoxide (AlfOCjH.la) were slowly added with mixing and then mixed until homogenous. Then 120 g of fumed silica (Cabosil M-5) were added with mixing. Next, 182.4 g of di-n-propylamine (PrgNH) were added, followed by 9.0 g of 8 5% H3PO4. Final mixing was done using a Polytron. The mixture had a pH of 6.5 and the following composition, expressed in molar ratio of oxides: The mixture was placed in a Teflon bottle in a stainless steel pressure vessel and heated for 5 days at 200C with no stirring and autogenous pressure. The supernatant liquid was removed and the product was filtered, washed with water, dried overnight at 12 1'C, and calcined in air for 8 hours at 566'C. The average crystallite siZje was less than 0.5 micron. The product was identified as SAPO-11 by X-ray diffraction analysis. Elemental analysis of the calcined sieve showed it to have the following anhydrous molar composition: The sieve was bound with 35% Catat>al alumina and made into 1/10 inch extrudate. The extrudate was dried 3 hours at 121 C, calcined in air for 4 hours at 454C, then impregnated with 0.5% Pt (as Pt(NH3)4Cl2.H20) by the pore-fill method, It was then dried for 2 hours at 93C, 2 hours at 149'C, and calcined in air for 8 hours at 454C. For the following examples, the catalyst was crushed and screened to 24-42 mesh. Example 2 The catalyst of Example 1 was used to isomerize a 800F+ hydrocracked waxy vacuum gas oil (Table IX) at 2200 psig, 1 LHSV, and 8 M SCF/bbl once-through H2. The catalyst was also run at 400 psig. The results are set forth in Table X and demonstrate that high lube yield at very low pour point is achieved by the present process. The data also evidences the substantial yield benefit from operating at a lower reactor pressure. Lube yield is defined as gfproduct) x 100% where the product g(feed) has the same 5 LV% boiling point as the feed. Example ,3 The catalyst of Example 1 was used to isomerize a slack wax derived from a 900'F+ hydrocracked vacuum gas oil (Table XI). Conditions were 160 psig reactor pressure, 0.3 LHSV, and 8 M SCF/bbl once-through Hj. At a catalyst temperature of 680F, a -27C pour point oil of 7.1 est viscosity at lOO'C and 149 . viscosity index was produced. Pour point reduction could be increased by raising che catalyst temperature. Figure 3 shows a plot of 700'F-t- lube yield versus pour point, where 700F + lube yield is defined as: Figure 4 shows a plot of viscosity index versus pour point. A -30C pour point oil prepared in this example was subsequently hydrofinished over a 0.5% Pd on silica-alumina catalyst at 500'F, ;>200 psig. 0.25 LHSV, and 8 M SCF/bbl H2. Inspections of the hydrofinished oil are given in Table XVI . Example 4 The catalyst of Example 1 was used to isomerize a deoiled slack wax derived from a 700-800'F solvent refined vacuum gas oil (Table XII). Conditions were 160 psig, 0.3 LHSV, and 8 M SCF/bbl once-through H2. The results are set forth in Table XIII. Example 5 The catalyst of Example 1 was used to isomerize a deoiled slack wax derived fr Example 6 ZSM-22 was prepared as follows: The following reactants were combined to produce a gel: N,N'-dimethyl imidazolium hydroxide, Ludox AS-30 silica sol, aluminum sulfate, sodium hydroxide, and water in the ratios: SiO2/Al2O3 = 100 H2O/SiO2 =30 template/SiO2 =0.15 NaOH/SiO2 = 0. 10 OH-SiO2 = 0.2 5 The reaction was run at autogenous pressure in a stainless steel autoclave at 150'C for 6 days. The product was filtered, calcinated to lOOO'F in air, ion-exchanged four times with excest; NH4NO3 and calcined again to lOOO'F. The product was identified by X-ray diffraction analysis as ZSM-22. The SiO2/Al2O3 mola ratio was about 100. The sieve was bound with 35% Catapal and the extrudate impregnated with 1% Pt and calcined in the same manner as the catalyst of Example 1. Example 7 The catalyst of Example 6 was used to isomerize the slack wax of Table XI at 500 psig, 0.3 LHSV, and 8M SCF/bbl once-through Hg. The results are set forth in Table XVII. Example 9 The catalyst of Example 6 was mixed with a 10-fold excess of 5 wt. % Mg CO3 in water, filtered, dried for 18 hours at 93'C, and calcined for 12 hours at 538'C. The Mg content was 22.7 wt.%. This catalyst was used to isomerize the slack wax of Table XI at 0.3 LHSV and 8 MSCF/bbl H2, both at 500 psig and 160 psig. The results are set forth in Table XVIII, showing a higher yield for this catalyst than that of Example 6 without Mg. The beneficial effect of low pressure on yield is also shown. Example 9 The catalyst of Example 6 was used to isomerize a deoiled slack wax derived from a 900'F+ solvent refined vacuum gas oil (Table XIX). Conditions were the same as Example 7. The results are set forth in Table XX. . Example 10 The catalyst of Example 8 was used to isomerize a slack wax (not deoiled) derived from a 700-800*F solvent refined vacuum gas oil (the same ^used to prepare the feed of Table XII). Inspections of the feed are given in Table XXI. Isomerization conditions were the same as; in Example 7. The results are set forth in Table XXII. Examplg 11 ZSM-23 was prepared as in U.S. Pat:ent No. 4,076,842, and identified as such by X-rc.y diffraction analysis after calcination at. lOOO'F in air. It was exchanged four times with excess NH4N03 and calcined again at lOOO'F. The sieve was impregnated with 0.5% Pt and calcined in the same manner as the catalyst of Example 1. Example 12 The catalyst of Example 11 was used to isomerize the feed of Table XI at 0.3 LHSV, 500 psig, and 8 MSCF/bbl H2. The results are set forth in Table XXIII. Example 13 The catalyst of Example 8 was used to isomerize a C30+ normal alphaolefin wax (Table XXIV) at 0.3 LHSV and 8 MSCF/bbl Hj, both at 500 psig and 300 psig. The results are set forth in Table XXV. While the invention has been described in connection with specific embodiments thereof, it will be understood that it is capable of further modification, and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure as come within known or customary practice in the art to which the invention pertains and as may be applied to the essential features hereinbefore set forth, and as fall within the scope of the invention and the limits of the appended claims. We Claim: 1. A process for producing lube oil comprising isomerizing a waxy feed having a wax content of greater than 50% and/or having a pour point above 0C and having greater than 70% paraffinic carbon over a silicoaluminophosphate catalyst comprising (a) nonzeolitic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minor axis between 4.2 A and 4.8 A and a major axis between 5.4 A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig. 2. The process as claimed in claim 1, wherein said waxy feed contains at least 80% wax. 3. The process as claimed in claim 1, wherein said waxy feed contains at least 80% paraffinic carbon. 4. The process as claimed in claim 1, wherein said waxy feed is selected from the group consisting of gas oil stock, lubricating oil stock, synthetic oil, foots oil, slack wax, deoiled wax, normal alphaolefin wax and microcrystalline wax. 5. The process as claimed in claim 1, wherein the liquid hourly space velocity during isomerization is from 0.1 to 20. 6. The process as claimed in claim 1, wherein the isomerized lube oil is optionally hydrofinished. 7. A process for producing lube oil, substantially as hereinabove described and illustrated, with reference to figures 2 and 3 of the accompanying drawings

Full Text

The present invention relates to a process for producing lube oil by isomerizing a waxy feed, including petroleum waxes, over a catalyst having a particular pore geometry and including at least one Group VIII metal the said lube oil has a low pour point and excellent viscosity and viscosity index properties.
High-quality hubricating oils are critical for the operation of modem machinery and automobiles. Unfortunately, the supply of natural crude oils having good tubricating properties is not adequate for present dernands. Due to uncortainties in world crude oil supplies, high-quality hibricating oils must be produced from ordinary crude feedstocks and can even be produced from paraffinic synthetic polymers. Numerous processes have been proposed for producmg lubricating oils that can be converted into other products by upgrading the ordinary and low quality stocks.
It is desirable to upgrade a crude fraction otherwise unsuitable for lubricant manufacture into one from which good yields of lube oils can

be obtained. Dewaxing is required when highly paraffinic oils are to be used in products which need to remain mobile at low temperatures;, e.g-, lubricating oils, heating oils and jet fiielH. The higher molecular weight straight chain normal and slightly branched paraffins which are prtssent in oils of this kind are waxes which cause high pour points and high cloud points in the oils. If adequately low pour points are to be obtained, these waxes must be wholly or partly removed. In the past, various solvent removal technicfues were used such as propane dewaxing and MEK dev?axing but these techniques are costly and timo consuming. Catalytic dewaxing processes are more economical and achieve this end by selectively crac):ing the longer chain n-paraffins to produce lower molecular weight products, some of which may be removed by distillation.
Because of their selectivity, prior art dewaxing catalysts generally comprise an aluminosilicate zeolite having a pore si:;e v/hich admits the straight chain n-paraffins either alone or with only slightly branched chain paraffins (sometimes referred to herein as waxes), but which excludes more highly branched materials, cycloaliphatics and aromatics. Zeolites such as ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35 anc. ZSM-3.3 have been proposed for this purpose in d^iwaxing processes and are described in U.S. Patents Nos. 3,894,938; 4,176,050; 4,181,598; 4,222,8S5; 4,229,282 and 4,247,388. Such processes as are set forth in the above-mentioned patents are used to accomplish dewaxing on feeds which cortain relatively low amounts of waxes, generally veil

below 50%, and they operate by selectively cracking the waxes. These processes are not readily adapted for treating high wax coatent feeds since, due to the large amount of cracking which occurs, such waxes would tend to ba cracked to provide very low molecular weight protiucts.
Since dewaxing processes of this kind function by means of cracking reactions, a number of useful products become degraded to lower molecular weight materials. For example, waxy paraffins may be cracked to butane, prop.ane, ethane and methane as may the lighter n-:?araffins which do not contribute to the waxy nature of the oil. Because these lighter products are generally of lower value than the higher molecular weight materials, it would obviously be desirable to limit the degree of cracking which takes place during a catalytic dewaxing process.
Although U.S. Patents Nos. 3,700,585; 3,894,938; 4,176,050; 4,181,598; 4,222,8:55; 4,222,282; 4,247,388 and 4,859,311 teach dewaxing of waxy feeds, the processes disclosed tJierein do not disclose a process for producing high yields of a lube oil having a very low pour point and high viscosity index from feeds containing a very high wax content, i.e., greater than 80% wax, such as slack wax, deoiled wax or synthetic liquid polymers such as low molecular weight polyethylene.
Also, the prior art does not disclose.a lube oil characterized by having both a low pour point (below about -24'C) and a viscosity index greater than 125. It is believed that tl^e closest that the prior art comes to accomplishimj this is

set forth in one or more of U.S. Patents 3,365,390 (pour point -23*C, viscosity index 124); 3,658,689 (pour point -54'C, viscosity index 92 as calculated from Table III of the patent); 3,764,516 (same as 3,658,689); 3,487,005 (pour point -29*C, viscosity index 121 and 125 and pour point -46'C, viscosity index 122) and 4,547,283 pour point not specified but probably above O'C as made by solvent dewaxing, viscosity index 154-156).
Since processes which remove wax vrill give a low yield with very waxy feeds, isomeri.zation processes are preferred. U.S. Patent No. 4,734,539 discloses a method for isomerij-.ing a naphtha feed using an intermediate pore s'.ize zeolite catalyst, such as an H-offretite catalyst. U.S. Patent No. 4,518,485 discloses a proceas for dewaxing a hydrocarbon feedstock containi.ng paraffins by a hydrotreating and isomerij;ation process.
U.S. Patent No. 4,689,138 disclosess an isomerization process for reducing the nc>rmal paraffin content of a hydrocarbon oil feeidstock using a catalyst comprising an intermediate pore size silicoaluminophosphate molecular si€!ve containing a Group VIII metal component vhich is occluded in the crystals during grovrth.
Lube oils may also be prepared from feeds having a high wax content such as slack v'ax by an isomerization process. In prior art wax isomerization processes, however, either the yield is low and thus the process is uneconomical, or the feed is not completely dewaxed. When the feed is not completely dewaxed it must be recycled to a

dewaxing process, e.g., a solvent dewaxer, which limits the throughput and increases cost. U.S. Patent No. 4,547,283 discloses converting wax to lube. However, the MEK dewaxing following isomerization disclosed therein severely limits pour reduction and thus, very low pour points cannot be achieved. Further, the catalyst disclosed therein is much less selective than the catalysts used in the present invention.
The present invention overcomes the problems and disadvantages of the prior art by providing a process for preparing a lube oil comprising isomerizing a waxy feed over a catalyst comprising an inorganic oxide molecular sieve having generally oval 1-D pores having a minor axis between about 4.2A and about 4.sA and a major axis between about 5.4A and about 7.OA as determined by X-ray crystallography and at le&st one Group VIII metal.
It is an object of the invention to produce a lube oil having excellent viscosity and viscosity index properties and a very low pour point.
It is a further object of the invention to provide a lube oil having low frictional resistance.
It is an additional object of the invention to provide a lube oil which causes less engine wear than prior art mineral oils.
It is an additional object of the invention to provide a lube oil which provides increased fuel efficiency.

It is yet a further object of the invention to provide a lube oil having improved oxidation resistance compared to conventional mineral oils. The term "oxidation resistance" refers to the resistance of the oil to oxygen addition, i.e., how rapidly oxygen is picked up and added to molecular species within the oil. Oxidation resistance is indicated by the oxidator BN measured in hours. Oxidator BN measures the time required for 100 grams of oil to absorb one liter of oxygen and is described in U.S. Pater.t No. 3,852,207 at column 6, lines 15-30 which is incorporated herein by reference.
Additional objects and advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention will be realized and attained by means of the instrumentalities and combinations, particularly pointed out in the appended claims.
In accordance with one embodiment the invention provides a process for producing a lube oil having excellent viscosity and viscosity index properties and a low pour point comprising isomerizing a waxy feed over a catalyst comprising an intermediate pore size silicoaluminophosphate molecular sieve and at least one Group VIII metal.
In accordance with another embodiment of the invention the catalyst in the process comprises an intermediate pore size ZSM-22, ZSM-23 or ZSM-35 zeolite.

The lube oil of the invention has a high paraffinic content which provides a low viscosity for its boiling range. Such properties result in less frictional resistance, less engine wear and increased fuel efficiency. The low viscosity and low pour point of the lube oil result in easier cold engine starting than prior art mineral oils. The lube oil has a high viscosity index ranging from about 125 to about 180 and a very low pour point, ranging from less than about -63*C to about -24*C, Since little or no viscosity index improver compositions or pour point depressant compositions are necessary for use with the lube oil of the invention, fewer performance-decreasing deposits are formed. The high paraffinic nature of the oil gives it improved oxidation resistance compared to conventional mineral oils.

Accordingly, the present invention provides a for producing lube oil comprising isomerizing a waxy feed having a wax content of greater than 50% and/or having a pour point above OC and having greater than 70% paraffinic carbon over a silicoaluminophosphate catalyst comprising (a) nonzeolitic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minor axis between 4,2 A and 4.8 A and a major axis between 5.4 A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig.
The invention will be better understood with reference to the accompanying figures of the drawings wherein like numbers denote like parts throughout and wherein:
Figure 1 is a ternary diagram showing the compositional parameters of the silicoalumino phosphates of U.S. Patent No. 4,440, 871 in terms of mole fractions of silicon, aluminum and phosphorus.
Figure 2 is a ternary diagram showing the preferred compositional parameters of the silicoaluminophosphates of mole fractions of silicon, aluminum and phosphorus.
Figure 3 is a plot of 700 F + lube yield versus pour point for the process set forth in Example 3.

Figure 4 is a plot of viscosity index versus pour point for the process set forth in Example 3.

Reference will now be made in deteiil to the present preferred embodiments of the invemtion.
As used herein, the term "waxy feed" includes petroleum waxes. The feedstock employed in the process of the invention preferably contains greater than about 50% wax, mores preferably greater than about 80% wax, most preferably greater than about 90% wax. However, a highly paraffinic feed having a high pour point, generally above about O'C, more usually cibove about lO'C, but containing less than 50% wax is also suitable for use in the process of the invention. Such a feed should preferably contain greater than about 70% paraffinic carbon, more preferably greater than about 80% paraffj.nic carbon, most preferably greater than aboxit 90% paraffinic carbon.
Exemplary additional suitable feeqls for use in the process of the invention include vraxy distillate stocks such as gas oils, lubricating oil stocks, synthetic oils such as those by Fischer-Tropsch synthesis, high pour point polyalphaolef ins, foots oils, synthetic vi^axes such as normal alphaolefin waxes, slack waxes, deoiled waxes and microcrystalline waxes. Foots oil is prepared by separating oil from the wax. The isolated oil is referred to as foots oil.
Feeds also suitable for use in the process of the invention are partially dewaxed oils

wherein dewaxing to an intermediate pour point has been carried out by a process other than that claimed herein, for example, conventional catalytic dewaxing processes and solvent dewaxing processes. Exemplary suitable solvent dtiwaxing processes are set forth in U.S. Patent No. 4,547,287.
The process of the invention may cilso be employed in combination with conventional dewaxing processes to achieve a lube oil having particular desired properties. For example, the process of the invention can be used to reduce the pour point of a lube oil to a desired degree. Further reduction of the pour point can then be achieved using a conventional dewaxing process. Under such circumstances, immediately following the isomerization process of the invention, the lube oil may have a pour point greater than about 15*F. Further, the pour point of the lube oil produced by the process of the invention can be reduced by adding pour point depressant compositions! thereto.
The feedstock will normally be a C20+ feedstock generally boiling above about (iOO'F. However, the process of the invention is particularly useful with waxy distillate stocks such as gas oils, lubricating oil stocks, heating oils and other distillate fractions whos
n-paraffins. The feedstock of the present process . will normally be a C20+ feedstock contain:.ng paraffins, olefins, naphthenes, aromaticti and heterocyclic compounds and a substantial proportion of higher molecular weight n-paraffins and slightly branched paraffins which contribute to the waxy nature of the feedstock. During processing, the n-paraffins and the slightly branched paraffins undergo some cracking or hydrocracking to form liquid range materials which contribute to a low viscosity product. The degree of cracking which occurs is, however, limited so that the yield of low boiling products is reduced, thereby preserving the econonic value of the feedstock.
Slack wax can be obtained from either a hydrocracked lube oil or a solvent refined lube oil. Hydrocracking is preferred because that process can also reduce the nitrogen content to low values. With slack wax derived from solvent refined oils, deoiling can be used to reduce the nitrogen content. Optionally, hydrotreating of the slack wax can be carried out to lower the nitrogen content thereof. Slack waxes possess a very high viscosity index, normally in the range of from 140 to 200, depending on the oil content and the starting material from which the wax has been prepared. Slack waxes are therefore eminently suitable for the preparation OJ: lubricating oils having very high viscosity indices, i.e., from about 120 to about HJO.
The present invention provides a unique lube oil product as characterized by its combination of low pour point and high viscosity

index. The lube oil is characterized by a pour point below -24*C (generally between -24*C and -63'C) and a viscosity index between 125 and 180, suitably greater than about 130. Preferably the pour point is below -30*C, more preferably below 40'C, and the viscosity index is greater than about 140.
While the process of the invention can be practiced with utility when the feed contains organic (nitrogen containing impurities), it is preferred that the organic nitrogen content of the feed be less than about 50 ppmw (parts per million by weight), more preferably less than about 10 ppmw. Particularly good results, in terir.s of activity and length of catalyst cycle (period between successive regenerations or start-up and first regeneration) are experienced when the feed contains less than about 10 ppmw of organic nitrogen.
The phrase "intermediate pore size", as used herein means an effective pore aperture in the range of from about 5.3 to about 6.5 A when the porous inorganic oxide is in the calcined form. Molecular sieves having pore apertures in this range tend to have unicjue molecular sieving characteristics. Unlike small pore zeolites such as erionite and chabazite, they will allow hydrocarbons having some branching into the molecular sieve void spaces. Unlike larger pore zeolites such as the faujasites and mordenites, they can differentiate between n-alkanes and slightly branched alkanes, and larger branched alkanes having, for example, ' quaternary carbon atoms.

The effective pore size of the molecular sieves can be measured using standard adsorption techniques and hydrocarbonaceous compounds of known minimum kinetic diameters. See Breck, Zeolite Molecular Sieves. 1974 (especially Chapter 8); Anderson, et al,, J. Catalysis 55./ 114 (1979); and U.S. Patent No. 4,440,871, the pertinent portions of which are incorporated herein by ? reference.
In performing adsorption measurements to determine pore size, standard techniques are vsed. It is convenient to consider a particular molecule as excluded if it does not reach at least 95% of its equilibrium adsorption value on the ir.olecular sieve in less than about 10 minutes (p/pc = 0.5; 25-C).
Intermediate pore size molecular sieves will typically admit molecules having kir.etic diameters of 5.3 to 6.5 A with little hir.drance. Examples of such compounds (and their kinetic diameters in A) are: n-hexane (4.3), 3-methylpentane (5.5), benzene (5.85), and toluene (5.8). Compounds having kinetic diameters of about 6 to 6.5 A can be admitted into the pores, depending on the particular sieve, but do not penetrate as quickly and in some cases are effectively excluded. Compounds having liiinetic diameters in the range of 6 to 6.5 A include: cyclohexane (6.0), 2,3-dimethylbutane (6.1), and m-xylene (6.1). Generally, compounds having , kinetic diameters of greater than about 6.5 A do not penetrate the pore apertures and thus are not absorbed into the interior of the molecular sieve lattice. Examples of such larger compour.ds

include: o-xylene (6.8), 1, 3 , 5-trimethylbeiizene (7.5), and tributylamine (8.1).
The preferred effective pore size range is from about 5.5 to about 6.2 A.
While the effective pore size as discussed above is important to the practice of the invention not all intermediate pore size molecular sieves having such effective pore sizes are advantageously usable in the practice of the present invention. Indeed, it is essential that the intermediate pore size molecular sieve catalysts used in the practice of the present invention have a very specific pore shape and size as measured by X-ray crystallography. First, the intracrystalline channels must be parallel and must not be interconnected. Such channels are conventionally referred to as 1-D diffusion types or more shortly as 1-D pores. The classification of intrazeolite channels as 1-D, 2-D and 3-D is set forth by R. M. Barrer in Zeolites, Science and Technology, edited by F. R. Rodrigues, L. D. Rollman and C. Naccache, NATO ASI Seiries, 1984 which classification is incorporated in its entirety by reference (see particularly page 75). Known 1-D zeolites include cancrinite hydrate, laumontite, mazzite, mordenite and zeolite L.
None of the above listed 1-D pore zeolites, however, satisfies the second essential criterion for catalysts useful in the practice of the present invention. This second essential criterion is that the pores must be generally oval in shape, by which is meant the pores must exhibit two unequal axes referred to herein as a minor axis and a major axis. The term oval as used

herein is not meant to require a specific: oval or elliptical shape but rather to refer to the pores exhibiting two unequal axes. In particular, the 1-D pores of the catalysts useful in the practice of the present invention must have a minor axis between about 4.2 A and about 4.8 A and a major axis between about 5.4 A and about 7.0 A as determined by conventional X-ray crystallography measurements.
The catalyst used in the isomerization
process of the invention has an acidic component
and a platinum and/or palladium hydrogenation
component. In accordance with one embod;Lment of
the invention the acidic component can suitably
comprise an intermediate pore size
silicoaluminophosphate molecular sieve whicli is
described in U.S. Patent No. 4,440,871, the
pertinent disclosure of which is incorporated
herein by reference. '
The most preferred intermediate pore size silicoaluminophosphate molecular sieve for use in the process of the invention is SAPO-11. SAPO-11 comprises a molecular framework of corner-sharing iSiOg) tetrahedra, lAlOj] tetrahedra and {POj] tetrahedra, [i.e., (Si^lyPJOj tetrahedra:. units]. When combined with a platinum or palladium hydrogenation component, the SAPO-11 com^erts the waxy components to produce a lubricating oil having excellent yield, very low pour poi.nt, low viscosity and high viscosity index.
SAPO-11 comprises a silicoaluminophosphate material having a three-dimensional microporous crystal framework structure of [POj], [AlOj] and (SiOj) tetrahedral units whose uni": empirical

formula on an anhydrous basis is:
mR: (Si^lyPJOj (I)
wherein "R" represents at least one organic templating agent present in the intracryistalline pore system; "m" represents the moles of "R" present per mole of (Si^lyP^)02 and has a value of from zero to about 0.3, "x", "y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounded by points A, B, C, D and E on the ternary diagram of Figure 1 or preferably within the are bounded by points a, b, c, d and e on the ternary diagram of Figure 2. The silicoaluminophosphate ha;3 a characteristic X-ray powder diffraction pattern which contains at least the d-spacings (as-synthesized and calcined) set forth below in Table I. When SAPO-11 is in the as-synthesized form "m" preferably has a value of from 0.02 to 0. 3.

All of the as-synthesized SAPO-11 compositions for which X-ray powder diffraction data have been obtained to date have patterns which are within the generalized pattern of Table II belov.
These values were determined by standard techniques. The radiation was the K-alpha doublet of copper and a diffractometer equipped with a scintillation counter and an associated computer was used. The peak heights, I, and the positions as a function of 2 9, where 9 is the Bragg angle, were determined using algorithms on the computer associated with the spectrometer. From these, the relative intensities, 100 I/Ij,, where I, Ls the intensity of the strongest line or peak, and d (obs.) the interplanar spacing in Angstroms, corresponding to the recorded lines, were determined. In the Tables, the relative intensities are given in terms of the symbols vs = very strong, s = strong, m = medium, w = weak, etc.

Another intermediate pore size silicoaluminophosphate molecular sieve preferably used in the process of the invention is SAPO-31. SAPO-31 comprises a silicoaluminophosphate having a three-dimensional microporous crystal framework of [POj], jAlOg] and (SiOjl tetrahedral units whose unit empirical formula on an anhydrous basis is:
mR: (Si^lyPJOj wherein R represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Si^lyPj,)02 and has a value of from zero to 0.3; "x", "y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounced by points A, B, C, D and E on the ternary diagram of Figure 1, or preferably within the area bounded by points a, b, c, d and e on the ternary diagram of Figure 2. The silicoaluminophosphate has a characteristic X-ray powder diffraction pattern (as-synthesized and calcined) which contains at least the d-spacings set forth below in Table III. When SAPO-31 is in the as-synthesized form, "m" preferably has a value of from 0.02 to 0.3.

All of the as-synthesized SAPO-31 compositions for which X-ray powder diffraction data have presently been obtained have patterns whxch are within the generalized pattern of Table IV below.

* Possibly contains peak from a minor impurity.
SAPO-4 1, also suitable for use in the process of the invention, comprises a silicoaluminophosphate having a three-dimensional microporous crystal framework structure cif (PO2], [AlOjl and (SiOjl tetrahedral units, and vrhose unit empirical formula on an anhydrous basis is:

mR: (SiAlyP2)02 wherein R represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Si^lyP^jOj and has a value of from zero to 0.3; "x", "y" and "z" repreisent respectively, the mole fractions of silicon, aluminum and phosphorous, said mole fractions being within the compositional area bounded by points A, B, C, D and E on the ternary d;.agram of Figure 1, or preferably within the area hounded by points a, b, c, d and e on the ternary d^.agram of Figure 2, and said silicoaluminophosphatt'. having a characteristic X-ray powder diffraction jiattern (as-synthesized and calcined) which contcins at least the d-spacings set forth belov; in Table V. When SAPO-41 is in the as-synthesized form "m" preferably has a value of from 0.02 to 0.03.

All of the as-synthesized SAPO-'U composizions for which X-ray powder diffraction data have jsrosently been obtained have patterns which are witliin the generalized pattern of Table VI below.

The process of the invention may also be carried out using a catalyst comprising an intermediate pore size nonzeolitic molecular sieve containing AlOg and POj tetrahedral oxide units, and at least one Group VIII metal. Exemjilary suitable intermediate pore size nonzeolitic molecular sieves are set forth in European patent Application No. 158,977 which is incorpojrated herein by reference.
The group of intermediate pore si:'.e zeolites of the present invention include, ZSM-22, ZSM-23 and ZSM-35. These catalysts are generally considered to be intermediate pore size catalysts based on the measure of their internal structure as represented by their Constraint Index. Zeolites which provide highly restricted access to and egress from their internal structure have a high value for the Constraint Index, whil.e

zeolites which provide relatively free ficcess to the internal zeolite structure have a low value for their Constraint Index, The method for determining Constraint Index is describe-d fully in U.S. Patent No. 4,016,218 which is incorporated herein by reference.
Those zeolites exhibiting a Constraint Index value within the range of from about 1 to about 12 are considered to be intermediate pore size zeolites. Zeolites which are considered to be in this range include ZSM-5, ZSM-11, etc. Upon careful examination of the intermediate pore size zeolites, however, it has been found that not all of them are efficient as a catalyst for isomerization of a paraffin-containing feedstock which are high in C20+ paraffins, and preferably which are high in C22+ paraffins. In particular, it has been found that the group including ZSM-22, ZSM-23 and ZSM-35 used in combination with Group VIII metals can provide a means whereby a hydrocarbon feedstock having a paraffinic content with molecules of 20 carbon atoms or more undergoes unexpectedly efficient isomerization without destroying the ultimate yield of the feedstock.
It is known to use prior art techniques for formation of a great variety of synthetic aluminosilicates. These aluminosilicates have come to be designated by letter or other convenient symbols. One of the zeolites of the present invention, ZSM-22, is a highly siliceous material which includes crystalline thre-a-dimensional continuous framework silicon containing structures or crystals which result

when all the oxygen atoms in the tetrahedra are mutually shared between tetrahedral atoms of silicon or aluminum, and which can exist with a network of mostly SiO2, i.e., exclusive of any intracrystalline cations. The description of ZSM-22 is set forth in full in U.S. Patent No. 4,556,477, U.S. Patent No. 4,481,177 and European Patent Application No. 102,716 the contents of which are incorporated herein by referencie.
As indicated in U.S. Patent No. 4,566,477 the crystalline material ZSM-22 has been designated with a characteristic X-ray di.ffraction pattern as set forth in Table VII.

It should be understood that the X-ray di.ffraction , pattern of Table VII is characteristic of a].l the species of ZSM-22 zeolite compositions. Ion exchange of the alkali metal cations with, other ions results in a zeolite which reveals substantially the same X-ray diffraction pattern

with some minor shifts in interplanar spacing and variation in relative intensity.
Furthermore, the original cations of the as-synthesized ZSM-22 can be replaced at least in part by other ions using conventional ion exchange techniques. It may be necessary to precalcine the ZSM-22 zeolite crystals prior to ion exchange. In accordance with the present invention, the replacement ions are those taken from Group VIII of the Periodic Table, especially platinum, palladium, iridium, osmium, rhodium and ruthenium.
ZSM-22 freely sorbs normal hexane and has a pore dimension greater than about 4 A. In addition, the structure of the zeolite provides constrained access to larger molecules. The Constraint Index as determined by the procedure set forth in U.S. Patent No. 4,016,246 foe 2SM-22 has been determined to be from about 2.5 to about 3.0.
Another zeolite which can be used with the present invention is the synthetic crystalline aluminosilicate referred to as ZSM-23, disclosed in U.S. Patent No. 4,076,842, the contents of which are incorporated herein by reference. The ZSM-23 composition has a characteristic X-ray diffraction pattern as set forth herein in Table VIII.
Other molecular sieves which can ba used with the present invention include, for example, Theta-1, as described in U.S. Patents 4,5 33,649 and 4,836,910, both of which are incorporated in their entireties by reference, Nu-10, as described in European Patent Application 065,400 which is incorporated in its entirety by reference and SSZ-

20 as described in U.S. Patent 4,483,835 which is incorporated in its entirety by reference.

The ZSM-23 composition can also be defined in terms of mole ratios of oxides in the anhydrous state as follows:
(0.58 - 3.4)M2/nO: Al2O3. (40 -250)SiO2 wherein M is at least 1 cation and n is the valence thereof. As in the ZSM-22, the original cations of as-synthesized ZSM-23 can be replaced in accordance with techniques well-known in the art, at. least in part by ionic exchange with other cations. In the present invention these cations include the Group VIII metals as set forth hereinbefore.

The third intermediate pore size zeolite which has been found to be successful in the present invention is ZSM-35, which is disclosed in U.S. Patent No. 4,016,245, the contents of which are incorporated herein by reference. The synthetic crystalline aluminosilicate knovn as ZSM-35, has a characteristic X-ray diffraction pattern which is set forth in U.S. Patent No. 4,016,245. ZSM-35 has a composition which can be defined in terms of mole ratio of oxides in the anhydrous state as follows:
(0.3-2.5) R2jO: (0-0.8) M20:Al203:>8 SiO2 wherein R is organic nitrogen-containing cation derived from ethylenediamine or pyrrolidine and M is an alkali metal cation. The original cations of the as-synthesized ZSM-35 can be removed using techniques well known in the art which includes ion exchange with other cations. In the present invention the cation exchange is used to leplace the as-synthesized cations with the Group VIII metals set forth herein. It has been observed that the X-ray diffraction pattern os ZSM-35 is similar to that of natural ferrierite with, a notable exception being that natural ferrierite patterns exhibit a significant line at 1.33 A.
X-ray crystallography of SAPO-ll, SAPO-31, SAPO-41, ZSM-22, ZSM-23 and ZSM-35 shows these molecular sieves to have the following major and minor axes: SAPO-ll, major 6.7 A, minor 4.4 A; (Benett, J. M., et al, Zeolites, 1, 160(87)), SAPO-31 and SAPO-41, believed to be slightly large than SAPO-ll, ZSM-22, major 5.5 A, minor 4.5 A (Kokotailo, G. T. , et al. Zeolites, i., 349(85)); ZSM-23, major 5.6 A, minor 4.5 A; ZSM-35, major

5.4 A, minor 4.2 A (Meier, W. M. and Olson, D. H., Atlas of Zeolite Structure Types, Butten^orths, 1987) .
The intermediate pore size molecular sieve is used in admixture with at least one Giroup VIII metal. Preferably the Group VIII metal is selected from the group consisting of at least one of platinum and palladium and optionally, other catalyticaliy active metals such as molybdenum, nickel, vanadium, cobalt, tungsten, zinc and mixtures thereof. Most preferably, the The term "metal" or "active metal" as .used herein means one or more metals in the elemental state or in some form such as sulfide, oxide and mixtures thereof. Regardless of the state in which the metallic component actually exj.sts, the

concentrations are computed as if they existed in the elemental state.
The catalyst may also contain metals which reduce the number of strong acid sites on the catalyst and thereby lower the selectivity for cracking versus isomerization. Especially preferred are the Group IIA metals such as magnesium and calcium.
It is preferred that relatively small crystal size catalyst be utilized in practicing the invention. Suitably, the average crystal size is no greater than about 10/ii, preferably no more than about 5/i, more preferably no more than about 1/x and still more preferably no more thai about 0.5M.
Strong acidity may also be reduced by introducing nitrogen compounds, e.g., NH., or organic nitrogen compounds, into the feed; however, the total nitrogen content should be less than 50 ppm, preferably less than 10 ppm. The physical form of the catalyst depends on the type of catalytic reactor being employed and may be in the form of a granule or powder, and is desirably compacted into a more readily usable form (e.g., larger agglomerates), usually with a silica or alumina binder for fluidized bed reaction, or pills, prills, spheres, extrudates, or o;her shapes of controlled size to accord adequate catalyst-reactant contact. The catalyst may be employed either as a fluidized catalyst, or in a fixed or moving bed, and in one or more reaction stages.
The catalytic isomerization step of che invention may be conducted by contacting the feed

with a fixed stationary bed of catalyst, with a fixed fluidized bed, or with a transport bed. A simple and therefore preferred configuration is a trickle-bed operation in which the feed is allowed to trickle through a stationary fixed bed, preferably in the presence of hydrogen.
The catalytic isomerization conditions employed depend on the feed used and the desired pour point. Generally, the temperature is from about 200*C to about 475C, preferably from about 250C and to about 450C. The pressure is typically from about 15 psig and to about 2000 psig, preferably from about 50 to about 1000 psig, more preferably from about 100 psig to about 600 psig. The process of the invention is preferably carried out at low pressure. The liquid hourly space velocity (LHSV) is preferably from about 0.1 to about 20, more preferably from about 0.1 to about 5, and most preferably from about 0.1 to about 1.0. Low pressure and low liquid hourly space velocity provide enhanced isomerization selectivity which results in more isomerization and less cracking of the feed thus producing an increased yield.
Hydrogen is preferably present in the reaction zone during the catalytic isomeriz The intermediate pore size molecular sieve used in the isomerization step provides selective

conversion of the waxy components to non-waxy components. During processing, isomerizeition of the paraffins occurs to reduce the pour point of the oil below that of the feed and form lube oil boiling range materials which contribute to a low pour point product having excellent viscosity index properties.
Because of the selectivity of the intermediate pore size molecular sieve used in the invention, the yield of low boiling products is reduced, thereby preserving the economic value of the feedstock.
The intermediate pore size molecular sieve catalyst can be manufactured into a wide variety of physical forms. The molecular sieves can be in the form of a powder, a granule, or a molded product, such as an extrudate having a particle size sufficient to pass through a 2-mesh (Tyler) screen and be retained on a 40-mesh (Tylttr) screen. In cases wherein the catalyst is: molded, such as by extrusion with a binder, the silicoaluminophosphate can be extruded before drying, or, dried or partially dried and then extruded.
The molecular sieve can be composited with other materials resistant to temperatures; and other conditions employed in the isomeri2:ation process. Such matrix materials include a.ctive and inactive materials and synthetic or natuially occurring zeolites as well as inorganic materials such as clays, silica and metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides.

Inactive materials suitably serve as diluents to control the amount of conversion in the isomerization process so that products can be obtained economically without employing other means for controlling the rate of reaction. The molecular sieve may be incorporated into naturally occurring clays, e.g., bentonite and kaolin. These materials, i.e., clays, oxides, eti:. , function, in part, as binders for the catalyst. It is desirable to provide a catalyst having,good crush strength because in petroleum refining, the catalyst is oft.en subjected to rough handling. This tends to break the catalyst down into powder¬like materials which cause problems in processing.
Naturally occurring clays which can be composited with the molecular sieve include the montmorillonite and kaolin families, which families include the sub-bentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Fibrous clays such as halloysite, sepiolite and attapulgite can also be use as supports. Such clays can be uised in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification.
In addition to the foregoing materials, the molecular sieve can be composited with porous matrix materials and mixtures of matrix naterials such as silica, alumina, titania, magnes;.a, silica-alumina, silica-magnesia, silica-irconia, silica-thoria, silica-beryllia, silica-titania, titania-zirconia as well as ternary compositions

such as silica-alumina-thoria, silica-alumina-titania, silica-alumina-magnesia and stl:.ca-magnesia-zirconia. The matrix can be in the form of a cogel.
The catalyst used in the process of this invention can also be composited with other zeolites such as synthetic and natural fe.ujasites, (e.g., X and Y) erionites, and mordenites. It can also be composited with purely synthetic zeolites such as those of the ZSM series. The coirbination of zeolites can also be composited in a porous inorganic matrix.
It is often desirable to use mild hydrogenation referred to as hydrofinishing after isomerization to produce more stable lubricating oils. Hydrofinishing is typically conducted at temperatures ranging from about 190'C to about 340'C, at pressures from about 400 psig to about 3000 psig, at space velocities (LHSV) from about 0.1 to about 20, and hydrogen recycle ratiss of from about 400 to about 1500 SCF/bbl. The hydrogenation catalyst employed must be active enough not only to hydrogenate the olefins;, diolefins and color bodies within the lubt; oil fractions, but also to reduce the aromatic; • content. The hydrofinishing step is beneficial in preparing an acceptably stable lubricatinc oil.
Suitable hydrogenation catalysts ir.clude conventional metallic hydrogenation catalysts, particularly the Group VIII metals such as cobalt, nickel, palladium and platinum. The metals are typically associated with carriers such as bauxite, alumina, silica gel, silica-alumina composites, and crystalline aluminosilicate

zeolites. Palladium is a particularly preferred hydrogenation metal. If desired, non-noble Group VIII metals can be used with molybdates. Metal oxides or sulfides can be used. Suitable catalysts are disclosed in U.S. Patent Nos. 3,852,207; 4,157,294; 3,904,513 and 4,673,487, which are incorporated herein by reference.
The high viscosity index lube oil produced by the process of the present invention can be used as a blending component to raise the: viscosity index of lube oils to a higher value. Since yield decreases with increasing viscosity index in either hydrocracking or solvent refining, the use of an isomerized wax to increase the viscosity index improves yield.
The invention will be further clamified by the following examples, which are intendsid to be purely exemplary of the invention.
The wax content of the oil set forth in the . following Examples was determined as follows:
300 g of oil was diluted 50/50 with a 4:1 mixture of methyl ethyl ketone and toluene which was cooled to -20*C in a refrigerator. The mixture was filtered through a Coors funnel at -15'C using Whatman No. 3 filter paper. The wax was removed from the filter and placed in a tared 2 liter flask. The solvent was removed cin a hot plate and the wax weighed.
Example 1
SAPO-11 was prepared as follows:
472.4 g of 85% H3PO4 were added to 1208 g of
distilled HgO in a Teflon beaker in an ice bath.
816.8 g of aluminum isopropoxide (AlfOCjH.la) were

slowly added with mixing and then mixed until homogenous. Then 120 g of fumed silica (Cabosil M-5) were added with mixing. Next, 182.4 g of di-n-propylamine (PrgNH) were added, followed by 9.0 g of 8 5% H3PO4. Final mixing was done using a Polytron. The mixture had a pH of 6.5 and the following composition, expressed in molar ratio of oxides:

The mixture was placed in a Teflon bottle in a stainless steel pressure vessel and heated for 5 days at 200*C with no stirring and autogenous pressure. The supernatant liquid was removed and the product was filtered, washed with water, dried overnight at 12 1'C, and calcined in air for 8 hours at 566'C. The average crystallite siZje was less than 0.5 micron. The product was identified as SAPO-11 by X-ray diffraction analysis. Elemental analysis of the calcined sieve showed it to have the following anhydrous molar composition:

The sieve was bound with 35% Catat>al alumina and made into 1/10 inch extrudate. The extrudate was dried 3 hours at 121 *C, calcined in air for 4 hours at 454*C, then impregnated with 0.5% Pt (as Pt(NH3)4Cl2.H20) by the pore-fill method, It was then dried for 2 hours at 93*C, 2 hours at 149'C, and calcined in air for 8 hours at 454*C. For the following examples, the catalyst was crushed and screened to 24-42 mesh.

Example 2
The catalyst of Example 1 was used to isomerize a 800*F+ hydrocracked waxy vacuum gas oil (Table IX) at 2200 psig, 1 LHSV, and 8 M SCF/bbl once-through H2. The catalyst was also run at 400 psig. The results are set forth in Table X and demonstrate that high lube yield at very low pour point is achieved by the present process. The data also evidences the substantial yield benefit from operating at a lower reactor pressure. Lube yield is

defined as gfproduct) x 100% where the product g(feed)
has the same 5 LV% boiling point as the feed.
Example ,3
The catalyst of Example 1 was used to isomerize a slack wax derived from a 900'F+ hydrocracked vacuum gas oil (Table XI). Conditions were 160 psig reactor pressure, 0.3 LHSV, and 8 M SCF/bbl once-through Hj. At a catalyst temperature of 680*F, a -27*C pour point oil of 7.1 est viscosity at lOO'C and 149 . viscosity index was produced. Pour point reduction could be increased by raising che catalyst temperature. Figure 3 shows a plot of 700'F-t- lube yield versus pour point, where 700*F + lube yield is defined as:

Figure 4 shows a plot of viscosity index versus pour point.
A -30*C pour point oil prepared in this example was subsequently hydrofinished over a 0.5% Pd on silica-alumina catalyst at 500'F, ;>200 psig.

0.25 LHSV, and 8 M SCF/bbl H2. Inspections of the hydrofinished oil are given in Table XVI .
Example 4
The catalyst of Example 1 was used to isomerize a deoiled slack wax derived from a 700-800'F solvent refined vacuum gas oil (Table XII). Conditions were 160 psig, 0.3 LHSV, and 8 M SCF/bbl once-through H2. The results are set forth in Table XIII.
Example 5
The catalyst of Example 1 was used to isomerize a deoiled slack wax derived fr

Example 6
ZSM-22 was prepared as follows:
The following reactants were combined to produce a gel: N,N'-dimethyl imidazolium hydroxide, Ludox AS-30 silica sol, aluminum sulfate, sodium hydroxide, and water in the ratios:
SiO2/Al2O3 = 100
H2O/SiO2 =30
template/SiO2 =0.15
NaOH/SiO2 = 0. 10
OH-SiO2 = 0.2 5
The reaction was run at autogenous pressure in a stainless steel autoclave at 150'C for 6 days. The product was filtered, calcinated to lOOO'F in air, ion-exchanged four times with excest; NH4NO3 and calcined again to lOOO'F. The product was identified by X-ray diffraction analysis as ZSM-22. The SiO2/Al2O3 mola ratio was about 100. The sieve was bound with 35% Catapal and the extrudate impregnated

with 1% Pt and calcined in the same manner as the catalyst of Example 1.
Example 7
The catalyst of Example 6 was used to isomerize the slack wax of Table XI at 500 psig, 0.3 LHSV, and 8M SCF/bbl once-through Hg. The results are set forth in Table XVII.
Example 9
The catalyst of Example 6 was mixed with a 10-fold excess of 5 wt. % Mg CO3 in water, filtered, dried for 18 hours at 93'C, and calcined for 12 hours at 538'C. The Mg content was 22.7 wt.%. This catalyst was used to isomerize the slack wax of Table XI at 0.3 LHSV and 8 MSCF/bbl H2, both at 500 psig and 160 psig. The results are set forth in Table XVIII, showing a higher yield for this catalyst than

that of Example 6 without Mg. The beneficial effect of low pressure on yield is also shown.
Example 9
The catalyst of Example 6 was used to isomerize a deoiled slack wax derived from a 900'F+ solvent refined vacuum gas oil (Table XIX). Conditions were the same as Example 7. The results are set forth in Table XX.
. Example 10
The catalyst of Example 8 was used to isomerize a slack wax (not deoiled) derived from a 700-800*F solvent refined vacuum gas oil (the same ^used to prepare the feed of Table XII). Inspections of the feed are given in Table XXI. Isomerization conditions were the same as; in Example 7. The results are set forth in Table XXII.
Examplg 11
ZSM-23 was prepared as in U.S. Pat:ent No. 4,076,842, and identified as such by X-rc.y diffraction analysis after calcination at. lOOO'F in air. It was exchanged four times with excess NH4N03 and calcined again at lOOO'F. The sieve was impregnated with 0.5% Pt and calcined in the same manner as the catalyst of Example 1.

Example 12
The catalyst of Example 11 was used to isomerize the feed of Table XI at 0.3 LHSV, 500 psig, and 8 MSCF/bbl H2. The results are set forth in Table XXIII.
Example 13
The catalyst of Example 8 was used to isomerize a C30+ normal alphaolefin wax (Table XXIV) at 0.3 LHSV and 8 MSCF/bbl Hj, both at 500 psig and 300 psig. The results are set forth in Table XXV.

While the invention has been described in connection with specific embodiments thereof, it will be understood that it is capable of further modification, and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure as come within known or customary practice in the art to which the invention pertains and as may be applied to the essential features hereinbefore set forth, and as fall within the scope of the invention and the limits of the appended claims.

We Claim:
1. A process for producing lube oil comprising isomerizing a waxy feed having a wax content of greater than 50% and/or having a pour point above 0C and having greater than 70% paraffinic carbon over a silicoaluminophosphate catalyst comprising (a) nonzeolitic molecular sieve containing AlO2 and PO2 tetrahedral oxide units having oval 1-D pores with a minor axis between 4.2 A and 4.8 A and a major axis between 5.4 A and 7.0A and (b) at least one Group VIII metal at a pressure of from 15 psig to 2000 psig.
2. The process as claimed in claim 1, wherein said waxy feed contains at least 80% wax.
3. The process as claimed in claim 1, wherein said waxy feed contains at least 80% paraffinic carbon.
4. The process as claimed in claim 1, wherein said waxy feed is selected from the group consisting of gas oil stock, lubricating oil stock, synthetic oil, foots oil, slack wax, deoiled wax, normal alphaolefin wax and microcrystalline wax.
5. The process as claimed in claim 1, wherein the liquid hourly space velocity during isomerization is from 0.1 to 20.
6. The process as claimed in claim 1, wherein the isomerized lube oil is optionally hydrofinished.

7. A process for producing lube oil, substantially as hereinabove described and illustrated, with reference to figures 2 and 3 of the accompanying drawings

Documents:

0074-mas-1996 abstract.pdf

0074-mas-1996 claims.pdf

0074-mas-1996 correspondence -others.pdf

0074-mas-1996 correspondence -po.pdf

0074-mas-1996 description (complete).pdf

0074-mas-1996 drawings.pdf

0074-mas-1996 form-1.pdf

0074-mas-1996 form-26.pdf

0074-mas-1996 form-4.pdf

0074-mas-1996 petition.pdf

« Previous Patent

Next Patent »

Patent Number

188403

Indian Patent Application Number

74/MAS/1996

PG Journal Number

30/2009

Publication Date

24-Jul-2009

Grant Date

27-Jun-2003

Date of Filing

16-Jan-1996

Name of Patentee

M/S. CHEVRON RESEARCH AND TECHNOLOGY COMPANY

Applicant Address

555 MARKET STREET, SAN FRANCISCO, CALIFORNIA 94105

Inventors:

#	Inventor's Name	Inventor's Address
1	STEPHEN J MILLER,	520-45TH AVENUE, SAN FRANCISCO, CA 94121

PCT International Classification Number

C10G 73/38

PCT International Application Number

N/A

PCT International Filing date

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1			NA