Indian Patents. 251160:INSULATED GLASS UNIT POSSESSING ROOM TEMPATURE-CURED SILOXANE SEALANT COMPOSITION OF REDUCED GAS PERMEABILITY

Title of Invention	INSULATED GLASS UNIT POSSESSING ROOM TEMPATURE-CURED SILOXANE SEALANT COMPOSITION OF REDUCED GAS PERMEABILITY
Abstract	The invention relates to an insulated glass unit having an increased service life. Wherein an outer glass pane and inner glass pane are sealed to a spacer to provide an improved gas impermeable space.

Full Text	FORM 2 THE PATENT ACT 1970 (39 of 1970) The Patents Rules, 2003 COMPLETE SPECIFICATION (See Section 10, and rule 13) TITLE OF INVENTION INSULATED GLASS UNIT POSSESSING ROOM TEMPATURE-CURED SEALANT COMPOSITION OF REDUCED GAS PERMEABILITY SILOXANE APPLICANT(S) a) Name b) Nationality c) Address MOMENTIVE PERFORMANCE MATERIALS, INC, AMERICAN Company 187 DANBURY ROAD, WILTON, CONNECTICUT 06897-4122, U.S.A. PREAMBLE TO THE DESCRIPTION The following specification particularly describes the invention and the manner in which it is to be performed : - FIELD OF THE INVENTION This invention is generally related to thermally insulating structures, and more particularly to a high thermal efficiency, insulated glass unit structure sealed with room temperature cured compositions having reduced permeability to gas, or mixtures of gases. BACKGROUND OF THE INVENTION Insulating glass units (IGU) commonly have two panels of glass separated by a spacer. The two panels of glass are placed parallel to each other and sealed at their periphery such that the space between the panels, or the inner space, is completely enclosed. The inner space is typically filled with air. The transfer of energy through an insulating glass unit of this typical construction is reduced, due to the inclusion of the insulating layer of air in the inner space, as compared to a single panel of glass. The energy transfer may be further reduced by increasing the separation between the panels to increase the insulating blanket of air. There is a limit to the maximum separation beyond which convection within the air between the panels can increase energy transfer. The energy transfer may be further reduced by adding more layers of insulation in the form of additional inner spaces and enclosing glass panels. For example three parallel spaced apart panels of glass separated by two inner spaces and sealed at their periphery. In this manner the separation of the panels is kept below the maximum limit imposed by convection effects in the airspace, yet the overall energy transfer can be further reduced. If further reduction in energy transfer is desired then additional inner spaces can be added. Additionally, the energy transfer of sealed insulating glass units may be reduced by substituting the air in a sealed insulated glass window for a denser, lower conductivity gas. Suitable gases should be colorless, non-toxic, non-corrosive, non¬flammable, unaffected by exposure to ultraviolet radiation, and denser than air, and of lower conductivity than air. Argon, krypton, xenon, and sulfur hexaflouride are examples of gases which are commonly substituted for air in insulating glass windows to reduce energy transfer. -2- Various types of sealants are currently used in the manufacture of insulated glass units including both curing and non-curing systems. Liquid polysulphides, polyurethanes and silicones represent curing systems, which are commonly used, while polybutylene-polyisoprene copolymer rubber based hot melt sealants are commonly used non-curing systems. Liquid polysulphides and polyurethanes are generally two component systems comprising a base and a curing agent that are then mixed just prior to application to the glass. Silicones may be one component as well as two component systems. Two component systems require a set mix ratio, two-part mixing equipment and cure time before the insulating glass units can be moved onto the next manufacturing stage. However, these sealant compositions are susceptible to permeability from the low conductivity energy transfer gases (e.g. argon) used to enhance the performance of insulated glass units. As a result of this permeability, the reduced energy transfer maintained by the gas between the panels of glass is lost over time. There remains a need for sealants with superior barrier protection and even higher thermal insulation stability that overcomes the deficiencies described above, and is highly suitable for applications that are easy to apply and have excellent adhesion. SUMMARY OF THE INVENTION The present invention relates to an insulated glass unit with increased thermal insulation stability. Specifically, the present invention relates to an insulated glass unit comprising at least two spaced-apart sheets of glass in spaced relationship to each other, a low thermal conductivity gas therebetween and gas sealant element including a curable sealant composition comprised of a) diorganopolysiloxane exhibiting permeability to said gas; b) at least one polymer having a permeability to said gas that is less than the permeability of diorganopolysiloxane polymer; c) cross-linker; and, d) catalyst for the cross-linker reaction. -3- The curable sealant composition of the present invention advantageously provides for a 50 percent reduction in gas permeability and reduced moisture leakage, which provides longer service life of insulated glass units (IGU). BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a sectional side view of a double glazed insulated glass unit (IGU). Fig. 2 is a graph illustration of the permeability of Examples 1-3 to argon gas. Fig. 3 is a graph illustration of the permeability of Example 5-7 to argon gas. Fig. 4 is a graph illustration of percent decrease in permeability of Example 5-7 to argon gas. DETAILED DESCRIPTION OF THE INVENTION The detailed embodiments of the present invention are disclosed herein. It should be understood, however, that the disclosed embodiments are merely exemplary of the invention, which may be embodied in various forms. Therefore, the details disclosed herein are not to be interpreted as limited, but merely as the basis for the claims and as a basis for teaching one skilled in the art how to make and/or use the invention. With reference to Fig. 1 an insulated glass unit 10 incorporating a curable sealant composition 7 providing separation of adjacent panes 1, 2 and sealing of the gas impermeable space 6 therebetween is shown. As those skilled in the art will readily appreciate, the inventive concepts of the present curable sealant composition 7 may be applied in various manners without departing from the spirit of the present invention. For example, it is contemplated that the present curable sealant composition may be used in conjunction with other materials, for example, various types of glass, including, clear float glass, annealed glass, tempered glass, solar glass, tinted glass, and Low-E glass, acrylic sheets and polycarbonate sheets. -4- In accordance with the present invention, the curable sealant composition 7 is applied in the construction of an insulated glass unit with a double pane glass structure. The insulated glass unit,- therefore, generally includes a first glass pane 1 and a second glass pane 2 separated by a continuous spacer 5, a primary sealant 4, and curable sealant composition 7 positioned between the first glass pane 1 and the second glass pane 2. The use of curable sealant composition 7 in accordance with the present invention provides improved gas barrier characteristics and moisture leakage characteristics. As a result, the curable sealant composition 7 provides for longer in service performance of insulated glass units. The dimensions of continuous spacer 5 will determine the size of the gas impermeable space 6 formed between the first glass 1 and second glass 2 when the sheets of glass are sealed to spacer 5 using primary sealant 1 and curable sealant composition 7 of the present invention. A glazing bead 8, as known in the art, is placed between glass sheets 1 and 2 and window frame 9. The spacer 5 may be filled with a desiccant that will keep the sealed interior of the gas impermeable space 6 of the insulated glass unit dry. The desiccant should be one which will not adsorb the low thermal conductivity gas or other gases used if a gas mixture is used to fill the interior of the insulated glass unit. The primary sealant 4 of the insulated glass unit may be comprised of polymeric materials as known in the art. For example, rubber base material, such as polyisobutylene, butyl rubber, polysulfide, EPDM rubber nitrile rubber, or the like. Other materials include, but are not limited to, compounds comprising polyisobutylene/polyisoprene copolymers, polyisobutylene polymers, brominated olefin polymers, copolymers of polisobutylene and para-methyl styrene, copolymers of polyisobutylene and brominated para-methylstyrene, butyl rubber-copolymer of isobutylene and isoprene, ethylene-propylene polymers, polysulfide polymers, polyurethane polymers, and styrene butadiene polymers. -5 As recited above, the primary sealant 4 can be fabricated of a material such as polyisobutylene, which has very good sealing properties. The glazing bead 8 is a sealant that is sometimes referred to as the glazing bedding and may be in the form of a silicone or butyl. A desiccant may be built into the continuous spacer 5 and is intended to remove moisture from the insulated glass or gas impermeable space between glass pane 1 and glass pane 2. The curable sealant composition 7 of the present invention comprises diorganopolysiloxane polymer or blend thereof and at least one additional polymer. A general description of each of the components of the formulation are given as follows: a diorganopolysiloxane or blend of diorganopolysiloxanes exhibiting permeability to a gas or mixtures of gases wherein the silicon atom at each polymer chain end is silanol terminated; whereby the viscosity of the siloxanes can be from about 1,000 to 200,000 cps at 25°C; a polymer exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a); an alkylsilicate cross-linker of the general formula: (R140)(RIS0)(RI6O)(Rl70)si; a catalyst useful for facilitating crosslinking in silicone sealant compositions. The sealant composition of the present invention may further comprise an optional component, such as, filler, adhesion promoter, non-ionic surfactant, and the like and mixtures thereof. The silanol terminated diorganopolysiloxane polymer (a), generally has the formula: -6- with the subscript a = 2 and b equal to or greater than 1 and with the subscript c zero or positive where M = (HO)3.x.yRlxR2ySi01/2; with the subscript x = 0, 1 or 2 and the subscript y is either 0 or 1, subject to the limitation that x + y is less than or equal to 2, where R1 and R2 are independently chosen monovalent Ci to C60 hydrocarbon radicals; where D = R3R4SiOl/2; where R3 and R4 are independently chosen monovalent Ci to Ceo hydrocarbon radicals; where D'=R5R6SiOM; where R5 and R6 are independently chosen monovalent Ci to Qo hydrocarbon radicals. In one embodiment of the invention, the level of incorporation of the diorganopolysiloxane wherein the silicon atom at each polymer chain end is silanol terminated (a) ranges from about 50 weight percent to about 99 weight percent of the total composition. In another embodiment of the invention, the level of incorporation of the diorganopolysiloxane polymer or blends of diorganopolysiloxane polymers (a) ranges from about 60 weight percent to about 95 weight percent of the total composition. In yet another embodiment of the present invention, the diorganopolysiloxane polymer or blends of diorganopolysiloxane polymers (a) ranges from about 65 weight percent to about 95 weight percent of the total composition. The curable sealant composition 7 of the present invention further comprises at least one polymer (b) exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a). Suitable polymers (b) exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a) include, inter alia, polyethylenes, such as, low density polyethylene (LDPE), very low density -7- polyethylene (VLDPE), linear low density polyethylene (LLDPE) and high density polyethylene (HDPE); polypropylene (PP), polyisobutylene (PIB), polyvinyl acetate(PV Ac), polyvinyl alcohol (PVoR), polystyrene, polycarbonate, polyester, such as, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene napthalate (PEN), glycol-modified polyethylene terephthalate (PETG); polyvinyl chloride (PVC), polyvinyliqene chloride, polyvinylidene floride, thermoplastic polyurethane (TPU), acrylonitrile butadiene styrene (ABS), polymethylmethacrylate (PMMA), polyvinyl fluoride (PVF), Polyamides (nylons), polymethylpentene, polyimide (PI), polyetherimide (PEI), polether ether ketone (PEEK), polysulfone , polyether sulfone, ethylene chlorotrifluoroethylene, polytetrafluoroethylene (PTFE), cellulose acetate, cellulose acetate butyrate, plasticized polyvinyl chloride, ionomers (Surtyn), polyphenylene sulfide (PPS), styrene-maleic anhydride, modified polyphenylene oxide (PPO), and the like and mixture thereof. Polymer (b) of the curable sealant composition 7 can also be elastomeric in nature, examples include, but are not limited to ethylene- propylene rubber (EPDM), polybutadiene, polychloroprene, polyisoprene, polyurethane (TPU), styrene- butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEEBS), polymethylphenyl siloxane (PMPS), and the like. These polymers can be blended either alone or in combinations or in the form of coplymers, e.g. polycarbonate-ABS blends, polycarbonate polyester blends, grafted polymers such as, silane grafted polyethylenes, and silane grafted polyurethanes. In one embodiment of the present invention, the curable sealant composition 7 has a polymer selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density polyethylene (RDPE), and mixtures thereof. In another embodiment of the invention, the curable sealant composition has a polymer selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene -8- (VLDPE), linear low density polyethylene (LLDPE), and mixture thereof. In yet another embodiment of the present invention, the curable sealant composition polymer is linear low density polyethylene (LLDPE). In one embodiment of the present invention, the curable sealant composition contains from about 50 to about 99 weight percent diorganopolysiloxane polymer and from about 1 to about 50 weight percent polymer (b). In another embodiment of the present invention, the curable sealant composition contains from about 60 to about 95 weight percent diorganopolysiloxane polymer and from about 5 to about 40 weight percent polymer (b). In yet another embodiment of the present invention, the curable sealant composition contains from about 65 to about 95 weight percent diorganopolysiloxane polymer and from about 5 to about 35 weight percent polymer (b). The blending method of diorganopolysiloxane polymer (a) with polymer (b) may be performed by those methods know in the art, for example, melt blending, solution blending or mixing of polymer powder component (b) in diorganopolysiloxane polymer (a). Suitable cross-linkers (c) for the siloxanes of the curable sealant composition may include an alkylsilicate of the general formula: where R14, R15, R16 and R17 are independently chosen monovalent CI to C60 hydrocarbon radicals. Crosslinkers useful herein include, but are not limited to, tetra-N-propylsilicate (NPS), tetraethylortho silicate and methyltrimethoxysilane and similar alkyl substituted alkoxysilane compostions, and the like. In one embodiment of the present invention, the level of incorporation of the alkyl silicate (crosslinker) ranges from about 0.1 weight percent to about 10 weight -9- percent. In another embodiment of the invention, the level of incorporation of the alkylsilicate (crosslinker) ranges from about 0.3 weight percent to about 5 weight percent. In yet another embodiment of the present invention, the level of incorporation of the alkyl silicate (crosslinker) ranges from about 0.5 weight percent to about 1.5 weight percent of the total composition. Suitable catalysts (d) can be any of those known to be useful for facilitating crosslinking in silicone sealant compositions. The catalyst may include metal and non-metal catalysts. Examples of the metal portion of the metal condensation catalysts useful in the present invention include tin, titanium, zirconium, lead, iron cobalt, antimony, manganese, bismuth and zinc compounds. In one embodiment of the present invention, tin compounds useful for facilitating crosslinking in curable sealant compositions include: tin compounds such as dibutyltindilaurate, dibutyltindiacetate, dibutyltindimethoxide, tinoctoate, isobutyltintriceroate, dibutyltinoxide, solubilized dibutyl tin oxide, dibutyltin bis-diisooctylphthalate, bis-tripropoxysilyl dioctyltin, dibutyltin bis-acetylacetone, silylated dibutyltin dioxide, carbomethoxyphenyl tin tris-uberate, isobutyltin triceroate, dimethyltin dibutyrate, dimethyltin di-neodecanoate, triethyltin tartarate, dibutyltin dibenzoate, tin oleate, tin naphthenate, butyltintri-2-ethylhexylhexoate, and tinbutyrate, and the like. In still another embodiment, tin compounds useful for facilitating crosslinking in the curable sealant composition are chelated titanium compounds, for example, 1,3-propanedioxytitanium bis(ethylacetoacetate); di-isopropoxytitanium bis( ethyl acetoacetate ); and tetra-alkyl titanates, for example, tetra n-butyl titanate and tetra-isopropyl titanate. In yet another embodiment of the present invention, diorganotin bis P-diketonates is used for facilitating crosslinking in the curable sealant composition. In one aspect of the present invention, the catalyst is a metal catalyst. In another aspect of the present invention, the metal catalyst is selected from the group -10- consisting of tin compounds, and in yet another aspect of the invention, the metal catalyst is solubilized dibutyl tin oxide. In one embodiment of the present invention, the level of incorporation of the catalyst, ranges from about 0.001 weight percent to about 1 weight percent of the total composition. In another embodiment off the invention, the level of incorporation of the catalyst, ranges from about 0.003 weight percent to about 0.5 weight percent of the total composition. In yet another embodiment of the present invention, the level of incorporation of the catalyst, ranges from about 0.005 weight percent to about 0.2 weight percent of the total composition. The curable sealant composition of the present invention may further comprises an alkoxysilane or blend of alkoxysilanes as an adhesion promoter. In one embodiment, the adhesion promoter may be a combination blend of n-2-aminoethyl-3- aminopropyltrimethoxysilane and 1,3 ,5-tris(trimethoxysilylpropyl)isocyanurate. Other adhesion promoters useful in the present invention include but are not limited to n- 2-aminoethyl-3-aminopropyltriethoxysilane, y-aminopropyltriethoxysilane, y - aminopropyltrimethoxysilane, aminopropyltrimethoxysilane, bis- y trimethoxysilypropyl)amine, N - Phenyl-y-aminopropyltrimethoxysilane, triaminofunctionaltrimethoxysilane, y -aminopropylmethyldiethoxysilane, y - aminopropylmethyldiethoxysilane, methacryloxypropyltrimethoxysilane, methylaminopropyltrimethoxysilane, y -glycidoxypropylethyldimethoxysilane, y - glycidoxypropyltrimethoxysilane, y - glycidoxyethyltrimethoxysilane, P~(3,4- epoxycyclohexyl )propyltrimethoxysilane, (3-(3 ,4-epoxycyclohexyl) ethylmethyldimethoxysilane, isocyanatopropyltriethoxysilane, isocyanatopropylmethyldimethoxysilane, p-cyanoethyltrimethoxysilane, y acryloxypropyltrimethoxysilane, y -methacryloxypropylmethyldimethoxysilane, 4-amino-3,3, -dimethylbutyltrimethoxysilane, and n-ethyl-3 -trimethoxysilyl- 2-methylpropanamine, and the like. -11- The level of incorporation of the alkoxysilane (adhesion promoter) ranges from about 0.1 weight percent to about 20 weight percent. In one embodiment of the invention, the adhesion promoter ranges from about 0.3 weight percent to about 10 weight percent of the total composition. In another embodiment of the invention, the adhesion promoter ranges from about 0.5 weight percent to about 2 weight percent of the total composition. The curable sealant composition of the present invention may also comprise a filler. Suitable fillers of the present invention include but are not limited to ground, precipitated and colloidal calcium carbonates which is treated with compounds such as stearate or stearic acid; reinforcing silicas such as fumed silicas, precipitated silicas, silica gels and hydrophobized silicas and silica gels; crushed and ground quartz, alumina, aluminum hydroxide, titanium hydroxide, diatomaceous earth, iron oxide, carbon black and graphite or clays such as kaolin, bentonite or montmorillonite, and the like. In one embodiment of the present invention, the filler is a calcium carbonate filler, silica filler or a mixture thereof. The type and amount of filler added depends upon the desired physical properties for the cured silicone composition. In another embodiment of the invention, the amount of filler is from 0 weight percent to about 80 weight percent of the total composition. In yet another embodiment of the invention, the amount of filler is from about 10 weight percent to about 60 weight percent of the total composition. In still another embodiment of the invention, the amount of filler is from about 30 weight percent to about 55 weight percent the total composition. The filler may be a single species or a mixture of two or more species. In a further embodiment of the present invention, the curable sealant composition contains an inorganic substance from the general class of so called "nano-clays" or "clays." "Organo-clays" are clays or other layered materials that have been treated with organic molecules (also called exfoliating agents) capable of undergoing ion exchange reactions with the cations present at the interlayer surfaces of the layers. -12- In one embodiment of the invention, the clay materials used herein include natural or synthetic phyllosilicates, particularly smectic clays such as montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, talc, mica, kaolinite, as well as vermiculite, halloysite, aluminate oxides, or hydrotalcite, and the like and mixtures thereof. In another embodiment, other useful layered materials include micaceous minerals, such as illite and mixed layered illite/smectite minerals, such as rectorite, tarosovite, ledikite and admixtures of illites with the clay minerals named above. Any swellable layered material that sufficiently sorbs the organic molecules to increase the interlayer spacing between adjacent phyllosilicate platelets to at least 5 angstroms, or to at least 10 angstroms, (when the phyllosilicate is measured dry) may be used in the practice of this invention. The aforementioned particles can be natural or synthetic such as smectite clay. This distinction can influence the particle size and for this invention, the particles should have a lateral dimension of between 0.01 pm and 5 um, and preferably between 0.05 um and 2um, and more preferably between 0.1 um and 1 pm. The thickness or the vertical dimension of the particles can vary between 0.5 ran and 10 nm, and preferably between 1 nm and 5 nm. In still another embodiment of the present invention, organic and inorganic compounds useful for treating or modifying the clays and layered materials include cationic surfactants such as ammonium, ammonium chloride, alkylammonium (primary, secondary, tertiary and quaternary), phosphonium or sulfonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides. Such organic molecules are among the "surface modifiers" or "exfoliating agents" discussed herein. Additional organic or inorganic molecules useful for treating the clays and layered materials include amine compounds (or the corresponding ammonium ion) with the structure R3 R4 R5N, wherein R3, R4, and R5 are Q to C30 alkyls or alkenes in one embodiment, c1 to C20 alkyls or alkenes in another -13- embodiment, which may be the same or different. In one embodiment, the organic molecule is a long chain tertiary amine where R3 is a C14 to C20 alkyl or alkene. In another embodiment, R4 and or R5 may also be a C14 to C20 alkyl or alkene. In yet another embodiment of the present invention, the modifier can be an amine with the structure R6 R7 R8N, wherein R6, R7, and R8 are Q to C30 alkoxy silanes or combination of O to C30 alky Is or alkenes and alkoxy silanes. Suitable clays that are treated or modified to form organo-clays include, but are not limited to, montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, vermiculite, halloysite, aluminate oxides, hydrotalcite, illite, rectorite, tarosovite, ledikite, and mixtures thereof. The organo-clays of the present invention may further comprise one or more of ammonium, primary alkyl ammonium, secondary alkyl ammonium, tertiary alkylammonium quaternary alkyl ammonium, phosphonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides or sulfonium derivatives of aliphatic, aromatic or arylaliphatic amines, phosphines or sulfides. In one embodiment of the present invention, the organo-clay is an alkyl ammonium modified montmorillonite. The amount of clay incorporated in the sealant composition of the present invention in accordance with embodiments of the invention, is preferably an effective amount to provide decrease the sealant's permeability to gas. In one embodiment of the present invention, the sealant composition of the present invention contains from 0 to about 50 weight percent nano-clay. In another embodiment, the compositions of the present invention have from about 1 to about 20 weight percent nano-clay. The curable sealant composition of the present invention may optionally comprise non-ionic surfactant compound selected from the group of surfactants consisting of polyethylene glycol, polypropylene glycol, ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide (EO) and -14- propylene oxide (PO) and copolymers of silicones and polyethers (silicone polyether copolymers), copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof in an amount ranging from, slightly above 0 weight percent to about 10 weight percent, more preferably from about 0.1 weight percent to about 5 weight percent, and most preferably from about 0.5 weight percent to about 0.75 weight percent of the total composition. The curable sealant composition of the present invention may be prepared using other ingredients that are conventionally employed in room temperature vulcanizing (RTV) silicone compositions such as colorants, pigments and plasticizers, as long as they do not interfere with the desired properties. Furthermore, these compositions can be prepared using melt, solvent and in-situ polymerization of siloxane polymers as known in the art. Preferably, the methods of blending the diorganopolysiloxane polymers with polymers may be accomplished by contacting the components in a tumbler or other physical blending means, followed by melt blending in an extruder. Alternatively, the components can be melt blended directly in an extruder, Brabender or any other melt blending means. The curable sealant composition of the invention is illustrated by the following non-limiting examples. Polydimethyl Siloxane (PDMS) mixture (Silanol 5000 and silanol 50000, Gelest), was melt blended with LLDPE (melt flow index (MFI) 20, from Sabic) by Rake internal mixer at 150°C, 200RPM, for total mixing time of 12 minutes. Three (3) such blends were prepared with weight percent LLDPE of 10,20 and 30, (see Example 1,2 and 3, respectively, listed below), by the following procedure: Mix silanols 5000 cPs and 50000 cPs in 1:1 ratio. Add 70 percent of silanol mixture into the Rake mixer @ 150°C -15- Start the experiment using program window. Add LLDPE to the mixer in small amounts. Time of addition 1-2 minutes. Add remaining mixture 30 percent of silanol into the mixer. Continue mixing for total of 12 minutes. At the end of 12th minute the rotation stops automatically, collect the blended material into a glass petridish. The following Examples were prepared from the batches obtained using above procedure: Example 1: 52 grams mix silanol (5000 and 50000 @ 50:50) + 6 grams LLDPE Example 2: 48 grams mix silanol (5000 and 50000 @ 50:50) + 12 grams LLDPE Example 3:42 grams mix silanol (5000 and 50000 @ 50:50) + 18 grams LLDPE Example 1,2 and 3, were then used to make cured sheets as follows: PDMS-LLDPE blends were mixed with n-propyl silicate (cross-linker, obtained from Gelest Chemicals, USA) and solubilized dibutyl tin oxide (DBTO)( catalyst, obtained from GE silicones, Waterford, USA), in amounts as shown in Table 1, using a hand blender for 5-7 minutes. Air bubbles were removed by vacuum and the mixture was poured in Teflon mould and kept for 24 hrs under ambient conditions (25°C and 50 percent humidity). The cured sheets were removed from mould after 24 hours and kept at ambient temperature for seven days for complete curing. -16- Table 1 Examples Amount (Grams) ml PBTO ml Comparative Example 1 Silanol Mixture t 0.06 Example 1 Silanol with IGwipereerit LLDPE 50 0.9 0.05 Example 2 Silanol with 20wtpercent LLDPE 50 0.72 0.04 Examples Silanol with 30wtperceat LLDPE 50 0.5 0.03 The Argon permeability of Examples 1-3 and Comparative Example 1 was measured using a gas permeability set-up. The measurements were based on the variable^ volume method at 100 PSI pressure and temperature of 25°C. Measurements were repeated under identical conditions for 2-3 times in order to ensure their reproducibility. The result of the permeability data is displayed in Figure 2. The variable-volume method as displayed in Figure 2 measures Argon (Ar) permeability in "barrer" units (0.0 to 1200.0). As shown in Table 2, Examples 1-3 displayed lowered Ar permeability relative to the Comparative Example 1. Examples 5,6 and 7 were prepared as follows: Polydimethyl Siloxane (PDMS) mixture (Silanol 3000 and silanol 30000, Gfi silicones), was melt blended with LLDPE (melt flow index (MFI) 20, from Sabic) in an extruder at 150°C, along with the mixture of Hakenuka TDD CaQb and Omya FT CaC03. The temperature settings of the barrel are given below in Table 2. Comparative Example 4 was prepared as follows: -17- Polydimethyl Siloxane (PDMS) mixture (Silanol 3000 and silanol 30000, GE silicones), was melt blended in an extruder at 150°C, along with the mixture of Hakenuka TDD CaC03 and Omya FT CaC03. The temperature settings of the barrel are given below in Table 2: Table 2 Temp settings: Bane] 1-2 75°C Barrel 3-10 150°C Barrel 11-15 cooling to 45°C The feed rate was set at 501bs/hr. The formulations of Examples 4, 5, 6 and 7 are displayed in Table 4 and were produced in an extruder at 150°C: Table 4 Silanol Silanol CaC03 Sabic Talc Examples 30OGcps 30000 (50:50 mixture ofHakmuka TDD and Omya FT LLDPE Comparative Example 4 25.0 25.0 50.0 to m Examples 22.7 22.7 50.0 4.7 ■" I Example 6 20.0 20.0 50.0 10.0 Example 7 20.0 20.0 25.0 10.0 25 The extruded material was collected in 6oz semco cartridges. Comparative Example 4, and Examples 5, 6, and 7 were then used to make cured sheets as follows: -18- PDMS-LLDPE blends were mixed with Part B (catalyst mixture consists of solubilized dibutyl tin oxide, n-propyl silicate, aminopropyl triethoxysilane, carbon black and silicone oil) in 12.5 :1 ratio in semkit mixer for 6 minutes. The mixture was then poured in Teflon mould and kept for 24 hrs under ambient conditions (25°C and 50 percent humidity). The cured sheets were removed from mould after 24 hours and kept at ambient temperature for seven days for complete curing. Permeability data of Comparative Example 4, and Examples 5, 6, and 7 with LLDPE and other fillers is displayed in Figures 3 and 4. As shown in Figures 3 and 4, Examples 5-7 displayed lowered Ar permeability relative to Comparative Example 4. While the preferred embodiment of the present invention has been illustrated and described in detail, various modifications of, for example, components, materials and parameters, will become apparent to those skilled in the art, and it is intended to cover in the appended claims all such modifications and changes which come within the scope of this invention. -19- WE CLAIM: 1. An insulated glass unit comprising at least two spaced-apart sheets of glass in spaced relationship to each other, a low thermal conductivity gas therebetween and gas sealant element including a curable sealant composition comprised of a) diorganopolysiloxane exhibiting permeability to said gas; b) at least one polymer having a permeability to said gas that is less than the permeability of diorganopolysiloxane polymer; c) cross-linker; and, d) catalyst for the cross-linker reaction. 2. The insulated glass unit window of Claim 1 wherein the diorganopolysiloxane polymer, component (a), is a silanol terminated diorganopolysiloxane having the formula: wherein a = 2, b is equal to or greater than 1, c is zero or a positive integer; M=(HO)3-x-yR'xR2SiO1/2; wherein x = 0,1 or 2 and y is either 0 or 1, with the proviso that x + y is less than or equal to 2, R1 and R2 are monovalent C1 to C60 hydrocarbon radicals; D = R3R4SiOi/2; wherein R3 and R4 are monovalent C1 to C60) hydrocarbon radicals; and D' = R5R6SiC>2/2; wherein R5 and R6 are independently chosen monovalent Ci to Qo hydrocarbon radicals. 3. The insulated glass unit of Claim 1 wherein polymer (b) is selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE), polypropylene (PP), polyisobutylene (PIB), polyvinyl acetate(PV Ac), polyvinyl alcohol (PVoH), polystyrene, polycarbonate, polyester, such as, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene napthalate (PEN), glycol-modified -20- polyethylene terephthalate (PETG); polyvinylchloride (PVC), polyvinylidene chloride, polyvinylidene floride, thermoplastic polyurethane (TPU), acrylonitrile butadiene chlorotrifluoroethylene, polytetrafluoroethylene (PTFE), cellulose acetate, cellulose acetate butyrate, plasticized polyvinyl chloride, ionomers (Surtyn), polyphenylene sulfide (PPS), styrene-maleic anhydride, modified polyphenylene oxide (PPO), ethylene- propylene rubber (EPDM), polybutadiene, polychloraprene, polyisoprene, polyurethane (TPU), styrene-butadiene-styrene (SBS)/ styrene-ethylene-butadiene-styrene (SEEBS), polymethylphenyl siloxane (PMPS), and mixture thereof. 4. The insulated glass unit of Claim 3 wherein polymer (b) is selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE), and mixtures thereof 5. The insulated glass unit of Claim 4 wherein polymer (b) is selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), and mixture thereof. 6. The insulated glass unit of Claim 5 wherein polymer (b) is linear low density polyethylene (LLDPE). 7. The insulated glass unit of Claim 1 containing at least one optional component selected from the group consisting of filler, adhesion promoter, non-ionic 8. The insulated glass unit of Claim 1 wherein the catalyst is a tin catalyst. -21- The insulated glass unit of Claim 8 wherein the tin catalyst is selected from the group consisting of dibutyltindilaurate, dibutyltindiacetate, dibutyltindimethoxide, tinoctoate, isobutyltintriceroate, dibutyltinoxide, solubilized dibutyl tin oxide, dibutyltin bis-diisooctylphthalate, bis-tripropoxysilyl dioctyltindibutyltin bis- acetyl acetone, silylated dibutyltin dioxide, carbomethoxyphenyl tin tris-uberate, isobutyltin triceroate, dimethyltin dibutyrate, dimethyltin di-neodecanoate, triethyltin tartarate, dibutyltin dibenzoate, tin oleate, tin naphthenate, butylrintri-2-ethylhexylhexoate, tinbutyrate, diorganotin bis P-diketonates and mixtures thereof. The insulated glass unit of Claim 7 wherein the adhesion promoter is selected from the group consisting of n-2-arninoethyl-3-aminopropyltrimethoxysilane, l,3,5tris( trimethoxysilylpropyl)isocyanurate, y-aminopropyltriethoxysilane, yaminopropyltrimethoxysilane, aminopropyltrimethoxysilane, bis- y " trimethoxysilypropyl ) amine, N -Phenyl-y-aminopropyltrimethoxysilane, triaminofunctionaltrimethoxysilane, y -aminopropylmethyldiethoxysilane, y - aminopropylmethyldiethoxysilane, methacryloxypropyltrimethoxysilane, methylaminopropyltrimethoxysilane, y glycidoxypropylethyldimethoxysilane, y-glycidoxypropyltrimethoxysilane, y -glycidoxyethylrrimethoxysilane, \|3-(3 ,4- epoxycyclohexyl)propyltrimethoxysilane, p-(3 ,4-epoxycyclohexyl) ethylmethyldimethoxysilane, isocyanatopropyltriethoxysilane, isocyanatopropylmethyldimethoxysilane, p-cyanoethyltrimethoxysilane, y - acryloxypropyltrimethoxysilane, y methacryloxypropylmethyldimethoxysilane, 4-amino- 3,3, dimethylbutyltrimethoxysilane, n-ethyl- 3 -trimethoxysilyl- 2-methylpropanamine, and mixtures thereof -22- 11. The insulated glass unit of Claim 1 wherein the a diorganopolysiloxane polymer, component (a), ranges from an amount from about 50 weight percent to about 99 weight percent of the total composition. 12. The insulated glass unit of Claim 11 wherein the a diorganopolysiloxane polymer, component (a), ranges from in amount from about 60 weight percent to about 95 weight percent of the total composition. 13. The insulated glass unit of Claim 1 wherein the polymer, component (b), ranges from in amount from about 1 weight percent to about 50 weight percent of the total composition. 14. The insulated glass unit of Claim 13 wherein the polymer, component (b), ranges from in amount from about 5 weight percent to about 40 weight percent of the total composition. 15. The insulated glass unit of Claim 7 wherein the filler is selected from the group consisting of clays, nano-clays, organo-clays, ground calcium carbonate, precipitated calcium carbonate, colloidal calcium carbonate, calcium carbonate treated with compounds stearate or stearic acid; fumed silica, precipitated silica, silica gels, d hydrophobized silicas, hydrophilic silica gels; crushed quartz, ground quartz, alumina, aluminum hydroxide, titanium hydroxide, clay, kaolin, bentonite montmorillonite, diatomaceous earth, iron oxide, carbon black and graphite, talc, mica, and mixtures thereof. 16. The insulated glass unit of Claim 7 wherein the non-ionic surfactant selected from the group of surfactants consisting of polyethylene glycol, polypropylene glycol, ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide and propylene oxide and copolymers of silicones and polyethers, copolymers of silicones and -23- copolymers of ethylene oxide and propylene oxide and mixtures thereof in an amount ranging from about 0.1 weight percent to about 10 weight percent. 17. The insulated glass unit of Claim 16 wherein the non-ionic surfactant selected from the group of surfactants consisting of copolymers of ethylene oxide and propylene oxide, copolymers of silicones and polyethers, copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof. 18. The insulated glass unit of Claim 1 wherein the amount of the cross-linker, component (c), ranges in amount from about 0.1 weight percent to about 10 weight percent of the total composition. 19. The insulated glass unit of Claim 1 wherein the amount of catalyst, component (d), ranges in amount from about 0.005 weight percent to about 1 weight percent of the total composition. 20. The insulated glass unit of Claim 7 wherein the amount of filler ranges in amount from 0 to about 80 weight percent of the total composition. 21. The insulated glass unit of Claim 7 wherein the amount of adhesion promoter ranges in amount from about 0.5 weight percent to about 20 weight percent of the total composition. 22. The insulated glass unit of Claim 15 wherein the clay is selected from one or more of montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, vermiculite, halloysite, aluminate oxides, hydrotalcite, illite, rectorite, tarosovite, ledikite, and kaolinite. -24- 23. The insulated glass unit of Claim 22 wherein the clay is modified with an amine compounds or ammonium ion having the structure R3 R4R5N, wherein R3, R4, and R5 are Ci to C30 30 alkyls or alkenes, and mixtures thereof. 24. The insulated glass unit of Claim 23 wherein R3, R4, and R5 are G to C20 alkyls or alkenes, and mixtures thereof 25. The insulated glass unit of Claim 24 wherein clay is modified with a tertiary amine wherein R3 is a C14 to C20 alkyl or alkene, and mixtures thereof. 26. The insulated glass unit of Claim 25 wherein R4 and or R5 is a Cu to C20 alkyl or alkene, and mixtures thereof 27. The sealant composition of Claim 22 wherein the clay is modified with an amine or ammonium ion having the structure R6R7 R8N, wherein at least one R6, R7, and R8 is C1 to C30 alkoxy silanes and the remaining are O to C30 alkyls or alkenes. 28. The sealant composition of Claim 27 wherein at least one ofR6, R7 and R8is a Ci to C20 alkoxy silanes and the remaining are O to C20 alkyls or alkenes. 29. The insulated glass unit of Claim 22 wherein the clay is modified with ammonium, primary alkyl ammonium, secondary alkyl ammonium, tertiary alkyl ammonium quaternary alkylammonium, phosphonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides or sulfonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides. 30. The insulated glass unit of Claim 15 wherein the clay is present in an amount from about 0.1 to about 50 weight percent of said composition. -25- 31. The insulated glass unit of Claim 1 wherein the gas is a transparent insulating gas. 32. The insulated glass unit of Claim 31 wherein the gas is selected from the group consisting of air, carbon dioxide, sulfur hexafloride, nitrohen, argon, krypton, xenon, and mixtures thereof. 33. The insulated glass unit of Claim 1 further comprising a primary sealant. 34. The insulated glass unit of Claim 1 further comprising a glazing bead. 35. The insulated glass unit of Claim 33 wherein the primary sealant is a rubber based material. 36. The insulated glass unit of Claim 34 wherein the glazing bead is a silicone or butyl material. 37. The sealant composition of Claim 1 wherein the cross-linkers (c) is an alkyl silicate having the formula: (R140)(Rl50)(R,60)(R,70)Si where R14, R1S, R16 and R17 are chosen independently from monovalent G to C6o hydrocarbon radicals. Dated this 16th day of May, 2008 HIRAL CHANDRAKANT JOSHI AGENT FOR MOMENTIVE PERFORMANCE MATERIALS INC. -26-

Full Text

FORM 2
THE PATENT ACT 1970 (39 of 1970)
The Patents Rules, 2003 COMPLETE SPECIFICATION (See Section 10, and rule 13)

TITLE OF INVENTION
INSULATED GLASS UNIT POSSESSING ROOM TEMPATURE-CURED
SEALANT COMPOSITION OF REDUCED GAS PERMEABILITY

SILOXANE

APPLICANT(S)
a) Name
b) Nationality
c) Address

MOMENTIVE PERFORMANCE MATERIALS, INC,
AMERICAN Company
187 DANBURY ROAD,
WILTON, CONNECTICUT 06897-4122,
U.S.A.

PREAMBLE TO THE DESCRIPTION
The following specification particularly describes the invention and the manner in which it is to be performed : -

FIELD OF THE INVENTION
This invention is generally related to thermally insulating structures, and more particularly to a high thermal efficiency, insulated glass unit structure sealed with room temperature cured compositions having reduced permeability to gas, or mixtures of gases.
BACKGROUND OF THE INVENTION
Insulating glass units (IGU) commonly have two panels of glass separated by a spacer. The two panels of glass are placed parallel to each other and sealed at their periphery such that the space between the panels, or the inner space, is completely enclosed. The inner space is typically filled with air. The transfer of energy through an insulating glass unit of this typical construction is reduced, due to the inclusion of the insulating layer of air in the inner space, as compared to a single panel of glass. The energy transfer may be further reduced by increasing the separation between the panels to increase the insulating blanket of air. There is a limit to the maximum separation beyond which convection within the air between the panels can increase energy transfer. The energy transfer may be further reduced by adding more layers of insulation in the form of additional inner spaces and enclosing glass panels. For example three parallel spaced apart panels of glass separated by two inner spaces and sealed at their periphery. In this manner the separation of the panels is kept below the maximum limit imposed by convection effects in the airspace, yet the overall energy transfer can be further reduced. If further reduction in energy transfer is desired then additional inner spaces can be added.
Additionally, the energy transfer of sealed insulating glass units may be reduced by substituting the air in a sealed insulated glass window for a denser, lower conductivity gas. Suitable gases should be colorless, non-toxic, non-corrosive, non¬flammable, unaffected by exposure to ultraviolet radiation, and denser than air, and of lower conductivity than air. Argon, krypton, xenon, and sulfur hexaflouride are examples of gases which are commonly substituted for air in insulating glass windows to reduce energy transfer.
-2-

Various types of sealants are currently used in the manufacture of insulated glass units including both curing and non-curing systems. Liquid polysulphides, polyurethanes and silicones represent curing systems, which are commonly used, while polybutylene-polyisoprene copolymer rubber based hot melt sealants are commonly used non-curing systems.
Liquid polysulphides and polyurethanes are generally two component systems comprising a base and a curing agent that are then mixed just prior to application to the glass. Silicones may be one component as well as two component systems. Two component systems require a set mix ratio, two-part mixing equipment and cure time before the insulating glass units can be moved onto the next manufacturing stage.
However, these sealant compositions are susceptible to permeability from the low conductivity energy transfer gases (e.g. argon) used to enhance the performance of insulated glass units. As a result of this permeability, the reduced energy transfer maintained by the gas between the panels of glass is lost over time.
There remains a need for sealants with superior barrier protection and even higher thermal insulation stability that overcomes the deficiencies described above, and is highly suitable for applications that are easy to apply and have excellent adhesion.
SUMMARY OF THE INVENTION
The present invention relates to an insulated glass unit with increased thermal insulation stability. Specifically, the present invention relates to an insulated glass unit comprising at least two spaced-apart sheets of glass in spaced relationship to each other, a low thermal conductivity gas therebetween and gas sealant element including a curable sealant composition comprised of a) diorganopolysiloxane exhibiting permeability to said gas; b) at least one polymer having a permeability to said gas that is less than the permeability of diorganopolysiloxane polymer; c) cross-linker; and, d) catalyst for the cross-linker reaction.
-3-

The curable sealant composition of the present invention advantageously provides for a 50 percent reduction in gas permeability and reduced moisture leakage, which provides longer service life of insulated glass units (IGU).
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 is a sectional side view of a double glazed insulated glass unit (IGU).
Fig. 2 is a graph illustration of the permeability of Examples 1-3 to argon gas.
Fig. 3 is a graph illustration of the permeability of Example 5-7 to argon gas.
Fig. 4 is a graph illustration of percent decrease in permeability of Example 5-7 to argon gas.
DETAILED DESCRIPTION OF THE INVENTION
The detailed embodiments of the present invention are disclosed herein. It should be understood, however, that the disclosed embodiments are merely exemplary of the invention, which may be embodied in various forms. Therefore, the details disclosed herein are not to be interpreted as limited, but merely as the basis for the claims and as a basis for teaching one skilled in the art how to make and/or use the invention.
With reference to Fig. 1 an insulated glass unit 10 incorporating a curable sealant composition 7 providing separation of adjacent panes 1, 2 and sealing of the gas impermeable space 6 therebetween is shown. As those skilled in the art will readily appreciate, the inventive concepts of the present curable sealant composition 7 may be applied in various manners without departing from the spirit of the present invention. For example, it is contemplated that the present curable sealant composition may be used in conjunction with other materials, for example, various types of glass, including, clear float glass, annealed glass, tempered glass, solar glass, tinted glass, and Low-E glass, acrylic sheets and polycarbonate sheets.
-4-

In accordance with the present invention, the curable sealant composition 7 is applied in the construction of an insulated glass unit with a double pane glass structure. The insulated glass unit,- therefore, generally includes a first glass pane 1 and a second glass pane 2 separated by a continuous spacer 5, a primary sealant 4, and curable sealant composition 7 positioned between the first glass pane 1 and the second glass pane 2. The use of curable sealant composition 7 in accordance with the present invention provides improved gas barrier characteristics and moisture leakage characteristics. As a result, the curable sealant composition 7 provides for longer in service performance of insulated glass units.
The dimensions of continuous spacer 5 will determine the size of the gas impermeable space 6 formed between the first glass 1 and second glass 2 when the sheets of glass are sealed to spacer 5 using primary sealant 1 and curable sealant composition 7 of the present invention. A glazing bead 8, as known in the art, is placed between glass sheets 1 and 2 and window frame 9.
The spacer 5 may be filled with a desiccant that will keep the sealed interior of the gas impermeable space 6 of the insulated glass unit dry. The desiccant should be one which will not adsorb the low thermal conductivity gas or other gases used if a gas mixture is used to fill the interior of the insulated glass unit.
The primary sealant 4 of the insulated glass unit may be comprised of polymeric materials as known in the art. For example, rubber base material, such as polyisobutylene, butyl rubber, polysulfide, EPDM rubber nitrile rubber, or the like. Other materials include, but are not limited to, compounds comprising polyisobutylene/polyisoprene copolymers, polyisobutylene polymers, brominated olefin polymers, copolymers of polisobutylene and para-methyl styrene, copolymers of polyisobutylene and brominated para-methylstyrene, butyl rubber-copolymer of isobutylene and isoprene, ethylene-propylene polymers, polysulfide polymers, polyurethane polymers, and styrene butadiene polymers.
-5

As recited above, the primary sealant 4 can be fabricated of a material such as polyisobutylene, which has very good sealing properties. The glazing bead 8 is a sealant that is sometimes referred to as the glazing bedding and may be in the form of a silicone or butyl. A desiccant may be built into the continuous spacer 5 and is intended to remove moisture from the insulated glass or gas impermeable space between glass pane 1 and glass pane 2.
The curable sealant composition 7 of the present invention comprises diorganopolysiloxane polymer or blend thereof and at least one additional polymer. A general description of each of the components of the formulation are given as follows:
a diorganopolysiloxane or blend of diorganopolysiloxanes exhibiting permeability to a gas or mixtures of gases wherein the silicon atom at each polymer chain end is silanol terminated; whereby the viscosity of the siloxanes can be from about 1,000 to 200,000 cps at 25°C;
a polymer exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a);
an alkylsilicate cross-linker of the general formula: (R140)(RIS0)(RI6O)(Rl70)si;
a catalyst useful for facilitating crosslinking in silicone sealant compositions.
The sealant composition of the present invention may further comprise an optional component, such as, filler, adhesion promoter, non-ionic surfactant, and the like and mixtures thereof.
The silanol terminated diorganopolysiloxane polymer (a), generally has the formula:
-6-

with the subscript a = 2 and b equal to or greater than 1 and with the subscript c zero
or positive where

M = (HO)3.x.yRlxR2ySi01/2;
with the subscript x = 0, 1 or 2 and the subscript y is either 0 or 1, subject to the
limitation that x + y is less than or equal to 2, where R1 and R2 are independently
chosen monovalent Ci to C60 hydrocarbon radicals; where
D = R3R4SiOl/2;
where R3 and R4 are independently chosen monovalent Ci to Ceo hydrocarbon
radicals; where
D'=R5R6SiOM;
where R5 and R6 are independently chosen monovalent Ci to Qo hydrocarbon
radicals.
In one embodiment of the invention, the level of incorporation of the diorganopolysiloxane wherein the silicon atom at each polymer chain end is silanol terminated (a) ranges from about 50 weight percent to about 99 weight percent of the total composition. In another embodiment of the invention, the level of incorporation of the diorganopolysiloxane polymer or blends of diorganopolysiloxane polymers (a) ranges from about 60 weight percent to about 95 weight percent of the total composition. In yet another embodiment of the present invention, the diorganopolysiloxane polymer or blends of diorganopolysiloxane polymers (a) ranges from about 65 weight percent to about 95 weight percent of the total composition.
The curable sealant composition 7 of the present invention further comprises at least one polymer (b) exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a).
Suitable polymers (b) exhibiting permeability to a gas or mixture of gases that is less than the permeability of diorganopolysiloxane polymer (a) include, inter alia, polyethylenes, such as, low density polyethylene (LDPE), very low density
-7-

polyethylene (VLDPE), linear low density polyethylene (LLDPE) and high density polyethylene (HDPE); polypropylene (PP), polyisobutylene (PIB), polyvinyl acetate(PV Ac), polyvinyl alcohol (PVoR), polystyrene, polycarbonate, polyester, such as, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene napthalate (PEN), glycol-modified polyethylene terephthalate (PETG); polyvinyl chloride (PVC), polyvinyliqene chloride, polyvinylidene floride, thermoplastic polyurethane (TPU), acrylonitrile butadiene styrene (ABS), polymethylmethacrylate (PMMA), polyvinyl fluoride (PVF), Polyamides (nylons), polymethylpentene, polyimide (PI), polyetherimide (PEI), polether ether ketone (PEEK), polysulfone , polyether sulfone, ethylene chlorotrifluoroethylene, polytetrafluoroethylene (PTFE), cellulose acetate, cellulose acetate butyrate, plasticized polyvinyl chloride, ionomers (Surtyn), polyphenylene sulfide (PPS), styrene-maleic anhydride, modified polyphenylene oxide (PPO), and the like and mixture thereof.
Polymer (b) of the curable sealant composition 7 can also be elastomeric in nature,
examples include, but are not limited to ethylene- propylene rubber (EPDM),
polybutadiene, polychloroprene, polyisoprene, polyurethane (TPU), styrene-
butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEEBS),
polymethylphenyl siloxane (PMPS), and the like.
These polymers can be blended either alone or in combinations or in the form of coplymers, e.g. polycarbonate-ABS blends, polycarbonate polyester blends, grafted polymers such as, silane grafted polyethylenes, and silane grafted polyurethanes.
In one embodiment of the present invention, the curable sealant composition 7 has a polymer selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density polyethylene (RDPE), and mixtures thereof. In another embodiment of the invention, the curable sealant composition has a polymer selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene
-8-

(VLDPE), linear low density polyethylene (LLDPE), and mixture thereof. In yet another embodiment of the present invention, the curable sealant composition polymer is linear low density polyethylene (LLDPE).
In one embodiment of the present invention, the curable sealant composition contains from about 50 to about 99 weight percent diorganopolysiloxane polymer and from about 1 to about 50 weight percent polymer (b). In another embodiment of the present invention, the curable sealant composition contains from about 60 to about 95 weight percent diorganopolysiloxane polymer and from about 5 to about 40 weight percent polymer (b). In yet another embodiment of the present invention, the curable sealant composition contains from about 65 to about 95 weight percent diorganopolysiloxane polymer and from about 5 to about 35 weight percent polymer
(b).
The blending method of diorganopolysiloxane polymer (a) with polymer (b) may be performed by those methods know in the art, for example, melt blending, solution blending or mixing of polymer powder component (b) in diorganopolysiloxane polymer (a).
Suitable cross-linkers (c) for the siloxanes of the curable sealant composition may include an alkylsilicate of the general formula:
where R14, R15, R16 and R17 are independently chosen monovalent CI to C60 hydrocarbon radicals.
Crosslinkers useful herein include, but are not limited to, tetra-N-propylsilicate (NPS), tetraethylortho silicate and methyltrimethoxysilane and similar alkyl substituted alkoxysilane compostions, and the like.
In one embodiment of the present invention, the level of incorporation of the alkyl silicate (crosslinker) ranges from about 0.1 weight percent to about 10 weight
-9-

percent. In another embodiment of the invention, the level of incorporation of the alkylsilicate (crosslinker) ranges from about 0.3 weight percent to about 5 weight percent. In yet another embodiment of the present invention, the level of incorporation of the alkyl silicate (crosslinker) ranges from about 0.5 weight percent to about 1.5 weight percent of the total composition.
Suitable catalysts (d) can be any of those known to be useful for facilitating crosslinking in silicone sealant compositions. The catalyst may include metal and non-metal catalysts. Examples of the metal portion of the metal condensation catalysts useful in the present invention include tin, titanium, zirconium, lead, iron cobalt, antimony, manganese, bismuth and zinc compounds.
In one embodiment of the present invention, tin compounds useful for facilitating crosslinking in curable sealant compositions include: tin compounds such as dibutyltindilaurate, dibutyltindiacetate, dibutyltindimethoxide, tinoctoate, isobutyltintriceroate, dibutyltinoxide, solubilized dibutyl tin oxide, dibutyltin bis-diisooctylphthalate, bis-tripropoxysilyl dioctyltin, dibutyltin bis-acetylacetone, silylated dibutyltin dioxide, carbomethoxyphenyl tin tris-uberate, isobutyltin triceroate, dimethyltin dibutyrate, dimethyltin di-neodecanoate, triethyltin tartarate, dibutyltin dibenzoate, tin oleate, tin naphthenate, butyltintri-2-ethylhexylhexoate, and tinbutyrate, and the like. In still another embodiment, tin compounds useful for facilitating crosslinking in the curable sealant composition are chelated titanium compounds, for example, 1,3-propanedioxytitanium bis(ethylacetoacetate); di-isopropoxytitanium bis( ethyl acetoacetate ); and tetra-alkyl titanates, for example, tetra n-butyl titanate and tetra-isopropyl titanate. In yet another embodiment of the present invention, diorganotin bis P-diketonates is used for facilitating crosslinking in the curable sealant composition.
In one aspect of the present invention, the catalyst is a metal catalyst. In another aspect of the present invention, the metal catalyst is selected from the group
-10-

consisting of tin compounds, and in yet another aspect of the invention, the metal catalyst is solubilized dibutyl tin oxide.
In one embodiment of the present invention, the level of incorporation of the catalyst, ranges from about 0.001 weight percent to about 1 weight percent of the total composition. In another embodiment off the invention, the level of incorporation of the catalyst, ranges from about 0.003 weight percent to about 0.5 weight percent of the total composition. In yet another embodiment of the present invention, the level of incorporation of the catalyst, ranges from about 0.005 weight percent to about 0.2 weight percent of the total composition.
The curable sealant composition of the present invention may further comprises an
alkoxysilane or blend of alkoxysilanes as an adhesion promoter. In one embodiment,
the adhesion promoter may be a combination blend of n-2-aminoethyl-3-
aminopropyltrimethoxysilane and 1,3 ,5-tris(trimethoxysilylpropyl)isocyanurate.
Other adhesion promoters useful in the present invention include but are not limited
to n- 2-aminoethyl-3-aminopropyltriethoxysilane, y-aminopropyltriethoxysilane, y -
aminopropyltrimethoxysilane, aminopropyltrimethoxysilane, bis- y
trimethoxysilypropyl)amine, N - Phenyl-y-aminopropyltrimethoxysilane,
triaminofunctionaltrimethoxysilane, y -aminopropylmethyldiethoxysilane, y -
aminopropylmethyldiethoxysilane, methacryloxypropyltrimethoxysilane,
methylaminopropyltrimethoxysilane, y -glycidoxypropylethyldimethoxysilane, y -
glycidoxypropyltrimethoxysilane, y - glycidoxyethyltrimethoxysilane, P~(3,4-
epoxycyclohexyl )propyltrimethoxysilane, (3-(3 ,4-epoxycyclohexyl)
ethylmethyldimethoxysilane, isocyanatopropyltriethoxysilane,
isocyanatopropylmethyldimethoxysilane, p-cyanoethyltrimethoxysilane, y acryloxypropyltrimethoxysilane, y -methacryloxypropylmethyldimethoxysilane, 4-amino-3,3, -dimethylbutyltrimethoxysilane, and n-ethyl-3 -trimethoxysilyl- 2-methylpropanamine, and the like.
-11-

The level of incorporation of the alkoxysilane (adhesion promoter) ranges from about 0.1 weight percent to about 20 weight percent. In one embodiment of the invention, the adhesion promoter ranges from about 0.3 weight percent to about 10 weight percent of the total composition. In another embodiment of the invention, the adhesion promoter ranges from about 0.5 weight percent to about 2 weight percent of the total composition.
The curable sealant composition of the present invention may also comprise a filler. Suitable fillers of the present invention include but are not limited to ground, precipitated and colloidal calcium carbonates which is treated with compounds such as stearate or stearic acid; reinforcing silicas such as fumed silicas, precipitated silicas, silica gels and hydrophobized silicas and silica gels; crushed and ground quartz, alumina, aluminum hydroxide, titanium hydroxide, diatomaceous earth, iron oxide, carbon black and graphite or clays such as kaolin, bentonite or montmorillonite, and the like.
In one embodiment of the present invention, the filler is a calcium carbonate filler, silica filler or a mixture thereof. The type and amount of filler added depends upon the desired physical properties for the cured silicone composition. In another embodiment of the invention, the amount of filler is from 0 weight percent to about 80 weight percent of the total composition. In yet another embodiment of the invention, the amount of filler is from about 10 weight percent to about 60 weight percent of the total composition. In still another embodiment of the invention, the amount of filler is from about 30 weight percent to about 55 weight percent the total composition. The filler may be a single species or a mixture of two or more species.
In a further embodiment of the present invention, the curable sealant composition contains an inorganic substance from the general class of so called "nano-clays" or "clays." "Organo-clays" are clays or other layered materials that have been treated with organic molecules (also called exfoliating agents) capable of undergoing ion exchange reactions with the cations present at the interlayer surfaces of the layers.
-12-

In one embodiment of the invention, the clay materials used herein include natural or synthetic phyllosilicates, particularly smectic clays such as montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, talc, mica, kaolinite, as well as vermiculite, halloysite, aluminate oxides, or hydrotalcite, and the like and mixtures thereof. In another embodiment, other useful layered materials include micaceous minerals, such as illite and mixed layered illite/smectite minerals, such as rectorite, tarosovite, ledikite and admixtures of illites with the clay minerals named above. Any swellable layered material that sufficiently sorbs the organic molecules to increase the interlayer spacing between adjacent phyllosilicate platelets to at least 5 angstroms, or to at least 10 angstroms, (when the phyllosilicate is measured dry) may be used in the practice of this invention.
The aforementioned particles can be natural or synthetic such as smectite clay. This distinction can influence the particle size and for this invention, the particles should have a lateral dimension of between 0.01 pm and 5 um, and preferably between 0.05 um and 2um, and more preferably between 0.1 um and 1 pm. The thickness or the vertical dimension of the particles can vary between 0.5 ran and 10 nm, and preferably between 1 nm and 5 nm.
In still another embodiment of the present invention, organic and inorganic compounds useful for treating or modifying the clays and layered materials include cationic surfactants such as ammonium, ammonium chloride, alkylammonium (primary, secondary, tertiary and quaternary), phosphonium or sulfonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides. Such organic molecules are among the "surface modifiers" or "exfoliating agents" discussed herein. Additional organic or inorganic molecules useful for treating the clays and layered materials include amine compounds (or the corresponding ammonium ion) with the structure R3 R4 R5N, wherein R3, R4, and R5 are Q to C30 alkyls or alkenes in one embodiment, c1 to C20 alkyls or alkenes in another
-13-

embodiment, which may be the same or different. In one embodiment, the organic molecule is a long chain tertiary amine where R3 is a C14 to C20 alkyl or alkene. In another embodiment, R4 and or R5 may also be a C14 to C20 alkyl or alkene. In yet another embodiment of the present invention, the modifier can be an amine with the structure R6 R7 R8N, wherein R6, R7, and R8 are Q to C30 alkoxy silanes or combination of O to C30 alky Is or alkenes and alkoxy silanes.
Suitable clays that are treated or modified to form organo-clays include, but are not limited to, montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, vermiculite, halloysite, aluminate oxides, hydrotalcite, illite, rectorite, tarosovite, ledikite, and mixtures thereof. The organo-clays of the present invention may further comprise one or more of ammonium, primary alkyl ammonium, secondary alkyl ammonium, tertiary alkylammonium quaternary alkyl ammonium, phosphonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides or sulfonium derivatives of aliphatic, aromatic or arylaliphatic amines, phosphines or sulfides. In one embodiment of the present invention, the organo-clay is an alkyl ammonium modified montmorillonite.
The amount of clay incorporated in the sealant composition of the present invention in accordance with embodiments of the invention, is preferably an effective amount to provide decrease the sealant's permeability to gas. In one embodiment of the present invention, the sealant composition of the present invention contains from 0 to about 50 weight percent nano-clay. In another embodiment, the compositions of the present invention have from about 1 to about 20 weight percent nano-clay.
The curable sealant composition of the present invention may optionally comprise non-ionic surfactant compound selected from the group of surfactants consisting of polyethylene glycol, polypropylene glycol, ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide (EO) and
-14-

propylene oxide (PO) and copolymers of silicones and polyethers (silicone polyether copolymers), copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof in an amount ranging from, slightly above 0 weight percent to about 10 weight percent, more preferably from about 0.1 weight percent to about 5 weight percent, and most preferably from about 0.5 weight percent to about 0.75 weight percent of the total composition.
The curable sealant composition of the present invention may be prepared using other ingredients that are conventionally employed in room temperature vulcanizing (RTV) silicone compositions such as colorants, pigments and plasticizers, as long as they do not interfere with the desired properties.
Furthermore, these compositions can be prepared using melt, solvent and in-situ polymerization of siloxane polymers as known in the art.
Preferably, the methods of blending the diorganopolysiloxane polymers with polymers may be accomplished by contacting the components in a tumbler or other physical blending means, followed by melt blending in an extruder. Alternatively, the components can be melt blended directly in an extruder, Brabender or any other melt blending means.
The curable sealant composition of the invention is illustrated by the following non-limiting examples.
Polydimethyl Siloxane (PDMS) mixture (Silanol 5000 and silanol 50000, Gelest), was melt blended with LLDPE (melt flow index (MFI) 20, from Sabic) by Rake internal mixer at 150°C, 200RPM, for total mixing time of 12 minutes. Three (3) such blends were prepared with weight percent LLDPE of 10,20 and 30, (see Example 1,2 and 3, respectively, listed below), by the following procedure:
Mix silanols 5000 cPs and 50000 cPs in 1:1 ratio.
Add 70 percent of silanol mixture into the Rake mixer @ 150°C
-15-

Start the experiment using program window.
Add LLDPE to the mixer in small amounts. Time of addition 1-2 minutes.
Add remaining mixture 30 percent of silanol into the mixer.
Continue mixing for total of 12 minutes.
At the end of 12th minute the rotation stops automatically, collect the blended material into a glass petridish.
The following Examples were prepared from the batches obtained using above procedure:
Example 1: 52 grams mix silanol (5000 and 50000 @ 50:50) + 6 grams LLDPE Example 2: 48 grams mix silanol (5000 and 50000 @ 50:50) + 12 grams LLDPE Example 3:42 grams mix silanol (5000 and 50000 @ 50:50) + 18 grams LLDPE Example 1,2 and 3, were then used to make cured sheets as follows:
PDMS-LLDPE blends were mixed with n-propyl silicate (cross-linker, obtained from Gelest Chemicals, USA) and solubilized dibutyl tin oxide (DBTO)( catalyst, obtained from GE silicones, Waterford, USA), in amounts as shown in Table 1, using a hand blender for 5-7 minutes. Air bubbles were removed by vacuum and the mixture was poured in Teflon mould and kept for 24 hrs under ambient conditions (25°C and 50 percent humidity). The cured sheets were removed from mould after 24 hours and kept at ambient temperature for seven days for complete curing.
-16-

Table 1

Examples Amount (Grams) ml PBTO ml
Comparative Example 1 Silanol Mixture t 0.06
Example 1
Silanol with IGwipereerit LLDPE 50 0.9 0.05
Example 2
Silanol with 20wtpercent LLDPE 50 0.72 0.04
Examples
Silanol with 30wtperceat LLDPE 50 0.5 0.03
The Argon permeability of Examples 1-3 and Comparative Example 1 was measured using a gas permeability set-up. The measurements were based on the variable^ volume method at 100 PSI pressure and temperature of 25°C. Measurements were repeated under identical conditions for 2-3 times in order to ensure their reproducibility. The result of the permeability data is displayed in Figure 2.
The variable-volume method as displayed in Figure 2 measures Argon (Ar) permeability in "barrer" units (0.0 to 1200.0). As shown in Table 2, Examples 1-3 displayed lowered Ar permeability relative to the Comparative Example 1.
Examples 5,6 and 7 were prepared as follows:
Polydimethyl Siloxane (PDMS) mixture (Silanol 3000 and silanol 30000, Gfi silicones), was melt blended with LLDPE (melt flow index (MFI) 20, from Sabic) in an extruder at 150°C, along with the mixture of Hakenuka TDD CaQb and Omya FT CaC03. The temperature settings of the barrel are given below in Table 2.
Comparative Example 4 was prepared as follows:
-17-

Polydimethyl Siloxane (PDMS) mixture (Silanol 3000 and silanol 30000, GE silicones), was melt blended in an extruder at 150°C, along with the mixture of Hakenuka TDD CaC03 and Omya FT CaC03. The temperature settings of the barrel are given below in Table 2: Table 2

Temp settings:
Bane] 1-2 75°C
Barrel 3-10 150°C
Barrel 11-15 cooling to 45°C
The feed rate was set at 501bs/hr. The formulations of Examples 4, 5, 6 and 7 are displayed in Table 4 and were produced in an extruder at 150°C: Table 4

Silanol Silanol CaC03 Sabic Talc
Examples 30OGcps 30000 (50:50 mixture ofHakmuka TDD and Omya FT LLDPE
Comparative Example 4 25.0 25.0 50.0 to m
Examples 22.7 22.7 50.0 4.7 ■" I
Example 6 20.0 20.0 50.0 10.0
Example 7 20.0 20.0 25.0 10.0 25
The extruded material was collected in 6oz semco cartridges.
Comparative Example 4, and Examples 5, 6, and 7 were then used to make cured
sheets as follows:
-18-

PDMS-LLDPE blends were mixed with Part B (catalyst mixture consists of solubilized dibutyl tin oxide, n-propyl silicate, aminopropyl triethoxysilane, carbon black and silicone oil) in 12.5 :1 ratio in semkit mixer for 6 minutes. The mixture was then poured in Teflon mould and kept for 24 hrs under ambient conditions (25°C and 50 percent humidity). The cured sheets were removed from mould after 24 hours and kept at ambient temperature for seven days for complete curing.
Permeability data of Comparative Example 4, and Examples 5, 6, and 7 with LLDPE and other fillers is displayed in Figures 3 and 4.
As shown in Figures 3 and 4, Examples 5-7 displayed lowered Ar permeability relative to Comparative Example 4.
While the preferred embodiment of the present invention has been illustrated and described in detail, various modifications of, for example, components, materials and parameters, will become apparent to those skilled in the art, and it is intended to cover in the appended claims all such modifications and changes which come within the scope of this invention.
-19-

WE CLAIM:
1. An insulated glass unit comprising at least two spaced-apart sheets of glass in spaced relationship to each other, a low thermal conductivity gas therebetween and gas sealant element including a curable sealant composition comprised of a) diorganopolysiloxane exhibiting permeability to said gas; b) at least one polymer having a permeability to said gas that is less than the permeability of diorganopolysiloxane polymer; c) cross-linker; and, d) catalyst for the cross-linker reaction.
2. The insulated glass unit window of Claim 1 wherein the diorganopolysiloxane polymer, component (a), is a silanol terminated diorganopolysiloxane having the formula:
wherein a = 2, b is equal to or greater than 1, c is zero or a positive integer;
M=(HO)3-x-yR'xR2SiO1/2;
wherein x = 0,1 or 2 and y is either 0 or 1, with the proviso that x + y is less
than or equal to 2, R1 and R2 are monovalent C1 to C60 hydrocarbon radicals;
D = R3R4SiOi/2;
wherein R3 and R4 are monovalent C1 to C60) hydrocarbon radicals; and
D' = R5R6SiC>2/2;
wherein R5 and R6 are independently chosen monovalent Ci to Qo hydrocarbon radicals.
3. The insulated glass unit of Claim 1 wherein polymer (b) is selected from the
group consisting of low density polyethylene (LDPE), very low density
polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density
polyethylene (HDPE), polypropylene (PP), polyisobutylene (PIB), polyvinyl
acetate(PV Ac), polyvinyl alcohol (PVoH), polystyrene, polycarbonate,
polyester, such as, polyethylene terephthalate (PET), polybutylene
terephthalate (PBT), polyethylene napthalate (PEN), glycol-modified
-20-

polyethylene terephthalate (PETG); polyvinylchloride (PVC), polyvinylidene chloride, polyvinylidene floride, thermoplastic polyurethane (TPU), acrylonitrile butadiene chlorotrifluoroethylene, polytetrafluoroethylene (PTFE), cellulose acetate, cellulose acetate butyrate, plasticized polyvinyl chloride, ionomers (Surtyn), polyphenylene sulfide (PPS), styrene-maleic anhydride, modified polyphenylene oxide (PPO), ethylene- propylene rubber (EPDM), polybutadiene, polychloraprene, polyisoprene, polyurethane (TPU), styrene-butadiene-styrene (SBS)/ styrene-ethylene-butadiene-styrene (SEEBS), polymethylphenyl siloxane (PMPS), and mixture thereof.
4. The insulated glass unit of Claim 3 wherein polymer (b) is selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE), and mixtures thereof
5. The insulated glass unit of Claim 4 wherein polymer (b) is selected from the group consisting of low density polyethylene (LDPE), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), and mixture thereof.
6. The insulated glass unit of Claim 5 wherein polymer (b) is linear low density polyethylene (LLDPE).
7. The insulated glass unit of Claim 1 containing at least one optional component selected from the group consisting of filler, adhesion promoter, non-ionic
8. The insulated glass unit of Claim 1 wherein the catalyst is a tin catalyst.
-21-

The insulated glass unit of Claim 8 wherein the tin catalyst is selected from the group consisting of dibutyltindilaurate, dibutyltindiacetate, dibutyltindimethoxide, tinoctoate, isobutyltintriceroate, dibutyltinoxide, solubilized dibutyl tin oxide, dibutyltin bis-diisooctylphthalate, bis-tripropoxysilyl dioctyltindibutyltin bis- acetyl acetone, silylated dibutyltin dioxide, carbomethoxyphenyl tin tris-uberate, isobutyltin triceroate, dimethyltin dibutyrate, dimethyltin di-neodecanoate, triethyltin tartarate, dibutyltin dibenzoate, tin oleate, tin naphthenate, butylrintri-2-ethylhexylhexoate, tinbutyrate, diorganotin bis P-diketonates and mixtures thereof.
The insulated glass unit of Claim 7 wherein the adhesion promoter is selected
from the group consisting of n-2-arninoethyl-3-aminopropyltrimethoxysilane,
l,3,5tris( trimethoxysilylpropyl)isocyanurate, y-aminopropyltriethoxysilane,
yaminopropyltrimethoxysilane, aminopropyltrimethoxysilane, bis- y "
trimethoxysilypropyl ) amine, N -Phenyl-y-aminopropyltrimethoxysilane,
triaminofunctionaltrimethoxysilane, y -aminopropylmethyldiethoxysilane, y -
aminopropylmethyldiethoxysilane, methacryloxypropyltrimethoxysilane,
methylaminopropyltrimethoxysilane, y
glycidoxypropylethyldimethoxysilane, y-glycidoxypropyltrimethoxysilane, y
-glycidoxyethylrrimethoxysilane, |3-(3 ,4-
epoxycyclohexyl)propyltrimethoxysilane, p-(3 ,4-epoxycyclohexyl)
ethylmethyldimethoxysilane, isocyanatopropyltriethoxysilane,
isocyanatopropylmethyldimethoxysilane, p-cyanoethyltrimethoxysilane, y -
acryloxypropyltrimethoxysilane, y
methacryloxypropylmethyldimethoxysilane, 4-amino- 3,3,
dimethylbutyltrimethoxysilane, n-ethyl- 3 -trimethoxysilyl- 2-methylpropanamine, and mixtures thereof
-22-

11. The insulated glass unit of Claim 1 wherein the a diorganopolysiloxane polymer, component (a), ranges from an amount from about 50 weight percent to about 99 weight percent of the total composition.
12. The insulated glass unit of Claim 11 wherein the a diorganopolysiloxane polymer, component (a), ranges from in amount from about 60 weight percent to about 95 weight percent of the total composition.
13. The insulated glass unit of Claim 1 wherein the polymer, component (b), ranges from in amount from about 1 weight percent to about 50 weight percent of the total composition.
14. The insulated glass unit of Claim 13 wherein the polymer, component (b), ranges from in amount from about 5 weight percent to about 40 weight percent of the total composition.
15. The insulated glass unit of Claim 7 wherein the filler is selected from the group consisting of clays, nano-clays, organo-clays, ground calcium carbonate, precipitated calcium carbonate, colloidal calcium carbonate, calcium carbonate treated with compounds stearate or stearic acid; fumed silica, precipitated silica, silica gels, d hydrophobized silicas, hydrophilic silica gels; crushed quartz, ground quartz, alumina, aluminum hydroxide, titanium hydroxide, clay, kaolin, bentonite montmorillonite, diatomaceous earth, iron oxide, carbon black and graphite, talc, mica, and mixtures thereof.
16. The insulated glass unit of Claim 7 wherein the non-ionic surfactant selected from the group of surfactants consisting of polyethylene glycol, polypropylene glycol, ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide and propylene oxide and copolymers of silicones and polyethers, copolymers of silicones and
-23-

copolymers of ethylene oxide and propylene oxide and mixtures thereof in an amount ranging from about 0.1 weight percent to about 10 weight percent.
17. The insulated glass unit of Claim 16 wherein the non-ionic surfactant selected from the group of surfactants consisting of copolymers of ethylene oxide and propylene oxide, copolymers of silicones and polyethers, copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof.
18. The insulated glass unit of Claim 1 wherein the amount of the cross-linker, component (c), ranges in amount from about 0.1 weight percent to about 10 weight percent of the total composition.
19. The insulated glass unit of Claim 1 wherein the amount of catalyst, component (d), ranges in amount from about 0.005 weight percent to about 1 weight percent of the total composition.
20. The insulated glass unit of Claim 7 wherein the amount of filler ranges in amount from 0 to about 80 weight percent of the total composition.
21. The insulated glass unit of Claim 7 wherein the amount of adhesion promoter ranges in amount from about 0.5 weight percent to about 20 weight percent of the total composition.
22. The insulated glass unit of Claim 15 wherein the clay is selected from one or more of montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, vermiculite, halloysite, aluminate oxides, hydrotalcite, illite, rectorite, tarosovite, ledikite, and kaolinite.
-24-

23. The insulated glass unit of Claim 22 wherein the clay is modified with an amine compounds or ammonium ion having the structure R3 R4R5N, wherein R3, R4, and R5 are Ci to C30 30 alkyls or alkenes, and mixtures thereof.
24. The insulated glass unit of Claim 23 wherein R3, R4, and R5 are G to C20 alkyls or alkenes, and mixtures thereof
25. The insulated glass unit of Claim 24 wherein clay is modified with a tertiary amine wherein R3 is a C14 to C20 alkyl or alkene, and mixtures thereof.
26. The insulated glass unit of Claim 25 wherein R4 and or R5 is a Cu to C20 alkyl or alkene, and mixtures thereof
27. The sealant composition of Claim 22 wherein the clay is modified with an amine or ammonium ion having the structure R6R7 R8N, wherein at least one R6, R7, and R8 is C1 to C30 alkoxy silanes and the remaining are O to C30 alkyls or alkenes.
28. The sealant composition of Claim 27 wherein at least one ofR6, R7 and R8is a Ci to C20 alkoxy silanes and the remaining are O to C20 alkyls or alkenes.
29. The insulated glass unit of Claim 22 wherein the clay is modified with ammonium, primary alkyl ammonium, secondary alkyl ammonium, tertiary alkyl ammonium quaternary alkylammonium, phosphonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides or sulfonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines or sulfides.
30. The insulated glass unit of Claim 15 wherein the clay is present in an amount from about 0.1 to about 50 weight percent of said composition.
-25-

31. The insulated glass unit of Claim 1 wherein the gas is a transparent insulating gas.
32. The insulated glass unit of Claim 31 wherein the gas is selected from the group consisting of air, carbon dioxide, sulfur hexafloride, nitrohen, argon, krypton, xenon, and mixtures thereof.
33. The insulated glass unit of Claim 1 further comprising a primary sealant.
34. The insulated glass unit of Claim 1 further comprising a glazing bead.
35. The insulated glass unit of Claim 33 wherein the primary sealant is a rubber based material.
36. The insulated glass unit of Claim 34 wherein the glazing bead is a silicone or butyl material.
37. The sealant composition of Claim 1 wherein the cross-linkers (c) is an alkyl silicate having the formula:
(R140)(Rl50)(R,60)(R,70)Si
where R14, R1S, R16 and R17 are chosen independently from monovalent G to
C6o hydrocarbon radicals.
Dated this 16th day of May, 2008

HIRAL CHANDRAKANT JOSHI AGENT FOR MOMENTIVE PERFORMANCE MATERIALS INC.
-26-

Documents:

1009-MUMNP-2008-ABSTRACT(10-6-2011).pdf

1009-MUMNP-2008-ABSTRACT(16-5-2008).pdf

1009-MUMNP-2008-ABSTRACT(GRANTED)-(28-2-2012).pdf

1009-mumnp-2008-abstract.doc

1009-mumnp-2008-abstract.pdf

1009-MUMNP-2008-ASSIGNMENT 5-8-2008.pdf

1009-MUMNP-2008-ASSIGNMENT(10-6-2011).pdf

1009-mumnp-2008-assignment.pdf

1009-MUMNP-2008-CANCELLED PAGES(10-6-2011).pdf

1009-MUMNP-2008-CANCELLED PAGES(25-1-2012).pdf

1009-MUMNP-2008-CLAIMS(AMENDED)-(10-6-2011).pdf

1009-MUMNP-2008-CLAIMS(AMENDED)-(25-1-2012).pdf

1009-MUMNP-2008-CLAIMS(GRANTED)-(28-2-2012).pdf

1009-MUMNP-2008-CLAIMS(MARKED COPY)-(25-1-2012).pdf

1009-mumnp-2008-claims.doc

1009-mumnp-2008-claims.pdf

1009-MUMNP-2008-CORRESPONDENCE 5-8-2008.pdf

1009-MUMNP-2008-CORRESPONDENCE(10-6-2011).pdf

1009-MUMNP-2008-CORRESPONDENCE(16-5-2008).pdf

1009-MUMNP-2008-CORRESPONDENCE(17-10-2011).pdf

1009-MUMNP-2008-CORRESPONDENCE(18-8-2011).pdf

1009-MUMNP-2008-CORRESPONDENCE(IPO)-(29-2-2012).pdf

1009-mumnp-2008-correspondence.pdf

1009-mumnp-2008-description(complete).doc

1009-mumnp-2008-description(complete).pdf

1009-MUMNP-2008-DESCRIPTION(GRANTED)-(28-2-2012).pdf

1009-mumnp-2008-drawing.pdf

1009-mumnp-2008-form 1.pdf

1009-mumnp-2008-form 18.pdf

1009-MUMNP-2008-FORM 2(GRANTED)-(28-2-2012).pdf

1009-MUMNP-2008-FORM 2(TITLE PAGE)-(GRANTED)-(28-2-2012).pdf

1009-mumnp-2008-form 2(title page).pdf

1009-mumnp-2008-form 2.doc

1009-mumnp-2008-form 2.pdf

1009-MUMNP-2008-FORM 3(10-6-2011).pdf

1009-mumnp-2008-form 3.pdf

1009-mumnp-2008-form 5.pdf

1009-mumnp-2008-form pct-isa-210.pdf

1009-mumnp-2008-form pct-isa-237.pdf

1009-MUMNP-2008-FORM PCT-RO-101(10-6-2011).pdf

1009-MUMNP-2008-GENERAL POWER OF ATTORNEY(10-6-2011).pdf

1009-mumnp-2008-international publication report a2.pdf

1009-MUMNP-2008-OTHER DOCUMENT 5-8-2008.pdf

1009-MUMNP-2008-PCT REQUEST 5-8-2008.pdf

1009-MUMNP-2008-PETITION UNDER RULE 137(10-6-2011).pdf

1009-MUMNP-2008-POWER OF AUTHORITY(25-1-2012).pdf

1009-MUMNP-2008-REPLY TO EXAMINATION REPORT(10-6-2011).pdf

1009-MUMNP-2008-REPLY TO HEARING(25-1-2012).pdf

abstract1.jpg

« Previous Patent

Next Patent »

Patent Number

251160

Indian Patent Application Number

1009/MUMNP/2008

PG Journal Number

09/2012

Publication Date

02-Mar-2012

Grant Date

28-Feb-2012

Date of Filing

16-May-2008

Name of Patentee

MOMENTIVE PERFORMANCE MATERIALS, INC.

Applicant Address

187 DANBURY ROAD, WILTON, CONNECTICUT 06897-4122,

Inventors:

#	Inventor's Name	Inventor's Address
1	LANDON, SHAYNE, J.	16 BIRCH HILL ROAD, BALLSTON LAKE, NY 12091,
2	WILLIAMS, DAVID, A.	26 CASTLEBERRY DRIVE, GANESVOORT, NY 12831,
3	SHELUKAR, SACHIN, A.	FLAT #4G, HIMGIRI ENCLAVE II, D-BLOCK, KAGGADASPURA MAIN ROAD,DV RAMAN NAGAR, BANGALORE 560093,
4	NESAKUMAR, EDWARD, J.	18, A1-SAINO, 5TH CROSS, NAL WIND TUNNEL ROAD, MURUGESH PALAYA, BANGALORE 560017,
5	RAMAKRISHNAN, INDUMATHI	918, C-BLOCK, 7TH MAIN, AECS LAYOUT, KUNDALAHALLI, BANGALORE 560037,
6	KUMAR, VIKRAM	B-411 SNS ARCADE, AIRPORT ROAD, BANGALORE 560017,

PCT International Classification Number

C08L 83/04

PCT International Application Number

PCT/US2006/043673

PCT International Filing date

2006-11-10

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	11/283,382	2005-11-18	U.S.A.