Title of Invention

ROCKBOLTS MADE OF HIGH- STRENGTH STEEL PIPES AND METHOD OF MANUFACTURING THEREOF.

Abstract

A high-strength steel pipe rockbolt has an expansive rockbolt main body prepared by processing a high-strength steel sheet of 1.8-2.3 mm in thickness with tensile strength of 490-640 N/mm2 and elongation of 20% or more to a welded pipe and roll-forming the welded pipe to a shaped pipe having one or more concavities extending along an axial direction. Use of the high-strength steel sheet ensures sufficient strength of the shaped pipe regardless of a decrease in thickness. The thin welded pipe is also advantageous in resistance to cracking caused by accumulation of strains introduced during roll-forming, swaging both ends of the welded pipe and hydraulic expansion. Moreover, expansive deformation of the shaped pipe is initiated by injection of a pressurized fluid at a low pressure, so that the expansive deformation is completed in a short time period with an improved working efficiency.

Full Text

ROCKBOLTS MADE OF HIGH-STRENGTH STEEL PIPES AND METHOD OF MANUFACTURING THEREOF BACKGROUND OF THE INVENTION Field of the-Invention The present invention relates to a high-strength steel pipe rockbolt, which is firmly fixed to a bedrock or ground in a state radially expanded by a hydraulic pressure, and a method of manufacturing thereof. Description of Related Art A steel pipe rockbolt, which is firmly fixed to a bedrock or ground in an expanded state, is manufactured from a hollow shaped pipe-having one or more expansive concavities extending an axial direction. The steel pipe rockbolt 1 has a sealed end, which is inserted into a rockbolt-setting hole • * . * formed in a bedrock or ground 2, as shown in Fig. 1. There is a vacancy between the rockbolt-setting hole and the un-expanded steel pipe rockbolt 1 (Fig. 2A). The steel pipe rockbolt 1 isexpanded by a hydraulic pressure (Fig. 2B), and finally pressed onto an inner wall of the rockbolt-setting hole (Fig. 2C). Consequently, the bedrock or ground 2 is reinforced with the rockbolt 1. A shaped pipe with at least an expansive concavity 4, which extends along an axial direction, has been used as an expansive rockbolt, in order to facilitate expansion by a hydraulic pressure. The shaped pipe has hermetically sealed top and rear ends and a hole for introduction of a pressurized fluid at its side wall. A shaped steel pipe, which has sleeves fixed to its both ends for introduction of a pressurized fluid, is also disclosed in JP 2003-501573A. For standardization of labors and saving of labor costs in construction sites such as tunnels, many rockbolt-setting holes of the same size are drilled in a bedrock or ground 2, and steel pipe rockbolts of the same diameter are placed in the rockbolt-setting holes. For instance, a shaped pipe, which is formed from a steel pipe of 54 mm in outer diameter to a profile having an outer diameter of 36 mm and a concavity 4, is placed in a rockbolt-setting hole of 45-50 mm in size and firmly fixed to a bedrock or ground 2 by hydraulic expansion. * The expansive steel pipe rockbolts are classified to a 110 kN group and a 170 kN group by yield strength necessary for construction conditions, e.g. competence and geomechanics of a bedrock or ground as well as cross-sectional profiles of tunnels. Rockbolts, which belong to the 110 kN group, are manufactured from steel sheets of 2 mm in thickness with tensile strength of 300 N/mm2 or more and total elongation of 30% or more. Rockbolts, which belong to the 170 kN group, are manufactured from steel sheets of 3 mm in ■ ^thickness with tensile strength of 300 N/mm2 or more and total elongation of 35% or more. In any case, the steel sheet is formed to a cylindrical pipe of 54 mm in outer diameter and further reformed to a shaped pipe of 36 mm in outer diameter with a concavity 4. The shaped pipe is manufactured by partially bending a cylindrical pipe with a small bending radius in a sectional plane, as shown in Fig. 2A. On the presumption that shaped pipes have the same outer diameter, a bending radius at a center is smaller as a thickness increase of a steel 'sheet, which is formed to a shaped pipe. The shaped pipes are further swaged at its both ends, since sleeves having inner and outer diameters regularized in size are fixed to the end parts of the shaped pipes. A thicker steel sheet is reformed with a smaller bending radius even in the swaging process. That is, a local bending radius becomes smaller as an thickness increase of a steel sheet for raising strength of a rockbolt. By the way, many strains are introduced into a steel sheet in a pipe-making process, a pipe-shaping process and a swaging process. Strains are also accumulated during hydraulic expansion of a shaped pipe. When the shaped pipe is further expanded, it is often cracked due to introduction of additional strains. Cracking causes leakage of a pressurized fluid, insufficient expansion of the shaped pipe and shortage of strength necessary for a rockbolt. SUMMARY OF THE INVENTION The present invention aims at provision of high-strength steel pipe rockbolts with high reliability. An object of the invention is to inhibit cracking of rockbolts, which are induced by strains introduced in a pipe-shaping process, a swaging process and a hydraulically expanding process. Another object of the invention is to initiate expansive deformation of the shaped pipe at a relatively lower pressure during hydraulic expansion and to complete the expansive deformation in a short time period. The invention proposes a high-strength steel pipe rockbolt, • • */ .*■ ■ ■ .....'.* comprising an expansive rockbolt main body formed from a shaped pipe having one or more concavities extending along an axial direction. The shaped pipe is manufactured from a high-strength steel sheet of 1.8-2.3 mm in thickness with tensile strength of 490~640 N/mm2 and elongation of 20% or more. The shaped pipe preferably has tensile strength of 530-690 N/mm2 and elongation of 20% or more. The material of the rockbolt may be a high-strength steel sheet coated with a Zn, Zn-Al or Zn-Al-Mg plating layer. The plating layer is present on a surface of the shaped pipe after being roll-formed and protects a rockbolt, which is embedded in a bedrock or ground, from a corrosive atmosphere. The inventive steel pipe rockbolt is manufactured by the following steps: (l) A step of forming a high-stren-gth steel sheet of 1.8-2.3 mm in thickness with tensile strength of 490-640 N/mm2 and elongation of 20% or more to a welded steel pipe of 50-55 mm in outer diameter. (2) A step of roll-forming the welded steel pipe to a shaped pipe having an outer diameter of 34.0-38.0 mm and one or more concavities extending along an axial direction. (3) A step of cutting the shaped pipe to a predetermined length. (4) A step of swaging both ends of the cut shaped pipe. (5) A step of sealing both ends (i.e. one end of the shaped pipe to be placed in a rockbolt-setting hole and the other end for introduction of a pressurized fluid) of the shaped pipe with sleeves. (6) A step of forming a hole, which extends to an interior of the shaped pipe for introduction of a pressurized fluid, at a side wall of the sleeve. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an explanatory view for reinforcement of a ground with an expanded rockbolt. Fig. 2A is a sectional view illustrating a rockbolt, which is placed in a rockbolt-setting hole of a ground but not expanded yet. Fig. 2B is an explanatory view for application of a hydraulic pressure to a rockbolt during expansion. Fig. 2C is an explanatory view for application of a pressure to a rockbolt, which incompletely expanded. Fig. 3 is a graph showing performance of a hydraulic pump. Fig. 4 is an explanatory view showing changes of a sectional profile of a pipe in response to shaping steps. Fig. 5 is a schematic view illustrating profiles of forming rolls, which are used at a first step of a pipe-shaping process. Fig. 6 is a schematic view illustrating profiles of forming rolls, which are used at a second step of a pipe-shaping process. Fig. 7 is a schematic view illustrating profiles of forming rolls, which are used at a third step of a pipe-shaping process. Fig. 8 is a schematic view illustrating profiles of forming rolls, which are used at a forth step of a pipe-shaping process. PREFERRED EMBODIMENTS OF THE INVENTION The inventive steel pipe rockbolt is manufactured from high-strength steel. Selection of the high-strength steel enables use of a thin steel sheet as material of the rockbolt. When a rockbolt formed from a thinner steel sheet is compared with a conventional rockbolt on the presumption that the rockbolts have the same outer diameter, a minimum bending radius of a curved part, which defines an axially extending concavity, is larger at a center along a radial direction. Strains, which are introduced into a steel pipe in a pipe-shaping process and hydraulic expansion of a shaped pipe,, are reduced in a total amount as a decrease of thickness of the steel sheet. Due to reduction of the strains, the shaped pipe is hydraulically expanded without cracking. Use of the thinner steel sheet also means lightening of the rockbolt. Consequently, the inventive rockbolt is good of handlability and workability with high reliability. Expansion of a concavity of the shaped pipe is initiated at a lower hydraulic pressure, as a rockbolt is thinner. Deformation of the shaped pipe continues at a lower hydraulic pressure even after initiation of expansion, so that a large volume of a pressurized fluid can be introduced into the shaped pipe without raising a load of a high-pressure pump. Consequently, hydraulic expansion is completed in a short time. In this respect, use of the thinner steel sheet as material of the rockbolt is advantageous for remarkable improvement of work efficiency. For instance, a shaped pipe with tensile strength of 400 N/mm2, which has been used for a rockbolt with yield strength of 170 kN, is manufactured by forming a steel sheet of 3 mm in thickness with tensile strength of about 300 N/mm2 and elongation of about 35% to a welded steel pipe of 54 mm in outer diameter and reforming the welded pipe to a shaped pipe of 36 mm in outer diameter. When a thin high-strength steel sheet is used as material for a 170 kN-class rockbolt, a strong and reliable rockbolt, which is hydraulically expanded without cracking, is obtained. In fact, a shaped pipe, which is manufactured by forming a high-strength steel sheet of "1.8-2.3 mm in thickness with tensile strength of 490-640 N/mm2 and elongation of 20% or more to a welded pipe of 54 mm in outer diameter and then shaping the welded pipe to an objective profile of 36 mm in outer diameter, has tensile strength of 530"690 N/mm2. Consequently, a rockbolt, which is formed from the high-strength shaped pipe, is firmly fixed to a bedrock or ground with .strength of about 170 kN, by placing it in a rockbolt-setting hole of the ** * ■•.-•■ bedrock or ground and hydraulically 'expanding it therein. Use of a thinner "steel sheet enables bending a surface part of a welded pipe with a larger bending radius in a pipe-shaping process. Presume that a cylindrical pipe of 54 mm in outer diameter is formed to a shaped pipe with a cross section shown in Fig. 2A, wherein a curved part (a concavity 4) has an outside bending radius of 5 mm. A shaped pipe, which is formed from a cylindrical pipe of 3 mm in thickness, has a curved part with an inside bending radius of 2 mm. On the other hand, a shaped pipe, which is formed from a cylindrical pipe of 2 mm in thickness, has a curved part with an inside bending radius of 3 mm. In short, as a decrease in thickness of a welded pipe (in other words, a steel sheet), a bending radius becomes larger, resulting in reduction of cumulative strains during pipe-shaping. Reduction of the cumulative strains means an increase of a tolerance limit until the shaped pipe is cracked due to accumulation of strains. Consequently, the inventive rockbolt is hydraulically expanded in a bedrock or ground without fears of bursting. A thickness of a steel sheet is determined within a range of 1.8-2.3 mm in order to effectively reduce accumulation of strains. If the thickness exceeds 2.3 mm, it is difficult to realize an increase of a bending radius in a pipe-shaping process. On the other hand, the thickness less than 1.8 mm means necessity of a high-strength steel sheet with tensile strength of 640 N/mm2 or more, otherwise strength of 170 kN or so would not be imparted to a rockbolt. However, such high-strength steel sheets can not be formed to an objective profile due to poor elongation in a pipe-shaping process, and shaped pipes useful as expansive rockbolts can not be manufactured with ease from welded steel pipes of 50-55 mm in outer diameter. Besides, steel sheets shall have tensile strength of 490 N/mm2 or morei otherwise rockbolts with 170 kN or so would not be manufactured from welded pipes of 50~55 mm in outer diameter. Elongation of 20% or more is also necessary, in order to hydraulic expand shaped pipes without bursting. The expansive steel pipe rockbolt has a shaped pipe with a cross section, as shown in Fig. 2A. At least one concavity 4 extends along an axial direction of the shaped pipe. When a pressurized fluid is introduced into the shaped pipe, the shaped pipe is expansively returned to its original cylindrical profile by bulging of the concavity 4. On the presumption that shaped pipes have the same outer diameter and the same profile of the concavity 4, a larger pressure is necessary for bulging the concavity 4 as an increase in thickness of the shaped pipe. The thickness effect of the shaped pipe on bulging of the concavity 4 is explained as follows: A moment for re-bending a dented steel sheet to its original profile with hydraulic expansion is roughly estimated according to a formula of (t2b/4) X ae (wherein t is thickness, b is width, and ae is yield stress of the steel sheet), and the moment increases at a ratio in proportion to square thickness t2. In the case where an internal pressure of a vessel is raised to a predetermined value by introduction of a pressurized fluid into the vessel from a hydraulic pump, a large amount of the pressurized fluid flows from the pump into the vessel at a relatively lower inner pressure, but the flow rate is gradually reduced as an increase of the internal pressure. Accounting the relationship of the internal pressure with the flow rate, initiation of bulging of the concavity 4 at a lower pressure means inflow of a large amount of the pressurized fluid into the shaped pipe at a low-pressure stage until expansion of the shaped pipe. If expansion of the shaped pipe is initiated at a higher pressure on the contrary, an inflow rate of the pressurized fluid gradually decreases in correspondence with an increase of the internal pressure of the shaped pipe. In this case, it is unavoidable to continue introduction of the pressurized fluid for a long time until the internal pressure is raised to a value necessary for initiation of expansion. In fact, Fig. 3 shows a relationship between a discharge rate of high-pressure water and a discharge pressure, wherein air is supplied at a pressure of 0.6 MPa to a hydraulic pump with an air/water area ratio of 65/1. It is noted from the relationship that the inflow rate of the high-pressure water is gradually reduced as an increase of an internal pressure of a rockbolt and finally to 10.6 liters/minute at an internal pressure of 7 MPa. Presume that a pressure of 7 MPa is necessary for initiation of bulging of the concavity 4, which is formed at a shaped pipe of 2 mm in thickness and that a pressure of 17 MPa is necessary for initiation of bulging of the concavity 4, which is formed at a shaped pipe of 3 mm in thickness. When a rockbolts is hydraulically expanded with a supply air pressure of 0.6 MPa under the above conditions, an inflow rate of the high pressure water is varied in correspondence with an internal pressure of the rockbolt as follows- The shaped pipe of 2mm in thickness starts expansion at a pressure of 7 MPa, but the shaped pipe of 3 mm in thickness does not start expansion at a pressure of 7 MPa. Expansion of the thicker shaped pipe is initiated, when the internal pressure reaches 17 MPa. A discharge rate of the high-pressure water is reduced to 7.2 litters/min at the internal pressure of 17 MPa. Once the bulging of the concavity 4 starts, the expansive deformation of the shaped pipe continues at a pressure lower than the expansion-initiating-"pressure, and the expansion mode is substantially constant nevertheless thickness of the shaped pipe. After the shaped pipe is expanded to a size corresponding to an inner diameter of a rockbolt-setting hole in a bedrock or ground, an additional pressure is further applied to the expanded rockbolt so as to press the expansively deformed pipe onto an inner wall of the rockbolt-setting hole. Although the thinner shaped pipe is expansively deformed by an internal pressure of 7 MPa, the internal pressure is necessarily raised to 17 MPa for the expansive deformation of the thicker shaped pipe. Injection of high-pressure water shall be continued at a discharge rate corresponding to a discharge pressure of 7-17 MPa. As a result, a hydraulic pump shall be compensatorily driven for a longer time. Moreover, a pressure for further expansive deformation is higher compared with the thinner shaped pipe, so that it is obliged to inject high-pressure water in a higher discharge pressure region, in other words a small discharge rate region, for continuation of the expansive deformation of the thicker shaped pipe. In-short, a time period for hydraulic expansion of the thicker shaped pipe is longer than that for the thinner shaped pipe. The completion of expansive deformation in a short time is also the advantage originated in the thinner rockbolt made of high-strength steel. The inventive rockbolts are manufactured from high-strength steel sheets by the following steps" A high-strength steel sheet of 1.8-2.3 mm in thickness with predetermined mechanical properties is processed to a welded pipe having an outer diameter of 50-55 mm by a conventional pipe-making process using high frequency welding, laser welding, TIG welding or the like. The welded pipe is rolbformed to a shaped pipe having an outer diameter of 34~38 mm and a dented sectional profile defined by a circumferential part and a concavity. A roll-forming process, proposed by JP 2003-145216 A, is suitable for forming the welded pipe to jthe shaped pipe. But, an extrusion or press-forming process may be also employed, instead of the roll-forming. According to the roll'forming process, a sectional profile of a welded pipe is reformed step by step, as shown in Fig. 4. At first, a welded pipe with a circular profile (Fig. 4a) is prepared by a high frequency welding method or the like. The welded pipe is roll-formed to a sectional profile Ci (Fig. 4b) comprising a convex surface Fn with a large radius of curvature and another convex surface F21 with a small radius of curvature. The convex surface Fn has a circumferential length corresponding to a circumferential length of a part of an objective shaped pipe including a concavity 4. The other convex surface F21 has a circumferential length corresponding to a circumferential length of the other part of the objective shaped pipe. These convex surfaces Fn and F21 are formed by a rolling stand equipped with a couple of forming rolls 11 and 12 having concave profiles with a radius of curvature different from each other, as shown in Fig. 5. A multi-stage rolling stand may be also employed for successively changing radii of curvatures of the convex surfaces Fn and F21. Concave profiles of the forming rolls 11 and 12 are transcribed to the welded pipe M, by passing the welded pipe M through a gap between the forming rolls 11 and 12. That is, a circular profile Co (Fig. 4a) is reformed to a sectional profile Ci (Fig. 4b) comprising the convex surface F11with a large radius of curvature and the convex surface F21 with a small radius of curvature. In the second roll-forming step, a disc roll 21 (Fig. 6) having an edge with a small radius of curvature is pressed onto a center of the convex surface F11, so as to dent the convex surface Fn inwards, as shown in Fig. 4c. A rolling stand in the second roll-forming step is equipped with a forming roll 22, which has a concave profile with a radius of curvature smaller than the concave profile of the forming roll 12 in the first roll-forming step, in addition to the disc roll 21, as shown in Fig. 6. A multistage rolling stand may be also employed for making radii of curvatures successively smaller. When the welded pipe M is passed though a gap between the disc roll 21 and the concave roll 22 in the manner that the disc roll 21 is pressed onto a center of the convex surface F11, the center of the convex surface Fn is dented inwards, so that the welded pipe M is reformed to a sectional profile C2 (Fig. 4c) having a guttered curved part F12 extending along an axial direction. The other curved part F22, which defines an external profile of a shaped pipe, -keepsan initial radius "of curvat'ure of the welded pipe M. Since an expansively deformed pipe is pressed onto an inner wall of a rockbolt-setting hole in a bedrock or ground for reinforcement, the inner diameter of the rockbolt-setting hole is larger than an outer diameter of a shaped pipe but smaller than an outer diameter of the welded pipe M. Therefore, the sectional profile C2 is reformed to a small diameter profile C3 in the third roll-forming step. A rolling stand in this step is equipped with a couple of forming rolls 31 and 32 having concave profiles with a radius of curvature smaller than the initial diameter of the welded pipe M, as shown in Fig. 7. Of course, a multi-stage rolling stand may be also used for making the radius of curvature successively smaller in the third roll-forming step. When the pipe with the sectional profile C2 is passed through a gap between the rolls 31 and 32, the convex surface F22 is curved to a circular profile F23 with a small radius of curvature so as to narrow an opening (0) in correspondence to concave profiles of the rolls 31 and 32, as shown in Fig. 4d. In response to the reformation of the convex surface F22, the guttered concavity part F12 is also reformed to a small diameter concavity part F13. In the third roll-forming step, the welded pipe M is preferably rotated by 90 degrees around its axis from a positional relationship with the rolls 11 and 12 in the first step or with the rolls 21 and 22 in the second step to' such, a ■ position that the opening (0) and the weld bead (w) are disposed between the rolls 31 and 32. Due to the 90 degree rotation, a forming pressure is uniformly applied from the rolls 31 and 32 to the convex surface F22, so that the sectional profile C2 is reformed to a circular profile C3 comprising an inner part F13 and a circumferential part F23, both of which have uniform radii of curvature, as shown in Fig. 4d. The sectional profile C3 with a narrowed opening (0) is dressed to a circular profile C4 haying an outer diameter smaller than an inner diameter of a rockbolt-setting hole in a bedrock or ground, in the fourth roll-forming step. A rolling stand in this step preferably has a pressing roll 43 in addition to a couple of forming rolls 41 and 42, as shown in Fig. 8. A multi-stage rolling stand may be also used for successively reforming the sectional profile C3 to the small diameter profile C4. When a forming pressure is applied from the rolls 41, 42 to the convex surface F22 in the manner that the roll 43 is pressed onto the center of the circumferential part F22, the welded pipe M is stationarily held at a predetermined positional relationship during roll-forming, so as to ensure uniform reformation of the convex surface F22 until a quasrdpuble sectional profile C4 is formed by the outer periphery F24 and the inner periphery F14 with the opening (0) being nearly closed. During roll-forming, escape of the circumferential part F23 from the gap is inhibited by the pressing roll 43, so that the welded pipe M is formed to an objective small diameter profile C4 without flattening. The shaped pipe with the objective profile C4 is sized to a predetermined length and sealed at both ends. A front end of the shaped pipe is sealed as follows- A part of 80 mm in longitudinal length from the front end is swaged to a size of 32-34 mm in outer diameter. A sleeve of 36-40 mm in outer diameter, 2.0-3.0 mm in thickness and 60-80 mm in ■'length is fixed* to the swaged end part. A punch is pressed into an open end of the shaped pipe so 'as to reform the end part to a flat shape corresponding to a collet of the punch, and the pressed end part is sealed by welding. The opposite end of the shaped pipe is designed for introduction of a pressurized fluid and sealed as follows: A part of 80 mm in longitudinal length from the opposite end is swaged in the same way. A sleeve of 40-42 mm in outer diameter, 3.5-4.5 mm in thickness and 60-80 mm in length is fixed to the swaged end part. A punch is pressed into an open end of the shaped pipe so to reform the end part to a flat shape corresponding to a collet of the punch, and the pressed end part is sealed by welding. The sleeve preferably has a circumferential groove for firmly chucking a rockbolt embedded in a bedrock or ground for pullout test. After both ends are sealed, a hole for introduction of a pressurizec fluid into the interior of the shaped pipe is formed by drilling the sleeve a the opposite end. A position of the hole is determined at a part slightly apar from the end of the sleeve. Rockbolts embedded.in a bedrock or ground are exposed to corrosiv. atmospheres of from acid to alkali in response to humidity, water quality ventilation and so on. Accounting the atmospheres, coated steel pipes, whic have plating layers formed on inner and outer surfaces, are appropriat material for corrosion-resistant and durable rockbolts in the bedrock c ground. Such coated steel pipes are offered by a pre-coating or post-coatin process, but pre-coated steel pipes, which are manufactured from coated stee sheets, are profitable in respect to productivity. A plating layer may be Zn, ZirAl or Zrr Al-Mg. A Zn plating layer is preferably formed on a steel base by immersing a steel strip in molten zinc containing 0.1-0.2% of Al, which suppresses growth of a Fe-Zn alloy layer * ' harmful on workability. A Zn-Al plating layer, e.g. Zn*5% Al or Zn-55% Al,' exhibits corrosion-resistance 2-4 times better than a Zn plating layer of the same thickness. A Zn\Al-Mg plating layer is hard and exhibits the optimum corrosion-resistance, so that a rockbolt coated with the hard Zn-Al-Mg plating layer is placed and expanded in a bedrock or ground without scratches caused by abrasion with the bedrock or collision of scatters. Scratching is also inhibited during handling or transporting the coated rockbolt. Since scratches, which act as starting points of corrosion, are scarcely formed, the embedded rockbolt maintains good durability and reliability in addition to the excellent corrosion-resistant even in a corrosive environment. ■ - excellent corrosion-resistance and hardness. The Zn-Al-Mg plating layer contains 0.05-10% Mg, 4-22% Al. It may further contain 0.001-0.1% Ti, 0.0005-0.045% B and/or 0.005-2.0% at least one selected from the group consisting of rare earth metals, Y, Zr and Si. An element Mg is incorporated in a zincic corrosion product, which is formed on a surface of the plating layer. The Mg-containing zincic corrosion product together with an element Al in the plating layer reduces a corrosion rate of the plating layer in a soil environment. Since a part of the Mg-containing zincic corrosion product also flows into a weld bead and a cut edge in a process of manufacturing a pre-coated steel pipe, the weld bead and the cut edge are also prevented from corrosion. Moreover, when a welded part is repaired by thermal spraying, the Mg-containing zincic corrosion product flows onto a sprayed layer or into a corrosion product on the sprayed layer, resulting in protection of a steel base from corrosion. Mg is also important for hardening the plating layer by formation of a Zn-Mg intermetallic compound. These effects are achieved by controlling a Mg content within a range of 0.05-10% (preferably 1-4%). The other element Al is converted to a clinging Zn-Al corrosion product effective as a corrosion inhibitor. Zn/Al/Zn2Mg ternary eutectic grains appear in a solidified plating layer due to presence of Al. The ternary eutectic grains have a microstructure finer than Zn/Zn2Mg binary eutectic grains and raise hardness of the plating layer. An Al content of 4% or more is necessary for formation of the clinging Zn-Al corrosion product and the Zn/Al/Zn2Mg ternary eutectic grains. However, an increase of the Al content raises a melting temperature of a plating metal and needs holding a hot-dip bath at an elevated temperature, resulting in poor productivity. In this sense, an upper limit of the Al content is determined at 22%. Optional elements Ti and B impedes formation of a ZnnMg2 phase harmful on an external appearance of a coated steel sheet, so that Zn-Mg intermetallic precipitates present in a plating layer are substantially composed of Zn2Mg. The effect of Ti on inhibiting formation of the ZnnMg2 phase is apparently noted by 0.001% or more (preferably 0.002% or more) of Ti. However, excess Ti above 0.1% promotes growth of a Ti-Al precipitate, resulting in a rugged surface of the plating layer with poor external appearance. Formation of the ZnnMg2 phase is also impeded by addition of B at a ratio of 0.0005% or more (preferably 0.001% or more): But, excess B above 0.045% promotes growth of TrB and Al-B intermetallic compounds, which degrade a smooth surface and external appearance of a plating layer. A rockbolt, which is prepared from a steel pipe hot-dip coated with a Zn-Al-Mg plating layer containing Al and Mg at relatively large ratios, often reduces its surface gloss. As reduction of the surface gloss, a surface of the plating layer is changed from a fine metallic luster to gray with the lapse of time. As a result, the rockbolt decreases its commercial value. Reduction of the surface gloss is prevented by adding at least one oxidizable element selected from the group consisting of rare earth metals, Y, Zr and Si at a ratio of 0.005% or more. However, a maximum ratio of the oxidizable element is determined at 2.0%, since its effect on reduction of the surface gloss can not be expected any more by excess addition above 2.0%. A Fe-Al intermetallic compound, harmful on workability and formability of the coated steel sheet or pipe, is more formed as an increase of Al in the ZirAl-Mg plating layer. The Fe-Al intermetallic compound at a boundary between a base steel and a plating layer unfavorably causes peeling-off of the plating layer during working or forming a coated steel sheet or pipe. Formation of the intermetallic compound is inhibited by inclusion of Si at a small ratio in the plating layer. EXAMPLES A high-strength steel sheet of 2.1 mm in thickness with tensile strength of 490 N/mm2 and elongation of 28% was processed to a welded pipe of 54 mm in outer diameter. The welded pipe was roll-formed to a shaped pipe of 36 mm in outer diameter with a sectional profile, as shown in Fig. 2A, having a concavity 4 extending along an axial direction. The shaped pipe had tensile strength of 550 N/mm2. The shaped pipe was sized to a length of 4 m. End parts in longitudinal length of 75 mm from edges of the sized pipe were swaged to a profile of 33.1 mm in outer diameter. A sleeve of 33.1 mm in inner diameter, 38.1 mm in outer diameter, 2.5 mm in thickness and 70 mm in length was fixed to one end part, and the end part was sealed with the sleeve by welding. Another sleeve of 33.1 mm in inner diameter, 41.1 mm in outer diameter, 4.0 mm in thickness and 70 mm in length was fixed to the opposite end part at a side for introduction of a pressurized fluid, and the end part was sealed with the sleeve by welding. After the ends were both sealed, a side wall of the latter sleeve was drilled so as to form a hole of 3.0 mm in diameter leading to an interior of the shaped pipe. As a comparative example, a rockbolt was manufactured from a steel sheet of 3.0 mm in thickness with tensile strength of 300 N/mm2 and elongation of 35% by processing the steel sheet to a welded pipe of 54 mm in outer diameter and then roll-forming the welded pipe to a shaped pipe of 36 mm in outer diameter under the same conditions. A seal head for hydraulic expansion was attached to each of the inventive and comparative rockbolts, and high-pressure water was injected into an interior of the shaped pipe by a hydraulic pump. The shaped pipe was hydraulically expanded. Expansive deformation was investigated in detail. The inventive rockbolt started expansive deformation, i.e. bulging of the'concavity 4 (Fig. 2A), when- a-hydraulic, pressure in the shaped pipe reached 7 MPa. Once the expansive deformation occurred, it continued at a . hydraulic pressure of 5 MPa. During propagation of the expansive deformation, high-pressure water was injected into the shaped pipe at a flow rate of 11.3 litters/minute, and the expansive deformation was completed in 31 seconds. On the other hand, the concavity 4 of the comparative rockbolt did not expansively reverse at a hydraulic pressure of 7 MPa, but the expansive deformation started when the hydraulic pressure reached 17 MPa. A hydraulic pressure necessary for continuation of the expansive deformation was 10 MPa. A feed rate of the high-pressure water at the hydraulic pressure of 10 MPa was only 9.6 litters/minute, and 41 seconds were spent for completion of the expansive deformation. It is noted from the comparison that the inventive rockbolt completes expansive deformation in a time period about 3/4 shorter than a conventional rockbolt. The short expansion time leads to a remarkable decrease in a term of works in practical reinforcement works wherein hundreds or thousands of rockbolts are to be embedded in a bedrock. Moreover, the expansion state is achieved by a relatively lower hydraulic pressure, so as to reduce a load applied to a hydraulic pump. Rockbolts, which were hydraulically expanded with an assumption, of placement in a construction site, were subjected to pullout test. Test results prove that the inventive rockbolts had strength of about 170 kN. Since the inventive rockbolts were thinned and lightened by about 30% compared with conventional rockbolts, transportation to or handling in a construction site becomes easy. Furthermore, shaped pipes, which are prepared from welded pipes with less accumulation of strains, are expansively deformed to objective profiles without bursting caused by introduction of strains during hydraulic expansion, resulting in safety of rock bolting works. CLAIMS 1. A high-strength steel pipe rockbolt comprising an expansive rockbolt main body made from a shaped pipe having one or more concavities extending along an axial direction, the shaped pipe being made from a high-strength steel sheet of 1.8-2.3 mm in thickness with tensile strength of 490-640 N/mm2 and elongation of 20% or more. 2. The high-strength steel pipe rockbolt as defined in Claim 1, wherein the shaped pipe is coated with a Zn, Zn\Al or Zn-Al-Mg plating layer. 3. The high-strength steel pipe rockbolt as defined in Claim 1, wherein the shaped pipe has tensile strength of 530-690 N/mm2 and elongation of 20% or more. 4. A method of manufacturing a steel pipe rockbolt involving the steps of: (1) processing a steel sheet of 1.8-2.3 mm in thickness with tensile strength of 490-640 N/mm2 and elongation of 20% or more to a welded pipe of 50™ 55 mm in outer diameter," (2) roll-forming the welded pipe to a shaped pipe of 34.0-38.0 mm in outer diameter having one or more concavities extending along an axial direction; (3) sizing the shaped pipe to a predetermined length; (4) swaging both ends of the sized shaped pipe; (5) hermetically fixing sleeves to the both ends of the shaped pipe, one end being a top to be inserted into a rbckbolt-setting hole in a bedrock or ground, and the opposite end being a site for introduction of a pressurized fluid; and (6) drilling the sleeve at the opposite end for formation of a pressure fluid inlet leading to an interior of the shaped pipe.

Documents:

2543-CHENP-2006 CORRESPONDENCE OTHERS 04-08-2011.pdf

2543-CHENP-2006 AMENDED CLAIMS 04-04-2012.pdf

2543-CHENP-2006 CORRESPONDENCE PO.pdf

2543-CHENP-2006 EXAMINATION REPORT REPLY RECEIVED 04-04-2012.pdf

2543-CHENP-2006 FORM-18.pdf

2543-CHENP-2006 FORM-3 04-04-2012.pdf

2543-CHENP-2006 POWER OF ATTORNEY 04-08-2011.pdf

2543-chenp-2006-abstract.pdf

2543-chenp-2006-claims.pdf

2543-chenp-2006-correspondnece-others.pdf

2543-chenp-2006-description(complete).pdf

2543-chenp-2006-drawings.pdf

2543-chenp-2006-form 1.pdf

2543-chenp-2006-form 3.pdf

2543-chenp-2006-form 5.pdf

2543-chenp-2006-pct.pdf