Title of Invention

SEMI FINISHED PRODUCT FOR MAKING PLUG-IN CONTACTS AND METHOD FOR MAKING THE SAME

Abstract The invention relates to a semi-finished product for producing plug contacts in plug connectors for electric direct-current systems in motor vehicles, which are operated with a nominal voltage at which arcs can arise. The semi-finished product comprises an electrically conductive base body, which is made of a non-precious metallic material and which supports, at least in part, a contacting coating made of a material that is more precious than the material of the base body. According to the invention, the coating has a thickness of at least 0.3 μm and is made of silver or of a silver-based alloy with an additive that, together with the silver or with the silver-based alloy, does not form any alloy or, at most, forms a precipitation alloy and has a higher melting point than silver.
Full Text

Electrical plug contacts and a semi-finished product for the production thereof
Specification:
The present invention relates to electric plug-in contacts for plug-in connectors in electric DC wiring systems operated at a nominal voltage, in which electric arcing may occur, and to a semi-finished product for the production of such plugs as defined in the preamble of Claim 1. Especially, the invention relates to plug-in contacts intended for use in automobiles. Today, passenger cars generally are equipped with electric wiring systems that operate at a nominal voltage of 14 V. Plug-in contacts in plug-in connectors intended for that use usually consist of a main body, made from copper, a copper-based alloy such as CuNiSi or stainless steel which provide the required electric conductivity and spring properties so ensure safe contact-making by the plug-in connector. In order to guarantee stable electric contact-making properties even in a corrosive atmosphere, it has been known to provide the main bodies of the plug-in contacts, or their semi-fished products, with a hard gold layer applied by galvanic deposition, or with a pure silver layer or a tin layer. Tin and tin alloy layers are frequently applied also using a fire-tinning process. Given the marginal conditions required heretofore (use in air at a nominal voltage of 14 V and a maximum ambient temperature of 150° Celsius - in which connection it must be considered that the temperature of the plug-in connector being heated by the current may further rise by 30° Celsius above ambient temperature) it has been

possible in this way to achieve a sufficient degree of wear resistance when plugging-in and pulling off the male and female plug-in contacts.
It is planned by automobile manufacturers for the future to increase the voltage of passenger car wiring systems to 42 Volts. In direct-voltage electric wiring systems, operating at a nominal voltage of 42 V, plugging-in and pulling off plug-in connectors under load may give rise to electric arcing with the result that the plug-in contact or even the vehicle may catch fire. In addition, shocks occurring during operation of the vehicle may cause micro-interruptions between the plug-in contacts in the plug-in connectors, which likewise may give rise to electric arcs. Whether or not an electric arc actually strikes across a gap between two contact surfaces, due to vibration or under the effect of a plug being plugged in or pulled off, depends not only on the electric voltage available but also on whether a capacitive load or an inductive load is being separated and on the particular material making up the contact surfaces concerned. Generally, all materials have a specific minimum voltage, determined by physical conditions, which must be reached before charge carriers come off the contact surface to feed the electric arc. The element having the highest arc voltage is carbon with an arc voltage of 20 Volts; metals all have arc voltages of between 12 Volts and 16 Volts. In passenger car wiring systems, operating at a nominal voltage of 14 Volts, separation of a plug-in connector under load will not yet lead to a permanently firing arc as the load impedance in the previously closed circuit leads to a voltage drop so that the required arc-firing voltage will not be reached in the gap formed between the contact surfaces concerned when separating a plug-in connector. Consequently, the contact surfaces of today's passenger cars are not designed for loads at which electric arcing may occur.
The problem that in the case of 42 V automotive wiring systems electric arcing may occur when separating electric plug-in contacts, which may lead to serious damage and even to the vehicle catching fire and which are likely to jeopardize the safety of the passengers, is generally known in the art. Persons skilled in the art are also aware of the fact that the entire electric wiring system, and its components, will have to be redesigned to meet the requirements of a nominal voltage of 42 Volts and that

considerable development effort will also have to be made for redesigning plug-in connectors and switchgear, see for example the paper by Thomas J. Sch6pf, "Electrical Contacts in the Automotive 42 VDC PowerNet", Proceedings of the 21st International Conference on Electrical Contacts, 09 to 12.09.2002, Zurich, pp. 43 6o 55, especially p. 52. That paper suggests to investigate means for the quenching of arcs.
The paper by N. Ben Jamaa et al. "Short Arc Duration Laws and Distribution at Low Current ( Another problem is seen in the fact that electric arcs occurring in 42V automotive power systems may alter the contact surface and lead to a higher contact transfer resistance and, thus, to undesirable heating-up of the contact, under certain circumstances even to welding of plug-in contacts so that the latter can no longer be separated.
Now, it is the object of the present invention to provide electric plug-in contacts and a semi-finished product for making the same, which will show improved behaviour in known semi-finished products and plug-in contacts, designed for a nominal voltage of 14 Volts,under the stresses to be expected in 42V automotive power systems and which meet the marginal conditions listed below that have been postulated for use in 42V power systems:

? On the one hand, the main body of the connectors should have a springiness which ensures reliable contact-making in electric plug-in connectors.
? On the other hand, the main body should be sufficiently ductile to make it workable, especially by bending.
? Plug-in-connectors made using such plug-in contacts should be capable of being repeatedly separated and joined under load without welding one to the other.
? Plug-in-connectors made using such plug-in contacts should be capable of being repeatedly separated and joined without the contact transfer resistance increasing inadmissibly. Especially, the contact layer applied should not wear even after repeated separating and joining operations of the plug-in connector. It should be possible to carry out the number of plugging-in operations typical for automobiles without failure.
? The plug-in contacts must be suited for use in ambient temperatures of up to 200° Celsius.
? The cost of the plug-in contacts and the semi-finished product for making the same must be low.
The object of the invention is achieved by a semi-finished product having the features defined in Claim 1, by a method for making it defined in Claim 20 and by plug-in contacts produced by such method having the features defined in Claim 19. Advantageous further developments of the invention are the subject-matter of the
sub-claims.
The invention offers considerable advantages:
? By using a main body made from a non-precious material and a coating with favourable properties with respect to electric contact-making in plug-in connectors both the mechanical and the electrical requirements can be met.
? By forming the coating intended to establish the electric contact on the basis of silver or a silver-based alloy, with pure silver being preferred because of its higher melting point, contact surfaces with sufficiently low contact transfer resistance and sufficiently high corrosion resistance can be obtained. A low contact transfer

resistance is favourable with respect to low heating-up of the plug-in contacts in a plug-in connector. Good corrosion resistance is favourable with respect to a permanently low contact transfer resistance.
? Pure silver would be unfavourable as contact-making coating with respect to the arc loading that may arise in 42V automotive power systems. It is the more surprising that even thin silver layers or layers of a silver-based alloy with small amounts of an addition selected according to the invention already have the effect to considerably improve the suitability of plug-in contacts for plug-in connectors in 42V automotive power systems.
? Even thin layers composed according to the invention are still completely in place after repeated loading by arcs and do not wear by repeated pulling and plugging-in of a plug designed according to the invention.
? It is further surprising that migration of components of the main body into the contact-making coating remains within narrow tolerable limits so that no re-alloying occurs even under repeated arcing. This even applies to copper from a main body containing copper.
? The thin contact-making coating is sufficiently hard for use in plug-in connectors.
? As the coating may be only thin, the costs for the use of rare silver are only low.
? The coating may be deposited at low cost by a PVD process, especially by sputtering. This permits silver and additions that will not alloy with silver to be deposited as a finely grained dense and hard mechanical mixture. The main body remains cold enough during the deposition process so that it will not loose its predetermined hardness.
? Using a reactive PVD process, compounds, especially metal oxides, may also be deposited as additions.
Preferably, the coating has a maximum thickness of 10 μm. A thicker coating might improve the resistance to stretching, drawing and arcing, but in view of the limited number of drawing and stretching events practically encountered during the lifetime of a passenger car - one expects that drawing and stretching will occur on no more than 10 to 20 occasions - is would not pay off and might, on the other hand, impair the workability of the semi-finished product. Preferably, the coating is selected to

have a maximum thickness of 5 μm. Especially good results have been achieved with coatings having a thickness of between 0.5 μm and 5 pm.
Surprisingly, minor additions to the silver or the silver-based alloy will already be sufficient. With an addition of 0.2 % by weight one already achieves a notable improvement compared with a coating of pure silver or a silver-based allow. Preferably, the addition should be contained in the silver or the silver-based alloy in an amount of at least 0.5 % by weight, maximally 50 % by weight. Most conveniently, the range of the addition in the coating is between 0.5 % by weight and 15 % by weight. Materials especially well suited as additions are tungsten, molybdenum, graphite, nickel, cobalt, metal oxides, especially tin oxide and zinc oxide, as well as tungsten carbide and molybdenum carbide. Especially well suited for purposes of the invention are refractory additions that build up in fine distribution in the grain boundaries of the silver matrix, such as tungsten and molybdenum.
Suited for use as main body are all non-precious alloys known in the prior art for electric plug-in contacts, the materials named in Claim 12 being particularly well
suited.
Preferably, the semi-finished product consists of a strip that can be continuously coated by a continuous process. Especially, the semi-finished product may also be a pre-punched strip, which likewise can be continuously coated, especially by a dry and cold PVD process. If pre-punched strips are used, where the contours of the plug-in contacts to be formed have been defined by the pre-punching operation, the plug-in contacts can then be economically formed from the strip by a simple separating and bending process.
Depositing the coating by a PVD process, especially by sputtering, provides the additional advantage that the composition of the coating can be altered by modification of the deposition conditions, and this even continuously during the deposition process. Thus, it is possible to give the coating a gradient regarding the

addition that will not form an alloy with silver or the silver alloy, for optimising the mechanical and electric properties of the contact-making coating.
In order to maintain the composition and, thus, the properties of the contact-making coating over a long period of time, it may further be of advantage to provide an intermediate layer between the main body and the contact-making coating which inhibits diffusion of components of the main body material into the contact-making coating on the contact surface. Such an intermediate layer may consist, for example, of a few μm of nickel. A few pm of silver as an intermediate layer are likewise suited. Silver should be the material of choice especially when a semi-finished product according to the invention is to be bent to radii so narrow that a nickel layer would break. Especially well suited as layer thicknesses for the intermediate layer are 1 pm to 5 pm, especially 2 pm ± 0.5 pm.
For testing the resistance to arcing, a number of plug-in contacts made from copper and provided with a layer of 2 pm thickness of silver with a tungsten content of 4 % by weight, were separated 20 times at a direct voltage of 42V, under a load current of 1.5 A and an inductance of 1.75 mH. After 20 separating operations, with an arc firing during each operation, the coating was not burnt off, not even in the area of the arc base points, but was still completely in place over the full surface, though it was roughened by melting-up processes. An analysis of the composition of the contact-making coating after the 20 arc exposures revealed a low copper content of maximally 1.5 % by weight in the area of the arc base points - a value that can be very well tolerated.
The attached drawing shows a cross-section through a strip-like semi-finished product - greatly enlarged and not true to scale - illustrating the structure of a semifinished product according to the invention with a main body 1, of 0.5 mm thickness for example, consisting of a spring alloy based on copper, for example copper with 3 % nickel and 0.5 % Si (material No. C7025 according to CDA) and on top, as diffusion inhibiting intermediate layer 2, a nickel layer of 2 pm thickness that can be deposited galvanically or by a PVD process. On top of the nickel layer 2, there can

be seen as contact-making layer 3 a silver layer of 4 μm thickness with a tungsten content of 5 % by weight, which have been sputtered jointly to form a finely distributed mechanical mixture.



Claims:
1. Semi-finished product for making plug-in contacts in plug-in connectors for electric DC power systems in motor vehicles which are operated at a nominal voltage at which electric arcing may occur, having an electrically conductive main body made of a non-precious metallic material that carries, at least in part, a contact-making coating of a material more precious than the material of the main body, characterized in that the coating has a thickness of at least 0.3 μm and consists of silver or of a silver-based alloy with an addition that will not form an alloy with silver or with the silver-based alloy, or will at best form a precipitation alloy, and which has a higher melting point than silver.
2. The semi-finished product as defined in Claim 1, characterized in that the
coating has a thickness of maximally 10 μm.
3. The semi-finished product as defined in Claim 1, characterized in that the coating has a thickness of maximally 5 pm.
4. The semi-finished product as defined in Claim 1, characterized in that the coating has a thickness of 0.5 μm to 4 μm.
5. The semi-finished product as defined in any of the preceding claims, characterized in that the addition is contained in the silver or in the silver-based alloy in an amount of at least 0.2 percent by weight.
6. The semi-finished product as defined in any of the preceding claims, characterized in that the addition is contained in the silver or in the silver-based alloy in an amount of at least 0.5 percent by weight.
7. The semi-finished product as defined in any of the preceding claims, characterized in that the addition is contained in the silver or in the silver-based alloy in an amount of maximally 50 percent by weight.

The semi-finished product as defined in any of the preceding claims, characterized in that the addition is contained in the silver or in the silver-based alloy in an amount of maximally 30 percent by weight.
The semi-finished product as defined in any of the preceding claims, characterized in that the addition is contained in the silver or in the silver-based alloy in an amount of maximally 15 percent by weight.
The semi-finished product as defined in any of the preceding claims, characterized in that the addition comprises one or more substances taken from the group of the following substances: Tungsten, molybdenum, graphite, nickel, cobalt and metal oxides, especially tin oxide and zinc oxide, as well as
tungsten carbide and molybdenum carbide.
The semi-finished product as defined in any of the preceding claims, characterized in that the coating is deposited by a PVD process, especially
by sputtering.
The semi-finished product as defined in any of the preceding claims, characterized in that a material from the following group is selected as material for the main body:
(a) CuNiSi(X): Materials designated C7025, C7026 according to CDA, for example;
(b) CuFeP: Materials designated C194, C19210 according to CDA, for example;
(c) CuSn: Materials designated C521, C511, C14415, according to CDA, for example;
(d) CuZn: Materials designated C272, C230, C260 according to CDA, for example;
(e) CuCrSiTi(X): Materials designated C18070, C18080, C18090 according to CDA, for example;

(f) CuNiSn: Materials designated C72500, C19025 according to CDA, for example;
(g) CuSnZn: Materials designated C663, C425 according to CDA, for example;
(h) CuNiZn: Materials designated C75700, C77000, C76400 according to
CDA, for example; (i) CuBe: Materials designated C17100, C17410, C17200 according to CDA,
for example; (j) CuTi: Materials from the family of materials designated C19900 according
to CDA, for example, (k) Stainless steel: Materials designated
1.4310 according to DIN 17224,
1.4311 according to DIN 17440, 1.4406 according to DIN 17440,

1.4428 according to DIN 17443,
1.4429 according to DIN 17440, 1.4568 according to DIN 17224, 1.4841 according to DIN 17224,
1.4318, 1.1231, 1.1248, 1.1269, 1.1274, 1.5029 according to DIN V 17006-100.
13. The semi-finished product as defined in any of the preceding claims, characterized in that the product is a strip.
14. The semi-finished product as defined in Claim 13, characterized in that the
strip is pre-punched.
15. The semi-finished product as defined in any of the preceding claims,
characterized in that the coating consists of silver with a tungsten or
molybdenum content of 4 to 6 % by volume, and is applied in a thickness of
0.5 μm to 5 μm.

16. The semi-finished product as defined in any of the preceding claims, characterized in that a diffusion-inhibiting intermediate layer is provided between the main body and the contact-making coating.
17. The semi-finished product as defined in Claim 16, characterized In that the
intermediate layer consists of silver or nickel.
18. The semi-finished product as defined in any of the preceding claims,
characterized in that the concentration of the addition in the silver or silver-
alloy coating is lower at the surface of the coating than in the deeper region of
the coating.
19. Plug-in contacts for electric plug-in connectors made from a semi-finished product according to any of the preceding claims.
20. The use of plug-in contacts as defined in Claim 19 in electric power systems of automobiles, which are operated at a nominal voltage at which arcing may occur, especially in 42 Volt DC power systems.
21. Method for making a semi-finished product as defined in any of Claims 1 to 18 by PVD coating of a strip, consisting of a non-precious metallic material, with silver or a silver-based alloy with an addition, which has a higher melting point than silver and which does not form an alloy, or at best a separation alloy, with the silver or the silver-based alloy.
22. The method as defined in Claim 21, characterized in that coating is effected by sputtering.
23. The method as defined in Claim 21, characterized in that the components of the coating are deposited simultaneous or in a fashion overlapping in time.

24. The method as defined in Claim 23, characterized in that the ratio of the
separation rates of the components of the coating is altered during the
separation process.
25. The method as defined in Claim 24, characterized in that the ratio between
the separation rate of the addition and the separation rate of the silver or the
silver alloy is reduced toward the end of the separation process.


Documents:

2670-chenp-2005 abstract-duplicate.jpg

2670-chenp-2005 abstract-duplicate.pdf

2670-chenp-2005 claims-duplicate.pdf

2670-chenp-2005 description (complete)-duplicate.pdf

2670-chenp-2005 drawings-duplicate.pdf

2670-chenp-2005-abstract.pdf

2670-chenp-2005-claims.pdf

2670-chenp-2005-correspondnece-others.pdf

2670-chenp-2005-correspondnece-po.pdf

2670-chenp-2005-description(complete).pdf

2670-chenp-2005-drawings.pdf

2670-chenp-2005-form 1.pdf

2670-chenp-2005-form 3.pdf

2670-chenp-2005-form 5.pdf

2670-chenp-2005-others.pdf

2670-chenp-2005-pct.pdf


Patent Number 224036
Indian Patent Application Number 2670/CHENP/2005
PG Journal Number 47/2008
Publication Date 21-Nov-2008
Grant Date 24-Sep-2008
Date of Filing 17-Oct-2005
Name of Patentee AMI DODUCO GMBH
Applicant Address Im Altgefall 12, 75181 Pforzheim
Inventors:
# Inventor's Name Inventor's Address
1 KASPAR, FRANZ Uhlandstrasse 21, 75223 Niefern-Oschelbronn
2 GANZ, JOACHIM Mauerackerstrasse 11, 75399 Kapfenhardt
3 BURESCH, ISABELL Bgm.-Wanner-Strasse 62, 89257 Illertissen
PCT International Classification Number DE10045783
PCT International Application Number PCT/EP04/04100
PCT International Filing date 2004-04-17
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 103 18 890.8 2003-04-17 Germany