Abstract A hybrid resin composition is described, with the composition comprising: A. an A part composition comprising an aliphatic polyfunctions! isocyanate compound and a free radical polymerization initiator; and B. a B part composition comprising an ethylenically unsaturated, substantially water-free polyester polyol and a polyurethane catalyst. The A part composition can contain a non-interfering solvent, e.g., styrene, and the B part composition typically has an acid value of 5 or less (based on solids). For outdoor use, the B part composition is preferably free of tertiary hydrogens, ether glycols and terephthalic acid residues.
Full Text 1
POLYESTER-POLYURETHANE HYBRID RESIN MOLDING COMPOSITIONS COMPRISING
POLYURETHANE WITH UMTS DERIVED FROM ALIPHATIC ISOCYANATES
This invention relates to hybrid resins. In one aspect, the invention relates to
hybrid resins comprising a polyester resin in combination with a polyurethane resin while
in another aspect, the invention relates to hybrid resins in which the polyurethane
comprises units derived from aliphatic isocyanates. In still another aspect, the invention
relates to coatings made from such hybrid resins.
Polyester-polyurethane hybrid resins are known in the art of thermoset molding
compositions (e.g., USP 5,153,261). These resins are normally tougher than polyesters
and stronger, suffer and less expensive than polyurethanes. Typical of such resins are
those comprising a hydros-terminated unsaturated polyester polyol, an ethylenically
unsaturated monomer (e.g., styrene) and a polyisocyanate. They are easily adapted to
many common thermoset molding techniques presently employed in the polyurethane
and unsaturated polyester industries. Xycon® hybrid resins available from Cook
Composites and Polymers are representative of these resins.
Hybrid resins are two component or part systems comprising an A part and a B
part. The A part contains the polyisocyanate and a polyester catalyst, while the B part
contains the hydroxy-terminated unsaturated polyester polyol/unsaturated monomer
solution, optionally with a polyurethane catalyst and/or filler. Upon mixing parts A and
B together under the appropriate conditions, an interpenetrating network of molecular
chains is formed. The polyester component of the mix provides the chain extension
function while the polyisocyanate component provides the crosslinking function. The
result is a molded part or coating that demonstrates improved toughness and thermal
properties over either component alone.
Gel coats are typically used as the outer or external surface layer of composite
molded article because they impart a smooth, durable appearance to the article.
Unsaturated polyesters resins are widely used for marine and cultured marble gel coats
because they are inexpensive, easy with which to work, and cure at room temperature.
Moreover, these resins provide a strong, flexible, abrasion and impact resistant surface.
However, these coating properties require improvement in certain stressful applications,
such as windmill blades. These applications require a coating with superior moisture-
resistance, toughness (e.g., resistance to cracking) and similar properties that will protect
the underlying laminate from deterioration by environmental forces.
In one embodiment, the invention is a hybrid resin composition comprising:

-2-
A. an A part composition comprising an aliphatic poryfunctional isocyanate
compound and a free radical polymerization initiator; and
B. a B part composition comprising an ethylenically unsaturated, substantially
water-free, polyester polyol and a polyurethane catalyst.
The hybrid resin compositions comprise about 10 to 50 weight percent A part, about 50
to 90 weight percent B part. The molar ratio of NCO groups to OH groups is between 0.3
to 2.0, preferably between 0.5 to 1.5. The aliphatic polyfunctional isocyanate in A part
has the NCO content of 5 to 50 percent, preferably 10 to 35 percent. The A part
composition can contain a non-interfering solvent, e.g., styrene, and the B part
composition typically has an acid value of 10 or less, preferably 5 or less (based on solids)
and a hydroxy] number on solids of about 120-170, preferably 130 to 160. For outdoor
use, the B part composition is preferably free of hydrogens on tertiary carbon, ether
glycols and terephthalic acid residues.
In another embodiment, the invention is a gel coat made from the hybrid resin and
in still another embodiment, the invention is an article comprising a gel coat made from
the hybrid resin.
The ethylenically unsaturated monomer used in the A part composition of the
hybrid resin can be any ethylenically unsaturated monomer capable of crosslinking the
unsaturated polyester polyol via vinyl addition polymerization. Examples of useful
ethylenically unsaturated monomers are styrene, o-, m-, p-methyl styrene, methyl
acrylate, methyl methacrylate, t-butylstyrene, divinyl benzene, diallyl phthalate, triallyl
cyanurate and mixtures of two or more unsaturated monomers. The preferred monomer
is styrene because it provides an economical monomer solution.
The unsaturated polyester polyol has at least one dicarboxylic alkene moiety and is
preferably an oligomer of an a.p-ethylenically unsaturated dicarboxylic acid compound
obtained by the condensation reaction of one or more of a saturated di- or polycarboxylic
acid or anhydride and an unsaturated di- or polycarboxylic acid or anhydride with a
glycol or a polyhydric alcohol. The unsaturated polyester polyol can also be prepared
from unsaturated di- or polycarboxylic acid(s) or anhydride(s) with glycols and/or
polyhydric alcohol(s). The polyols used in this invention have an acid number or value of
less than five, and preferably Jess than about two. Further, the polyols used in this
indention have equivalent weights of between about 250 and about 1000, and preferably
between about 250 and about 500. Examples of suitable saturated di- or polycarboxylic
acids include isophthalic, orthophthalic, terephthalic, adipic, succinic, sebacic acid and
mixtures of two or more of these compouhds with isophthalic acid being, preferred.

-3-
Typical unsaturated carboxylic acids or anhydrides include maleic acid, fumaric acid,
citraconic acid, chloromaleic acid, allyl succinic acid, itaconic acid, mesaconic acid, their
anhydrides and mixtures of two or more such compounds, with maleic anhydride being
the preferred choice. Examples of polyhydric alcohols which are useful in the invention
include neopentyl glycol, ethylene glycol, diethylene glycol, triethylene glycol, propylene
glycol, dipropylene glycol, 1,4-butanediol, polyethylene glycols, glycerol, mannitol, 1,2-
propanediol, pentaerythritol, 1,6-hexanediol, 1,3-butylene glycol and mixtures of two or
more of such compounds. For outdoor use, the B part composition is preferably free of
tertiary hydrogens, ether glycols and terephthalic acid residues.
The B part should be substantially water-free. "Substantially water-free" means
that the water content of the B part is sufficiently low to avoid unacceptable levels of
foaming. Preferably, the B part comprises no more than about 2000 ppm water,
preferably no more than 1000 ppm water, based on the total weight of the B part.
The aliphatic isocyanate compound, typically referred to as an aliphatic
pohyisocyanate, must have at least two functional groups and be capable of reacting with
the polyester polyol. Examples of suitable isocyanate compounds include 2,2,4-
trimethyl-hexamethylene diisocyanate, hexamethylene diisocyanate, isophorone
diisocyanate and their biuret and cyclic trimer forms. Preferably, the aliphatic isocyanate
compound is hexamethylene diisocyanate, more preferably the dimer or trimer form of
hexamethylene diisocyanate.
In one embodiment, the aliphatic isocyanate compound may be modified with a
polyol, such as a glycol, to provide a polymeric form for ease of handling. Typically, the
isocyanate content ranges from about 5% to about 50%, more preferably from about 10%
to about 35% based on the combined atomic weight of the isocyanate functional groups
and the total molecular weight of the aliphatic isocyanate compound.
The free radical polymerization catalysts useful in producing the hybrid resin
compositions of this invention are vinyl polymerization catalysts such as peroxides,
persulfides, perborates, percarbonates, and azo compounds or any other suitable catalyst
capable of catalyzing the vinyl polymerization of the polyester polyol and/or the
ethylenically unsaturated monomer. Illustrative of a few such catalysts are benzoyl
peroxide (BPO), tertiarybutyl peroxybenzoate (TBPB), 2,2'-azo-bis-isobutyronitrile,
dibenzoyl peroxide, lauryl peroxide, di-t-butyl peroxide, diisopropyl peroxide carbonate
and t-butyl peroxy-2-ethylhexanoate. Promoters can also be used in combination with
vinyl polymerization peroxide catalysts to control the rate of free radical initiation. A
common benzoyl peroxide promoter is N,N-diethylaniline.

-4-
Catalysts that are useful in catalyzing the polyurethane formation in producing the
hybrid resin in accordance with this invention include: (a) tertiary amines such as
N,N-dimethylcyclohexylamine; (b) tertiary phosphines such as trialkylphosphines; (c)
strong bases such as alkali and alkaline earth metal hydroxides, alkoxides, and
phenoxides; (d) acidic metal salts of strong acids such as ferric chloride; and (e)
organometallic compounds such as dibutyltin dilaurate, bismuth carboxylate, and
zirconium chelate 2,4-pentanedione. Other commonly used catalysts for making
polyurethanes can be found in USP 4,280,979.
The hybrid resins of the invention can be prepared by a process based on liquid
reactive molding or compression molding techniques commonly employed in the
unsaturated polyester and polyurethane industries. Liquid molding is the direct injecting
or pouring of a hybrid resin into a mold (closed molding) or onto a mold (open molding).
In liquid injection closed molding, the polyisocyanate and hydroxy-terminated polyester
in the monomer solution (polyol) are fed separately into the chamber of a mixing head
where the two components are mixed. Upon mixing, the hybrid reaction begins
instantaneously whereby the rate of reactivity is dependent on the catalyst used. The
hybrid liquid stream is injected between mold halves wherein the reactions between the
various components of the hybrid resin system continue. After sufficient time for cure,
typical 1 to 120 minutes, preferably 2 to 60 minutes, the part is removed from the mold.
The part can be used as molded or be further post-annealed in an oven. Common liquid
closed molding techniques include resin transfer molding (RTM), reaction injection
molding (RIM) and structural reaction injection molding (S-RIM).
It is also an object of the present invention to obtain a curable resin composition,
comprising at least one hybrid resin as defined according to the invention, which can be
used for preparing, by curing, coatings like gels coats (or barrier coats) or composite
molded articles. So, the resins of the invention can be used for either composite molded
articles, based on SMC, BMC, DMC or for coatings like gel coats (or barrier coats).
The said coatings may be applied to a composite molded substrate made from
either a resin according to the invention or from other resins, including UPR or vinyl ester
or any other thermosetting resin.
Liquid injection open molding follows the same procedure except the hybrid resin
is sprayed onto a mold where one side of the molded part is exposed to the atmosphere.
This molding process is commonly termed "spray-up molding." Direct pour liquid
molding comprises hand-mixing the polyol and polyisocyanate and then pouring the
hybrid liquid into or onto a mold wherein curing occurs. The main differences between

-5-
injection and pouring are the mix time, mix intensity and injection pressure. In both
liquid molding techniques, the polyol and/or polyisocyanate can contain fibrous
materials, fillers and/or other additives but in gel coat applications, the resin is typically
free of any fibrous materials and fillers.
Hybrid resins are also amendable to compression molding. Common compression
molding techniques include sheet, bulk or dough molding compounds, identified as SMC,
BMC and DMC, respectively. Regardless of the molding technique employed, the hybrid
resins of the invention have the advantages of improved shrinkage control, surface
appearance and impact strength without significantly sacrificing thermal properties.
The gel coats of this invention are thick relative to a coat of paint but typically still
less than half of a millimeter in thickness. For a liquid layer of this thickness to stay in
place on a mold surface that is not in a horizontal orientation, the resin should be
thixotropic. In other words, the viscosity is relatively low during applications by such
means as spraying, brushing or rolling, but viscous enough to resist gravity as soon as
the application procedure stops. Convenient thixotropic agents may be selected from:
{fumed) silica, fatty acid amides, clays at a weight content from 0.2 to 5% with respect to
the weight of B part.
In the molding process in which the hybrid resins are typically used, generally two
or more shaped elements cooperate with one another to define a mold cavity. Otherwise
a single cavity of complex shape can be provided. The hybrid resin of the present
invention is applied to at least a portion of the overall mold surface. The mold contact
surfaces may be formed from any conventional materials such as glass, reinforced
polyesters, epoxies, steel, aluminum or other metals.
In one illustrative example, the A part or component of the hybrid resin comprises
an isocyanate or an isocyanate solution in a non-interfering solvent such as styrene.
Aliphatic isocyanates, such as 2,2,4-trimethyl-hexamethylene diisocyanate, are
particularly well adapted for outdoor applications because of their resistance to yellowing
or other discoloration relative to aromatic diisocyanates.
The part B side or component comprises unsaturated polyester resin, wetting
agents, leveling aids, a promotion package, fillers, polyurethane catalyst, viscosity
modifiers and pigments. One typical formula, in parts by weight, comprises the following:

-6-

Component Description Weight parts
unsaturated polyester polyol 873.43
black pigment dispersion 1.12
yellow iron oxide pigment dispersion 1.80
white pigment dispersion 92.83
air release agent 2.5
clay (quaternary ammonium treated) 12.48
talc 12.48
cobalt octoate solution 0.87
dibutyltin dilaurate 1.25
silicon fluid 200cSt-fisheye eliminator 1.25
As is evident from the above formulations, the hybrid resins of this invention can
contain one or more additives such as fillers, pigments, processing aids, curing aids, anti-
oxidants, UV-inhibitors, catalyst promoters and the like. These additives can be included
in either or both of the A and B parts although inclusion in the B part composition is
more typical.
The following examples further illustrate the invention. In these examples, all
viscosity measurements were taken after the viscometer was running at the set speed for
about 2 minutes.
Example 1 Preparation of Unsaturated Polyester Resin (Comparative)
Into a 4-liter flask equipped with agitator, condenser, thermometer, and pipe for
introducing nitrogen gas were charged 740 grams of diethylene glycol, 456 grams of
propylene glycol, 1060 grams of isophthalic acid. The mixture was heated at 210°C for
about 10 hours until the acid number drops to 10 mg KOH/g. After the temperature was
reduced to 150°C, 624 grams of maleic anhydride was added into the mixture. The
reaction was continued at 210°C for another 6 hours to an acid number of 30 to 50 mg
KOH/g. The product was blended with 1460 grams inhibited styrene to form 4000 grams
clear resin solution (Resin A). The viscosity of resin solution is around 1000 mPa.s (cP) at
63% solids content. The resin viscosity is measured by Brookfield viscometer with RVT
#2 spindle at 20 rpm at 25°C.
Example 2 Preparation of Conventional Gel Coat (Comparative)
A gel coat composition is then prepared by blending the following ingredients:

-7-

Component Weight Percent
Resin A 53.2
Titanium Dioxide 15.0
Fumed Silica 1.5
Monomer 19.4
Talc 10.5
12% Cobalt 0.2
Ethylene Glycol 0.2
The resulting gel coat has a Brookfield viscosity of 19000 mPa.s (cP) at 4 rpm at
77°C and a thixotropic index of 6.0-7.0 (RVF #4 spindle, 2/20 rpm). 1.8% methyl ethyl
ketone peroxide (MEKP) is used to cure gel coat. The gel time is around 15 minutes and
cure time is around 60 minutes. The weathering characteristics of the cured gel coat as
measured by QUV-A, ASTM G154 using the standard 8 hours UV exposure at 60°C
followed by 4 hours condensation at 50°C, are listed below.

Hours Total Color change, AE % Gloss Retention
0 0.00 100
500 1.52 99
1000 5.82 86
1500 5.73 12
Example 3 Preparation of OH-terminated Unsaturated Polyester Resin
Into a 4-liter flask equipped with agitator, condenser, thermometer, and pipe for
introducing nitrogen gas were charged 1380 grams of neopentyl glycol, 202 grams of
propylene glycol, 994 grams of isophthalic acid. The mixture was heated at 210°C for
about 10 hours until the acid number drops to 10 mg KOH/g. After the temperature was
reduced to 150°C, 587 grains of maleic anhydride was added into the mixture. The
reaction was continued at 210°C until an acid number of less than 5 mg KOH/g and an
OH number of 130 to 150 mg KOH/g. The product was blended with 1160 grams
inhibited styrene to form 4000 grams clear resin solution (Resin Bj. The viscosity of resin
solution is 700 mPa.s (cP) at 71% solids content.
Example 4 Preparation of Polyester-Polyurethane Hybrid Gel Coat
A two-component gel coat composition is then prepared by blending the following
ingredients to form the B-side component:

-8-

Component Weight Percent
Resin B 42.6
Titanium Dioxide 24.5
Fumed Silica 2.0
Monomer 19.9
Talc 10.1
12% Cobalt 0.2
Dibutyltin dilaurate 0.3
Ethylene Glycol 0.3
Promoter 0.1
The resulting gel coat has a Brookfield viscosity of 15000 mPa.s (cP) at 4 rpm at
77°C and a thixotropic index of 5.0-6.0. The A-side component contains aliphatic
diisocyanate and methyl ethyl ketone peroxide (MEKP). The A-side and B-side was mixed
at the 20/80 ratio to cure the polyester-polyurethane hybrid gel coat. The gel time is
around 15 minutes and cure time is around 60 minutes. The weathering characteristics
of the gel coat as measured by QUV-A are listed below.

Hours Total Color change,
AE % Gloss Retention
0 0.00 100
500 0.60 100
1000 0.65 100
1500 0.78 100
Example 5 Comparison of 100 Hours Water Boil of Laminates
The gel-coated laminates were prepared with the gel coat samples from example 2
and 4. The laminate had two different thicknesses of gel coat. The thick section (TK) of
gel coat had the cured gel coat thickness around 0.762 mm (30 mils) and the thin section
(TN) of gel coat had the cured gel coat thickness around 0.381 mm (15 mils). The panels
were immersed in boiling de-ionized water for 100 hours and the performance was rated
in a scale of 0-5 at 5 different categories. The 0 rating was indication of no change and
the 5 rating was indication of extreme change. The results indicated the Polyester-
Polyurethane Hybrid gel coat has much better water resistance compared to the
conventional gel coat.

100 Hours Boil Example 2 Example 4
Blister (TK/TN) 2.7/2.7 0/0
Color Change (TK/TN) 1.4/1.4 0.64/0.64
Fiber Prom. Change (TK/TN) 0.8/1.8 0.66/0.66
Cracks (TK/TN) 0.8/1.0 0/0
Loss of gloss (TK/TN) 0.3/0.3 0/0
Total Rating (TK/TN) 6.0/7.2 1.30/1.30

-9-
Example 6 Comparison of the Casting Mechanical Properties at Various
Temperatures.
The gel coat samples were made into castings and the tensile properties of the
castings were measured following the ASTM Standard D-638. The tensile properties were
measured at the ambient temperature, -10°C, and -30°C. The results indicated the
Polyester-Polyurethane Hybrid gel coat has much better retention of tensile elongation at
the lower temperature compared to conventional gel coat.

Example 2 -
23°C Example 2 -
10°C Example 2 -
30°C
Tensile Strength (MPa) 49 + 3 50 + 4 41+7
Tensile Modulus (MPa) 2299 ±134 3013 + 134 3107 ±180
Elongation (%) 2.6 + 0.2 2.2 ±0.2 1.5 + 0.3

Example 4
23°C Example 4 -
10°C Example 4 -
30°C
Tensile Strength (MPa) 44 + 4 49 ±3 50 ±6
Tensile Modulus (MPa) 2038 ±85 2441 + 113 2713 ±149
Elongation (%) 2.9 + 0.4 2.4 ± 0.2 2.2 ±0.3
Example 7 Comparison of the Reverse Impact Strength
The reverse impact strength of gel-coated laminate was measured by following the
a ASTM Standard D-3029. A total of 9 tests were conducted for each sample, and the
average was reported. The results showed that the Polyester-Polyurethane Hybrid gel
coat has much better reverse impact strength compared to conventional gel coat.

Reverse Impact Test Example 2 Example 4
Ave. Number of Cracks
Std Dev. 14.8
1.169 5.7
0.951
Ave. Length of Crack in cm
(inch)
Std Dev. in cm
(inch) 3.18
(1.25)
0.00 2.24
(0.88)
0.086
(0.034)
Ave. Gel Coat Thickness in mm
(mil)
Std Dev. in mm
(mil) 0.58
(23.0)
0.008
(0.3) 0.51
(20.0)
0.0
Ave. Overall Thickness in cm
(inch)
Std Dev. in cm
(inch) 1.04
(0.41)
0.030
(0.012) 0.79
(0.31)
0.23
(0.09)
While the invention has been described above in considerable detail, this detail is
for the purpose of illustration and is not to be construed as a limitation on the spirit and

-10-
scope of the invention as it is described in the following claims. All U.S. patents and
allowed patent applications cited above are incorporated herein by reference.

-11-
CLAIMS
1. A gel-coat, wherein it is made by curing a curable hybrid resin
comprising :
A. an A part composition comprising an aliphatic poryfunctional
isocyanate compound and a free radical polymerization initiator ;
and optionally a non interfering solvent
B. a B part composition comprising an ethylenically unsaturated,
substantially water-free, polyester polyol and a polyurethane
catalyst.
2. The gel-coat according to claim 1, wherein the said isocyanate
compound is at least one of 2,2,4-trimethyl-hexamethylene
diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate
and their biuret and cyclic trimer derivatives.
3. The gel-coat according to claims 1 or 2, wherein the said isocyanate
compound is hexamethylene diisocyanate or/and derivatives
4. The gel-coat according to claim 3, wherein the said isocyanate is a
hexamethylene diisocyanate cyclic trimer derivative.
5. The gel-coat according to any one of claims 1 to 4, wherein the said
polyester polyol comprises at least one dicarboxylic alkene moiety.
6. The gel-coat according to any one of claims 1 to 5, wherein the said
polyester polyol comprises an oligomer of an a,f}-ethylenicaUy
unsaturated dicarboxylic acid compound obtained by the
condensation reaction of one or more saturated di- or polycarboxylic
acid or anhydride and an unsaturated di- or polycarboxylic acid or
anhydride with a glycol or a polyhydric alcohol.
7. The gel-coat according to any one of claims 1 to 6, wherein the said
free radical polymerization initiator is at least one of a peroxide,
persulfide, perborate, percarbonate, and azo compound.
8. The gel-coat according to any one of claims 1 to 7, wherein the said
polyurethane catalyst is at least one of a tertiary amine, tertiary
phosphine, strong base, acidic metal salt, and an organometallic
compound.
9. The gel-coat according to any one of claims 1 to 8, wherein the said B
part composition comprises less than about 2000 ppm of water, based
on the total weight of the B part composition.

- 12-
10. The gel-coat according to claim 9, wherein the said B part composition
comprises less than about 1000 ppm of water, based on the total
weight of the B part composition.
11. The gel-coat according to any one of claims 1 to 10, wherein the said
B part composition is preferably free of tertiary hydrogens, ether
glycols and terephthalic acid residues.
12. A gel-coat wherein it is made by curing a curable hybrid resin
composition comprising :
10 to 50% by weight of part A, as defined in any one of claims 1
to 11,
50 to 90% by weight of part B, as defined in any one of claims 1
to 11.
13. A gel-coat according to any one of claims 1 to 12, wherein the said
part B has an acid value of 10 or less and a hydroxyl number on
solids of 120-170.
14. A gel-coat according to claim 13, wherein the said hydroxyl number is
from 130 to 160.
15. A gel-coat according to any one of claims 1 to 14, wherein the said
aliphatic polyfunctional isocyanate in part A has an NCO content of 5
to 50%, preferably 10 to 35%.
16. A gel-coat according to any one of claims 1 to 15, wherein the said
aliphatic polyisocyanate has at least two functional groups and is
capable of reacting with the said polyester polyol of part B.
17. A gel-coat according to any one of claims 1 to 16, wherein the said
polyester polyol of part B is a thixotropic resin.
18. A gel-coat according to claim 17, wherein the said hybrid resin is
rendered thixotropic by addition of thixotropic agents selected from
silica, fatty amides, clays at a weight content of 0.2 to 5% by weight of
part B.
19. A gel-coat according to any one of claims 1 to 18, wherein it is coated
on a composite molded substrate, made from either a hybrid resin of
the gel-coat as defined according to any one of claims 1 to 18, or from
(UPR) unsaturated polyester resin or from vinyl ester or from any
other thermosetting resin.
20. An article comprising the gel-coat of any one of claims 1 to 19.

A hybrid resin composition is described, with the composition comprising: A. an A part composition comprising an
aliphatic polyfunctions! isocyanate compound and a free radical polymerization initiator; and B. a B part composition comprising an
ethylenically unsaturated, substantially water-free polyester polyol and a polyurethane catalyst. The A part composition can contain
a non-interfering solvent, e.g., styrene, and the B part composition typically has an acid value of 5 or less (based on solids). For
outdoor use, the B part composition is preferably free of tertiary hydrogens, ether glycols and terephthalic acid residues.

Documents:

00403-kolnp-2008-abstract.pdf

00403-kolnp-2008-claims 1.0.pdf

00403-kolnp-2008-claims 1.1.pdf

00403-kolnp-2008-correspondence others.pdf

00403-kolnp-2008-description complete.pdf

00403-kolnp-2008-form 1.pdf

00403-kolnp-2008-form 3.pdf

00403-kolnp-2008-form 5.pdf

00403-kolnp-2008-international exm report.pdf

00403-kolnp-2008-international publication.pdf

00403-kolnp-2008-international search report.pdf

403-KOLNP-2008-(01-04-2014)-CORRESPONDENCE.pdf

403-KOLNP-2008-(12-08-2013)-AMANDED PAGES OF SPECIFICATION.pdf

403-KOLNP-2008-(12-08-2013)-CORRESPONDENCE.pdf

403-KOLNP-2008-(12-08-2013)-OTHERS.pdf

403-KOLNP-2008-(17-12-2013)-CORRESPONDENCE.pdf

403-KOLNP-2008-(17-12-2013)-OTHERS.pdf

403-KOLNP-2008-(23-12-2013)-ANNEXURE TO FORM 3.pdf

403-KOLNP-2008-(23-12-2013)-CORRESPONDENCE.pdf

403-KOLNP-2008-(25-03-2013)-CLAIMS.pdf

403-KOLNP-2008-(25-03-2013)-CORRESPONDENCE.pdf

403-KOLNP-2008-(25-03-2013)-FORM 1.pdf

403-KOLNP-2008-(25-03-2013)-FORM 2.pdf

403-KOLNP-2008-(25-03-2013)-FORM 3.pdf

403-KOLNP-2008-(25-03-2013)-FORM 5.pdf

403-KOLNP-2008-(25-03-2013)-OTHERS.pdf

403-KOLNP-2008-(25-03-2013)-PETITION UNDER RULE-137.pdf

403-KOLNP-2008-(28-04-2014)-CLAIMS.pdf

403-KOLNP-2008-(28-04-2014)-CORRESPONDENCE.pdf

403-KOLNP-2008-(28-04-2014)-PA.pdf

403-kolnp-2008-ASSIGNMENT-1.1.pdf

403-KOLNP-2008-ASSIGNMENT.pdf

403-kolnp-2008-CANCELLED PAGES.pdf

403-KOLNP-2008-CORRESPONDENCE OTHERS 1.1.pdf

403-KOLNP-2008-CORRESPONDENCE OTHERS 1.2.pdf

403-kolnp-2008-CORRESPONDENCE.pdf

403-kolnp-2008-EXAMINATION REPORT.pdf

403-kolnp-2008-FORM 18-1.1.pdf

403-KOLNP-2008-FORM 18.pdf

403-KOLNP-2008-FORM 3-1.1.pdf

403-kolnp-2008-GPA.pdf

403-kolnp-2008-GRANTED-ABSTRACT.pdf

403-kolnp-2008-GRANTED-CLAIMS.pdf

403-kolnp-2008-GRANTED-DESCRIPTION (COMPLETE).pdf

403-kolnp-2008-GRANTED-FORM 1.pdf

403-kolnp-2008-GRANTED-FORM 2.pdf

403-kolnp-2008-GRANTED-FORM 3.pdf

403-kolnp-2008-GRANTED-FORM 5.pdf

403-kolnp-2008-GRANTED-LETTER PATENT.pdf

403-kolnp-2008-GRANTED-SPECIFICATION-COMPLETE.pdf

403-kolnp-2008-INTERNATIONAL PUBLICATION.pdf

403-kolnp-2008-INTERNATIONAL SEARCH REPORT & OTHERS.pdf

403-kolnp-2008-OTHERS.pdf

403-KOLNP-2008-PCT PRIORITY DOCUMENT NOTIFICATION.pdf

403-kolnp-2008-PETITION UNDER RULE 137.pdf

403-kolnp-2008-REPLY TO EXAMINATION REPORT.pdf

403-kolnp-2008-TRANSLATED COPY OF PRIORITY DOCUMENT.pdf


Patent Number 262584
Indian Patent Application Number 403/KOLNP/2008
PG Journal Number 36/2014
Publication Date 05-Sep-2014
Grant Date 28-Aug-2014
Date of Filing 29-Jan-2008
Name of Patentee COOK COMPOSITES AND POLYMERS COMPANY
Applicant Address 820 EAST 14TH AVENUE NORTH KANSAS CITY, MO
Inventors:
# Inventor's Name Inventor's Address
1 BAUCHET FREDERIC 10205 NORTH CHERRY, APT. 2 C, KANSAS CITY, MO 64155
2 MORRIS LARRY 14614 KILLARNEY LANE, SMITHVILLE, MO 64089
3 SEROOGY KEN 1531 MAPLE WOODS DRIVE, LIBERTY, MO 64068
4 HOLLEY WOODY 4001 NE 77TH STREET, GLADSTONE, MO 64119
PCT International Classification Number C08G 18/28
PCT International Application Number PCT/EP2006/008199
PCT International Filing date 2006-08-21
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 60/710641 2005-08-23 U.S.A.