Title of Invention	"A PROCESS FOR THE PREPARATION OF ACID-BASE POLYMER BLENDS OR MEMBRANES THEREOF"
Abstract	The invention relates to novel compatible binary and tertiary cation exchange polymer and anion exchange polymer acid base blend membranes.

Full Text

The present invention relates to a process for the preparation of acid-base polymer blends or membranes thereof. The invention further relates to the use of such binary and ternary ionomer blend membranes in electromembrane processes, such as polymer electrolyte membrane fuel cells (PEFC), direct methanol fuel cells (DMFC), electrodialysis, and in other membrane processes, such as dialysis and inverse osmosis, diffusion dialysis, gas permeation, pervaporation and perstraction. For ionomer membrane applications, such as polymer electrolyte membrane fuel cells (PEMFC), direct methanol fuel cells (DMFC), polymer electrolyte membrane electrolysis (PEM-E), a high chemical, mechanical and thermal stability of the membrane is necessary. The perfluorinated ionomer Nafion® (Grot, W.G.: Perfluorinated Ion-Exchange Polymers and Their Use in Research and Industry, Macromolecular Symposia, 82, 161-172 (1994)) is the only commercially available ionomer to date to meet the high requirements of chemical, mechanical and thermal stability (Ledjeff, K.; Heinzel, A.; Mahlendorf, F.; Peinecke, V.: Die reversible Membran-Brennstoffzelle, Dechema-Monographien Band 128, VCH Verlagsgesellschaft, 103-118 (1993)). However, it has various disadvantages which necessitate the search for alternative materials: It is very expensive (DM 1400.-/m2). The very complex production process comprises highly toxic intermediates (see Grot, W.G.). The environment-compatibility of Nafion® is to be evaluated critically: as a perfluorinated polymer, it is hardly degradable. The recydability of Nafion® is questionable. When applying Nafion® in direct methanol fuel cells (DMFC), it was discovered that it shows a very high methanol-permeability, especially when pure methanol is used (Surampudi, S., Narayanan, S.R.; Vamos, E.; Frank, H.; Halpert, G.; LaConti, A,; Kosek, J.; Surya Prakash, G.K.; Olah, G.A.: Advances in direct oxidation methanol fuel cells, J. Power Sources, 47, 377-385 (1994)), which greatly reduces the energy efficiency of the DMFC by mixed potential formation. Possible alternative materials to the perfluorinated ionomers are arylene main chain ion-exchanger polymers, such as sulfonated polyethersulfone (Nolte, R.; Ledjeff, K.; Bauer, M,; Mulhaupt, R.: Partially Sulfonated poly(arylene ether sulfone) - A Versatile Proton Conducting Membrane Material for Modern Energy Conversion Technologies, Journal of Membrane Science 83, 211-220 (1993)) and sulfonated poly(etheretherketone) (Helmer-Metzmann, F.; Ledjeff, K.; Nolte, R., et a!-: Polymerelektrolyt-Membran und Verfahren zu ihrer Herstellung, EP 0 574 791 A2), which have a disadvantage, however, in that they exhibit a high brittleness when drying out, which is unfavorable when used, for example, in membrane fuel cells. Searching for polymers with high thermal and mechanical stability leads one to find polyimides, imidazole containing polymers and benzimidazoles which show excellent thermal stabilities, such as the polybenzimidazole (PBI) poly[(2,2'-m-phenylene)-5/5-bibenzimidazoie] of general formula (Formula Removed) and the polyetherimide poly[2,2'-bls(3,4-dicarboxyphenoxy)phenyl-propane-2-phenylenebisimide] (Musto, P.j'Karasz, F.E., MacKnight, W.J.: Fourier transform infra-red spectroscopy on the thermooxidative degradation of polybenzimidazole and of a polybenzimidazole/poly-etherimide blend, Polymer, 34(12), 2934-2945 (1993)).Polybenzimidazoles can be sulfonated by various methods. One possible way is the following sequence of reactions (Gieselman, M.B.; Reynolds, J.R.: Water-Soluble Polybenzimidazole-Based Polyelectrolytes); 1. Deprotonation of the imidazole N-H with LiH in DMAc; 2a. Reaction of the deprotonated polymer with propanesulfone to give the corresponding polybenzimidazole-N-propanesulfonate; 2b. Reaction of the deprotonated polymer with Na-4-(bromomethyl)- benzenesulfonate to give the corresponding polybenzimidazole-N- benzylsu,lfonate. A patent describes another method for obtaining sulfonated poly-tienzfmidazoles (Sansone, M.J.; Gupta, B.; Forbes, C.E.; Kwiatek, M.S.: Sulfalkylation of Hydroxyethylated Polybenzimidazole Polymers, US 4,997,892) which involves the following sequence of reactions; 1. Reaction of polybenzimidazole at the N-H group of the imidazole ring with ethylene carbonate in a dipolar-aprotic solvent, such as IM-methylpyrrolidinone, to give the hydroxyethylated polybenz-imidazGle N-(CH2)2OH; 2. Deprotonation of the OH group of the hydroxyethylated poly- benzimidazole with a suitable base to give the hydroxyethylated polybenzimidazole anion N-(CH2)2O"; 3. Reaction of the hydroxyethylated polybenzimidazole anion N- (CH2)2O" with a sulfone, e.g., propanesulfone, to give the sulfo- alkylated polymer N-(CH2)20(CH2)3-SQ3~. It has been found that the excellent thermal stability of polybenz-imidazoles is partially retained with these sulfonating methods (see Gieselman et al.). For some applications of the sulfonated polybenz-imidazoles mentioned, such as their use in membrane fuel cells, it may be a disadvantage, however, that they contain. -CH2- groups which result in a lower oxidation stability than that of purely aromatic sulfonated polymers, In addition, the sulfonated polybenzimidazoles can form inner salts in their protonated form which reduce the proton conduction according to the following reaction scheme: (Scheme Removed) Further, the sulfonated polybenzimidazoles may lose part of their mechanical stability by interference of the substituent with the chain conformation. Polybenzimidazole can be alkylated at both imidazole nitrogens by the following method to obtain an anion-exchanger polymer which may also be water-soluble (Hu, Ming; Pearce, Eli.M,; Kwei, T.K.: Modification of Polybenzimidazole: Synthesis and thermal stability of Poly(Nrmethyf-benzimidazole and Poly(Ni,N3-dimethylbenzimidazole), Salt Journal of Polymer Science: Part A: Polymer Chemistry, 31, 553-561, 1993): 1. Deprotonation of the imidazole N-H with LiH in DMAc or NMP to give the N-Li salt; 2. Alkylation of the Li salt ≈N-Li with methyl iodide to give ≈N-CH3; 3. Reaction of the methylated polybenzimidazole with an excess of methyl iodide at 80 °C to obtain poly(N1,N3-dlmethylbenzimidaz- olium) diiodide. A disadvantage of this poly(N1,N3-dimethylbenzirnidazolium) iodide is its poor thermal stability (thermogravimetry; onset loss of weight at 180 °C (heating rate 10°/min)). This loss of weight can be explained by the cleavage of methyl iodide to form the monomethylated polybenzimidazole, which results in a loss, of the anion-exchanger properties of the polymer, In the patent literature a work claiming blends/mixtures of low-molecular non-aqueous amphoters and high-molecular acids (proton donors) or high-molecular amphoters and low-molecular adds is found (Kreuer, K.D.; Fuchs, A.; Maier, J.; Frank, G.; Soczka-Guth, Th.; Clauß, J.; Protonenleiter mit einer Temperaturbestandigkeit in einem weiten Bereich und guten Protonenleitfahigkeiten, DE 196 32 285 Al), Said amphoters are heterocyclic and heteroaromatic N-contaim'ng compounds including, among others, also imidazole or benzimidazole and imidazole or benzimidazole containing organic low-molecular, oligomer, or high-molecular compounds functioning as proton solvents, the acids being present in the system being the proton donors for the amphoters. "Proton solvent" indicates that the protons are directed by the molecules or groups of the amphoters. In the application examples of DE 196 32 285 Al only the preparation and characterization of blends of sulfonated polyetherketones and imidazole and/or pyrazole are quoted, the blends containing 10 imidazole and/or pyrazole molecules showing the best proton conductivities. The good proton conductivity of said blends is presumably due to the high mobility of the imidazole and/or pyrazole molecules within the polymer matrix. This high mobility of the low-molecular heterocycles involves the danger that said molecules possibly can be re-discharged from the acidic polymer matrix, in particular, if they are present in molar excess with respect to the acid groups and in particular at temperatures exceeding 200 - 250 °C (boiling temperature of imidazole: 256 °C; boiling temperature of pyrazole: 186 °C). Examples of the proton conductivity of blends of polymers containing high-molecular polymeric acids and high-molecular imidazole or pyrazole groups are not given in DE 196 32 285 Al. The proton conductivity in the anhydrous state of blends consisting of polybenzimidazoles and polymeric sulfonic acids (for a proton conduction in the anhydrous state the imidazole component has to be present in molar excess) is supposed to be very low, if it exists at all, as the mobility of polybenzimidazoles, in particular if the imidazole groups are contained within the backbone chain, is much lower than the mobility of imidazole or pyrazole. All sulfonated aryl polymers exhibit a high brittleness when drying out, for example, when they are applied in fuel cells at intermittent conditions. In addition, the thermal stability of the sulfonated aryl polymers is still worth improving. To conclude, the reduction in brittleness and the further Increase in thermal stability of the sulfonated aryl polymer ionomer membranes must have priority in their further development for long-term application in PEM fuel cells, PEM electrolysis and other (electro)membrane processes in which the membranes are subjected to heavy-duty conditions. Statement of Invention According to the present invention there is provided a process for the preparation of acid-base polymer blends or membranes thereof, wherein solutions of polymeric sulfonic acids or sulfonic acid salts, polymeric phosphonic acids or phosphonic acid salts and/or polymeric carboxylic acids or carboxylic acid salts and a polymer containing basic imidazole, benzimidazole and/or other heterocyclic, especially heteroaromatic, nitrogen-containing basic moieties, such as oxazole, isoxasole, carbazole, indole, isoindole, thiazole, isothiazole, benzoxazole, benzothiazole, imidazolidine, indazole, 1,2,3,-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,3,-triazole, benzotriazole, 1,2,4-triazole, tetrazole, pyrrole, pyrrolidine, pyrrazole groups are reacted, optionally with the addition of LiCl, in dipolar-aprotic solvents, and the solvent is evaporated from the solutions, and wherein the SO3H, PO3H2 or COOH form of the blends is prepared by aftertreating the blend polymer or the blend polymer membrane in diluted mineral acids at temperatures of from 20 to 80°C. The present invention provides acid-base polymer blends or acid-base polymer blend membranes which are characterized by excellent chemical, mechanical and thermal stabilities and which are composed of: (la) a cation-exchanger polymer, optionally with an aryl and/or heteroaryl polymer main chain, comprising SO3X moieties (X = any cation including hydrogen); or (Ib) an anion-exchanger polymer with quaternary ammonium groups, pyridinium groups, imidazolinium groups, pyrazolinium groups, triazolinium groups, tetrazolinium groups etc.; and (2) polymers containing benzimidazole, imidazole, and/or other heterocyclic, especially heteroaromatic, nitrogen-containing basic moieties, especially oxazole, isoxazole, carbazole, indole, iso- indole, thiazole, isothiazole, benzoxazole, benzothiazole, imidazol- idine, indazole, 1,2,3-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thia- diazole, 1,2,3-triazole, benzotriazole, 1,2,4-triazole, tetrazole, pyrrole, pyrrolidine, pyrrazole groups and optionally (for ternary ionomer blend membranes), in addition: (3) other polymers containing primary, secondary or tertiary basic nitrogens, such as poly(4-vinylpyridine), poly(2-vinylpyridine), (block) copolymers containing poly(4-vinylpyridine) or poly(2- vinylpyridine), poly(sulfone-ortho-sulfone-diamine), poly(sulfone- ortho-ether-diamine), poly(aniline), poly(ethyleneimine). Thus, the invention provides the following combinations; binary blends: 1a-2 or 1b-2 ternary blends: 1a-2-3 or 1b-2-3 Surprisingly, it has now been found that mixing a polymeric sulfonic acid salt, for example, poly(ethersulfone fithium sulfonate), of the following formula (Formula Removed) with 2 sulfonate groups per repeating unit; obtainable according to Kerres, J.; Cui, W.; Reichle, S,: New sulfonated engineering polymers via the metalation route. I. Sulfonated poly(ethersulfone) PSU Udel® via metalation-sulfmation-oxidation, Journal of Polymer Science, Part A: Polymer Chemistry 34, 2421-2438 (1996), or poly(etheretherketone lithium sulfonate) of the following formula (Formula Removed) with one sulfonate group per repeating unit; obtainable according to Helmer-Metzmann et al,, with only 3-25% by weight of the polybenzimidazole (PBI) Celazol® yields an ion-conducting polymer blend membrane which is characterized by the following properties: a large improvement in mechanical strength as compared to the respective pure polymeric sulfonic acid (the respective polymeric sulfonic acid salt); water-soluble polymeric sulfonic acid salts surprisingly lose their water-solubility upon mixing with PBI because of the interactions between the polymeric chains of the blend components (formation of hydrogen bonds); the blends of the polymeric sulfonic acids with PBI exhibit high thermal stability already at surprisingly low contents of PBI in the blend (3-10%), caused by proton transfer from the sulfonic acid to the basic polybenzimidazole nitrogen to form a polysalt, and by the high thermal stability of the PBI, When aftertreating the blends consisting of sulfonic acid salt and PBI in a diluted mineral acid (e.g., 10 % HCI or 10 % H2SO4), according to the following reaction scheme ionic crosslinking bridges between the acidic and the basic blend components are formed due to a proton transfer to the basic N of the imidazole: (Formula Removed) These ionic crosslinking bridges account for the high thermal and mechanic stability of the acid-base blends according to the invention. The essential differences of the blends claimed in the present invention with respect to DE 196 32 285 are: • The blends according to the invention are used exclusively in aqueous media, I.e., in this case waters the ampholyte (see the application examples, where the proton conductivity or the proton resistance was measured in 0.5 molar aqueous HCI). • In the acid-base blends according to the invention the polymer containing imidazole, benzimidazole or other basic nitrogen-containing heterocycfic/ especially heteroaromatic, groups serves exclusively as a base, i.e., ionic bonds to said base are formed by a proton transfer from the acid component, IR spectroscopic measurements revealed that the proton does not dissociate from the imidazole cation in the aqueous medium because the imidazole group is a strong base (pkb about 9 - 10). • In the acid-base blends according to the invention the proton conduction takes place exclusively by the sutfonic acid groups of the acidic blend component. Therefore, in the present invention acid-base blends containing the acidic component in molar excess are preferred, OE 196 32 285 Al does not disclose binary anion exchanger blends of imidazole containing polymers and anion exchanger polymers and ternary blends, In particular, the blends of imidazole containing polymers, polymeric acids, and an additional basic polymer are very promising, as the mechanic and thermal stability of said blends can be improved further. It has surprisingly been found that when ternary tonomer blend membranes are prepared from; sultonated UEEK/PSU polybenzimidazole arninated PSU, these blends also exhibit very high mechanical stability and high thermal stability. It is also possible to prepare PBI-containing anion-exchanger polymer blends and anion-exchanger polymer blend membranes, the PBI serving as a mechanically and thermally stabilizing component: Thus, PBI can be dissolved in a dlpoter-aprotlc solvent together with poly(4-vinylpyridine). Then, a mixture of monofunctional and difunctional haloalkanes (for example, a mixture of 1,6-diiodohexane and l-iodohexane) is added to the polymer solution. While the solvent is being evaporated, the pyridine nitrogen is alkylated to give the corresponding pyridinium salt, with partial cross-linking (by the difunctional haloalkanes, for example, 1,6,-diiodohexane). The halide anion remains as an exchangeable counter-ion in the anion-exchanger polymer formed. Another type of anion-exchanger polymer blend membrane can be prepared by dissolving poly(N1,N3-dimethylbenzimidazolium) iodide (11) and polybenzimidazole together in a dipolar-aprotic solvent, such as DMAc, NMP or DMSO, followed by evaporation of the solvent at elevated temperature, Example 1 Preparation of an acid-base blend from sulfonated PEEK and PBI 10.067 g of a 20.16% solution of sulfonated poly(etheretherketone) (Ion-exchange capacity of 1.8 meq SO3H/g of polymer) and 26.8 g of a 1.875% solution of polybenzimidazole CELAZOL® (poly[2,2'-(m-phenylene)-5,5'-bibenzimidazo!e]) were mixed in N-methylpyrrolidinone. This solution was used to knife-coat about a 300 µm thick film onto a glass plate. The solvent was evaporated at a temperature of 120-140 °C. The glass plate with the thin polymeric film was placed in a trough with deionized water which caused the film to separate from the glass plate. The membrane was aftertreated first in 8% HCI at temperatures of 60-80 °C for 24 h and then in deionized water at temperatures of 20-80 °C for 24 h. Characterization results: Ion-exchange capacity: 1.06 meq SO3H/g of polymer Thickness: 20 urn Swelling (H2O, RT, H+ form): 22.8% Surface resistance (RT, H* form) 0.116 Ω-cm2 (measured in 0.5 N HCI) Specific resistance (RT, Hf form): 58.125 Ω-cm Thermal stability (by DSC, TGA): onset of decomposition: ≈350 °C (conditions: air, heating rate 20 °C/min) Example 2; Preparation of acid-base blends from sulfonated PSU and PBI The PBI and the sulfonated PSU Udel® in the SO3Li form were combined into a homogeneous solution (data see Table 1). This solution was used to knife-coat about a 300 pm thick film onto a glass plate. The solvent was evaporated at a temperature of 120-140 °C. The glass plate with the thin polymeric film was placed in a trough with deionized water which caused the film to separate from the glass plate. The membrane was aftertreated first in 8% HCI at temperatures of 60-80 °C for 24 h and then in deionized water at temperatures of 20-80 °C for 24 h. Table 1: Data for the preparation and characterization of blend membranes made from sulfonated PSU and the polybenzimidazole (PBJ) poly[2,2'-(m-phenylene)-5,5'~bibenzimidazole] (Table Removed) ¥ dissolved in 13.75 g of NMP * with water-soluble PSU, capacity 2.5 meq SO3H/g ** with water-insoluble PSU, capacity 1.6 meq SO3H/g *** as a 15% by weight solution in NMP **** as a 1.785% by weight solution t as a 1.785% by weight solution, plus addition of 6.557 g of NMP as a 1.785% by weight solution, plus addition of 19.647 g of NMP # as a 1.785% by weight solution, plus addition of 50 g of NMP Example 3 Preparation of a ternary acid-base blend from sulfonated PEEK, PBI and aminated PSU 22.5 g of a 20% by weight solution of sulfonated poly(etherether-ketone) (ion-exchange capacity of 1.9 meq SO3H/g of polymer) in DMAc was mixed with 10 g of a 6.4% by weight solution of polybenzimidazole (PBI) CELAZOL® (po!y[2,21-(m-phenylene)-5,5(-biben2imidazo!e]) in DMAc (PBI solution with addition of LiCI). Then, 10 g of a 15% by weight solution of poly(sulfone-ortho-sulfone-diamine) in NMP was also added to the polymer solution, and stirring was performed until the solution was homogeneous. This solution was used to knife-coat about a 400 um thick film onto a glass plate. The solvent was evaporated at a temperature of 120-140 °C, The glass plate with the thin polymeric film was placed in a trough with deionized water which caused the film to separate from the glass plate. The membrane was aftertreated first in 8% HCI at temperatures of 60-80 °C for 24 h and then in deionized water at temperatures of 20-80 °C for 24 h. Characterization results: Ion-exchange capacity: 0.93 meq SO3H/g of polymer Thickness: 54 µm Swelling (H20, RT, H+ form}: 25.6% Surface resistance (RT, H* form) 0.62 Q-cm2 (measured in 0.5 N HCI) Specific resistance (RT, H* form): 114.82 n-cm Thermal stability (by DSC, TGA): onset of decomposition: *300 °C (conditions: air, heating rate 5 °C/min) We claim: 1. A process for the preparation of acid-base polymer blends or membranes thereof, wherein solutions of polymeric sulfonic acids or sulfonic acid salts, polymeric phosphonic acids or phosphonic acid salts and/or polymeric carboxylic acids or carboxylic acid salts and a polymer containing basic imidazole, benzimidazole and/or other heterocyclic, especially heteroaromatic, nitrogen-containing basic moieties, such as oxazole, isoxasole, carbazole, indole, isoindole, thiazole, isothiazole, benzoxazole, benzothiazole, imidazolidine, indazole, 1,2,3,-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,3,-triazole, benzotriazole, 1,2,4-triazole, tetrazole, pyrrole, pyrrolidine, pyrrazole groups are reacted, optionally with the addition of LiCl, in dipolar-aprotic solvents, and the solvent is evaporated from the solutions, and wherein the SO3H, PO3H2or COOH form of the blends is prepared by aftertreating the blend polymer or the blend polymer membrane in diluted mineral acids at temperatures of from 20 to 80°C. 2. The process as claimed in claim 1, wherein said polymeric sulfonic acids, phosphonic acids and/or carboxylic acids or salts thereof are selected from polyetheretherkentones, polyethersulfones, polyphenylsulfones, polyphenylene sulfides and/or polyphenylene oxides. 3. The process as claimed in claim 1, wherein said polymeric sulfonic acid, phosphonic acid or carboxylic acid salts to be reacted with said polymers containing imidazole groups or benzimidazole groups are selected from polymers having aromatic core structures of formulas R1 or R2 as repeating units, where (Formula Removed) wherein R3 is hydrogen, trifluoromethyl or CnH2n+i, n = 1 to 10, especially methyl, R4 is hydrogen, CnH2n+i, n = 1 to 10, especially methyl or phenyl, and X= 1,2 or 3 which are connected via bridge groups R5, R6, R7 or R8, where R5 is -O-, R6 is -SO2-, R7 is >C=O, and R8 is -S-, especially: poly(etheretherketones) with ([R5-R2-R5-R2-R7-R2]n; X = 1, R4 = H) poly(ethersulfones) ([R1-R5-R2-R6-R2-R5]n; R2: X = 1, R4 = H, poly(ethersulfones) ([R2-R6-R2-R5]n; R2: X = 1, R4 = H, poly(phenylsulfones) ([(R2)2-R5-R2-R6-R2]n; R2: X = 2, R4 = H), poly(etherethersulfones)([R5-R2-R5-R2-R6]n-[R5-R2-R6-R]m; R2: X - 1, R4 = H, n/m = 0.18), poly(phenylenesulfides) ([R2-R8]n; R: X= 1, R4 = H); and/or poly(phenyleneoxides) ([R2-R5]n; R4 = CH3). 4. The process as claimed in claims 1 to 3, wherein a polymeric sulfonic acid, phosphonic acid and/or carboxylic acid is first dissolved in a dipolar-aprotic solvent, an equimolar amount, corresponding to the polymer's content of acid groups, of a primary, secondary or tertiary amine is added, then a basic polymer containing imidazole groups or benzimidazole groups and/or heterocyclic, especially heteroaromatic, nitrogen-containing basic moieties according to claim 1 in solid form or dissolved in a dipolar-aprotic solvent is added, and the latter polymer is also dissolved in the solution. 5. The process as claimed in any of claims 1 to 4, wherein polymer containing primary, secondary or tertiary basic nitrogen groups is added to and dissolved in said solution of the polymeric sulfonic acid or polymeric sulphonic acid salt, polymeric phosphonic acid or polymeric phosphonic acid salt, polymeric carboxylic acid or polymeric carboxylic acid salt and the basic polymer containing imidazole groups or benzimidazole groups and/or other heterocyclic, especially heteroaromatic, nitrogen- containing basic moieties according to claim 1. 6. Acid-base polymer blends or acid-base polymer blend membranes, obtainable by a process as claimed in claims 1-5. 7. The process as claimed in any of the preceding claims, wherein poly[2,2'-m- phenylene)-5,5'-bibenzimidazole] is used as said basic polymer containing benzimidazole groups. 8. The acid-base polymer blends or membranes thereof as claimed in claim 6 as and when used as proton-conducting electrolytes in membrane fuel cells (H2 polymer electrolyte fuel cells or direct methanol fuel cells), in polymer electrolyte membrane (PEM) electrolysis, in aqueous or non-aqueous electrodialysis, or in diffusion dialysis, or in per-vaporation, perstraction, gas separation, dialysis, ultrafiltration, nanofiltration or reverse osmosis. 9. A process for the preparation of acid-base polymer blends or acid-base polymer blend membranes, substantially as hereinbefore described with reference to the foregoing examples.

Documents:

in-pct-2000-00272-del-abstract.pdf

in-pct-2000-00272-del-claims.pdf

IN-PCT-2000-00272-DEL-Correspondence Others-(27-04-2011).pdf

in-pct-2000-00272-del-correspondence-others.pdf

in-pct-2000-00272-del-correspondence-po.pdf

in-pct-2000-00272-del-description (complete).pdf

in-pct-2000-00272-del-form-1.pdf

in-pct-2000-00272-del-form-13.pdf

in-pct-2000-00272-del-form-19.pdf

in-pct-2000-00272-del-form-2.pdf

in-pct-2000-00272-del-form-26.pdf

IN-PCT-2000-00272-DEL-Form-27-(27-04-2011).pdf

in-pct-2000-00272-del-form-3.pdf

in-pct-2000-00272-del-form-5.pdf

in-pct-2000-00272-del-form-6.pdf

in-pct-2000-00272-del-gpa.pdf

in-pct-2000-00272-del-pct-210.pdf

in-pct-2000-00272-del-pct-304.pdf

in-pct-2000-00272-del-pct-331.pdf

in-pct-2000-00272-del-pct-409.pdf

IN-PCT-2000-00272-DEL-Petition-137-(27-04-2011).pdf

in-pct-2000-00272-del-petition-137.pdf

in-pct-2000-00272-del-petition-138.pdf