Title of Invention	CEMENT-BASED PAVING BLOCKS FOR PHOTOCATALYTIC PAVING FOR THE ABATEMENT OF URBAN POLLUTANTS
Abstract	ABSTRACT 2281/CHENP/20Q5 "Cement-based paving blocks for photocatalytic paving for the abatement of urban pollutants" Paving blocks for photocatalytic paving comprising at least a base layer in cementitious material and a surface layer based on a cementitious composition comprising; at least a hydraulic binder, a photocatalyst capable of oxidizing organic and inorganic polluting substances present in the environment in the presence of environmental light, air and humidity, at least an aggregate, water and, optionally, a water reducing additive. Fig.2.

Title of Invention

CEMENT-BASED PAVING BLOCKS FOR PHOTOCATALYTIC PAVING FOR THE ABATEMENT OF URBAN POLLUTANTS

Abstract

ABSTRACT 2281/CHENP/20Q5 "Cement-based paving blocks for photocatalytic paving for the abatement of urban pollutants" Paving blocks for photocatalytic paving comprising at least a base layer in cementitious material and a surface layer based on a cementitious composition comprising; at least a hydraulic binder, a photocatalyst capable of oxidizing organic and inorganic polluting substances present in the environment in the presence of environmental light, air and humidity, at least an aggregate, water and, optionally, a water reducing additive. Fig.2.

Full Text	Cement-based paving blocks for photocatalytic paving for the abatement of urban pollutants FIELD OF THE INVENTION The present invention relates to a cement-based paving block for photocatalytic paving for the abatement of urban pollutants, more specifically to a paving block comprising a surface layer based on a cementitious composition with photocatalytic properties capable of abating organic and inorganic pollutants, such as condensation polymer aromatics, aldehydes, benzene, carbon black equivalent to PM10, oxides of nitrogen (NOx) and of sulfur (SOx), carbon monoxide (CO) and a base layer of cementitious nature. PRIOR ART Atmospheric pollution is caused by the presence of one or more undesirable or foreign substances in the air, in.quantities and for a duration that modify the healthiness of the air and create a hazard for human health. By considering the amount of air inhaled each day by one person (from 6 to 9 liters of air per minute at rest, that is around 9-13 cubic meters of air per day), it is easy to understand its importance for health and the risks related to inhaling polluted air. in general, the main sources of pollution are formed of atmospheric emissions deriving from production processes (industries and small businesses) and combustion processes (heating and vehicle traffic). The main source of pollution comes from vehicle traffic. This is responsible for atmospheric emissions of the combustion products of engines, for powders released through wear on brakes, tires and the road surface and finally for the hydrocarbons that vaporize from vehicle fuel tanks. Exhaust fumes from motor vehicles, deriving from incomplete fuel combustion, include numerous substances in the form of gases and powders. Among these, the main substances are: carbon monoxide (CO); oxides of nitrogen (NOx); oxides of sulfur (SOx); volatile organic compounds (VOC); total suspended particulates (TSP) containing a large number of pollutants: lead, cadmium, aromatic polycyclic hydrocarbons, to name but the most significant. A. The vast contribution of vehicle traffic towards atmospheric emissions is also confirmed by the fact that pollution in urban areas is no longer limited to the winter but has become, with more or less acute episodes, a constant throughout the entire year. The aforesaid atmospheric pollutants have an irritating action on the mucous membranes, in particularly those of the respiratory tract. To solve these problems different solutions have been proposed; one of the most interesting relates to the use of cementitious materials containing photocatalyste that, applied to the outside walls of buildings, are capable of oxidizing the polluting substances present in the environment that come into contact with the surfaces of these components.. The Applicant has filed in its name two patent applications for_ cementitious materials containing photocatalysts. The first application WO 98/05601, relates to cementitious materials comprising Ti02 particles mainly in anatase form capable of photo-oxidizing the polluting substances present in the environment in order to prolong preservation of the original color of the material once (aid. The second application WO 01/00541, instead relates to the use of specific additives to obtain a cementitious based paint with photocatalytic properties. Interlocking paving blocks are made of vibration-compressed concrete characterized by different geometries that are generally laid using "mosaic" laying solutions. Paving made of paving blocks can be used in residential and urban settings, where they are subject to light loads, and to produce surfaces subjected to medium-heavy loads such as pavements, pedestrian areas, areas surrounding buildings, cycle lanes, car parks, and roads with slow vehicle traffic. The patent EP 786283 describes interiocktng paving blocks for the abatement of NOx containing titanium dioxide in the surface layer. According to this document it is however necessary to use quantities of T1O2 varying from 5 to 50 percent in weight with respect to the cement in order to obtain an adequate degrading activity of the oxides of nitrogen. However, these quantities of Ti02 have the disadvantage of increasing the slipperiness of the paving block, which may be reduced by adding a suitable amount of sand to the mix. Therefore, the need was felt to obtain a interlocking paving block in which the quantity of Ti02 was minimized, not only for reasons related to cost, but also to decrease the slipperiness of the paving block, without reducing its photocatalytic activity. The interlocking paving block has some particularities that make it essentially different to normal road paving; in fact it is characterized by a high level of permeability that allows optimum drainage of water, is maintenance free and is easily removed and replaced. SUMMARY OF THE INVENTION The applicant has now surprisingly found that it is possible to obtain paving blocks for photocatalytic paving with a surface layer produced by a cementitious composition comprising a TiCVbased photocatalyst that allows the photocatalytic activity to be increased for contents of Ti02 equivalent to those used in prior art ranging from 0.1 % to 50% in mass with respect to the cement and that also allow efficacious use of Ti02 for lower dosages to those indicated in prior art, namely ranging from 0.1% to 4.9% in mass with respect to the cement or binder. The aforesaid paving blocks have photocatalytic activity in oxidizing urban pollutants equal to or even higher than the one described in prior art, for higher photocatalyst contents. Said application also allows considerable economic advantages to be obtained, as the quantity of photocatalyst can be reduced. The use of such low dosages for the surface layer allows slipperiness of the paving to be reduced without modification to the draining capacities. The Applicant has thus found a way to produce an improved type of paving block for photocatalytic paving, for the abatement of urban pollution, comprising at least a base layer, for example constituted by a cementitious material, and a surface layer, which remains in direct contact with the environment, based on a cementitious mixture, containing a TI02-based photocatalyst with photocatalytic properties, said photocatalyst having a surface area ranging from 15 to 350 m2/g and being added in a proportion ranging from 0.1 % to 50% in mass with respect to the cement, preferably from 0.1 % to 4.9% in mass with respect to the cement, said paving blocks for photocatalytic paving being capable of abating organic and inorganic pollutants present in the environment, such as condensation polymer arom&tics, aldehydes, benzene, carbon black equivalent to PM10, oxides of nitrogen (NO) and of sulfur (SOx). J DESCRIPTION OF THE FIGURES Figure 1: graphic representation of experimental details of the reaction chamber (1.5 L or 3.5 L) containing the photocatalyst sample, or catalyst sample, said chamber having a Pyrex optical window, as described in Example 3. Figure 2: graphic representation of the diagram I, as described in Example 3, wherein A is a mixing chamber, B is the reaction chamber, C is the NO* chemifuminescence detector, P is the inlet of chamber A, 1 and 2 are the paths taken by the flow of gas. DETAILED DESCRIPTION OF THE INVENTION Therefore, an object of the present invention is a paving block for photocatalytic paving capable of abating the pollutants present in the environment, comprising at least a base layer, generally in cementitious material, and a surface layer based on a cementitious composition comprising: I. a hydraulic binder II. a Ti02-based photocatalyst capable of oxidizing polluting organic and inorganic substances present in the environment in the presence of environmental light, air and humidity HI. water IV. at least an aggregate V. optionally a water reducing additive said TiOrbased photocatalyst having a specific surface ranging from 15 to 350 m2/g. In a preferred embodiment of the present invention, the surface layer of the paving block for photocatalytic paving has a void volume of 10-40% and/or. a water permeability of at least 0.01 cm/sec. The TiOrbased photocatalyst present in the surface layer of the paving block, forming the object of the present invention, is contained in the cementitious composition, or in its precursor the corresponding dry premix, constituting the base oi the surface layer, in a quantity ranging from 0.1% to 50% in mass with respect to the cement or binder, preferably from 0.1% to 4.9% in mass with respect to the cement or binder. More specifically, the quantity of Ti02 based photocatalyst having a specific surface ranging from 15 to 350 m2/g, present in the surface layer of the paving block, forming the object of the present invention, ranges from 0.12% to 2.6% in mass with respect to the cement or binder, preferably from 0.25% to 2.5% in mass with respect to the cement or binder, more preferably from 0.5% to 2.45% in mass with respect to the cement or binder, the most preferable being 1% in mass with respect to the cement or binder; alternatively said quantity of photocatalyst ranges from 2.6% to 4.9% in mass with respect to the cement or binder, preferably from 3% to 4.5% in mass with respect to the cement or binder, more preferably from 3.5% to 4% in mass with respect to the cement or binder. In a further embodiment of the present invention, the Applicant found a synergic effect, in the photocatalytic activity of oxidizing NOx, by Ti02-based photocatalysts with specific surface from 15 to 350 m2/g when in combination with Ti02 based photocatalysts with specific surface below 15 m2/gj Therefore, a further object of the present invention is a paving block for photocatalytic paving as described hereinbefore wherein the Ti02 with specific surface from 15 to 350m2/g is combined with TIO2 with specific surface below 15m2/g to provide a mixture comprising: from 99.9% to 0.1% in mass of said mixture, of Ti02 with specific surface from 15 to 350m2/g and from 0.1% to 99.9% in mass of said mixture, of TiOj with specific surface below 15m2/g, preferably a mixture comprising: from 75% to 25% in mass of said mixture, of Ti02 with specific surface from ■* 5 to 350m2/g and from 25% to 75% in mass of said mixture, of TI02 with specific surface below 15m2/g, more preferably a mixture comprising: from 70% to 55% in mass of said mixture, of Ti02 with specific surface from 15 to 350m2/g and from 30% to 45% in mass of said mixture, of Ti02 with specific surface below 15m2/g. The preferred photocatalyst according to the present invention is titanium dioxide (TiOz) or one of its precursors, and more typically "titanium oxide at least partially in anatase form". The expression "titanium oxide at least partially in anatase form" means that the photocatalyst particles present in the hydraulic binder of the present invention are particles of titanium dioxide (Ti02) having anatase structure for at least 5%, preferably for 25%, more preferably for at least 50% and even more preferably for at least for 70%, as percentage in mass with respect to the total titanium oxide Jn a particularly preferred aspect of the invention, the photocatalyst particles are particles of anatase titanium oxide at 100%. Said particles of titanium oxide having photocatalytic activity and present in the cementitious composition, and of its precursor the corresponding dry premix, forming the base of the surface layer of the paving block forming the object of the present invention, in any case have a specific surface ranging from 15 to 350 m2/gr, more specifically from 60 to 290 m2/gr, preferably from 105 to 250 m2/g. In a further preferred aspect of the invention Ti02 PC 105 and PC 500, commercialized by "Millennium Inorganic Chemical", was used. The expression "titanium dioxide precursor" means that the preferred photocatalyst is not only limited to Ti02 at least partially in anatase form" but it Is also extended to any product which added to the clinker, to the hydraulic binder, to the premix or to the mix, can form the Ti02 mainly in anatase form, optionally with suitable heat treatments. For example, "titanium paste" may be considered a valid precursor for the titanium dioxide-based photocatalyst of the present invention. Photocatalytic activity may also be obtained on Ti02 matrices doped with suitable atoms such as Fe(lll), Mg(ll), Mo(V), Ru(lll). Os(lll), Re(V), V((V) and Rh(lll). In particular, these atoms may substitute, at atomic level, the Ti(IV) present in the Ti02 matrix for at least 0.5% in mass of the total titanium dioxide (TtC^J. The method for obtaining these photocatalysts is described in the literature for example in J. Pnys. Chern. 1994, 98, 1127-34, Angew. Chemie 1994, 1148-9 and in Angew. Chemie int, Ed. 1994, 33, 1091 and in the Applicant's patent WO 01/00541. The thickness of the photocatalytic surface layer of the paving block for paving forming the object of the present invention, irrespective of the type of screed, may vary from values of around 0.1 mm to values of around 20 mm, without modifying its photocatalytic activity, preferably from 5 to 12 mm and even more preferably from 7 to 10 mm. The surface of the surface layer of the aforesaid paving block may be roughened in order to increase the specific surface in contact with the air and, at the same time, increase friction. This result may be obtained by suitably shaping the formworks or by acting mechanically on the surface after stripping. In the \atter case manual or automatic action can be taken, using suitable tools, to produce grooves or small craters distributed over the surface of the upper layer of the paving block. The term "paving block for photocatalytic paving" is intended as a paving block destined for road and also pedestrian paving, for example for pavements or pedestrian areas in general, having at least two layers; at least a layer based on cementitious material, and a surface layer based on a cementitious composition comprising photocatalysts capable of abating organic pollutants present in the environment. The term "organic pollutants present in the environment" is intended, purely as an example, as organic pollutants such as condensation polymer aromatics, aldehydes, benzene, carbon black equivalent to PM10, and inorganic pollutants such as oxides of nitrogen The paving blocks for photocatalytic paving according to the present invention are laid or produced according to common rules of good practice. The pollutants abated through the photocatalytic action of the surface layer of the paving block forming the object of the present invention are then removed from said photocatalytic surface through the cleansing action of rainfall or by periodically washing urban roads. The production or laying of the paving block forming the object of the present invention represents the essential eiement of the method for the abatement of organic and inorganic pollutants present in the environment. A further object of the present invention is therefore formed of a method for the abatement of organic and inorganic pollutants present in the environment comprising the faying of paving blocks for photocatalytic paving as described hereinbefore. Yet another object of the present invention is formed of the cementitious compositions, and of their precursors the corresponding dry premixes, suitable to prepare the surface layer of paving blocks for photocatalytic paving according to the invention. In particular, as a further preferred embodiment of the present invention the cementrtious composition, or its precursor the dry premix, essential components of the surface layer of the paving block do not include at least one of the following organic additives: a) at least a melamine resin, obtained from melamine condensed with formaldehyde; b) at least a cellulose ether; c') at least a polymer chosen from ethylene polymer, acrylic polymer and terpolymer comprising as co-monomers at least an ester of acrylic acid with an alcohol and at least an ester of vinyl alcohol with a carboxylic acid, or alternatively to the component c'), c") a latex chosen from acrylic latex, styrene latex, butadiene latex; d) at least a chemically modified starch. In paving blocks for paving according to the present invention the cementitious composition, or its precursor the corresponding dry premix, the base component of the surface layer of the paving block for paving may also include fillers of mineral origin or inorganic filling materials, synonymous with each other according to the present invention. Example of fillers of mineral origin are pozzolanas, metakaolin, slag, fly ash and silica fumes. !n the present text "binder" or "hydraulic binder" is intended as a. powdered material in solid state, dry, which when mixed with water provides plastic mixtures capable of setting and hardening, even under water, for example a cement. "Dry premix" is intended as a homogeneous mixture suitable to be mixed with water and provide cementitious compositions (such as mortars and concretes) comprising at least one cementitious binder, one or more additives for cementrtious compositions and, optionally, one or more aggregates. "Cementitious composition" or "cementitious mix" is intended as a composition wherein a binder is mixed with water, optionally with aggregates of different granulometry. Cementitious compositions therefore include both cementitious "pastes", i.e. mixtures of binder and water, without aggregates, and mixes, that is mixtures comprising water, binder and aggregates. The "aggregates", "inert materials" or "inert aggregates", synonymous with one another according to the present invention, may be fine aggregates, such as sand and fillers, and are defined in the standard UNI EN 206. Examples of mixes are mortars (mixtures with binder, water and fine aggregate), and concretes (mixtures with water, binder, fine aggregate and coarse aggregate). The "clinker" used to prepare a binder for the present invention is any clinker of Portland cement as defined according to the standard UNI EN 197.1, that is a hydraulic material at least two thirds in mass of which are composed of calcium silicates (3CaO Si02) and (2CaO Si02), the remaining part being composed of Al203, Fe203 and other oxides. The broad definition of "hydraulic binder", according to the present invention, includes both cements (white, grey or pigmented) defined according to the aforesaid standard UNI EN 197.1 and the so-called cements for storage dams, cementitious agglomerates and hydraulic limes as defined in Italian Law 26 May 1965 No. 595 and inorganic silicates. The broad definition "water reducing additive" according to the present invention includes both water reducing additives with normal efficacy and with high efficacy, which can respectively be called "fluidifying" and "super fluidifying" agents as defined in the standard UNI EN 934-2. According to the present invention, the dry premix or the cementitious compositions obtained from it may therefore contain white, grey or pigmented cement. In the present text the term in mass indicates that the photocatalyst is added to the mass of the binder, in the dry premix or in the cementitious compositions according to the present invention and is therefore distributed throughout the entire mass, that is also in the inner and deeper layers and not merely on the surface. Particularly preferred cementitious compositions of the present invention to produce the surface layer of the paving block are mortars and concretes suitable to produce, by means of vibration-compacting, precast components containing the aforesaid photocatalyst. Dry state is intended as the degree of humidity that does not significantly modify the composition of the mixture. Dry premixes, precursors of the cementitious compositions forming the surface layer of the paving block according to the present invention, therefore include at least a hydraulic binder (for example a cement), the aforesaid catalyst and at least an aggregate. According to typical embodiments of the present invention, the dry premix, precursor of the cementitious compositions, contains the following inorganic components: at least a hydraulic binder (typically a cement); at least an aggregate or inert material; optionally a.filler of mineral origin or an inorganic material, synonymous with each other according to the present invention, the aforesaid photocatalyst and the necessary water. The types and preferred quantities of hydraulic binder, aggregate and, optionally, filler of mineral origin are the same as those specified hereunder for the cementitious compositions. Preferred cementitious compositions, and their precursors the corresponding dry premixes, of the present invention, particularly suitable to prepare paving blocks for photocatalytic paving according to the present invention, in addition to the aforesaid photocatalyst, a hydraulic binder (typically a cement), include the following inorganic materials: at least an aggregate and optionally a filler of mineral origin or inorganic filling material. The cementitious compositions, and their precursors the corresponding dry premixes, to produce the surface layer of the paving blocks for photocata lytic paving according to the present invention, contain for example the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - hydraulic binder (typically cement): from 12% to 50% in mass, more preferably around 25% in mass; - aggregate (typically sand): from 50% to 88% in mass, more preferably around 75% in mass; - filler of mineral origin: up to 10% in mass, more preferably around 5% in mass. The hydraulic binder is typically a cement, preferably a grey cement. For example, it is possible to use a grey cement type I according to the standard UNI EN 197.1 (such as the grey cement type I- 52.5 R), more particularly in a quantity ranging from 12% to 45%, more preferably around 25% in mass of the total inorganic components in dry state, or type II (such as cement type ll/B-L, according to the standard UNI EN 197.1), in particular in a quantity ranging from 15% to 50% in mass of the total inorganic components in dry state. The aggregate is typically sand, silica or calcareous, having for example particles with dimensions ranging from 0.075 mm to 4 mm. The filler of mineral origin increases the strength and decreases the porosity of cementitious compositions containing it. The filler of mineral origin is for example chosen from metakaolin (Al203-SiO2) and silica fumes and their mixtures, preferably a mixture of these. The water reducing additive allows the water content in the cementitious composftions to be reduced without influencing their consistency or their rheological properties to be varied without influencing the water content or both these effects to be produced simultaneously. The water reducing additive is, for example, chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based. The quantity of water reducing additive optionally employed in cementitious compositions is the quantity required to provide optimum consistency when the mixture is fresh. In typical compositions according to the present invention described hereinbefore, the titanium dioxide is preferably 100% in anatase form. The cementitious compositions and their typical precursors the corresponding dry premixes according to the present invention have the compositions indicated hereunder in Examples 1 and 2. Cementitious compositions, and their corresponding precursors the corresponding dry premixes, are in particular mortars having binder/aggregate mass ratios ranging from 1/4 to 1/1 or concrete having binder/aggregate mass ratios ranging from 1/3 to 1/7. The quantity of water employed in the cementitious compositions is the quantity required for the hydration reaction of the binder and to provide optimum consistency when the mixture is fresh. The proportion of water, binder and, optionally, aggregates of the cementitious compositions may vary within wide limits, and is a function of the properties and of the final uses required of the mortars and concretes. In general terms, the quantity of water ranges from around 20% to 60% in mass with respect to the mass of the binder. The mixing method may be any conventional method. The temperature at which the binder, and any aggregates, are mixed with water is generally between +5°C and 30°C and preferably at least 20°C. The way in which the photocatalyst is added is not an essential characteristic of the invention; the photocatalyst may simply be added to the powder of the hydraulic binder or to the components of the mixture of additives, of the premix or of the cementitious compositions and mixed with any of the prior art methods, either using an automatic mixer or manually. The photocatalyst may also be suitably mixed with the mixture in the form of aqueous suspension. The fact that the photocatalyst can be added in such a simple manner makes the use of premixes particularly preferred to implement the present invention. A few examples, to be considered non-limiting, relative to the described invention, are provided hereunder. EXAMPLE 1 Cement-based formulation with high photocatalytic activity for the production of the surface layer of photocatalytic paving blocks. Dry mix n: 1 Optimal 1 Grey cement Type ll/B-LL 42,5 R % Silica sand {0,25 - 4 mm) % Titanium Dioxide % 1317 82.5 + 85.5 0.3 + 0.9 15.4 84 0.6 The quantity of water ranges from 6 to 6.5% in mass of the inorganic materials in dry state. EXAMPLE 2 Cement-based formulation with high photocatalytic activity for the production of the surface layer of photocatalytic paving blocks. Dry mix n. 2 Optimal 2 Grey cement Typell/A-LL 42,5 R % 1923 20.6 Silica sand (0.25 - 4 mm) % 7780 78.6 Titanium Dioxide % 0.6 + 1.0 0.8 The quantity of water ranges from 7 to 7.5% in mass of the inorganic materials in dry state. EXAMPLE 3 Some samples of paving block are prepared comprising a surface layer having the composition described in Examples 1 and 2, the NOx abating properties of which are verified. Instruments NOx are analyzed using a Monitor Labs Mode/ 8440E instrument, which functions according to the principle of chemiluminescence detection. The instrument has four sensitivity ranges: from 0.2 to 5 ppm {parts per million); from 0.1 to 10ppm; from 0.05 to 5 ppm; from 0.2to10ppm. As a function of the sensitivity ranges chosen, the precision of the instrument is 4 ppb (parts per billion) out of 100 ppb or 2.5 ppb out of 400 ppb. Experimentaf Set UP Diagram I hereunder, as shown in Figure 2, describes the method of measuring the degree of NOx and N02 abatement through photocatalytic action. DIAGRAM I A - is a mixing chamber wherein a mixture of NO/N02 or of N02 salts is diluted in air to provide the established quantity of poltutants. The adopted experimental procedure uses small bottles (2-5 L) of pure NO and N02 that are used to fill a vacuum line of the pure gas. By means of suitable sampling vials, the quantities of gas required are collected from this line to be diluted in air through the inlet P of the chamber. B - is the reaction chamber (1.5 L o 3.5 L) containing the photocatalyst sample, the experimental details of which are shown in Figure 1. C - in diagram I it is the NOx chemiluminescence detector described hereinbefore. The set-up shown in diagram I can operate both in conditions of continuous flow and with gas recirculation. The first case is shown in diagram I: if the flow of gas follows the path 1, the quantity of NOx can be measured at the reactor inlet; instead, with the path 2, the quantity of NOx can be measured at the outlet after the gas has come into contact with the catalyst, both in the dark and under irradiation. NOv abatement test Test pieces.with surfaces measuring 10 cm x 10 cm were inspected using an optical microscope in order to exclude the presence of cracks that could endanger the quallty.of the photocatalytic efficiency analysis. The degree of NOx abatement, using the layout of the path 1 described in the experimental set up, was evaluated as: Degree of NOx abatement (%) = (NOr concentration at the inlet- NCX concentration at the outlet) x 100 NOx concentration at the inlet The values are indicated in Table 1. TABLE 1 Percentage of NO oxidized through test pieces of paving block having different types of Ti02 in the surface layer Ti02 identification %ofTi02 compared with the cement Ti02 surface area (m2/g) After 20 min of recirculation in the dark After 20 min of recirculation in the light AT1* 3 AT1* 10 PC 105 3 60 78.6 91.5 PC 500 3 290 83.0 94.5 PC 50 3 35 81.0 90.8 ) for comparison in practice, it is observed that activity is higher if Ti02 with a surface area ranging from 15 to 290 m2/g is used; in other words, Ti02 with a surface area below 15 m2/g dosed at 10% in weight with respect to the binder acts like Ti02 dosed at 3% with a larger surface area. The use of Ti02 according to the indications in the present invention allows reduction of its weight percentage with respect to the binder, without penalizing the photocatalytic activity of the surface layer of the paving block. This makes it possible to reduce the unit cost of the cementitious mixture employed for the surface layer of the paving block forming the object of the present invention and, at the same time, reduce the slipperiness of said layer. EXAMPLE 4 In order to verify the efficacy of the photocatalytic system of the paving blocks of the invention, the content of the wash water of the paving blocks was analyzed. The photocatalytic action causes oxidizing of NO to N02 and consequent forming of nitrate ion that remains adsorbed in the cementitious matrix. Table 2 shows the distribution of the NC^'/NCy ratio detected in the leaching waters after having washed the test pieces with denatured water. Washing is considered complete after around 90% of the N02 adsorbed has been recovered. TABLE 2 Distribution of the N02" /N03" ratio detected in the leaching waters after having washed the test pieces with denatured water °) Tt02 identification %0fTiO2 compared with cement Ti02 surface area (m2/g) % N027NCV in the dark % N027NCV in the light AT1 3 AT1- 10 PC105 3 60 62.4/37.6 17.8/82.2 PC 500 3 290 68.3/317 13.0/87.0 PC 50 3 35 64.3/35.7 15.5/84.5 ) for comparison As canbe observed in Table 2, the ratio between nitrite and nitrate ions moves to increasing quantities of nitrate after exposure to light. Also in this case the activity of the photocatalyst with surface area > 15 m2/g is decidedly higher than the activity of the photocatalyst with surface area EXAMPLE 5 Essentially following the preparations described in examples 1 and 2, another three compositions were prepared characterized by equivalent dry components, as indicated hereunder Dry mix n. 3 White cement Type 1 42,5 R % Silica sand (0.25 - 4 mm) % Titanium Dioxide AT 1 % 19 80.2 0.80 Dry mix n. 4 White cement Type I 42,5 R % Silica sand (0.25-4 mm) % Titanium Dioxide PC 105 % 19 80.2 0.80 Dry mix n. White cement Type I 42.5 R % Silica sand (0,25 - 4 mm) % Titanium Dioxide PC 105+AT1 % 19 80.2 0.80 Essentially following the procedure described in Example 3 and the relative NO„ abatement test, the three compositions described hereinbefore were tested. TABLE 3 Composition % N02 abated 3 X 4 XX 5 XXX Evaluation of the % of N02 abated is expressed qualitatively, indicated as X= minimum, XX = high, XXX = optimum. As can be seen in table 3 there is a synergic effect due to the use of Ti02 mixtures with different surface areas. EXAMPLE 6 Tests were performed on samples of paving btock containing in the cementitious surface layer 3% of Ti02 with a surface area of 60 (m2/g) (samples B and C). The experiments were conducted in conditions of gas recirculation (NO2 + air). Sample A has no T1O2. The results are summarized in Table 4. TABLE 4 Sample Initial ppm ppm (60 min) Residual ppm (%) A (dark) 0.5 0.18 36 A (light) 0.48 0.20 40 B (light) 0.45 0.05 11 C (light) 0.48 0.06 12.5 The two samples B and C behave analogously under light. WE CLAIM: 1. A paving block for photocatalytic paving capable of abating pollutants present in the environment, comprising at least a base layer in cementitious material and a surface layer based on a cementitious composition which comprises : I. cement or lime II. a TiCVbased photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity III. water IV. at least an aggregate as defined in the standard UNI EN 206 V. optionally, a water reducing additive, as defined in the standard UNI EN 934-2 wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g. 2. The paving block as claimed in claim 1, wherein the surface layer of the paving block for photocatalytic paving has a void volume of 10-40% and/or water permeability of at least 0.01 cm/sec. 3. The paving block as claimed in claim 1, wherein the Ti02-based photocatalyst is present in the surface layer in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime. 4. The paving block as claimed in claim 1, wherein the titanium oxide photocatalyst is at least partially in anatase form. 5. The paving block as claimed in claim 4, wherein the particles of titanium dioxide (TiCh) have anatase structure for at (east 5%, as percentage in mass of the total titanium oxide (Ti02> 19 6. The paving block as claimed in claim 5, wherein the particles of titanium dioxide (Ti02) have anatase structure at 100% in mass of the total titanium oxide (Ti02). 7. The paving block as claimed in claim 1, wherein the thickness of the photocatalytic surface layer varies from values of around 0.1 mm to values of around 20 mm. 8. The paving block as claimed in claim 1, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures. 9. The paving block as claimed in claim 1, wherein the cementitious composition forming the base of the surface layer is in the form of mortar or concrete. 10. The paving block as claimed in claim 9, wherein the cementitious composition is a mortar having cement/aggregate mass ratios ranging from 1/4 to 1/1, or concrete having cement/aggregate mass ratios ranging from 1/3 to 1/7. 11. The paving block as claimed in claim 1, wherein the cementitious composition of the surface layer contains the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime : from 12% to 50% in mass; - aggregate: from 50% to 88% in mass; - filler of mineral origin: up to 10% in mass. 12. The paving block as claimed in claim 8, wherein the grey cement is grey cement of type I according to the standard UNI EN 197.1 (such as the grey cement type 1-52. 5 R), in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type II/B-L, according to the standard UNI EN 197.1), in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state. 20 13. The paving block as claimed in claim 1, wherein the aggregate is sand, silica or calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm. 14. The paving block as claimed in claim 1, wherein the quantity of water in the cementitious mixture of the surface layer ranges from around 20 to 60% in mass with respect to the mass of the cement or lime. 15. The paving blocks as claimed in claim 1, wherein the water reducing additive is chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based. 16. A cementitious composition which comprises : I. cement or lime II. a Ti02-based photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity III. water IV. at least an aggregate, as defined in the standard UNI EN 206 V. optionally, a water reducing additive, as defined in the standard UNI EN 934-2 wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g. 17. The composition as claimed in claim 16, wherein the Ti02-based photocatalyst is present in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime. 18. The composition as claimed in claim 16, wherein the titanium oxide photocatalyst is at least partially in anatase form. 21 19. The composition as claimed in claim 18, wherein the titanium oxide (Ti02) particles have anatase structure for at least 5%, as percentage in mass of the total titanium oxide (TiC>2). 20. The composition as claimed in claim 19, wherein the titanium oxide (Ti02) particles have anatase structure at 100% in mass of the total titanium oxide (Ti02). 21. The composition as claimed in claim 16, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures. 22. The composition as claimed in claim 16, wherein said composition is in the form of mortar or concrete. 23. The composition as claimed in claim 16, wherein the cementitious composition is a mortar having cement/aggregate mass ratios ranging from 1/4 to 1/1, or concrete having cement/aggregate mass ratios ranging from 1/3 to 1/7. 24. The composition as claimed in claim 16, containing the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime: from 12% to 50% in mass; - aggregate: from 50% to 88% in mass; - filler of mineral origin: up to 10% in mass. 25.The composition as claimed in claim 21, wherein the grey cement is grey cement of type I according to the standard UNI EN 197.1 (such as the grey cement type 1-52.5 R) in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type H/B-L, according to the standard UNI EN 197.1) in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state. 22 26. The composition as claimed in claim 16, wherein the aggregate is sand, silica or calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm. 27. The composition as claimed in claim 16, wherein the quantity of water in the cementitious mixture ranges from around 20 to 60% in mass with respect to the mass of the cement or lime. 28. The composition as claimed in claim 16, wherein the water reducing additive is chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based. 29. A dry premix, which comprises: I. cement or lime II. a TiC>2-based photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity III. at least an aggregate, as defined in the standard UNI EN 206 IV. optionally a water reducing additive as defined in the standard UNI EN 934-2 wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g. 30. The dry premix as claimed in claim 29, wherein the Ti02-based photocatalyst is present in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime. 31. The dry premix as claimed in claim 29, wherein the titanium oxide photocatalyst is at least partially in anatase form. 23 32. The dry premix as claimed in claim 31, wherein the titanium oxide (Ti02) particles have anatase structure for at least 5% in mass of the total titanium oxide (Ti02). 33. The dry premix as claimed in claim 32, wherein the titanium oxide (Ti02) particles have anatase structure at 100% in mass of the total titanium oxide (Ti02). 34. The dry premix as claimed in claim 29, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures. 35. The dry premix as claimed in claim 29, wherein said premix is in a form to provide a mortar or concrete. 36. The dry premix as claimed in claim 35, wherein the premix to provide a mortar has cement/aggregate mass ratios ranging from 1/4 to 1/1, or the premix to provide concrete has cement/aggregate mass ratios ranging from 1/3 to 1/7. 37. The dry premix as claimed in claim 29, containing the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime: from 12% to 50% in mass; -aggregate: from 50% to 88% in mass; -filler of mineral origin: up to 10% in mass. 38. The dry premix as claimed in claim 34, wherein the grey cement is grey cement of type 1 according to the standard UNI EN 197.1 (such as the grey cement type 1-52.5 R) in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type II/B-L, according to the standard UNI EN 197.1) in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state. 24 39. The dry premix as claimed in claim 29, wherein the aggregate is sand, silica or calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm. 40. The dry premix as claimed in claim 29, wherein the water reducing additive is chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based.

Full Text

Cement-based paving blocks for photocatalytic paving for the abatement of
urban pollutants
FIELD OF THE INVENTION
The present invention relates to a cement-based paving block for photocatalytic
paving for the abatement of urban pollutants, more specifically to a paving block
comprising a surface layer based on a cementitious composition with
photocatalytic properties capable of abating organic and inorganic pollutants, such
as condensation polymer aromatics, aldehydes, benzene, carbon black equivalent
to PM10, oxides of nitrogen (NOx) and of sulfur (SOx), carbon monoxide (CO) and
a base layer of cementitious nature.
PRIOR ART
Atmospheric pollution is caused by the presence of one or more undesirable or
foreign substances in the air, in.quantities and for a duration that modify the
healthiness of the air and create a hazard for human health.
By considering the amount of air inhaled each day by one person (from 6 to 9 liters
of air per minute at rest, that is around 9-13 cubic meters of air per day), it is easy
to understand its importance for health and the risks related to inhaling polluted
air.
in general, the main sources of pollution are formed of atmospheric emissions
deriving from production processes (industries and small businesses) and
combustion processes (heating and vehicle traffic).
The main source of pollution comes from vehicle traffic. This is responsible for
atmospheric emissions of the combustion products of engines, for powders
released through wear on brakes, tires and the road surface and finally for the
hydrocarbons that vaporize from vehicle fuel tanks.
Exhaust fumes from motor vehicles, deriving from incomplete fuel combustion,
include numerous substances in the form of gases and powders.
Among these, the main substances are: carbon monoxide (CO); oxides of nitrogen
(NOx); oxides of sulfur (SOx); volatile organic compounds (VOC); total suspended
particulates (TSP) containing a large number of pollutants: lead, cadmium,
aromatic polycyclic hydrocarbons, to name but the most significant.
A.

The vast contribution of vehicle traffic towards atmospheric emissions is also confirmed by the fact that pollution in urban areas is no longer limited to the winter but has become, with more or less acute episodes, a constant throughout the entire year. The aforesaid atmospheric pollutants have an irritating action on the mucous membranes, in particularly those of the respiratory tract. To solve these problems different solutions have been proposed; one of the most interesting relates to the use of cementitious materials containing photocatalyste that, applied to the outside walls of buildings, are capable of oxidizing the polluting substances present in the environment that come into contact with the surfaces of these components..
The Applicant has filed in its name two patent applications for_ cementitious materials containing photocatalysts. The first application WO 98/05601, relates to cementitious materials comprising Ti02 particles mainly in anatase form capable of photo-oxidizing the polluting substances present in the environment in order to prolong preservation of the original color of the material once (aid. The second application WO 01/00541, instead relates to the use of specific additives to obtain a cementitious based paint with photocatalytic properties.
Interlocking paving blocks are made of vibration-compressed concrete characterized by different geometries that are generally laid using "mosaic" laying solutions. Paving made of paving blocks can be used in residential and urban settings, where they are subject to light loads, and to produce surfaces subjected to medium-heavy loads such as pavements, pedestrian areas, areas surrounding buildings, cycle lanes, car parks, and roads with slow vehicle traffic. The patent EP 786283 describes interiocktng paving blocks for the abatement of NOx containing titanium dioxide in the surface layer.
According to this document it is however necessary to use quantities of T1O2 varying from 5 to 50 percent in weight with respect to the cement in order to obtain an adequate degrading activity of the oxides of nitrogen. However, these quantities of Ti02 have the disadvantage of increasing the slipperiness of the paving block, which may be reduced by adding a suitable amount of sand to the mix. Therefore, the need was felt to obtain a interlocking paving block in which the quantity of Ti02 was minimized, not only for reasons related to cost, but also to

decrease the slipperiness of the paving block, without reducing its photocatalytic activity. The interlocking paving block has some particularities that make it essentially different to normal road paving; in fact it is characterized by a high level of permeability that allows optimum drainage of water, is maintenance free and is easily removed and replaced. SUMMARY OF THE INVENTION
The applicant has now surprisingly found that it is possible to obtain paving blocks for photocatalytic paving with a surface layer produced by a cementitious composition comprising a TiCVbased photocatalyst that allows the photocatalytic activity to be increased for contents of Ti02 equivalent to those used in prior art ranging from 0.1 % to 50% in mass with respect to the cement and that also allow efficacious use of Ti02 for lower dosages to those indicated in prior art, namely ranging from 0.1% to 4.9% in mass with respect to the cement or binder. The aforesaid paving blocks have photocatalytic activity in oxidizing urban pollutants equal to or even higher than the one described in prior art, for higher photocatalyst contents. Said application also allows considerable economic advantages to be obtained, as the quantity of photocatalyst can be reduced. The use of such low dosages for the surface layer allows slipperiness of the paving to be reduced without modification to the draining capacities.
The Applicant has thus found a way to produce an improved type of paving block for photocatalytic paving, for the abatement of urban pollution, comprising at least a base layer, for example constituted by a cementitious material, and a surface layer, which remains in direct contact with the environment, based on a cementitious mixture, containing a TI02-based photocatalyst with photocatalytic properties, said photocatalyst having a surface area ranging from 15 to 350 m2/g and being added in a proportion ranging from 0.1 % to 50% in mass with respect to the cement, preferably from 0.1 % to 4.9% in mass with respect to the cement, said paving blocks for photocatalytic paving being capable of abating organic and inorganic pollutants present in the environment, such as condensation polymer arom&tics, aldehydes, benzene, carbon black equivalent to PM10, oxides of nitrogen (NO*) and of sulfur (SOx).
J*

DESCRIPTION OF THE FIGURES
Figure 1: graphic representation of experimental details of the reaction chamber
(1.5 L or 3.5 L) containing the photocatalyst sample, or catalyst sample, said
chamber having a Pyrex optical window, as described in Example 3.
Figure 2: graphic representation of the diagram I, as described in Example 3,
wherein A is a mixing chamber, B is the reaction chamber, C is the NO*
chemifuminescence detector, P is the inlet of chamber A, 1 and 2 are the paths
taken by the flow of gas.
DETAILED DESCRIPTION OF THE INVENTION
Therefore, an object of the present invention is a paving block for photocatalytic
paving capable of abating the pollutants present in the environment, comprising at
least a base layer, generally in cementitious material, and a surface layer based
on a cementitious composition comprising:
I. a hydraulic binder
II. a Ti02-based photocatalyst capable of oxidizing polluting organic and inorganic substances present in the environment in the presence of environmental light, air and humidity
HI. water
IV. at least an aggregate
V. optionally a water reducing additive
said TiOrbased photocatalyst having a specific surface ranging from 15 to 350
m2/g.
In a preferred embodiment of the present invention, the surface layer of the paving
block for photocatalytic paving has a void volume of 10-40% and/or. a water
permeability of at least 0.01 cm/sec.
The TiOrbased photocatalyst present in the surface layer of the paving block,
forming the object of the present invention, is contained in the cementitious
composition, or in its precursor the corresponding dry premix, constituting the base
oi the surface layer, in a quantity ranging from 0.1% to 50% in mass with respect
to the cement or binder, preferably from 0.1% to 4.9% in mass with respect to the
cement or binder.
More specifically, the quantity of Ti02 based photocatalyst having a specific

surface ranging from 15 to 350 m2/g, present in the surface layer of the paving block, forming the object of the present invention, ranges from 0.12% to 2.6% in mass with respect to the cement or binder, preferably from 0.25% to 2.5% in mass with respect to the cement or binder, more preferably from 0.5% to 2.45% in mass with respect to the cement or binder, the most preferable being 1% in mass with respect to the cement or binder; alternatively said quantity of photocatalyst ranges from 2.6% to 4.9% in mass with respect to the cement or binder, preferably from 3% to 4.5% in mass with respect to the cement or binder, more preferably from 3.5% to 4% in mass with respect to the cement or binder.
In a further embodiment of the present invention, the Applicant found a synergic effect, in the photocatalytic activity of oxidizing NOx, by Ti02-based photocatalysts with specific surface from 15 to 350 m2/g when in combination with Ti02 based photocatalysts with specific surface below 15 m2/gj
Therefore, a further object of the present invention is a paving block for photocatalytic paving as described hereinbefore wherein the Ti02 with specific surface from 15 to 350m2/g is combined with TIO2 with specific surface below 15m2/g to provide a mixture comprising: from 99.9% to 0.1% in mass of said mixture, of Ti02 with specific surface from 15 to 350m2/g and from 0.1% to 99.9% in mass of said mixture, of TiOj with specific surface below 15m2/g, preferably a mixture comprising: from 75% to 25% in mass of said mixture, of Ti02 with specific surface from ■* 5 to 350m2/g and from 25% to 75% in mass of said mixture, of TI02 with specific surface below 15m2/g, more preferably a mixture comprising: from 70% to 55% in mass of said mixture, of Ti02 with specific surface from 15 to 350m2/g and from 30% to 45% in mass of said mixture, of Ti02 with specific surface below 15m2/g.
The preferred photocatalyst according to the present invention is titanium dioxide (TiOz) or one of its precursors, and more typically "titanium oxide at least partially in anatase form".
The expression "titanium oxide at least partially in anatase form" means that the photocatalyst particles present in the hydraulic binder of the present invention are particles of titanium dioxide (Ti02) having anatase structure for at least 5%, preferably for 25%, more preferably for at least 50% and even more preferably

for at least for 70%, as percentage in mass with respect to the total titanium oxide
Jn a particularly preferred aspect of the invention, the photocatalyst particles are
particles of anatase titanium oxide at 100%. Said particles of titanium oxide
having photocatalytic activity and present in the cementitious composition, and of
its precursor the corresponding dry premix, forming the base of the surface layer
of the paving block forming the object of the present invention, in any case have
a specific surface ranging from 15 to 350 m2/gr, more specifically from 60 to 290
m2/gr, preferably from 105 to 250 m2/g.
In a further preferred aspect of the invention Ti02 PC 105 and PC 500,
commercialized by "Millennium Inorganic Chemical", was used.
The expression "titanium dioxide precursor" means that the preferred
photocatalyst is not only limited to Ti02 at least partially in anatase form" but it Is
also extended to any product which added to the clinker, to the hydraulic binder,
to the premix or to the mix, can form the Ti02 mainly in anatase form, optionally
with suitable heat treatments.
For example, "titanium paste" may be considered a valid precursor for the
titanium dioxide-based photocatalyst of the present invention.
Photocatalytic activity may also be obtained on Ti02 matrices doped with
suitable atoms such as Fe(lll), Mg(ll), Mo(V), Ru(lll). Os(lll), Re(V), V((V) and
Rh(lll).
In particular, these atoms may substitute, at atomic level, the Ti(IV) present in the
Ti02 matrix for at least 0.5% in mass of the total titanium dioxide (TtC^J.
The method for obtaining these photocatalysts is described in the literature for
example in J. Pnys. Chern. 1994, 98, 1127-34, Angew. Chemie 1994, 1148-9 and
in Angew. Chemie int, Ed. 1994, 33, 1091 and in the Applicant's patent WO
01/00541.
The thickness of the photocatalytic surface layer of the paving block for paving
forming the object of the present invention, irrespective of the type of screed, may
vary from values of around 0.1 mm to values of around 20 mm, without modifying
its photocatalytic activity, preferably from 5 to 12 mm and even more preferably
from 7 to 10 mm.

The surface of the surface layer of the aforesaid paving block may be roughened
in order to increase the specific surface in contact with the air and, at the same
time, increase friction. This result may be obtained by suitably shaping the
formworks or by acting mechanically on the surface after stripping. In the \atter
case manual or automatic action can be taken, using suitable tools, to produce
grooves or small craters distributed over the surface of the upper layer of the
paving block.
The term "paving block for photocatalytic paving" is intended as a paving block
destined for road and also pedestrian paving, for example for pavements or
pedestrian areas in general, having at least two layers; at least a layer based on
cementitious material, and a surface layer based on a cementitious composition
comprising photocatalysts capable of abating organic pollutants present in the
environment.
The term "organic pollutants present in the environment" is intended, purely as an
example, as organic pollutants such as condensation polymer aromatics,
aldehydes, benzene, carbon black equivalent to PM10, and inorganic pollutants
such as oxides of nitrogen The paving blocks for photocatalytic paving according to the present invention are
laid or produced according to common rules of good practice.
The pollutants abated through the photocatalytic action of the surface layer of the
paving block forming the object of the present invention are then removed from
said photocatalytic surface through the cleansing action of rainfall or by
periodically washing urban roads.
The production or laying of the paving block forming the object of the present
invention represents the essential eiement of the method for the abatement of
organic and inorganic pollutants present in the environment.
A further object of the present invention is therefore formed of a method for the
abatement of organic and inorganic pollutants present in the environment
comprising the faying of paving blocks for photocatalytic paving as described
hereinbefore.
Yet another object of the present invention is formed of the cementitious
compositions, and of their precursors the corresponding dry premixes, suitable to

prepare the surface layer of paving blocks for photocatalytic paving according to the invention.
In particular, as a further preferred embodiment of the present invention the cementrtious composition, or its precursor the dry premix, essential components of the surface layer of the paving block do not include at least one of the following organic additives:
a) at least a melamine resin, obtained from melamine condensed with formaldehyde; b) at least a cellulose ether; c') at least a polymer chosen from ethylene polymer, acrylic polymer and terpolymer comprising as co-monomers at least an ester of acrylic acid with an alcohol and at least an ester of vinyl alcohol with a carboxylic acid, or alternatively to the component c'), c") a latex chosen from acrylic latex, styrene latex, butadiene latex; d) at least a chemically modified starch.
In paving blocks for paving according to the present invention the cementitious composition, or its precursor the corresponding dry premix, the base component of the surface layer of the paving block for paving may also include fillers of mineral origin or inorganic filling materials, synonymous with each other according to the present invention. Example of fillers of mineral origin are pozzolanas, metakaolin, slag, fly ash and silica fumes.
!n the present text "binder" or "hydraulic binder" is intended as a. powdered material in solid state, dry, which when mixed with water provides plastic mixtures capable of setting and hardening, even under water, for example a cement.
"Dry premix" is intended as a homogeneous mixture suitable to be mixed with water and provide cementitious compositions (such as mortars and concretes) comprising at least one cementitious binder, one or more additives for cementrtious compositions and, optionally, one or more aggregates. "Cementitious composition" or "cementitious mix" is intended as a composition wherein a binder is mixed with water, optionally with aggregates of different granulometry. Cementitious compositions therefore include both cementitious "pastes", i.e. mixtures of binder and water, without aggregates, and mixes, that is mixtures comprising water, binder and aggregates.

The "aggregates", "inert materials" or "inert aggregates", synonymous with one another according to the present invention, may be fine aggregates, such as sand and fillers, and are defined in the standard UNI EN 206. Examples of mixes are mortars (mixtures with binder, water and fine aggregate), and concretes (mixtures with water, binder, fine aggregate and coarse
aggregate).
The "clinker" used to prepare a binder for the present invention is any clinker of
Portland cement as defined according to the standard UNI EN 197.1, that is a
hydraulic material at least two thirds in mass of which are composed of calcium
silicates (3CaO Si02) and (2CaO Si02), the remaining part being composed of
Al203, Fe203 and other oxides.
The broad definition of "hydraulic binder", according to the present invention,
includes both cements (white, grey or pigmented) defined according to the
aforesaid standard UNI EN 197.1 and the so-called cements for storage dams,
cementitious agglomerates and hydraulic limes as defined in Italian Law 26 May
1965 No. 595 and inorganic silicates.
The broad definition "water reducing additive" according to the present invention
includes both water reducing additives with normal efficacy and with high
efficacy, which can respectively be called "fluidifying" and "super fluidifying"
agents as defined in the standard UNI EN 934-2.
According to the present invention, the dry premix or the cementitious
compositions obtained from it may therefore contain white, grey or pigmented
cement.
In the present text the term in mass indicates that the photocatalyst is added to
the mass of the binder, in the dry premix or in the cementitious compositions
according to the present invention and is therefore distributed throughout the
entire mass, that is also in the inner and deeper layers and not merely on the
surface.
Particularly preferred cementitious compositions of the present invention to
produce the surface layer of the paving block are mortars and concretes suitable
to produce, by means of vibration-compacting, precast components containing the
aforesaid photocatalyst.

Dry state is intended as the degree of humidity that does not significantly modify the composition of the mixture.
Dry premixes, precursors of the cementitious compositions forming the surface layer of the paving block according to the present invention, therefore include at least a hydraulic binder (for example a cement), the aforesaid catalyst and at least an aggregate.
According to typical embodiments of the present invention, the dry premix, precursor of the cementitious compositions, contains the following inorganic components: at least a hydraulic binder (typically a cement); at least an aggregate or inert material; optionally a.filler of mineral origin or an inorganic material, synonymous with each other according to the present invention, the aforesaid photocatalyst and the necessary water. The types and preferred quantities of hydraulic binder, aggregate and, optionally, filler of mineral origin are the same as those specified hereunder for the cementitious compositions. Preferred cementitious compositions, and their precursors the corresponding dry premixes, of the present invention, particularly suitable to prepare paving blocks for photocatalytic paving according to the present invention, in addition to the aforesaid photocatalyst, a hydraulic binder (typically a cement), include the following inorganic materials: at least an aggregate and optionally a filler of mineral origin or inorganic filling material.
The cementitious compositions, and their precursors the corresponding dry premixes, to produce the surface layer of the paving blocks for photocata lytic paving according to the present invention, contain for example the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state:
- hydraulic binder (typically cement): from 12% to 50% in mass, more preferably
around 25% in mass;
- aggregate (typically sand): from 50% to 88% in mass, more preferably around 75% in mass;
- filler of mineral origin: up to 10% in mass, more preferably around 5% in mass. The hydraulic binder is typically a cement, preferably a grey cement.
For example, it is possible to use a grey cement type I according to the standard

UNI EN 197.1 (such as the grey cement type I- 52.5 R), more particularly in a
quantity ranging from 12% to 45%, more preferably around 25% in mass of the
total inorganic components in dry state, or type II (such as cement type ll/B-L,
according to the standard UNI EN 197.1), in particular in a quantity ranging from
15% to 50% in mass of the total inorganic components in dry state.
The aggregate is typically sand, silica or calcareous, having for example particles
with dimensions ranging from 0.075 mm to 4 mm.
The filler of mineral origin increases the strength and decreases the porosity of
cementitious compositions containing it.
The filler of mineral origin is for example chosen from metakaolin (Al203-SiO2) and
silica fumes and their mixtures, preferably a mixture of these.
The water reducing additive allows the water content in the cementitious
composftions to be reduced without influencing their consistency or their
rheological properties to be varied without influencing the water content or both
these effects to be produced simultaneously. The water reducing additive is, for
example, chosen from products based on lignosulphonates or naphthalene,
melamine or acrylic based. The quantity of water reducing additive optionally
employed in cementitious compositions is the quantity required to provide optimum
consistency when the mixture is fresh.
In typical compositions according to the present invention described hereinbefore,
the titanium dioxide is preferably 100% in anatase form.
The cementitious compositions and their typical precursors the corresponding dry
premixes according to the present invention have the compositions indicated
hereunder in Examples 1 and 2.
Cementitious compositions, and their corresponding precursors the
corresponding dry premixes, are in particular mortars having binder/aggregate
mass ratios ranging from 1/4 to 1/1 or concrete having binder/aggregate mass
ratios ranging from 1/3 to 1/7.
The quantity of water employed in the cementitious compositions is the quantity
required for the hydration reaction of the binder and to provide optimum
consistency when the mixture is fresh. The proportion of water, binder and,
optionally, aggregates of the cementitious compositions may vary within wide

limits, and is a function of the properties and of the final uses required of the
mortars and concretes. In general terms, the quantity of water ranges from
around 20% to 60% in mass with respect to the mass of the binder.
The mixing method may be any conventional method. The temperature at which
the binder, and any aggregates, are mixed with water is generally between +5°C
and 30°C and preferably at least 20°C.
The way in which the photocatalyst is added is not an essential characteristic of
the invention; the photocatalyst may simply be added to the powder of the
hydraulic binder or to the components of the mixture of additives, of the premix or
of the cementitious compositions and mixed with any of the prior art methods,
either using an automatic mixer or manually.
The photocatalyst may also be suitably mixed with the mixture in the form of
aqueous suspension. The fact that the photocatalyst can be added in such a
simple manner makes the use of premixes particularly preferred to implement the
present invention. A few examples, to be considered non-limiting, relative to the
described invention, are provided hereunder.
EXAMPLE 1
Cement-based formulation with high photocatalytic activity for the production of
the surface layer of photocatalytic paving blocks.

Dry mix n: 1 Optimal 1
Grey cement Type ll/B-LL 42,5 R % Silica sand {0,25 - 4 mm) % Titanium Dioxide % 13*17
82.5 + 85.5
0.3 + 0.9 15.4 84 0.6
The quantity of water ranges from 6 to 6.5% in mass of the inorganic materials in
dry state.
EXAMPLE 2
Cement-based formulation with high photocatalytic activity for the production of
the surface layer of photocatalytic paving blocks.

Dry mix n. 2 Optimal 2

Grey cement Typell/A-LL 42,5 R % 19*23 20.6
Silica sand (0.25 - 4 mm) % 77*80 78.6
Titanium Dioxide % 0.6 + 1.0 0.8
The quantity of water ranges from 7 to 7.5% in mass of the inorganic materials in
dry state.
EXAMPLE 3
Some samples of paving block are prepared comprising a surface layer having the
composition described in Examples 1 and 2, the NOx abating properties of which
are verified.
Instruments
NOx are analyzed using a Monitor Labs Mode/ 8440E instrument, which functions
according to the principle of chemiluminescence detection. The instrument has
four sensitivity ranges:
from 0.2 to 5 ppm {parts per million); from 0.1 to 10ppm; from 0.05 to 5 ppm; from
0.2to10ppm.
As a function of the sensitivity ranges chosen, the precision of the instrument is 4
ppb (parts per billion) out of 100 ppb or 2.5 ppb out of 400 ppb.
Experimentaf Set UP
Diagram I hereunder, as shown in Figure 2, describes the method of measuring
the degree of NOx and N02 abatement through photocatalytic action.
DIAGRAM I
A - is a mixing chamber wherein a mixture of NO/N02 or of N02 salts is diluted in
air to provide the established quantity of poltutants. The adopted experimental
procedure uses small bottles (2-5 L) of pure NO and N02 that are used to fill a
vacuum line of the pure gas. By means of suitable sampling vials, the quantities of
gas required are collected from this line to be diluted in air through the inlet P of
the chamber.
B - is the reaction chamber (1.5 L o 3.5 L) containing the photocatalyst sample,
the experimental details of which are shown in Figure 1.
C - in diagram I it is the NOx chemiluminescence detector described hereinbefore.
The set-up shown in diagram I can operate both in conditions of continuous flow
and with gas recirculation. The first case is shown in diagram I: if the flow of gas

follows the path 1, the quantity of NOx can be measured at the reactor inlet;
instead, with the path 2, the quantity of NOx can be measured at the outlet after
the gas has come into contact with the catalyst, both in the dark and under
irradiation.
NOv abatement test
Test pieces.with surfaces measuring 10 cm x 10 cm were inspected using an
optical microscope in order to exclude the presence of cracks that could endanger
the quallty.of the photocatalytic efficiency analysis. The degree of NOx abatement,
using the layout of the path 1 described in the experimental set up, was evaluated
as:
Degree of NOx abatement (%) =
(NOr concentration at the inlet- NCX concentration at the outlet) x 100
NOx concentration at the inlet The values are indicated in Table 1. TABLE 1
Percentage of NO* oxidized through test pieces of paving block having different types of Ti02 in the surface layer

Ti02 identification %ofTi02
compared with
the cement Ti02 surface area (m2/g) After 20 min of
recirculation in
the dark After 20 min of
recirculation in
the light
AT1* 3 AT1* 10 PC 105 3 60 78.6 91.5
PC 500 3 290 83.0 94.5
PC 50 3 35 81.0 90.8
*) for comparison
in practice, it is observed that activity is higher if Ti02 with a surface area ranging
from 15 to 290 m2/g is used; in other words, Ti02 with a surface area below 15
m2/g dosed at 10% in weight with respect to the binder acts like Ti02 dosed at 3%
with a larger surface area.
The use of Ti02 according to the indications in the present invention allows
reduction of its weight percentage with respect to the binder, without penalizing

the photocatalytic activity of the surface layer of the paving block. This makes it possible to reduce the unit cost of the cementitious mixture employed for the surface layer of the paving block forming the object of the present invention and, at the same time, reduce the slipperiness of said layer. EXAMPLE 4
In order to verify the efficacy of the photocatalytic system of the paving blocks of the invention, the content of the wash water of the paving blocks was analyzed. The photocatalytic action causes oxidizing of NO to N02 and consequent forming of nitrate ion that remains adsorbed in the cementitious matrix. Table 2 shows the distribution of the NC^'/NCy ratio detected in the leaching waters after having washed the test pieces with denatured water. Washing is considered complete after around 90% of the N02 adsorbed has been recovered. TABLE 2
Distribution of the N02" /N03" ratio detected in the leaching waters after having washed the test pieces with denatured water °)

Tt02 identification %0fTiO2
compared with
cement Ti02 surface area (m2/g) % N027NCV in the dark % N027NCV in the light
AT1 * 3 AT1- 10 PC105 3 60 62.4/37.6 17.8/82.2
PC 500 3 290 68.3/317 13.0/87.0
PC 50 3 35 64.3/35.7 15.5/84.5
*) for comparison
As canbe observed in Table 2, the ratio between nitrite and nitrate ions moves to
increasing quantities of nitrate after exposure to light.
Also in this case the activity of the photocatalyst with surface area > 15 m2/g is
decidedly higher than the activity of the photocatalyst with surface area EXAMPLE 5
Essentially following the preparations described in examples 1 and 2, another three compositions were prepared characterized by equivalent dry components, as indicated hereunder

Dry mix n. 3
White cement Type 1 42,5 R % Silica sand (0.25 - 4 mm) % Titanium Dioxide AT 1 % 19 80.2 0.80

Dry mix n. 4
White cement Type I 42,5 R % Silica sand (0.25-4 mm) % Titanium Dioxide PC 105 % 19 80.2 0.80

Dry mix

n.

White cement Type I 42.5 R % Silica sand (0,25 - 4 mm) % Titanium Dioxide PC 105+AT1 %

19 80.2 0.80

Essentially following the procedure described in Example 3 and the relative NO„ abatement test, the three compositions described hereinbefore were tested.
TABLE 3

Composition % N02 abated
3 X
4 XX
5 XXX
Evaluation of the % of N02 abated is expressed qualitatively, indicated as X=
minimum, XX = high, XXX = optimum.
As can be seen in table 3 there is a synergic effect due to the use of Ti02 mixtures
with different surface areas.
EXAMPLE 6
Tests were performed on samples of paving btock containing in the cementitious
surface layer 3% of Ti02 with a surface area of 60 (m2/g) (samples B and C). The

experiments were conducted in conditions of gas recirculation (NO2 + air). Sample A has no T1O2. The results are summarized in Table 4.
TABLE 4

Sample Initial ppm ppm (60 min) Residual ppm
(%)
A* (dark) 0.5 0.18 36
A (light) 0.48 0.20 40
B (light) 0.45 0.05 11
C (light) 0.48 0.06 12.5
The two samples B and C behave analogously under light.

WE CLAIM:
1. A paving block for photocatalytic paving capable of abating pollutants
present in the environment, comprising at least a base layer in cementitious
material and a surface layer based on a cementitious composition which
comprises :
I. cement or lime
II. a TiCVbased photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity
III. water
IV. at least an aggregate as defined in the standard UNI EN 206
V. optionally, a water reducing additive, as defined in the standard UNI EN 934-2
wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g.
2. The paving block as claimed in claim 1, wherein the surface layer of the paving block for photocatalytic paving has a void volume of 10-40% and/or water permeability of at least 0.01 cm/sec.
3. The paving block as claimed in claim 1, wherein the Ti02-based photocatalyst is present in the surface layer in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime.
4. The paving block as claimed in claim 1, wherein the titanium oxide photocatalyst is at least partially in anatase form.
5. The paving block as claimed in claim 4, wherein the particles of titanium dioxide (TiCh) have anatase structure for at (east 5%, as percentage in mass of the total titanium oxide (Ti02>
19

6. The paving block as claimed in claim 5, wherein the particles of titanium dioxide (Ti02) have anatase structure at 100% in mass of the total titanium oxide (Ti02).
7. The paving block as claimed in claim 1, wherein the thickness of the photocatalytic surface layer varies from values of around 0.1 mm to values of around 20 mm.
8. The paving block as claimed in claim 1, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures.
9. The paving block as claimed in claim 1, wherein the cementitious composition forming the base of the surface layer is in the form of mortar or concrete.
10. The paving block as claimed in claim 9, wherein the cementitious composition is a mortar having cement/aggregate mass ratios ranging from 1/4 to 1/1, or concrete having cement/aggregate mass ratios ranging from 1/3 to 1/7.
11. The paving block as claimed in claim 1, wherein the cementitious composition of the surface layer contains the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime : from 12% to 50% in mass; - aggregate: from 50% to 88% in mass; - filler of mineral origin: up to 10% in mass.
12. The paving block as claimed in claim 8, wherein the grey cement is grey cement of type I according to the standard UNI EN 197.1 (such as the grey cement type 1-52. 5 R), in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type II/B-L, according to the standard UNI EN 197.1), in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state.
20

13. The paving block as claimed in claim 1, wherein the aggregate is sand, silica or calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm.
14. The paving block as claimed in claim 1, wherein the quantity of water in the cementitious mixture of the surface layer ranges from around 20 to 60% in mass with respect to the mass of the cement or lime.
15. The paving blocks as claimed in claim 1, wherein the water reducing additive is chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based.
16. A cementitious composition which comprises :

I. cement or lime
II. a Ti02-based photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity
III. water
IV. at least an aggregate, as defined in the standard UNI EN 206
V. optionally, a water reducing additive, as defined in the standard UNI EN 934-2
wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g.
17. The composition as claimed in claim 16, wherein the Ti02-based photocatalyst is present in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime.
18. The composition as claimed in claim 16, wherein the titanium oxide photocatalyst is at least partially in anatase form.
21

19. The composition as claimed in claim 18, wherein the titanium oxide (Ti02) particles have anatase structure for at least 5%, as percentage in mass of the total titanium oxide (TiC>2).
20. The composition as claimed in claim 19, wherein the titanium oxide (Ti02) particles have anatase structure at 100% in mass of the total titanium oxide (Ti02).
21. The composition as claimed in claim 16, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures.
22. The composition as claimed in claim 16, wherein said composition is in the form of mortar or concrete.
23. The composition as claimed in claim 16, wherein the cementitious composition is a mortar having cement/aggregate mass ratios ranging from 1/4 to 1/1, or concrete having cement/aggregate mass ratios ranging from 1/3 to 1/7.
24. The composition as claimed in claim 16, containing the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime: from 12% to 50% in mass; - aggregate: from 50% to 88% in mass; - filler of mineral origin: up to 10% in mass.
25.The composition as claimed in claim 21, wherein the grey cement is grey cement of type I according to the standard UNI EN 197.1 (such as the grey cement type 1-52.5 R) in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type H/B-L, according to the standard UNI EN 197.1) in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state.
22

26. The composition as claimed in claim 16, wherein the aggregate is sand, silica or calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm.
27. The composition as claimed in claim 16, wherein the quantity of water in the cementitious mixture ranges from around 20 to 60% in mass with respect to the mass of the cement or lime.
28. The composition as claimed in claim 16, wherein the water reducing additive is chosen from products based on lignosulphonates or naphthalene, melamine or acrylic based.
29. A dry premix, which comprises:

I. cement or lime
II. a TiC>2-based photocatalyst capable of oxidizing polluting organic and inorganic substances in the environment in the presence of environmental light, air and humidity
III. at least an aggregate, as defined in the standard UNI EN 206
IV. optionally a water reducing additive as defined in the standard UNI EN 934-2
wherein the Ti02-based photocatalyst has a specific surface area selected in the range from 60 to 290 m2/g.
30. The dry premix as claimed in claim 29, wherein the Ti02-based photocatalyst is present in quantities ranging from 0. 1% to 50% in mass with respect to the cement or lime.
31. The dry premix as claimed in claim 29, wherein the titanium oxide photocatalyst is at least partially in anatase form.
23

32. The dry premix as claimed in claim 31, wherein the titanium oxide (Ti02) particles have anatase structure for at least 5% in mass of the total titanium oxide (Ti02).
33. The dry premix as claimed in claim 32, wherein the titanium oxide (Ti02) particles have anatase structure at 100% in mass of the total titanium oxide (Ti02).
34. The dry premix as claimed in claim 29, wherein the cement is chosen from the group consisting of: white, grey or pigmented cement or their mixtures.
35. The dry premix as claimed in claim 29, wherein said premix is in a form to provide a mortar or concrete.
36. The dry premix as claimed in claim 35, wherein the premix to provide a mortar has cement/aggregate mass ratios ranging from 1/4 to 1/1, or the premix to provide concrete has cement/aggregate mass ratios ranging from 1/3 to 1/7.
37. The dry premix as claimed in claim 29, containing the following percentages in mass of inorganic components, with reference to the total mass of the inorganic components in dry state: - cement or lime: from 12% to 50% in mass; -aggregate: from 50% to 88% in mass; -filler of mineral origin: up to 10% in mass.
38. The dry premix as claimed in claim 34, wherein the grey cement is grey cement of type 1 according to the standard UNI EN 197.1 (such as the grey cement type 1-52.5 R) in a quantity ranging from 12% to 45% in mass of the total inorganic components in dry state, or type II (such as cement type II/B-L, according to the standard UNI EN 197.1) in a quantity ranging from 15% to 50% in mass of the total of inorganic components in dry state.
24

39. The dry premix as claimed in claim 29, wherein the aggregate is sand, silica or
calcareous, having particles with dimensions ranging from 0.075 mm to 4 mm.
40. The dry premix as claimed in claim 29, wherein the water reducing additive is
chosen from products based on lignosulphonates or naphthalene, melamine or
acrylic based.

Documents:

2281-chenp-2005 abstract duplicate.pdf

2281-chenp-2005 abstract.jpg

2281-chenp-2005 abstract.pdf

2281-chenp-2005 assignment.pdf

2281-chenp-2005 claims duplicate.pdf

2281-chenp-2005 claims.pdf

2281-chenp-2005 correspondence-others.pdf

2281-chenp-2005 correspondence-po.pdf

2281-chenp-2005 description(complete) duplicate.pdf

2281-chenp-2005 description(complete).pdf

2281-chenp-2005 drawings duplicate.pdf

2281-chenp-2005 drawings.pdf

2281-chenp-2005 form-1.pdf

2281-chenp-2005 form-18.pdf

2281-chenp-2005 form-26.pdf

2281-chenp-2005 form-3.pdf

2281-chenp-2005 form-5.pdf

2281-chenp-2005 others.pdf

2281-chenp-2005 pct search report.pdf

2281-chenp-2005 pct.pdf

2281-chenp-2005 petition.pdf

« Previous Patent

Next Patent »

Patent Number

229736

Indian Patent Application Number

2281/CHENP/2005

PG Journal Number

13/2009

Publication Date

27-Mar-2009

Grant Date

19-Feb-2009

Date of Filing

15-Sep-2005

Name of Patentee

ITALCEMENTI S.P.A.

Applicant Address

Via Camozzi, 24, I-24121 Bergamo,

Inventors:

#	Inventor's Name	Inventor's Address
1	CASSAR, Luigi	Via Europa, 42, I-20097 San Donato Milanese,
2	CUCITORE, Roberto	Via Lombardia 6, I-24124 Redona,
3	PEPE, Carmine	Via Tremana, 38, I-24123 Bergamo,

PCT International Classification Number

C04B14/30

PCT International Application Number

PCT/EP2004/001525

PCT International Filing date

2004-02-18

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	MI2003A000291	2003-02-18	Italy