Title of Invention

A PROCESS FOR THE PRODUCTION OF A SUSPENSION OF CELLULOSE IN A LIQUID AQUEOUS TERTIARY AMINE-OXIDE"

Abstract

The invention is concerned with a process for the production of a suspension of cellulose in a liquid, aqueous tertiary amme-oxide, wherein shredded cellulose is mixed with said Liquid, aqueous tertiary amine-oxide, said process comprising: (A) contacting the shredded cellulose with the liquid, aqueous tertiary amine-oxide, a first mixture being prepared, and (B) spreading this first mixture mechanically as a layer on a surface and transporting it along this surface while intensively being mixed, until a homogeneous suspension is produced which is removed from the surface, wherein (C) measures (A) and (B) are carried out continuously.

Full Text

The present invention relates to a process for the production of a suspension of cellulose in a liquid aqueous tertiary amine-oxide. The present invention is concerned with a process for the production of a suspension of cellulose in a tertiary amine-oxide which is present in liquid state, as well as a process for the production of cellulose moulded bodies such as films, fibres and membranes. For some decades there has been searched for processes for the production of cellulose moulded bodies able to substitute the viscose process, today widely employed. As an alternative which is interesting among other reasons for its reduced environmental impact, it has been found to dissolve celluslose without derivatisation in an organic solvent and extrude from this solution moulded bodies, e.g. fibres, films and membranes. Fibres thus extruded have received by BISFA (The International Bureau for the Standardization of the man made fibres) the generic name Lyocell. By an organic solvent, BISFA understands a mixture of an organic chemical and water. It has turned out that as an organic solvent, a mixture of a tertiary amine-oxide and water is particularly appropriate for the production of cellulose moulded bodies. As the amine-oxide, primarily N-methylmorpholine-N-oxide (NMMO) is used. Other amine-oxides are described e.g. in EP-A-0553070. A process for the production of mouldable cellulose solutions is known e.g. from EP-A-0 356 419. In US-A-4,246,221, an amine-oxide process for the production of spinnable cellulose solutions using as starting material, among other substances, a mixture of cellulose in liquid, aqueous N-methylmorpholine-N-oxide (NMMO) is described. According to this process, a suspension of cellulose in the aqueous amine-oxide solution is prepared in a discontinuously operating mixing device, the mixture being simultaneously heated at reduced pressure, while water is withdrawn and a first solution prepared, which after filtration and postprocessing in an extruder is transformed into a mouldable solution. A disadvantage of this known process is the discontinuous preparation of the cellulose suspension in the mixer. This discontinuous initial step makes the amine-oxide process as a whole discontinuous, which is disadvantageous, since any moulding process such as spinning to fibres is best carried out continuously. From WO 94/28217, a process for the production of a premixture based on cellulose, wherefrom a mouldable cellulose solution may be prepared, is known. According to this process, shredded cellulose and an amine-oxide solution are introduced into a horizontal cylindrical mixing chamber with a rotor having axially spaced stirring elements. The mixture is stirred in the mixing chamber by rotating the rotor at a rate of from 40 to 80 revolutions per minute. Preferably, the mixture in the mixing chamber is kept at a temperature of above 65°C. This process however has the following drawbacks: The process is very time-consuming, since among other things the amine-oxide solution and the cellulose cannot be introduced into the mixing chamber at once, bur must be introduced one after the other.. 2 . Another drawback of the process consists in that it may be carried out only discontinuously, each batch requiring approximately 21 minutes. 3 Due to the discontinuous operation, two such mixers must be operated in order to deliver the cellulose/amine-oxide mixture continuously to a device wherein the cellulose solution is produced and continuously delivered to e.g. a spinning machine. 4 . The use of two mixers implies that every device such as storing tanks, conducts, pumps, filters etc. provided between the mixers and the spinning machine must also be present twice, evidently involving a considerable additional technical and financial effort. 5. Another drawback lies in the fact that relatively big amounts of amine-oxide are processed per batch. These big amounts imply a safety risk, since; tertiary amine-oxides are unstable and tend to decompose at elevated temperature. 6. Moreover, discontinuously operated mixers are difficult to empty. Thus it is the object of the present invention to provide a process not exhibiting the drawbacks mentioned above, according to which a homogenous cellulose suspension may be produced in a single step and at a high rate from shredded cellulose and an aqueous amine-oxide solution, which homogeneous cellulose suspension can be as a starting material for the amine-oxide process. According to the present invention there is provided a process for the production of a suspension of cellulose in a liquid aqueous tertiary amine-oxide said suspension to be used for the production of a mouldable cellulose solution, said soluciton to be used for the production of cellulose moulded bodies, wherein shredded cellulose is mixed with said liquid, aqueous tertiary amine-oxide, characterized in that (A) said shredded cellulose is contacted with said liquid aqueous tertiary amine-oxide, a first mixture being prepared, and (B) said first mixture is spread mechanically as a layer on a surface and transported along said surface while intensively being mixed, until a homogeneous suspension is produced which is removed from said surface, wherein (C) wherein (A) and (B) are being carried out continuously. The invention is based on the finding that by employing the film technique, particularly the thin-film technique, a homogeneous cellulose suspension may be produced in a simple and rapid way. Furthermore, it has been shown that in the process according to the invention it is also readily possible to add homogeneously, together with the cellulose, auxiliary agents such as stabilizers, dispersants, auxiliary spinning agents, reactivity-improving reagents, incorporation media of an inorganic or organic nature (barite, activated carbon, SiO2, CMC, modifiers (polyethyleneglycoles) and other polymers such as nylon; dyes. This is of decisive importance for these auxiliary agents to develop their maximum effect. Furthermore, it has been shown that such an addition does not sxow down the production of the homogeneous suspension. Another advantage of the process according to the invention consists in that as the liquid, aqueous tertiary amine-oxide wherein the shredded cellulose is suspended, an aqueous solution of the tertiary amine-oxide which is liquid at room temperature and a molten tertiary amine-oxide hydrate may be employed. In the process according to the invention, a liquid, aqueous tertiary amine-oxide having a temperature in the range of from 5 0 to 85°C is preferably employed. According to the process according to the invention, the cellulose is transported along the surface preferably during a time perid of from 1 to 5 minutes. This means that the cellulose suspension is obtained in a homogeneous form and in a continuous way already within a few minutes. Thus the process according to the invention represents a considerable simplification of the amine-oxide process. The invention is also concerned with the use of a device for carrying out the process according to the invention having an indirectly heatable or coolable vessel provided with a stirring element, said vessel being a cylindrical vessel provided with a centrally arranged rotor having stirring elements attached thereto, said stirring elements having an inclination angle a towards the axis of the rotor for mixing and transporting the cellulose contacted with the liquid aqueous tertiary amine-oxide, the radial distance of the stirring elements to the internal wall of the vessel amounting to not more than 2 0 mm and inlets for the shredded cellulose and the liquid aqueous tertiary amine-oxide being provided in the upper part of the vessel and an outlet for the homogeneous suspension being provided in the lower part of the vessel. Preferably, a device wherein the inclination angle a is adjustable is used. The invention is further concerned with a process for the production of a mouldable cellulose solution, characterized m that a homogeneous suspension produced according to the process according to the invention is transformed into a mouldable cellulose solution while water is evaporated. The piroduction of the cellulose solution is conveniently carried out in a thin-film treatment apparatus. Such a process is described for instance in EP-A - 0 356 419. An embodiment of a thin-film treatment apparatus is for instace a so-called filmtruder, as made by the company Buss AG (Switzerland). A thin-film treatment apparatus is also describesd in DE-OS 2 Oil 49 3. WO 94/06530 published in 1994 uses the thin-film technique known from EP-A - 0 356 419 to obtain a mouldable solution from a mixture of cellulose in an aqueous solution of a tertiary amine-oxide. The process is carried out in a iiilmtruder, analogously to an embodiment described in EP-A -o 356 419. The process of WO 94/06530 has as its object to save energy, and to solve this object it proposes to rotate the rotor more slowly. Further, "he present invention is concerned with a process for the production of cellulose moulded bodies consisting in the transformation of a cellulose suspension produced according to the invention into a mouldable cellulose solution, which subsequently is processed into films, fibres membranes or other moulded bodies in a substantially known By means of a dosing apparatus, the suspension prepared according to the invention may be fed directly to the filmtruder, therein being transformed into a solution- A degassing extruder is also appropiate for preparing the solution. In the latter case however, the suspension must be present in concentrated state, since a degassing extruder has only a very reduced evaporation capacity. The suspension prepared according to the invention may be transformed into the cellulose solution also by means of other devices. Farther, before being transformed into the solution, the suspension may be additionally subjected to a grinding step. By means of the attached drawing, a device wherein the process according to the invention may be carried out in a particularly appropiate way is described. The drawing schematically shows the configuration of a mixer used according to the invention. Such mixers are commercialized tor instance as ring layer mixer by the company Draiswerke GmbH, Mannheim, Germany, under the name K-TT. The Figure schematically shows a longitudinal section of a Horizontally mounted mixer, consisting substantially of a cylindrical vessel 1 having a double jacket for indirect Heating or cooling of thej material to be processed, a rotor ' The shredded cellulose is introduced into the cylindrical vessel 1 through inlet 6, seized by the transport blades 3 and transported into the interior of vessel 1, rotor 2 being rotated so rapidly that the shredded cellulose, due to centrifugal force, is thrown by the transport blades to the cylindrical wall of the vessel, therein being transported as a Layer into the interior of vessel 1. The liquid, aqueous amine-oxide solution is fed to the vessel througn inlet pipe 7. Inlet pipe 7 extends nearly to rotor 2 and is disposed in a gap between neighbouring transport blades and spiniform elements, so that the rotation of rotor 2 is not impeded. Due to the centrifugal force conferred to the amine-oxide solution, it is thrown radially outwards, fxrst wetting the cellulose, a mixture being formed. This wetting state is represented in the Figure by section Ixnes. Depending on the intensity of the mixing and the ratio of amine-oxide solution to cellulose, during the transport of the mixture along the wall of vessel 1 a homogeneous suspension is formed, which is removed through aperture 8 and may be used for the production of the cellulose solution either immediatly or after a subsequent processing, such as a grinding step. The spiniform elements 4 are somewhat inclined towards the axis of rotor 2, thus being able to pass on the suspension. It is important that the rotor is rotated at such a high rate chat the cellulose/amine-oxide mixture is thrown to the vessel wall, forming a layer thereon.If the radius of the vessel is for instance 15 cm, an exemplary revolution number of the rotor to form a layer is about 700 revolutions per minute . By means of the following Example, the invention will be illustrated in more detail. Example For the preparation of the suspension, a so-called rxng layer mixer K-TT 80 (made of stainless steel) of the company Draiswerke GmbH, Mannheim, Germany, was used. The function mode of this mixer is described above by means of the drawing. To the rxng layer mixer, 55 kg of shredded cellulose per houi having a particle size of not more than 4 mm and 375 kg of an aqueous solution containing 75 % by mass of NMMO were continuously fed. As a heating medium, water having a temperature of 75°C was employed. In the ring layer mixer, normal pressure prevailed. The rotor was rotated at 700 revolutions per minute. Per hour, 430 kg of homogeneous suspension having a dry substance density of 12,8 % by mass of cellulose and a temperature of 65°C could be obtained from the ring layer mixer. The suspension produced in the ring layer mixer was fed to a filmtruder of the Buss HS 0200 type according to the process described in EP-A - 0 356 419 at a rate of 430 kg/h and a temperature of 7 5°C, therein being transformed into a mouldable solution having a cellulose concentration of 15,0%, The heating surface of the filmtruder was heated by means of saturated vapor at 142°C. The circumferential rate of the rotor was 4m/s and the pressure in the filmtruder was 5 0 mbar. Approximately 63 kg of water vapor per hour were withdrawn. Jstng the above process parameters, approximately 367 kg per nour of mouldable cellulose solution having a temperature of 105°C could be removed from the filmtruder. The mouldable solution obtained did not contain any undissolved cellulose particles (microscopical, analysis;, was degassed and could be easily processed into fibres and films by means of the process known from WO 93/19230 and WO 95 07811 respectively of the applicant. The residence time of the cellulose in the ring layer mixer ,vas 2 minutes. This means that using the process according to the invention it is possible to produce in only a few minutes a homogeneous suspension from the starting materials cellulose and amine-oxide solution, which can be easily transformed into a mouldable cellulose solution. WE CLAIM: 1. A process for the production of a suspension of cellulose in a liquid aqueous tertiary amine-oxide said suspension to be used for the production of a mouldable cellulose solution, said solution to be used for the production of cellulose moulded bodies, wherein shredded cellulose is mixed with said liquid, aqueous tertiary amine- oxide, characterized in that (A) said shredded cellulose is contacted with said liquid aqueous tertiary amine-oxide, a first mixture being prepared, and (B) said first mixture is spread mechanically as a layer on a surface and transported along said surface while intensively being mixed, until a homogeneous suspension is produced which is removed from said surface, wherein (C) wherein (A) and (B) are being carried out continuously. 2. A process as claimed in claim 1, wherein as said liquid aqueous tertiary amine-oxide a molten, tertiary amine-oxide hydrate is employed. 3. A process as claimed in any one of claim 1 or 2, wherein a liquid aqueous tertiary amine-oxide having a temperature in the range of from 50 to 85°C is employed. 4. A process as claimed in any one of claims 1 to 3, wherein the cellulose contacted with the liquid aqueous tertiary amine-oxide is transported along the surface for a time interval of 1 to 5 minutes. 5. A process for the production of a mouldable cellulose solution, wherein a homogeneous suspension prepared by a process as claimed in claims 1 to 4 is processed to a mouldable cellulose solution by mixing and simultaneously heating at reduced pressure to evaporate water. 6. A process substantially as hereinbefore described with reference to the accompanying drawings.

Documents:

828-del-1996-abstract.pdf

828-del-1996-claims.pdf

828-del-1996-complete specification (granded).pdf

828-del-1996-correspondence-others.pdf

828-del-1996-correspondence-po.pdf

828-del-1996-description (complete).pdf

828-del-1996-drawings.pdf

828-del-1996-form-1.pdf

828-del-1996-form-13.pdf

828-del-1996-form-2.pdf

828-del-1996-form-3.pdf

828-del-1996-form-4.pdf

828-del-1996-form-6.pdf

828-del-1996-pa.pdf

828-del-1996-petition-137.pdf

828-del-1996-petition-138.pdf