Title of Invention

"AN IMPROVED PROCESS FOR THE PREPARATION OF POLYORETHANE SPHERICAL PARTICLE"

Abstract

An improved process for the preparation ofpolyurethane spherical particles of size ranging from 100nm to l000microns, which comprises reacting a diol and an organic dilsocyanate and optionally a multifunctional hydroxyl compound in presence of a polycondensable macro monomer such as herein described and a catalyst such as herein described in an organic solvent under stirring condition and agitator speed of 200-800rpm at temperatures ranging from 40 to 100°C for a period ranging between 2 and 12 hours, separating the spherical polyurethane particles from the reaction mixture by conventional methods to get the desired product.

Full Text

The present invention relates to a process for the preparation of polyurethane in spherical particle form-with controlled particle size_and shape. More particularly it relates to the production of polyurethane microspheres from a diol and diisocyanate by dispersion polymerization in presence of a steric stabilizer particularly a polycondensable macromonomer having formula (I) in the drawing accompanying the specification. Polyurethane particulates obtained by this invention are suitable for a wide variety of useful applications such as coatings, adhesives and also an encapsulant material for pigments, agrochemicals, drugs and reactive chemicals like curing agents. In prior art, polyurethane powders are prepared by cryogenic grinding or extrusion and granulation of thermoplastic polyurethanes. (U.S.Pat. 3214411; JP-02-124978). JP 03- ' 181526 discloses a process for producing polyurethane microparticles by dissolving polyurethane resin in amino alcohol at 130 to 150°C followed by cooling, filtering and drying under vacuum. In another method (JP 04-248875), hydroxyl and/or amino group containing resin is reacted with blocked isocyanates in a suitable solvent at elevated temperature. The solvent is femoved under reduced pressure. The polyurethane powder obtained is filtered and dried. These techniques however, do not yield polyurethane powder in controlled particle size and shape. Spherical polyurethane particles are prepared by suspension polymerization of an isocyanate terminated prepolymer in aqueous or non-aqueous medium. U.S.Pat. 4083831 describes oil in water suspension polycondensation technique wherein an isocyanate terminated prepolymer is suspended in aqueous media. The reaction proceeds in aqueous medium and produces polyurethane urea powder which is stabilized by a combination of anionic and homopolymeric stabilizers. In an another variant, polyurethane spherical particles are obtained by suspension polycondensation in non- aqueous media (U.S. Pat. 4032516). In this art, the isocyanate terminated prepolymer is suspended in paraffin oil using sodium dodecylsulfosuccinate as a stabilizer. The chain extension was carried out with 1,4-butane diol in n-heptane and in the presence of an amphiphilic block copolymer namely 1-hexadecane vinylpyrrolidone as steric stabilizer. Stabilization of polyurethane spherical particles in aqueous and non-aqueous medium is known in the prior art. For instance, JP 04-225755; JP 03-31359 and JP 04-202311 describes the use of a stabilizer derived from polycaprolactone, polybutadiene and isophrone diisocyanate to prepare polyurethane powder in n-heptane. In yet another application JP 02-38453 discloses the preparation of stabilizers derived from poly (butylene adipate), maleic anhydride and lauryl methacrylate. In addition to these block copolymers, protective colloids such as polyvinyl alcohol, methylcellulose, gelatin, sodium alkyl sulfate are also employed to stabilize polyurethane microspheres (JP 04-161416). Polyurethane spherical particles obtained by this prior art are polydisperse and their size ranging between 1 and 1000 p. even at higher stabilizer concentrations. Furthermore, none of the application uses diol and diisocyanate directly. Instead, an isocyanate terminated prepolymer is used to produce polyurethane microspheres. The object of the present invention is to provide a process for preparing polyurethane microspheres with controlled particle size from a diol and a diisocyanate. Another object of this invention is to stabilize polyurethane particles using a polycodensable macromonomer, particularly a macrodiol, which is enchained in the polymer backbone and stabilizes the polyurethane particles. Yet another object of the present invention is to produce polyurethane particles of size ranging from 100 nm to 1000 fa by varying the concentration of the stabilizer. Accordingly, the present invention provides an improved process for the preparation of polyurethane spherical particles of size ranging from l00nm to l000microns, which comprises reacting a diel and an organic diisocyanate and optionally a multifunctional hydroxyl compound in presence of a polycondensable macro monomer such as herein described and a catalyst such a herein described an organic solvent under stirring condition and agitator speed of 200-800rpm at temperatures ranging from 40 to 100°C for a period ranging between 2 and 12 hours, separating the spherical polyurethane particles from the reaction mixture by conventional methods to get the desireffproduct. .In an embodiment of the present invention the diols used are isocyanate reactive which are exemplified by ethylene glycol, 1,2-propyleneglycol, 1,3-propyleneglycol, diethylene glycol, 1,4-butane diol, 1,3-butane diol, 1,6-hexane diol, 2-ethyl-l,3-hexane diol, 1,8-octane diol, neopentyl glycol, 2-methyl-l,3- propane diol and 1,4-cyclohexane dimethanol trimethyloi propane, ditrimethylol propane, 1,2,6-hexane triol (its isomers), pentaerythrytol, di and tripentaerythrytol, sorbitol and glycerine and polyols such as polyether diol, polyester diol, polycaprolactone diol, hydroxyl terminated polybutadienc with 2 or more hydroxyl group and hydroxyl number ranging between 50 and 100 mg KOH/gm and acid number preferably less than 2 mg. KOH/ gm with number average molecular weights ranging from 200 to 3000. In another embodiment the diisocyanates used may be selected from 2,2,4-trimethyl hexamethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), 4,4'-methylene-bis- (cyclohexane diisocyanate), meta or para- tetramethyl xylene diisocyanate, a, a'-xylylene diisocyanate, toluene diisocyanate, 1,4 phenylene diisocyanate, 4,4'-diphenyl methane diisocyanate, meta or para- tetramethyl xylene diisocyanate and higher polyfunctional isocyanates like 2,4,6-triisocyanato toluene, 4,4',4"- triisocyanate triphenyl methane, 1,2,4- benzene triisocyanate, biurets of diisocyanates, trimer of HDI, IPDI and TMP adducts of TDI.IP.DI, HDI, MDI, TMXDI and the like. In yet another embodiment of the present invention, the polycondensable macromonomer, particularly a macrodiol, contains a long chain hydrophobic moiety with reactive hydroxyl groups at the chain terminal, as mentioned in formula (I) in the drawing accompanying the specification, wherein R = an alkyl group with 1 -40 carbon atoms R1 = hydrogen or methyl R2 = alkylene units X = bifunctional moiety F - functional group n = 3-45;m = ≥2 The preparation of which have been claimed and disclosed in our copending application 1635del98. In still another embodiment the catalyst used enhances the isocyanate - hydroxyl reaction and may be selected from triethylene diamine, morpholine, N-ethylmorpholine, piperazine, triethanolamine, triethylamine, dibutyltindilaurate, stannous octoate, dioctyl tin di acetate, lead octoate, stannous tallate and dibutyltindioxide. In another embodiment of the present invention, the organic solvent used may be are isocyanate non reactive and good solvent for the monomers and non-solvent for the polymer particles, which are exemplified by aliphatic hydrocarbons such as hexane, heptane, octane, decane, isooctane, dodecane, hexadecane, superior kerosene, paraffin oil, white mineral oil, and aromatic hydrocarbons such as benzene, toluene, xylene and the like or a suitable mixture of aliphatic and aromatic hydrocarbons. In a feature of the present invention, the ratio of isocyanate to diol is maintained between 1 and 2, more preferably in the range from 1.05 to 1.5. The amount of macrodiol varies from 1 to 25 percent, preferably from 3 to 18 percent based on the total quantity of urethane forming reactants. The amount of catalyst is in the range from 0.005 to 1 weight percent based on the total amount of diol and diisocyanate. The ratio of monomer to organic continuous phase is between 5 and 50 and preferably in the range from 10 to 30. The polymerization can be carried out in any conventional resin reactor equipped with a cooling jacket, a double walled condenser, a thermowell, an inlet tube for nitrogen gas purging and an addition funnel for monomer feeding. Stirring can be done by using any conventional stirring device. The agitator speed may be in between 200 and 800 revolutions per minute (rpm). The polymerization reaction can be carried out between 40°C and 100°C and more preferably between 60°C and 90°C. The reaction time is typically between 3 and 10 hours. The conversion of isocyanate is in the range between 82 and 100 percent. The polyurethane microspheres formed at the end of the reaction is washed thoroughly with a low boiling aliphatic hydrocarbon particularly hexane and dried at room temperature under vacuum. The particle size of the polyurethane microsphere ranges from 150 nm to 500 µ. depending on the concentration of the macrodiol stabilizer. The process of the present invention is described by the following examples which are illustrative only and should not be construed to limit the scope of the application in any manner. Example 1 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.38 g macrodiol (derived from polylauryl methacrylate of molecular weight 2000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3- hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hexane to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder. Example 2 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.76 g macrodiol (derived from polylauryl methacrylate of molecular weight 2000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3-hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hexane to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder. Example 3 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 1.14 g macrodiol (derived from polylauryl methacrylate of molecular weight 2000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3-hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres' formed was washed with hexane to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder with average particle size 1.2 microns Example 4 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.38 g macrodiol (derived from polylauryl methacrylate of molecular weight 5000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3-hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hexane to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder. Example 5 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.76 g macrodiol (derived from polylauryl methacrylate of molecular weight 2000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3-hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hexane to remove paraffin oil'and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder with average particle size 220 nm. Example 6 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 1.14 g macrodiol (derived from polylauryl methacrylate of molecular weight 5000), 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3-hexane diol and 4.6 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hexane to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder with average particle size180 nm. Example 7 In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.25 g macrodiol (derived from polylauryl methacrylate of molecular weight 2000), 0.38 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 1.5 g polyester diol (number average molecular weight 750) and 0.45 g toluene diisocyanate were added. The reaction was continued for 5h. The polyurethane microspheres formed was washed with hcxanc to remove paraffin oil and it is dried under vacuum at room temperature for about 4 h to obtain a free flowing polyurethane powder. Example 8 (comparative example) In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-1,3-hexane diol and 4.6 g toluene diisocyanate were added. After a period of 10 minutes the reaction mixture was gelled and large lumps were seperated out from the paraffin oil medium. Example 9 (comparative example) In a four neck 250 mL round bottom flask fitted with a stirrer, condenser, nitrogen inlet and a thermowell, 1.14 g carboxyl terminated polylauryl methacrylate of molecular weight 5000, 0.5 g of 1% dibutyl tin dilaurate in paraffin oil and 25 g paraffin oil were added and stirred at 500 rpm. The mixture was then heated to 65°C and 3 g 2-ethyl-l,3- hexane diol and 4.6 g toluene diisocyanate were added. After a period of 10 minutes the reaction mixture was gelled and large lumps were seperated out from the paraffin oil medium. The two comparative examples suggest that polyurethane in powder form cannot be prepared without the use of the stabilizer described herein. We Claim: 1. An improved process for the preparation of polyurethane spherical particles of size ranging from l00nm to l000microns, which comprises reacting a die and an organic diisocyanate and optionally a multifunctional hydroxyl compound in presence of a polycondensable macro monomer such as herein described and a catalysl such sa herien described is in an-organic solvent under stirring condition and agitator speed of 200-800rpm at temperatures ranging from 40 to 100°C for a period ranging between 2 and 12 hours, separating the spherical polyurethane particles from the reaction mixture by product. 2. The process as claimed in claim 1 wherein, the diols may be isocyanate reactive which are selected form ethylene glycol, 1,2-propyleneglycol, 1,3-propyleneglycol, diethylene glycol, 1,4-butane diol, 1,3-butane diol, 1,6-hexane diol, 2-ethyl-1,3- hexane diol, 1,8-octane diol, neopentyl glycol, 2-methyl-l,3- propane diol and 1,4- cyclohexane dimethanol trimethylol propane, ditrimethylol propane, 1,26-hexane triol (its isomers), pentaerythrytiol, di and tripentaerythrytol, sorobitol and glycerine and polyols such as polyether diol, polyester diol, polycaprolactone diol, hydroxyl terminated polybutadine with 2 or more hydroxyl group and hydroxyl number ranging between 50 and 100 mg KOH/gm and acid number preferably less thn 2 mg. KOH/ gm with number average molecular weights ranging from 200 to 3000. 3. The process as claimed in claim 1, wherein the diisocyanates are selected from 2,2,4- trimethyl hexamethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6- hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), 4,4'- methylene- bis- (cyclohexane diisocyaate), meta or para- tetramethyl xylene diisocyanate, a, a'- xylylene diisocyanate, toluene diisocyanate, 1,4 phenylene diisocyanate, 4,4'- diphenyl methane diisocyanate, meta or para- tetramethyl xylene diisocyanate and higher polyfunctional isocyanates like 2,4,6-triisocyanato toluene, 4,4', 4"- triisocyanate tripheny! methane, 1,2,4- benzene tri isocyanate, biurets of diisocyanates, trimer of HDI, IPDI and TMP adducts of TDI, IPDI, HDI, MDI, TMXDI and the like. 4. The process as claimed in claim 1 wherein, the polycondensable macro monomer, particularly a macrodiol, and more particularly contains a long chain hydrophobic moiety with reactive hydroxyl groups at the chain terminal, as mentioned in formula (I) in the drawing accompanying the specification, wherein. R = an alkyl group with 1-40 carbon atoms R1 = hydrogen or methyl R2 = alkylene units X = bifunctional moiety F = functional group N = 3-45 5. The process as claimed in claim 1 wherein, the catalysts used are selected from triethylene diamine, morpholine, N-ethylmorpholine, piperazine, triethanolamine, triethylamine, dibutylindilaurate, stannous octoate, dioctyl tin di acetate, lead octoate, stannous tallate and dibutyltindioxide. 6. The process as claimed in claim 1, wherein the organic solvent used are isocyanate non-reactive, non-solvent for the polymer particles, such as aliphatic hydrocarbons such as hexane, heptane, octane, decane, isooctane, dodecane, hexadecane, superior kerosene, paraffin oil, white mineral oil, molex raffinate and aromatic hydrocarbons such as benzene, toluene, xylene or a suitable mixture of aliphatic and aromatic hydrocarbons. 7. The process as claimed in claim 1 wherein, the ratio of isocyanate to diol is maintained between 1.05 to 1.5. 8. The process as claimed in claim 1 wherein, the amount of macrodiol varies from 3 to 18 weight percent based on the total quantity of urethane forming reactants. 9. The process as claimed in claim 1 wherein, the amount of catalyst is in the range from 0.005 to 1 weight percent based on the total amount of diol and diiscoyante. 10. The process as claimed in claim 1 wherein, the ratio of monomer to organic continuous phase is between 10 and 30. 11. The process as claimed in claim 1 wherein, the size of polyurethane spherical particle ranges from 150nm to 500microns. 12. The process for the preparation of polyurethane micro spheres by dispersion polymerization using a polycondensable macro monomer substantially as herein described with reference to examples.

Documents:

1634-del-1998-abstract.pdf

1634-del-1998-claims.pdf

1634-del-1998-correspondence-others.pdf

1634-del-1998-correspondence-po.pdf

1634-del-1998-description (complete).pdf

1634-del-1998-drawings.pdf

1634-del-1998-form-1.pdf

1634-del-1998-form-19.pdf

1634-del-1998-form-2.pdf

1634-del-1998-form-3.pdf

1634-del-1998-petition-138.pdf