Title of Invention	METHOD OF PREPARING A MINERAL AND/OR FILLER MATERIAL,LIKE,GYPSUM MATERIAL
Abstract	The invention discloses a method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and (ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler and optionally water and/or a catalyst for condensation of the hydrolysate. The invention is also for a making a gypsum product, e.g. plasterboard by using said mineral or filler material.

Title of Invention

METHOD OF PREPARING A MINERAL AND/OR FILLER MATERIAL,LIKE,GYPSUM MATERIAL

Abstract

The invention discloses a method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and (ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler and optionally water and/or a catalyst for condensation of the hydrolysate. The invention is also for a making a gypsum product, e.g. plasterboard by using said mineral or filler material.

Full Text	[0001 ] This invention relates to a process of making minerals and filler materials, particularly gypsum and gypsum products that are hydrophobic and/or water resistant. In particular, hydrophobicity and/or water resistance is provided by adding during the process, certain aqueous solutions of polysiloxanes obtained by prehydrolyzing under acidic conditions certain hydrolyzable silanes such as alkylalkoxysilanes, arylalkoxysilanes, alkenylalkoxysilanes, and mixtures thereof. [0002] Gypsum products such as gypsum plasterboard are made by mixing stucco with water to produce a slurry. The slurry is fed onto a sheet of cardboard, covered with a second sheet of cardboard, and passed over a moulding platform to be shaped into an encased strip. The strip of gypsum plasterboard is initially soft, but then quickly sets as the calcium sulphate hemihydrates (stucco) rehydrates back to calcium sulphate dihydrate (gypsum), and therefore hardens, and is cut into separate panels of gypsum plasterboard. [0003] In particular, gypsum plasterboard is produced from basic materials including paper in the form of cardboard, stucco, water, starch, and additives such as accelerators and foams. Other additives for making gypsum plasterboard are also added, including retarders such as proteins and organic acids; viscosity modifying agents; anti-burning agents; water-resisting chemicals such as polysiloxanes and wax emulsions; glass fibres; fire-resistance enhancers such as vermiculite, clays, and fumed silica; and polymeric compounds such as polyvinyl alcohol. As noted, wallboards or plasterboards are large thin gypsum panels covered with cardboard. This invention relates to an improved process for the incorporation of polysiloxane in gypsum, a gypsum product or another mineral or filler to impart water resistance. [0004] WO-A-81/01702 describes a process for the preparation of a plaster mortar containing gypsum powder, water, conventional additives and ballast material, comprising adding said materials during the process of manufacture, in the preparation of the gypsum powder, in the mixing of the powder and water or to the mixing water or to the wet mortar, alkoxysilanes and optionally a solvent and optionally a tenside/emulsifier/surfactant and optionally a silanol polymerisation catalyst and optionally substancesTprbViding for acid or basic reaction conditions in the mixing water and optionally a fine powder consisting of reactive silica. [0005] In one embodiment of the present invention there is provided a method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and (ii) combining the polysiloxane hydrolyzate with minerals and/or fillers, and optionally water and/or a catalyst for condensation of the hydrolysate. [0006] The process of the invention can be used for the treatment of a wide range of minerals or fillers in powder form. [0007] The method of the invention can be used in preparing other types of hydrophobic and/or water resistant materials such as minerals and fillers. Some representative examples include non-hydrated, partially hydrated, or hydrated fluorides, chlorides, bromides, iodides, chromates, carbonate hydroxides, hydroxides, phosphates, hydrogen phosphates, nitrates, oxides, and sulphates of sodium, potassium, magnesium, calcium, and barium; titanium dioxide, zinc oxide, aluminium oxide, aluminium tnhydroxide, vermiculite, silica including fumed silica, fused silica, precipitated silica, quartz, sand, and silica gel; rice hull ash, ceramic and glass beads, zeolites, hydrous calcium silicate, silica-carbon black composite, functionalized carbon nanotubes, cement, fly ash, slate flour, bentonite, clay, mica, kaolin, talc, calcium carbonate, wollastonite, polymeric fillers, rubber particles, wood flour, wood fibres, cellulose and cellulose-containing products, aramid fibres, nylon fibres, cotton fibres, or glass fibres. [0008] One example is in the preparation of hydrophobic gypsum and gypsum products, and the invention will be described in terms of gypsum although it can be applied to other minerals and fillers. As used herein, the term gypsum is intended to mean all solid forms of calcium sulphate including calcium sulphate dihydrate CaS042H20. The term stucco is intended to mean calcium sulphate hemihydrate CaSO40.5H2O, commonly known as plaster of Paris or calcined gypsum but for the sake of this invention should also be understood to be dehydrate and anhydrate derivatives thereof. Stucco is made by heating gypsum to remove 3/2 H2O molecule. The method of preparing hydrophobic and/or water resistant gypsum and gypsum products according to the invention, can be used to prepare hydrophobic gypsum and gypsum products derived from all sources of gypsum and stucco, including natural gypsum (calcium sulphate dihydrate), synthetic gypsum from plasterboard waste stations, or synthetic gypsum (desulphogypsum) produced at coal fired power plants that convert sulphur dioxide to synthetic gypsum, and other forms of synthetic gypsum such as titanogypsum, fluorogypsum or phosphogypsum. The method of the invention is particularly suitable for treating stucco in powder form, as used in the preparation of gypsum . products such as gypsum plasterboard [0009] Hence one embodiment is particularly directed to a method of making hydrophobic and/or water resistant gypsum and gypsum products by: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture under acidic conditions; (ii) combining the polysiloxane hydrolyzate with stucco and/or gypsum, and optionally water and/or a basic catalyst, to form a slurry; and (iii) discharging the slurry onto a support or mould, and drying the slurry to form a hydrophobic gypsum or hydrophobic gypsum product. [0010] As used herein, the terms hydrolyzate containing polysiloxane and polysiloxane hydrolyzate are intended to include the various species resulting from the hydrolysis of alkoxysilanes, chlorosilanes, and/or acetoxysilanes, including combinations of monomeric hydroxysilanes such as organotrihydroxysilanes, linear, cyclic , or branched hydroxysiloxanes in oligomeric or polymeric form, and any species containing both the hydroxyl and remaining hydrolysable groups such as organodihydroxymonoalkoxysilanes and organomonohydroxydialkoxysilanes, in oligomeric or polymeric siloxane forms, resulting either from the partial hydrolysis or the residual esterification of hydroxyl group into alkoxy groups, and the residual alcoholysis of siloxanes into hydroxy or alkoxy" functional silanes, or shorter siloxane mixtures. Although the post-distillation of the alcohol by-product does reduce significantly the re-generation of residual alkoxysilanes, alkoxyoligosiloxanes, and alkoxypolysiloxanes, it is not a requirement for obtaining low water uptake, and the consequent hydrophobing properties of gypsum and gypsum products. [0011] The hydrolysable organosilane in accordance vyith the present invention may comprise one or more silanes, each silane being the same or different and comprising one or more alkoxy groups and/or one or more acetoxy groups and/or one or more halide groups (typically chloride groups) and mixtures thereof. Hence, the hydrolysable organosilane can for example be an alkoxysilane or acefoxysilane or a silane containing both alkoxy and acetoxy groups bonded to a silicon atom. The alkoxysilane can be a monoalkoxysilane, dialkoxysilane, trialkoxysilane, ortetra-alkoxysilane. The alkoxysilane can contain the same or different alkoxy groups Optionally, it may contain one or more halogenated substituted organic groups. The alkoxysilane can be an alkylalkoxysilanes, arylalkoxysilanes or alkenylalkoxysilane. Mixtures of alkoxysilanes can be used, or a mixture of alkoxysilane with acetoxysilane can be used. [0012] One group of organosilanes suitable for use in the method of the invention are trialkoxysilanes having the formula RSi(OR')3, wherein R represents an alkyl or alkenyl group having 1 to 18 carbon atoms and R' represents an alkyl group having 1 to 4 carbon atoms. Examples of alkyl trialkoxysilanes include methyltrimethoxysilane, methyltriethoxysilahe, methyftri-n-propoxysilane, methyltri-i-propoxysilane, methyltri-n-butoxysilane, methyltri-i-butoxysilane, methyltri-sec-butoxysilane, methyttri-t-butoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, ethyftri-n-propoxysilane, ethyltri-i-propoxysilane, ethyltri-n-butoxysilane, ethyltri-i-butoxysilane, ethyltri-t-butoxysilane, n-propyttrimethoxysilane, n-propyltriethoxysilane, isopropyltrimethoxysilane, n-butyltrimethoxysilane, isobutyttrimethoxysilane, isobutyftriethoxysilane, pentyltrimethoxysilane, pentyltriethoxysilane, hexyltrimethoxysilane, n-octyftrimethoxysilane, n-octyltriethoxysilane, iso-octyltrimethoxysilane, chloromethyttrimethoxysilane, chloromethyltriethoxysilane, chloroethyltrimethoxysilane, chloroethyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, trifluoropropyltrimethoxysilane, trifluoropropyltriethoxysilane, trifluoropropyltri-n-propoxysilane, trifluoropropyltri-i-propoxysilane, trifIuoropropyItri-n-butoxysilane, trifluoropropyltri-t-butoxysilane, methyldimethoxyethoxysilane, methyldimethoxy-n-propoxysilane, methyldimethoxy-i-propoxysilane, methyldimethoxy-n--butoxysilane, methyldimethoxy-t-bi4Qxysilane, methyldiethoxy-n-propoxysilane, methyldiethoxy-i-propoxysilane, methyldiethoxy-n-butoxysilane and methyldietho*y-t-butoxysilane. Examples of a.lke.nyl trialkoxysilanes include vinyltrimethoxysilane, vinyltriethoxysilane, vinyltri-isopropoxysilane, allytrimethoxysilane, allytriethoxysilane, hexenyttrimethoxysilane and hexenyltriethoxysilane or mixtures thereof. We have found that mixtures containing at least two of methyltripropoxysilane and/or methyltrimethoxysilane and/or methyltriacetoxysilane and/or alkenyltnalkoxysilane and/or alkenyltriacetoxysilane are particularly effective in the process of the invention. [0013] Some examples of dialkyldialkoxysilanes that can be used in the method of the invention include dimethyldimethoxysilane, dimethyldiethoxysilane, ethylmethyldimethoxysilane, ethylmethyldiethoxysilane, isobutylmethyldimethoxysilane, isobutylmethyldiethoxysilane and trifluoropropylmethyldimethoxysilane. Examples of trialkylalkoxysilanes that can be used in the method of the invention include trimethylmethoxysilane, tri-n-propylmethoxysilane, trimethylethoxysilane, triethylethoxysilane, tri-n-propylethoxysilane, tri-i-propylethoxysilane and tri-n-butylethoxysilane. Examples of tetra-alkoxysilanes include tetramethoxysilane, tetraethoxysilane, tetra-n-propoxysilane, tetra-i-propoxysilane, tetra-n-butoxysilane and tetra-t-butoxysilane. [0014] Some examples of arylalkoxysilanes that can be used in the method of the invention include phenyldimethylmethoxysilane, phenylethylmethylmethoxysilane, diphenylmethylmethoxysilane, triphenylmethoxysilane, triphenylethoxysilane, phenylethyldimethoxysilane, phenylethyldiethoxysilane, phenylmethyldimethoxysilane, phenylmethyldiethoxysilane, phenylmethoxydiethoxysilane, phenyftrimethoxysilane, phenyltriethoxysilane and phenylmethyttrimethoxysilane. [0015] Some examples of alkenyalkoxysilanes that can be used in the method of the invention include vinyldimethylmethoxysilane, vinyldimethylethoxysilane, vinylmethyldimethoxysilane, vinylmethyldiethoxysilane, vinylphenyldiethoxysilane, triallylethoxysilane, diallylmethylethoxysilaneand allyldimethylethoxysilane. [0016] If desired, other types of hydrolysable organosilanes such as acetoxysilanes can be used. The acetoxysilanes can be monoacetoxysilanes, diacetoxysilanes, triacetoxysilanes, tetra-acetoxysilanes, and mixtures thereof. Some examples of suitable acetoxysilanes include phenylmethyldiacetoxysilane, vinylmethyldiacetoxysilane, methyltriacetoxysilane, ethyltriacetoxysilane, propyltriacetoxysilane, butyltriacetoxysilane, phenyltriacetoxysilane, vinyltriacetoxysilane and tetra-acetoxysilane. [0017) Examples of silanes containing both alkoxy and acetoxy groups are methyldiacetoxymethoxysilane, methylacetoxydimethoxysilane vinyldiacetoxymethoxysilane, vinylacetoxydimethoxysilane, methyldiacetoxyethoxysilane and methylacetoxydiethoxysilane. [0018] The acid hydrolysis catalyst in step (i) of the present invention may be any suitable acid which can be used in hydrolysis processes. Examples of suitable inorganic acids include sulphuric acid, phosphoric acid, and hydrochloric acid Some examples of suitable organic acids include acetic acid, formic acid, oxalic acid, citric acid, trichloroacetic acid, and sulfonic acids such as dodecylbenzenesulfonic acid The pH preferred during step (i) of the process can be from 0.1-6, preferably between 3-5. The acid is added to the hydrolysis solution in the amount of 0.1-1.0 percent by weight, based on the total weight of water and alkoxysilanes in the hydrolysis solution. . Organotrialkoxysilanes are commonly dissolved in water by shaking or stirring vigorously with acidified water until a clear solution results. Trialkoxysilanes hydrolyze stepwise in water to the corresponding silanols which condense to polysiloxanes. The hydrolysis of organotrialkoxysilanes is relatively rapid while the condensation reaction is slower. The hydrolysis of silanes is typically conducted at a high dilution in water. We have found according to the present invention, however, that improved results are achieved, particularly for hydrophobic gypsum, if the hydrolysate is prepared at a relatively high concentration of silane in water. While in general hydrolysis can be carried out at a silane concentration of 0.1 to 90% in water, concentrations greater than about 5% by weight may be preferred The concentration of silane in water can for example be from 10 or 15% up to 50% or even greater. [0019] Following hydrolysis and condensation, the solution may, if required be at least partially freed of the acid, and this is accomplished by neutralization with a base. A mild base is generally preferred since over-neutralization can result in product instability. Following neutralization, the solution is generally distilled to remove the by-product alcohol formed during hydrolysis, and the distilled solution can be filtered to separate any excess neutralizing agent and any neutralization products in the composition. While alcohol stripping is preferable, it is not a requirement. When using other hydrolysable silanes such as acetoxysilanes and chlorosilanes, the hydrolysis is similar, however the by-product is an acid, i.e., acetic acid and hydrochloric acid, instead of an alcohol. Preferably the acid is removed or partially neutralized with a neutralizing agent. It will be appreciated that in accordance with the present invention in many instances the mineral and/or filler materials introduced in step (ii) may be sufficiently basic in water to effect the partial neutralisation without the need for any additional basic material. Examples of such minerals include calcium carbonate or calcium sulphate such as stucco [0020] When used, the catalyst utilised in step (ii) for catalysing condensation of the hydrolysed silane can for example be a base catalyst, an organic compound of a metal such as a metal alkoxide, or a fluoride salt, or a combination of any of these [0021] When the catalyst used in step (ii) is a base it may be any suitable strong or weak base. Some examples of suitable bases include calcium oxide powder, calcium carbonate, solid calcium hydroxide or liquid lime, calcium acetate, sodium hydroxide, potassium hydroxide, sodium methylate, sodium carbonate, sodium bicarbonate, sodium borate, sodium acetate, solutions of a siliconate or silicate salt such as a sodium, potassium, calcium or aluminium siliconate or silicate, fly ash, amines such as triethylamine, ethylenetnamine, butylamine, octylamine, dibutylamine, monoethanolamine, diethanolamine, triethanolamine, diethylenetriamine, triethylenetetramine, cyclohexylamine, benzylamine, diethylaminopropylamine, xylylenediamine, triethylenediamine, guanidine, diphenylguanidine, morpholine, laurylamine or N,N-dimethylbenzylamine, ammonium hydroxide, ammonium carbonate, ammonium acetate, a phosphazene base, potassium acetate, magnesium carbonate, dolomite, potassium carbonate, sodium carbonate, magnesium oxide, cement such as Portland cement, sulphate resisting cement, blast furnace cement, pozzolanic cement, white cement, high alumina cement or expansive cement, and mixtures thereof. The pH generated in an aqueous slurry of stucco and organosilane with the base catalyst can be from pH 8-14. Strong bases, capable of generating a pH of at least 10, preferably about 10-13, are effective catalysts in the process of the invention provided that the mineral or filler is not adversely affected by strong base. Sodium hydroxide is one example of a strong base. It can be added in solid form, e.g. flakes, or as an aqueous solution. Weaker bases, generating a pH of 8-10 in an aqueous slurry of stucco and organosilane, are also effective catalysts used alone or in conjunction with an organic compound of a metal. The base catalyst is added to the stucco slurry in an amount sufficient to achieve the desired pH, typically in an amount of 0.1 -1.0% based on the total weight of the stucco slurry. The basic catalyst functions as a condensation catalyst, and enhances formation of higher molecular weight siloxane species which improve anchorage of the siloxanes to the stucco or other mineral imparling durable hydrophobicity. [0022] The organic compound of a metal which may be used as the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler in step (ii) of the present invention may for example be a compound of titanium, tin, aluminium, zirconium or vanadium. It can for example be a metal alkoxide or a metal carboxylate salt or a chelated metal compound. Preferred titanium compounds are titanium alkoxides, otherwise known as titanate esters, for example a titanium tetraalkoxide such as titanium tetra-n-butoxide (tetrabutyl titanate), tetraethyl titanate, tetranonyl titanate or tetraisopropoxy titanate. A titanium chelate can be used, for example a chelated titanate ester such as bis(acetylacetonyl) diisopropyl titanate or diisopropoxy titanium bis(ethylacetoacetate). The titanium tetraalkoxides are usually more catalytically active than the titanium chelate compounds. Analogous zirconium or vanadium compounds, for example zirconate or vanadate esters, can alternatively or additionally be used. Preferred aluminium compounds are aluminium alkoxides, for example aluminium sec-butanolate, or aluminium chelate compounds. [0023] If the organic compound of a metal is a tin compound it is usually a tin carboxylate or organotin carboxylate, for example dibutyltin dilaurate, dioctyltin dilaurate, stannous octoate, stannous acetate, stannous oxalate, stannous naphthenate, dibutyltin dioctoate, dibutyltin bis(isooctyl maleate) or dioctyttin i)is(isooctyl thioglycolate), although an organotin chelate compound such as dibutyltinbis(2,4-pentadionate)tin can be used. The combination of an organic compound of tin with an amine such as laurylamine can be particularly effective as a catalyst. [0024] The amount of organic compound of a metal added as catalyst can for example be 0.01-2% based on the total weight of the stucco slurry, preferably 0.02-0.5%. [0025] The fluoride satt which may be used as a catalyst in step (ii) of the present invention is preferably an ammonium fluoride of the formula [R" hexafluorosilicate or fluorophosphate. Preferred ammonium fluorides include tetrabutylammonium fluoride, fetramethylammonium fluoride, benzylmethylammonium fluoride and methylammonium fluoride and adducts thereof with carbonyl compounds such as acetylacetone, methyl acetoacetate, 2-ethylhexyl acetoacetate, isopropyl acetoacetate or ethyl acetoacetate. The amount of fluoride salt added as catalyst can for example be 0.01-5% based on the total weight of the stucco slurry, preferably 0.02-1 %. [0026] Combinations of two or more different hydrolysis catalysts can be used in step(ii), for example a base catalyst can be used in conjunction with a metal alkoxide such as an alkoxide of titanium, zirconium, vanadium or aluminium, or another organic compound of a metal such as an organic compound of tin and/or with a fluoride salt. [0027] The hydrolysis catalyst may be introduced to the hydrolysable organosilane and water mix shortly, typically immediately before combination with the stucco to form a slurry We have found that if the organosilane is hydrolysed in the presence.of the gypsum or other mineral or filler, so that the organosilane hydrolysis product condenses to form polyorganosiloxane in the presence of the mineral or filler, the polyorganosiloxane becomes intimately incorporated in the mineral or filler. [0028] The mixtures used in step (i) and/or step (ii) may further include other organosilicon compounds such as silane diols and hydroxyl endblocked polydimethylsiloxane fluids. Some examples include silanols, hydroxyl functional polydimethylsiloxanes, and alkoxy functional polydimethylsiloxanes. The silanols can be silanols, silanediols, or silanetriols. Some examples include trimethylsilanol, triethylsilanol, tripropylsilanol, triisopropylsilanol, tributylsilanol, triisobutylsilanol, tri-(sec-butyl)silanol, tri-(tert-butyl)silanol, tripentylsilanol, triisopentylsilanol, tri-(sec-pentyl)silanol, tri-(tert-pentyl)silanol; dimethylsilanediol, diethylsilanediol, dipropylsilanediol, diisopropylsilanediol, dibutylsilanediol, diisobutylsilanediol, di-(sec-butyl)silanediol, di-(tert-butyl)silanediol, di-pentylsilanediol, diisopentylsilanediol, di-(sec-pentyl)silanediol, di-(tert-pentyl)silanediol, methylsilanetriol, ethylsilanetnol, propylsilanetnol, isopropylsilanetnol, butylsiianetrioL isobutylsilanetriol, sec-butyl-silanetriol, tert-butyl-silanetriol, pentylsilanetriol, isopentylsilanetriol, sec-pentyl-silanetriol, tert-pentyl-silanetriol, tnphenylsilanol, triphenylethylsilanol, triphenylpropylsiianol, diphenylsilanediol, diphenylethylsilanediol, diphenylpropylsilanediol, methylphenylsilanediol, phenylsilanetriol, and mixtures thereof. The hydroxyl functional polydimethylsiloxanes and the alkoxy functional polydimethylsiloxanes may contain terminal, pendant, or terminal and pendant, functional groups. Suitable functional polydimethylsiloxanes will generally have from 2-300 repeating units in the chain. These organosilicon compounds are capable of functioning as crosslinking agents and/or chain extenders. If such another silicon compound is used, silanol- functional polydimethylsiloxanes having 4-100 repeating units in the chain are preferred. In general the hydrolysable organosilane is hydrolysed and then condensed to form a polysiloxane, although when a silanol-functional polysiloxane is present the hydrolysable groups of the silane can condense with the silanol groups to form an extended or crosslinked polysiloxane The weight ratio of hydrolysable organosilane to silanol-functional or alkoxy-functional polyorganosiloxane is preferably at least 1:10, more preferably at least 1:3, for example 1:1 to 10:1. [0029] The concentration of silane hydrolysis product in water in the slurry of mineral or filler as the mineral or filler is being treated is generally about 0.1-50 percent by weight.. Preferably, the amount of water is chosen so that the solution contains 0.3-20 percent by weight, most preferably about 0.3-10 percent by weight, of the hydrolyzate. When the polysiloxane hydrolyzate contains sufficient water, the addition of more water in step (ii) of the process is not required in order to form the slurry. In that instance, water is an optional component in step (ii), although it can be included when additional amounts of water are needed to form a slurry. OPTIONAL ADDITIVES [0030] As noted above, other additives for making gypsum plasterboard are often used in commercial operations including starch; foaming agents; wetting agents; accelerators; retarders such as proteins and organic acids; paper or pulp; viscosity modifying agents; anti-burning agents; non-silicon atom containing water-resisting chemicals such as wax emulsions; glass fibres; fire-resistance enhancers such as vermiculite, clays, and fumed silica; and polymeric compounds such as polyvinyl alcohol. One or more additives such as these may be included in step (ii) of the present process. EXAMPLES [0031] The following examples are set forth in order to illustrate the invention in more detail. EXAMPLE 1 [0032] To 795 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 5 gram of methytrimethoxysilane (MTM) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time. EXAMPLE 2 [0033] To 790 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 10 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time. EXAMPLE 3 ' [0034] To 75.0 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The.mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time. EXAMPLE 4 [0035] To 795 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 5 gram of methytriethoxysilane (MTE) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time. EXAMPLE 5 [0036] To 790 milliliter of water was added undeV stirring, acetic acid to adjust the.pH to. 3.6. 10 gram of methytriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring ior 2 days before n was packaged and stored prior to testing on stucco over time. EXAMPLE 6 [0037] To 750 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram ot methytriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for 2 days before it was packaged and stored prior io testing on stucco over time. EXAMPLE 7: GENERAL PROCEDURE [0038] Aqueous solutions containing the polysiloxane hydrolyzate composition were prepared so that the weight of the polysiloxane hydrolyzate based on the weight of stucco was from 0 5 to 5.0 percent To 80 gram of the aqueous solution containing the polysiloxane hydrolyzate composition was added 100 gram of stucco under vigorous stirring. No further catalyst was added, and the pH of the resulting slurry was measured to be about 6-7 The slurry was stirred for another 60 seconds and poured into disk shaped moulds. The samples were allowed to set at room temperature (20-25 qC) for 15-60 minutes. The disks separated from the moulds were gypsum disks of three centimetre in diameter and one centimetre in depth. The samples were further dried in an air circulating oven for 30 minutes at 110 'C, and then for 12-24 hours at 40 °C. The disks were cooled down and immersed in water for two hours. The weight of the disks before and after immersing the disks in water was measured. The water uptake expressed in percent, was used as the measure of the hydrophobing property of the polysiloxane hydrolyzate compositions. The water uptake of the disks treated with the polysiloxane hydrolyzate composition was compared to the water uptake of untreated gypsum stucco that has a value of about 40 percent. Table 1 shows results obtained by following the above procedure. [0039] In Table 1, MTM designates methyltrimethoxysilane and MTE designates methyltriethoxysilane. Examples 1 -6 Table 1 show that a reduction in water-absorption, and the consequent improvement in water resistance, was obtained at various loadings of the polysiloxane hydrolyzate. Table 1 also shows that good stability, and an improvement in water-absorption over time, can be obtained with the polysiloxane hydrolyzates. EXAMPLE 8 [0040] To 3,962.5 millilitre of tap water was added under stirring, acetic acidlo adjust fPff pH to 3.6. 37.5 gram of methytrimethoxysilane (MTM) was then added drop-wise under-constant stirring The aqueous mixture became clear within minutes. The mixture wars maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 9 [0041] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 10 [0042] To 3,962.5 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 37.5 gram of methytriethoxysilane (MTE) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 11 [0043] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of methytriethoxysilane was.then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 12 [0044] To 3,962.5 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 37.5 gram of vinyltriethoxysilane (VTE) was then added drop-wise under constant stirring The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. ■ EXAMPLE 13 [0045] To 3,950 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram of vinyltriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 14 [0046] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of vinyltriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco. EXAMPLE 15: GENERAL PROCEDURE [0047] Aqueous solutions containing the polysiloxane hydrolyzate composition were prepared. The weight of the polysiloxane hydrolyzate based on the weight of stucco was from 0.5 to 5.0 percent. To 80 gram of the aqueous solution containing the polysiloxane hydrolyzate composition was added 100 gram of stucco under vigorous stirring, and several drops of a 40 weight percent aqueous solution of NaOH to adjust the pH to 12. The slurry was stirred for another 60 seconds and poured into disk shaped moulds. The samples were allowed to set at room temperature (20-25 °C) for 15-60 minutes. The disks separated from the moulds were gypsum disks of three centimetre in diameter and one centimetre in depth. The samples were further dried in an air circulating oven for 30 minutes at 110 "C, and then for 12-24 hours at 400. The disks were cooled down and immersed in water for two hours. The weight of the disks before and after immersing the disks in water was measured. The water uptake expressed in percent was used as the measure of the hydrophobing property of the polysiloxane hydrolyzate composition. The water uptake of the disks treated with the polysiloxane hydrolyzate composition was compared to the water uptake of untreated gypsum stucco that has a value of about 37-40 percent. Table 2 below sets forth the results obtained according to the above procedure. [0048] In Table 2, MTM designates methyltrimethoxysilane, MTE designates methyltriethoxysilane, and VTE designates vinyltriethoxysilane. Examples 1-6 and Examples 8-14 in Table 2 show that a dramatic reduction in water-absorption, and the consequent improvement in water resistance, can be obtained at various loadings of Jhe polysiloxane hydrolyzate under base catalysis in comparison to Table 1. Table 2 also shows That good stability, and an improvement in water absorption overtime, can ho obtained with the polysiloxane hydrolyzates EXAMPLE 15 [0049] To 85 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 15 gram of methytrimethoxysiiane (MTM) was then added drop-wise under constant stirring The mixture was packaged prior to testing on stucco. EXAMPLE 16 [0050] To 70 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 30 gram of methytrimethoxysiiane (MTM) was then added drop wise under constant stirring. The mixture was packaged prior to testing on stucco. EXAMPLE 17 [0051] To 50 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 50 gram of methytrimethoxysiiane (MTM) was then added drop-wise under constant stirring The mixture was packaged prior to testing on stucco [0052] Aqueous solutions were prepared from the hydrolysates of Examples 15 to 17 so that the weight of the polysiloxane hydroiyzate based on the weight of stucco was 1 to 2 percent. To 80 gram of the aqueous solution containing the polysiloxane hydroiyzate composition was added 100 gram of stucco under vigorous stirring. No further catalyst was added, and the pH of the resulting slurry was measured to be about 5-7. The slurry was stirred for another 60 seconds and poured into disk shaped molds, then tested as described in Example 7 Table 3 shows results obtained by following the above procedure 10053] Examples 15 -17 and Table 3-show that a reduction in water-absorption, and the consequent improvement in water resistance, was obtained at various loadings of the polysiloxane hydrolyzate starting from concentrated hydrolysed solutions. [0054] Other variations may be made in compounds, compositions, and methods described herein without departing from the essential features of the invention. The embodiments of the invention specifically illustrated herein are exemplary only arid not intended as limitations on their scope except as defined in the appended claims. We Claim: 1. A method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture, such as herein described, in the presence of an acid hydrolysis catalyst, such as herein described; and (ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler, such as herein described, and optionally water and/or a catalyst for condensation of the hydrolysate, such as herein described. 2. A method as claimed in Claim 1 in which the hydrolysable silane comprises one or more silanes, each silane comprising one or more alkoxy groups and/or one or more acetoxy groups and/or one or more halide groups. 3. A method as claimed in Claim 2 wherein the hydrolysable silane is selected from at least one alkylalkoxysilane, arylalkoxysilane, and/or alkenylalkoxysilane or a mixture thereof. 4. A method as claimed in claim 2 wherein the hydrolysable organosilane comprises a mixture containing at least two of methyltripropoxysilane and/or methyltrimethoxysilane and/or methyltriacetoxysilane and/or alkenyltrialkoxysilane and/or alkenyltriacetoxysilane. 5. A method as claimed in any of Claims 2 to 4 in which any alcohol generated during preparation of the polysiloxane hydrolyzate is removed before the polysiloxane hydrolyzate is contacted with the mineral or filler material. 6. A method as claimed in Claim 2, in which the hydrolysable silane is an acetoxysilane or a mixture of acetoxysilanes, which silane(s) may additionally comprise one or more chloro groups per molecule. 7. A method as claimed in Claim 2, in which the hydrolysable silane is a chlorosilane or a mixture of chlorosilanes. 8. A method as claimed in Claim 6 or Claim 7 in which any excess acid generated during preparation of the polysiloxane hydrolyzate is partially neutralized or removed before the polysiloxane hydrolyzate is contacted with the mineral or filler material. 9. A method in accordance with any preceding claim wherein the pH during step (i) is 0.1-6. 10. A method as claimed in any of Claims 1 to 9 in which the hydrolysate is prepared at a concentration of silane in water greater than 5% by weight. 11. A method as claimed in any of Claims 1 to 9 in which the hydrolysate is prepared at a concentration of silane in water in the range 15 to 90% by weight. 12. A method as claimed in any of Claims 1 to 11 in which the minerals and fillers are selected from non-hydrated, partially hydrated, or hydrated, fluorides, chlorides, bromides, iodides, chromates, carbonate hydroxides, hydroxides, phosphates, hydrogen phosphates, nitrates, oxides, sulphates of sodium, potassium, magnesium, calcium, and barium, titanium dioxide, zinc oxide, aluminium oxide, aluminium trihydroxide, vermiculite, silica, fumed silica, fused silica, precipitated silica, quartz, sand, silica gel, rice hull ash, ceramic and glass beads, zeolites, hydrous calcium silicate, silica-carbon black composite, functionalized carbon nanotubes, cement, fly ash, slate flour, bentonite, clay, mica, kaolin, talc, calcium carbonate, wollastonite, polymeric fillers, rubber particles, wood flour, wood fibres, cellulose and cellulose-containing products, aramid fibres, nylon fibres, cotton fibres or glass fibres. 13. A method as claimed in any of Claims 1 to 12 wherein the mineral and /or filler is stucco and optionally gypsum. 14. A method as claimed in Claim 13 wherein the gypsum comprises one or more of calcium sulphate dehydrate, phospho-gypsum and/or desulphogypsum and/or titanogypsum and/or fluorogypsum and wherein the stucco is derived from natural gypsum and/or synthetic gypsum. 15. A method as claimed in any preceding claim wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is a base and the pH during step (ii) is from pH 8 to pH14 16 A method as claimed in Claim 13 or Claim 14 of preparing hydrophobic gypsum and gypsum products comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing under acidic conditions a hydrolyzable silane or hydrolyzable silane mixture; and (ii) combining the polysiloxane hydrolyzate with stucco, a basic catalyst, and optionally water to form a slurry. 17. A method as claimed in any of Claims 1 to 14 wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is an alkoxide of titanium, zirconium, vanadium or aluminium. 18. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is an organic compound of tin. 19. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is a fluoride salt. 20. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler comprises a base and an alkoxide of titanium, zirconium, vanadium or aluminium, an organic compound of tin or a fluoride salt. 21. A method as claimed in any of Claims 1 to 20 wherein the hydrolyzable silane mixture and/or the materials with which it is combined in step (ii) further comprises a silanol, a silanediol, a silanetriol, a hydroxyl functional polydimethylsiloxane, or an alkoxy functional polydimethylsiloxane. 22. A method as claimed in any preceding claim in which at least one additive comprising starch, a foaming agent, a wetting agent, an accelerator, a retarder, paper, pulp, a viscosity modifying agent, an anti-burning agent, a non-silicon atom containing water-resisting chemical, glass fibres, a fire-resistance enhancer, a polymeric compound and/or uncalcined gypsum is additionally introduced during step (ii). 23. A method as claimed in Claim 13 or Claim 14 wherein the acid hydrolysis catalyst is mixed with water and the hydrolysable organosilane immediately prior to the addition of stucco and a further catalyst for condensation of the hydrolysate, wherein the catalyst and stucco are mixed. 24. A method of preparing a hydrophobic gypsum product, for example plasterboard, comprising preparing a hydrophobic gypsum material as claimed in Claim 13 or Claim 14 and discharging the hydrophobic gypsum material onto a support or mould, and drying. ABSTRACT METHOD OF PREPARING A MINERAL AND/OR FILLER MATERIAL, LIKE, GYPSUM MATERIAL The invention discloses a method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and (ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler and optionally water and/or a catalyst for condensation of the hydrolysate. The invention is also for a making a gypsum product, e.g. plasterboard by using said mineral or filler material.

Full Text

[0001 ] This invention relates to a process of making minerals and filler materials, particularly gypsum and gypsum products that are hydrophobic and/or water resistant. In particular, hydrophobicity and/or water resistance is provided by adding during the process, certain aqueous solutions of polysiloxanes obtained by prehydrolyzing under acidic conditions certain hydrolyzable silanes such as alkylalkoxysilanes, arylalkoxysilanes, alkenylalkoxysilanes, and mixtures thereof.
[0002] Gypsum products such as gypsum plasterboard are made by mixing stucco with water to produce a slurry. The slurry is fed onto a sheet of cardboard, covered with a second sheet of cardboard, and passed over a moulding platform to be shaped into an encased strip. The strip of gypsum plasterboard is initially soft, but then quickly sets as the calcium sulphate hemihydrates (stucco) rehydrates back to calcium sulphate dihydrate (gypsum), and therefore hardens, and is cut into separate panels of gypsum plasterboard.
[0003] In particular, gypsum plasterboard is produced from basic materials including paper in the form of cardboard, stucco, water, starch, and additives such as accelerators and foams. Other additives for making gypsum plasterboard are also added, including retarders such as proteins and organic acids; viscosity modifying agents; anti-burning agents; water-resisting chemicals such as polysiloxanes and wax emulsions; glass fibres; fire-resistance enhancers such as vermiculite, clays, and fumed silica; and polymeric compounds such as polyvinyl alcohol. As noted, wallboards or plasterboards are large thin gypsum panels covered with cardboard. This invention relates to an improved process for the incorporation of polysiloxane in gypsum, a gypsum product or another mineral or filler to impart water resistance.
[0004] WO-A-81/01702 describes a process for the preparation of a plaster mortar containing gypsum powder, water, conventional additives and ballast material, comprising adding said materials during the process of manufacture, in the preparation of the gypsum powder, in the mixing of the powder and water or to the mixing water or to the wet mortar, alkoxysilanes and optionally a solvent and optionally a tenside/emulsifier/surfactant and optionally a silanol polymerisation catalyst and optionally substancesTprbViding for acid or basic reaction conditions in the mixing water and optionally a fine powder consisting of reactive silica.

[0005] In one embodiment of the present invention there is provided a method of preparing a mineral and/or filler material comprising:
(i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable
silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and
(ii) combining the polysiloxane hydrolyzate with minerals and/or fillers, and optionally
water and/or a catalyst for condensation of the hydrolysate.
[0006] The process of the invention can be used for the treatment of a wide range of minerals or fillers in powder form.
[0007] The method of the invention can be used in preparing other types of hydrophobic and/or water resistant materials such as minerals and fillers. Some representative examples include non-hydrated, partially hydrated, or hydrated fluorides, chlorides, bromides, iodides, chromates, carbonate hydroxides, hydroxides, phosphates, hydrogen phosphates, nitrates, oxides, and sulphates of sodium, potassium, magnesium, calcium, and barium; titanium dioxide, zinc oxide, aluminium oxide, aluminium tnhydroxide, vermiculite, silica including fumed silica, fused silica, precipitated silica, quartz, sand, and silica gel; rice hull ash, ceramic and glass beads, zeolites, hydrous calcium silicate, silica-carbon black composite, functionalized carbon nanotubes, cement, fly ash, slate flour, bentonite, clay, mica, kaolin, talc, calcium carbonate, wollastonite, polymeric fillers, rubber particles, wood flour, wood fibres, cellulose and cellulose-containing products, aramid fibres, nylon fibres, cotton fibres, or glass fibres.
[0008] One example is in the preparation of hydrophobic gypsum and gypsum products, and the invention will be described in terms of gypsum although it can be applied to other minerals and fillers. As used herein, the term gypsum is intended to mean all solid forms of calcium sulphate including calcium sulphate dihydrate CaS042H20. The term stucco is
intended to mean calcium sulphate hemihydrate CaSO40.5H2O, commonly known as
plaster of Paris or calcined gypsum but for the sake of this invention should also be understood to be dehydrate and anhydrate derivatives thereof. Stucco is made by heating gypsum to remove 3/2 H2O molecule. The method of preparing hydrophobic and/or water

resistant gypsum and gypsum products according to the invention, can be used to prepare hydrophobic gypsum and gypsum products derived from all sources of gypsum and stucco, including natural gypsum (calcium sulphate dihydrate), synthetic gypsum from plasterboard waste stations, or synthetic gypsum (desulphogypsum) produced at coal fired power plants that convert sulphur dioxide to synthetic gypsum, and other forms of synthetic gypsum such as titanogypsum, fluorogypsum or phosphogypsum. The method of the invention is particularly suitable for treating stucco in powder form, as used in the preparation of gypsum . products such as gypsum plasterboard
[0009] Hence one embodiment is particularly directed to a method of making hydrophobic and/or water resistant gypsum and gypsum products by:
(i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture under acidic conditions;
(ii) combining the polysiloxane hydrolyzate with stucco and/or gypsum, and optionally water and/or a basic catalyst, to form a slurry; and
(iii) discharging the slurry onto a support or mould, and drying the slurry to form a hydrophobic gypsum or hydrophobic gypsum product.
[0010] As used herein, the terms hydrolyzate containing polysiloxane and polysiloxane hydrolyzate are intended to include the various species resulting from the hydrolysis of alkoxysilanes, chlorosilanes, and/or acetoxysilanes, including combinations of monomeric hydroxysilanes such as organotrihydroxysilanes, linear, cyclic , or branched hydroxysiloxanes in oligomeric or polymeric form, and any species containing both the hydroxyl and remaining hydrolysable groups such as organodihydroxymonoalkoxysilanes and organomonohydroxydialkoxysilanes, in oligomeric or polymeric siloxane forms, resulting either from the partial hydrolysis or the residual esterification of hydroxyl group into alkoxy groups, and the residual alcoholysis of siloxanes into hydroxy or alkoxy" functional silanes, or shorter siloxane mixtures. Although the post-distillation of the alcohol by-product does reduce significantly the re-generation of residual alkoxysilanes, alkoxyoligosiloxanes, and alkoxypolysiloxanes, it is not a requirement for obtaining low water uptake, and the consequent hydrophobing properties of gypsum and gypsum products.

[0011] The hydrolysable organosilane in accordance vyith the present invention may comprise one or more silanes, each silane being the same or different and comprising one or more alkoxy groups and/or one or more acetoxy groups and/or one or more halide groups (typically chloride groups) and mixtures thereof. Hence, the hydrolysable organosilane can for example be an alkoxysilane or acefoxysilane or a silane containing both alkoxy and acetoxy groups bonded to a silicon atom. The alkoxysilane can be a monoalkoxysilane, dialkoxysilane, trialkoxysilane, ortetra-alkoxysilane. The alkoxysilane can contain the same or different alkoxy groups Optionally, it may contain one or more halogenated substituted organic groups. The alkoxysilane can be an alkylalkoxysilanes, arylalkoxysilanes or alkenylalkoxysilane. Mixtures of alkoxysilanes can be used, or a mixture of alkoxysilane with acetoxysilane can be used.
[0012] One group of organosilanes suitable for use in the method of the invention are trialkoxysilanes having the formula RSi(OR')3, wherein R represents an alkyl or alkenyl group having 1 to 18 carbon atoms and R' represents an alkyl group having 1 to 4 carbon atoms. Examples of alkyl trialkoxysilanes include methyltrimethoxysilane, methyltriethoxysilahe, methyftri-n-propoxysilane, methyltri-i-propoxysilane, methyltri-n-butoxysilane, methyltri-i-butoxysilane, methyltri-sec-butoxysilane, methyttri-t-butoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, ethyftri-n-propoxysilane, ethyltri-i-propoxysilane, ethyltri-n-butoxysilane, ethyltri-i-butoxysilane, ethyltri-t-butoxysilane, n-propyttrimethoxysilane, n-propyltriethoxysilane, isopropyltrimethoxysilane, n-butyltrimethoxysilane, isobutyttrimethoxysilane, isobutyftriethoxysilane, pentyltrimethoxysilane, pentyltriethoxysilane, hexyltrimethoxysilane, n-octyftrimethoxysilane, n-octyltriethoxysilane, iso-octyltrimethoxysilane, chloromethyttrimethoxysilane, chloromethyltriethoxysilane, chloroethyltrimethoxysilane, chloroethyltriethoxysilane, chloropropyltrimethoxysilane, chloropropyltriethoxysilane, trifluoropropyltrimethoxysilane, trifluoropropyltriethoxysilane, trifluoropropyltri-n-propoxysilane, trifluoropropyltri-i-propoxysilane, trifIuoropropyItri-n-butoxysilane,
trifluoropropyltri-t-butoxysilane, methyldimethoxyethoxysilane, methyldimethoxy-n-propoxysilane, methyldimethoxy-i-propoxysilane, methyldimethoxy-n--butoxysilane, methyldimethoxy-t-bi4Qxysilane, methyldiethoxy-n-propoxysilane, methyldiethoxy-i-propoxysilane, methyldiethoxy-n-butoxysilane and methyldietho*y-t-butoxysilane. Examples of a.lke.nyl trialkoxysilanes include vinyltrimethoxysilane, vinyltriethoxysilane,

vinyltri-isopropoxysilane, allytrimethoxysilane, allytriethoxysilane, hexenyttrimethoxysilane and hexenyltriethoxysilane or mixtures thereof. We have found that mixtures containing at least two of methyltripropoxysilane and/or methyltrimethoxysilane and/or methyltriacetoxysilane and/or alkenyltnalkoxysilane and/or alkenyltriacetoxysilane are particularly effective in the process of the invention.
[0013] Some examples of dialkyldialkoxysilanes that can be used in the method of the invention include dimethyldimethoxysilane, dimethyldiethoxysilane, ethylmethyldimethoxysilane, ethylmethyldiethoxysilane, isobutylmethyldimethoxysilane, isobutylmethyldiethoxysilane and trifluoropropylmethyldimethoxysilane. Examples of trialkylalkoxysilanes that can be used in the method of the invention include trimethylmethoxysilane, tri-n-propylmethoxysilane, trimethylethoxysilane, triethylethoxysilane, tri-n-propylethoxysilane, tri-i-propylethoxysilane and tri-n-butylethoxysilane. Examples of tetra-alkoxysilanes include tetramethoxysilane, tetraethoxysilane, tetra-n-propoxysilane, tetra-i-propoxysilane, tetra-n-butoxysilane and tetra-t-butoxysilane.
[0014] Some examples of arylalkoxysilanes that can be used in the method of the invention include phenyldimethylmethoxysilane, phenylethylmethylmethoxysilane, diphenylmethylmethoxysilane, triphenylmethoxysilane, triphenylethoxysilane, phenylethyldimethoxysilane, phenylethyldiethoxysilane, phenylmethyldimethoxysilane, phenylmethyldiethoxysilane, phenylmethoxydiethoxysilane, phenyftrimethoxysilane, phenyltriethoxysilane and phenylmethyttrimethoxysilane.
[0015] Some examples of alkenyalkoxysilanes that can be used in the method of the invention include vinyldimethylmethoxysilane, vinyldimethylethoxysilane, vinylmethyldimethoxysilane, vinylmethyldiethoxysilane, vinylphenyldiethoxysilane, triallylethoxysilane, diallylmethylethoxysilaneand allyldimethylethoxysilane.
[0016] If desired, other types of hydrolysable organosilanes such as acetoxysilanes can be used. The acetoxysilanes can be monoacetoxysilanes, diacetoxysilanes, triacetoxysilanes, tetra-acetoxysilanes, and mixtures thereof. Some examples of suitable acetoxysilanes include phenylmethyldiacetoxysilane, vinylmethyldiacetoxysilane, methyltriacetoxysilane, ethyltriacetoxysilane, propyltriacetoxysilane, butyltriacetoxysilane, phenyltriacetoxysilane, vinyltriacetoxysilane and tetra-acetoxysilane.

[0017) Examples of silanes containing both alkoxy and acetoxy groups are methyldiacetoxymethoxysilane, methylacetoxydimethoxysilane vinyldiacetoxymethoxysilane, vinylacetoxydimethoxysilane, methyldiacetoxyethoxysilane and methylacetoxydiethoxysilane.
[0018] The acid hydrolysis catalyst in step (i) of the present invention may be any suitable acid which can be used in hydrolysis processes. Examples of suitable inorganic acids include sulphuric acid, phosphoric acid, and hydrochloric acid Some examples of suitable organic acids include acetic acid, formic acid, oxalic acid, citric acid, trichloroacetic acid, and sulfonic acids such as dodecylbenzenesulfonic acid The pH preferred during step (i) of the process can be from 0.1-6, preferably between 3-5. The acid is added to the hydrolysis solution in the amount of 0.1-1.0 percent by weight, based on the total weight of water and alkoxysilanes in the hydrolysis solution. . Organotrialkoxysilanes are commonly dissolved in water by shaking or stirring vigorously with acidified water until a clear solution results. Trialkoxysilanes hydrolyze stepwise in water to the corresponding silanols which condense to polysiloxanes. The hydrolysis of organotrialkoxysilanes is relatively rapid while the condensation reaction is slower. The hydrolysis of silanes is typically conducted at a high dilution in water. We have found according to the present invention, however, that improved results are achieved, particularly for hydrophobic gypsum, if the hydrolysate is prepared at a relatively high concentration of silane in water. While in general hydrolysis can be carried out at a silane concentration of 0.1 to 90% in water, concentrations greater than about 5% by weight may be preferred The concentration of silane in water can for example be from 10 or 15% up to 50% or even greater.
[0019] Following hydrolysis and condensation, the solution may, if required be at least partially freed of the acid, and this is accomplished by neutralization with a base. A mild base is generally preferred since over-neutralization can result in product instability. Following neutralization, the solution is generally distilled to remove the by-product alcohol formed during hydrolysis, and the distilled solution can be filtered to separate any excess neutralizing agent and any neutralization products in the composition. While alcohol stripping is preferable, it is not a requirement. When using other hydrolysable silanes such as acetoxysilanes and chlorosilanes, the hydrolysis is similar, however the by-product is an acid, i.e., acetic acid and hydrochloric acid, instead of an alcohol. Preferably the acid is removed or partially neutralized with a neutralizing agent. It will be appreciated that in

accordance with the present invention in many instances the mineral and/or filler materials introduced in step (ii) may be sufficiently basic in water to effect the partial neutralisation without the need for any additional basic material. Examples of such minerals include calcium carbonate or calcium sulphate such as stucco
[0020] When used, the catalyst utilised in step (ii) for catalysing condensation of the hydrolysed silane can for example be a base catalyst, an organic compound of a metal such as a metal alkoxide, or a fluoride salt, or a combination of any of these
[0021] When the catalyst used in step (ii) is a base it may be any suitable strong or weak base. Some examples of suitable bases include calcium oxide powder, calcium carbonate, solid calcium hydroxide or liquid lime, calcium acetate, sodium hydroxide, potassium hydroxide, sodium methylate, sodium carbonate, sodium bicarbonate, sodium borate, sodium acetate, solutions of a siliconate or silicate salt such as a sodium, potassium, calcium or aluminium siliconate or silicate, fly ash, amines such as triethylamine, ethylenetnamine, butylamine, octylamine, dibutylamine, monoethanolamine, diethanolamine, triethanolamine, diethylenetriamine, triethylenetetramine, cyclohexylamine, benzylamine, diethylaminopropylamine, xylylenediamine, triethylenediamine, guanidine, diphenylguanidine, morpholine, laurylamine or N,N-dimethylbenzylamine, ammonium hydroxide, ammonium carbonate, ammonium acetate, a phosphazene base, potassium acetate, magnesium carbonate, dolomite, potassium carbonate, sodium carbonate, magnesium oxide, cement such as Portland cement, sulphate resisting cement, blast furnace cement, pozzolanic cement, white cement, high alumina cement or expansive cement, and mixtures thereof. The pH generated in an aqueous slurry of stucco and organosilane with the base catalyst can be from pH 8-14. Strong bases, capable of generating a pH of at least 10, preferably about 10-13, are effective catalysts in the process of the invention provided that the mineral or filler is not adversely affected by strong base. Sodium hydroxide is one example of a strong base. It can be added in solid form, e.g. flakes, or as an aqueous solution. Weaker bases, generating a pH of 8-10 in an aqueous slurry of stucco and organosilane, are also effective catalysts used alone or in conjunction with an organic compound of a metal. The base catalyst is added to the stucco slurry in an amount sufficient to achieve the desired pH, typically in an amount of 0.1 -1.0% based on the total weight of the stucco slurry. The basic catalyst functions as a condensation catalyst, and enhances formation of higher molecular weight siloxane species which improve anchorage of the siloxanes to the stucco or other mineral imparling durable hydrophobicity.

[0022] The organic compound of a metal which may be used as the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler in step (ii) of the present invention may for example be a compound of titanium, tin, aluminium, zirconium or vanadium. It can for example be a metal alkoxide or a metal carboxylate salt or a chelated metal compound. Preferred titanium compounds are titanium alkoxides, otherwise known as titanate esters, for example a titanium tetraalkoxide such as titanium tetra-n-butoxide (tetrabutyl titanate), tetraethyl titanate, tetranonyl titanate or tetraisopropoxy titanate. A titanium chelate can be used, for example a chelated titanate ester such as bis(acetylacetonyl) diisopropyl titanate or diisopropoxy titanium bis(ethylacetoacetate). The titanium tetraalkoxides are usually more catalytically active than the titanium chelate compounds. Analogous zirconium or vanadium compounds, for example zirconate or vanadate esters, can alternatively or additionally be used. Preferred aluminium compounds are aluminium alkoxides, for example aluminium sec-butanolate, or aluminium chelate compounds.
[0023] If the organic compound of a metal is a tin compound it is usually a tin carboxylate or organotin carboxylate, for example dibutyltin dilaurate, dioctyltin dilaurate, stannous octoate, stannous acetate, stannous oxalate, stannous naphthenate, dibutyltin dioctoate, dibutyltin bis(isooctyl maleate) or dioctyttin i)is(isooctyl thioglycolate), although an organotin chelate compound such as dibutyltinbis(2,4-pentadionate)tin can be used. The combination of an organic compound of tin with an amine such as laurylamine can be particularly effective as a catalyst.
[0024] The amount of organic compound of a metal added as catalyst can for example be 0.01-2% based on the total weight of the stucco slurry, preferably 0.02-0.5%.
[0025] The fluoride satt which may be used as a catalyst in step (ii) of the present invention is preferably an ammonium fluoride of the formula [R"
hexafluorosilicate or fluorophosphate. Preferred ammonium fluorides include tetrabutylammonium fluoride, fetramethylammonium fluoride, benzylmethylammonium fluoride and methylammonium fluoride and adducts thereof with carbonyl compounds such as acetylacetone, methyl acetoacetate, 2-ethylhexyl acetoacetate, isopropyl acetoacetate or ethyl acetoacetate. The amount of fluoride salt added as catalyst can for example be 0.01-5% based on the total weight of the stucco slurry, preferably 0.02-1 %.
[0026] Combinations of two or more different hydrolysis catalysts can be used in step(ii), for example a base catalyst can be used in conjunction with a metal alkoxide such as an alkoxide of titanium, zirconium, vanadium or aluminium, or another organic compound of a metal such as an organic compound of tin and/or with a fluoride salt.
[0027] The hydrolysis catalyst may be introduced to the hydrolysable organosilane and water mix shortly, typically immediately before combination with the stucco to form a slurry We have found that if the organosilane is hydrolysed in the presence.of the gypsum or other mineral or filler, so that the organosilane hydrolysis product condenses to form polyorganosiloxane in the presence of the mineral or filler, the polyorganosiloxane becomes intimately incorporated in the mineral or filler.
[0028] The mixtures used in step (i) and/or step (ii) may further include other organosilicon compounds such as silane diols and hydroxyl endblocked polydimethylsiloxane fluids. Some examples include silanols, hydroxyl functional polydimethylsiloxanes, and alkoxy functional polydimethylsiloxanes. The silanols can be silanols, silanediols, or silanetriols. Some examples include trimethylsilanol, triethylsilanol, tripropylsilanol, triisopropylsilanol, tributylsilanol, triisobutylsilanol, tri-(sec-butyl)silanol, tri-(tert-butyl)silanol, tripentylsilanol, triisopentylsilanol, tri-(sec-pentyl)silanol, tri-(tert-pentyl)silanol; dimethylsilanediol, diethylsilanediol, dipropylsilanediol, diisopropylsilanediol, dibutylsilanediol, diisobutylsilanediol, di-(sec-butyl)silanediol, di-(tert-butyl)silanediol, di-pentylsilanediol, diisopentylsilanediol, di-(sec-pentyl)silanediol, di-(tert-pentyl)silanediol, methylsilanetriol, ethylsilanetnol, propylsilanetnol, isopropylsilanetnol, butylsiianetrioL isobutylsilanetriol, sec-butyl-silanetriol, tert-butyl-silanetriol, pentylsilanetriol, isopentylsilanetriol, sec-pentyl-silanetriol, tert-pentyl-silanetriol, tnphenylsilanol, triphenylethylsilanol, triphenylpropylsiianol, diphenylsilanediol, diphenylethylsilanediol, diphenylpropylsilanediol, methylphenylsilanediol, phenylsilanetriol, and mixtures thereof. The hydroxyl functional polydimethylsiloxanes and the alkoxy functional polydimethylsiloxanes may contain terminal, pendant, or terminal and

pendant, functional groups. Suitable functional polydimethylsiloxanes will generally have from 2-300 repeating units in the chain. These organosilicon compounds are capable of functioning as crosslinking agents and/or chain extenders. If such another silicon compound is used, silanol- functional polydimethylsiloxanes having 4-100 repeating units in the chain are preferred. In general the hydrolysable organosilane is hydrolysed and then condensed to form a polysiloxane, although when a silanol-functional polysiloxane is present the hydrolysable groups of the silane can condense with the silanol groups to form an extended or crosslinked polysiloxane The weight ratio of hydrolysable organosilane to silanol-functional or alkoxy-functional polyorganosiloxane is preferably at least 1:10, more preferably at least 1:3, for example 1:1 to 10:1.
[0029] The concentration of silane hydrolysis product in water in the slurry of mineral or filler as the mineral or filler is being treated is generally about 0.1-50 percent by weight.. Preferably, the amount of water is chosen so that the solution contains 0.3-20 percent by weight, most preferably about 0.3-10 percent by weight, of the hydrolyzate. When the polysiloxane hydrolyzate contains sufficient water, the addition of more water in step (ii) of the process is not required in order to form the slurry. In that instance, water is an optional component in step (ii), although it can be included when additional amounts of water are needed to form a slurry.
OPTIONAL ADDITIVES
[0030] As noted above, other additives for making gypsum plasterboard are often used in commercial operations including starch; foaming agents; wetting agents; accelerators; retarders such as proteins and organic acids; paper or pulp; viscosity modifying agents; anti-burning agents; non-silicon atom containing water-resisting chemicals such as wax emulsions; glass fibres; fire-resistance enhancers such as vermiculite, clays, and fumed silica; and polymeric compounds such as polyvinyl alcohol. One or more additives such as these may be included in step (ii) of the present process.
EXAMPLES
[0031] The following examples are set forth in order to illustrate the invention in more detail.

EXAMPLE 1
[0032] To 795 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 5 gram of methytrimethoxysilane (MTM) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time.
EXAMPLE 2
[0033] To 790 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 10 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time.
EXAMPLE 3 '
[0034] To 75.0 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The.mixture was used fresh or maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time.
EXAMPLE 4
[0035] To 795 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 5 gram of methytriethoxysilane (MTE) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was maintained under stirring for 2 days before it was packaged and stored prior to testing on stucco over time.
EXAMPLE 5
[0036] To 790 milliliter of water was added undeV stirring, acetic acid to adjust the.pH to. 3.6. 10 gram of methytriethoxysilane was then added drop-wise under constant stirring.

The mixture was maintained under stirring ior 2 days before n was packaged and stored prior to testing on stucco over time.
EXAMPLE 6
[0037] To 750 milliliter of water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram ot methytriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for 2 days before it was packaged and stored prior io testing on stucco over time.
EXAMPLE 7: GENERAL PROCEDURE
[0038] Aqueous solutions containing the polysiloxane hydrolyzate composition were prepared so that the weight of the polysiloxane hydrolyzate based on the weight of stucco was from 0 5 to 5.0 percent To 80 gram of the aqueous solution containing the polysiloxane hydrolyzate composition was added 100 gram of stucco under vigorous stirring. No further catalyst was added, and the pH of the resulting slurry was measured to be about 6-7 The slurry was stirred for another 60 seconds and poured into disk shaped moulds. The samples were allowed to set at room temperature (20-25 qC) for 15-60 minutes. The disks separated from the moulds were gypsum disks of three centimetre in diameter and one centimetre in depth. The samples were further dried in an air circulating oven for 30 minutes at 110 'C, and then for 12-24 hours at 40 °C. The disks were cooled down and immersed in water for two hours. The weight of the disks before and after immersing the disks in water was measured. The water uptake expressed in percent, was used as the measure of the hydrophobing property of the polysiloxane hydrolyzate compositions. The water uptake of the disks treated with the polysiloxane hydrolyzate composition was compared to the water uptake of untreated gypsum stucco that has a value of about 40 percent. Table 1 shows results obtained by following the above procedure.

[0039] In Table 1, MTM designates methyltrimethoxysilane and MTE designates methyltriethoxysilane. Examples 1 -6 Table 1 show that a reduction in water-absorption, and the consequent improvement in water resistance, was obtained at various loadings of the polysiloxane hydrolyzate. Table 1 also shows that good stability, and an improvement in water-absorption over time, can be obtained with the polysiloxane hydrolyzates.
EXAMPLE 8
[0040] To 3,962.5 millilitre of tap water was added under stirring, acetic acidlo adjust fPff pH to 3.6. 37.5 gram of methytrimethoxysilane (MTM) was then added drop-wise under-constant stirring The aqueous mixture became clear within minutes. The mixture wars

maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 9
[0041] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of methytrimethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 10
[0042] To 3,962.5 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 37.5 gram of methytriethoxysilane (MTE) was then added drop-wise under constant stirring. The aqueous mixture became clear within minutes. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 11
[0043] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of methytriethoxysilane was.then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 12
[0044] To 3,962.5 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 37.5 gram of vinyltriethoxysilane (VTE) was then added drop-wise under constant
stirring The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
■

EXAMPLE 13
[0045] To 3,950 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 50 gram of vinyltriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 14
[0046] To 3,900 milliliter of tap water was added under stirring, acetic acid to adjust the pH to 3.6. 100 gram of vinyltriethoxysilane was then added drop-wise under constant stirring. The mixture was maintained under stirring for one day before it was packaged and stored prior to testing on stucco.
EXAMPLE 15: GENERAL PROCEDURE
[0047] Aqueous solutions containing the polysiloxane hydrolyzate composition were prepared. The weight of the polysiloxane hydrolyzate based on the weight of stucco was from 0.5 to 5.0 percent. To 80 gram of the aqueous solution containing the polysiloxane hydrolyzate composition was added 100 gram of stucco under vigorous stirring, and several drops of a 40 weight percent aqueous solution of NaOH to adjust the pH to 12. The slurry was stirred for another 60 seconds and poured into disk shaped moulds. The samples were allowed to set at room temperature (20-25 °C) for 15-60 minutes. The disks separated from the moulds were gypsum disks of three centimetre in diameter and one centimetre in depth. The samples were further dried in an air circulating oven for 30 minutes at 110 "C, and then for 12-24 hours at 400. The disks were cooled down and immersed in water for two hours. The weight of the disks before and after immersing the disks in water was measured. The water uptake expressed in percent was used as the measure of the hydrophobing property of the polysiloxane hydrolyzate composition. The water uptake of the disks treated with the polysiloxane hydrolyzate composition was compared to the water uptake of untreated gypsum stucco that has a value of about 37-40 percent. Table 2 below sets forth the results obtained according to the above procedure.

[0048] In Table 2, MTM designates methyltrimethoxysilane, MTE designates methyltriethoxysilane, and VTE designates vinyltriethoxysilane. Examples 1-6 and Examples 8-14 in Table 2 show that a dramatic reduction in water-absorption, and the consequent improvement in water resistance, can be obtained at various loadings of Jhe polysiloxane hydrolyzate under base catalysis in comparison to Table 1. Table 2 also shows

That good stability, and an improvement in water absorption overtime, can ho obtained with the polysiloxane hydrolyzates
EXAMPLE 15
[0049] To 85 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 15 gram of methytrimethoxysiiane (MTM) was then added drop-wise under constant stirring The mixture was packaged prior to testing on stucco.
EXAMPLE 16
[0050] To 70 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 30 gram of methytrimethoxysiiane (MTM) was then added drop wise under constant stirring. The mixture was packaged prior to testing on stucco.
EXAMPLE 17
[0051] To 50 milliliter of water was added under stirring, citric acid to adjust the pH to 3.6. 50 gram of methytrimethoxysiiane (MTM) was then added drop-wise under constant stirring The mixture was packaged prior to testing on stucco
[0052] Aqueous solutions were prepared from the hydrolysates of Examples 15 to 17 so that the weight of the polysiloxane hydroiyzate based on the weight of stucco was 1 to 2 percent. To 80 gram of the aqueous solution containing the polysiloxane hydroiyzate composition was added 100 gram of stucco under vigorous stirring. No further catalyst was added, and the pH of the resulting slurry was measured to be about 5-7. The slurry was stirred for another 60 seconds and poured into disk shaped molds, then tested as described in Example 7 Table 3 shows results obtained by following the above procedure

10053] Examples 15 -17 and Table 3-show that a reduction in water-absorption, and the consequent improvement in water resistance, was obtained at various loadings of the polysiloxane hydrolyzate starting from concentrated hydrolysed solutions.
[0054] Other variations may be made in compounds, compositions, and methods described herein without departing from the essential features of the invention. The embodiments of the invention specifically illustrated herein are exemplary only arid not intended as limitations on their scope except as defined in the appended claims.

We Claim:
1. A method of preparing a mineral and/or filler material comprising:
(i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture, such as herein described, in the presence of an acid hydrolysis catalyst, such as herein described; and
(ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler, such as herein described, and optionally water and/or a catalyst for condensation of the hydrolysate, such as herein described.
2. A method as claimed in Claim 1 in which the hydrolysable silane
comprises one or more silanes, each silane comprising one or more alkoxy groups and/or one or more acetoxy groups and/or one or more halide groups.
3. A method as claimed in Claim 2 wherein the hydrolysable silane is
selected from at least one alkylalkoxysilane, arylalkoxysilane, and/or alkenylalkoxysilane or a mixture thereof.
4. A method as claimed in claim 2 wherein the hydrolysable organosilane
comprises a mixture containing at least two of methyltripropoxysilane
and/or methyltrimethoxysilane and/or methyltriacetoxysilane and/or
alkenyltrialkoxysilane and/or alkenyltriacetoxysilane.
5. A method as claimed in any of Claims 2 to 4 in which any alcohol
generated during preparation of the polysiloxane hydrolyzate is removed

before the polysiloxane hydrolyzate is contacted with the mineral or filler material.
6. A method as claimed in Claim 2, in which the hydrolysable silane is an
acetoxysilane or a mixture of acetoxysilanes, which silane(s) may
additionally comprise one or more chloro groups per molecule.
7. A method as claimed in Claim 2, in which the hydrolysable silane is a chlorosilane or a mixture of chlorosilanes.
8. A method as claimed in Claim 6 or Claim 7 in which any excess acid generated during preparation of the polysiloxane hydrolyzate is partially neutralized or removed before the polysiloxane hydrolyzate is contacted with the mineral or filler material.
9. A method in accordance with any preceding claim wherein the pH during step (i) is 0.1-6.
10. A method as claimed in any of Claims 1 to 9 in which the hydrolysate is prepared at a concentration of silane in water greater than 5% by weight.
11. A method as claimed in any of Claims 1 to 9 in which the hydrolysate is prepared at a concentration of silane in water in the range 15 to 90% by weight.
12. A method as claimed in any of Claims 1 to 11 in which the minerals and fillers are selected from non-hydrated, partially hydrated, or hydrated, fluorides, chlorides, bromides, iodides, chromates, carbonate hydroxides, hydroxides, phosphates, hydrogen phosphates, nitrates, oxides, sulphates of sodium, potassium, magnesium, calcium, and barium, titanium

dioxide, zinc oxide, aluminium oxide, aluminium trihydroxide, vermiculite, silica, fumed silica, fused silica, precipitated silica, quartz, sand, silica gel, rice hull ash, ceramic and glass beads, zeolites, hydrous calcium silicate, silica-carbon black composite, functionalized carbon nanotubes, cement, fly ash, slate flour, bentonite, clay, mica, kaolin, talc, calcium carbonate, wollastonite, polymeric fillers, rubber particles, wood flour, wood fibres, cellulose and cellulose-containing products, aramid fibres, nylon fibres, cotton fibres or glass fibres.
13. A method as claimed in any of Claims 1 to 12 wherein the mineral and /or
filler is stucco and optionally gypsum.
14. A method as claimed in Claim 13 wherein the gypsum comprises one or more of calcium sulphate dehydrate, phospho-gypsum and/or desulphogypsum and/or titanogypsum and/or fluorogypsum and wherein the stucco is derived from natural gypsum and/or synthetic gypsum.
15. A method as claimed in any preceding claim wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is a base and the pH during step (ii) is from pH 8 to pH14
16 A method as claimed in Claim 13 or Claim 14 of preparing hydrophobic gypsum and gypsum products comprising:
(i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing under acidic conditions a hydrolyzable silane or hydrolyzable silane mixture; and
(ii) combining the polysiloxane hydrolyzate with stucco, a basic catalyst, and optionally water to form a slurry.

17. A method as claimed in any of Claims 1 to 14 wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is an alkoxide of titanium, zirconium, vanadium or aluminium.
18. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is an organic compound of tin.
19. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler is a fluoride salt.
20. A method as claimed in any of Claims 1 to 14, wherein the catalyst that is combined with the polysiloxane hydrolyzate and the mineral or filler comprises a base and an alkoxide of titanium, zirconium, vanadium or aluminium, an organic compound of tin or a fluoride salt.
21. A method as claimed in any of Claims 1 to 20 wherein the hydrolyzable silane mixture and/or the materials with which it is combined in step (ii) further comprises a silanol, a silanediol, a silanetriol, a hydroxyl functional polydimethylsiloxane, or an alkoxy functional polydimethylsiloxane.
22. A method as claimed in any preceding claim in which at least one additive comprising starch, a foaming agent, a wetting agent, an accelerator, a retarder, paper, pulp, a viscosity modifying agent, an anti-burning agent, a non-silicon atom containing water-resisting chemical,

glass fibres, a fire-resistance enhancer, a polymeric compound and/or uncalcined gypsum is additionally introduced during step (ii).
23. A method as claimed in Claim 13 or Claim 14 wherein the acid hydrolysis
catalyst is mixed with water and the hydrolysable organosilane immediately prior to the addition of stucco and a further catalyst for condensation of the hydrolysate, wherein the catalyst and stucco are mixed.
24. A method of preparing a hydrophobic gypsum product, for example
plasterboard, comprising preparing a hydrophobic gypsum material as
claimed in Claim 13 or Claim 14 and discharging the hydrophobic
gypsum material onto a support or mould, and drying.

ABSTRACT

METHOD OF PREPARING A MINERAL AND/OR FILLER MATERIAL, LIKE, GYPSUM MATERIAL
The invention discloses a method of preparing a mineral and/or filler material comprising: (i) preparing a hydrolyzate containing polysiloxanes by hydrolyzing a hydrolysable silane or hydrolysable silane mixture in the presence of an acid hydrolysis catalyst; and (ii) combining the polysiloxane hydrolyzate with at least one mineral and or filler and optionally water and/or a catalyst for condensation of the hydrolysate.
The invention is also for a making a gypsum product, e.g. plasterboard by using said mineral or filler material.

METHOD OF PREPARING A MINERAL AND/OR FILLER MATERIAL,LIKE,GYPSUM MATERIAL