Indian Patents. 264329:COMPOSITE ARTICLE WITH MAGNETOCALORICALLY ACTIVE MATERIAL AND METHOD FOR ITS PRODUCTION

Title of Invention	COMPOSITE ARTICLE WITH MAGNETOCALORICALLY ACTIVE MATERIAL AND METHOD FOR ITS PRODUCTION
Abstract	Composite article with magnetocalorically active material and method for its production A composite article (1; 10; 40) comprises a plurality of inclusions (5) of a magnetocalorically active material embedded in a matrix (4) of a magnetocalorically passive material. The inclusions (5) and the matrix (4) have a microstructure characteristic of a compacted powder.

Full Text	Description Composite article with magnetocalorically active material and method for its production The invention relates to a composite article with magnetocalorically active material and to methods for producing a composite article with magnetocalorically active material. The magnetocaloric effect describes the adiabatic conversion of a magnetically induced entropy change to the evolution or absorption of heat. Therefore, by applying a magnetic field to a magnetocaloric material, an entropy change can be induced which results in the evolution or absorption of heat. This effect can be harnessed to provide refrigeration and/or heating. In recent years, materials such as La(Fe1-aSia)13, Gd5(Si,Ge)4, Mn (As,Sb) and MnFe(P,As) have been developed which have a Curie Temperature, Tc, at or near room temperature. The Curie Temperature translates to the operating temperature of the material in a magnetic heat exchange system. Consequently, these materials are suitable for use in applications such as building climate control, domestic and in-dustrial refrigerators and freezers as well as automotive climate control. Magnetic heat exchange technology has the advantage that magnetic heat exchangers are, in principle, more energy efficient than gas compression/expansion cycle systems. Furthermore, magnetic heat exchangers are environmentally friendly as ozone depleting chemicals such as CFC's are not used. Consequently, magnetic heat exchanger systems are being developed in order to practically realise the advantages provided by the newly developed magnetocaloric materials. Magnetic heat exchangers, such as that disclosed in US 6,676,772, typically include a pumped recirculation system, a heat exchange medium such as a fluid coolant, a chamber packed with particles of a magnetic refrigerant working material which displays the magnetocaloric effect and a means for applying a magnetic field to the chamber. Further developments of these systems have been directed towards optimizing the composition of the magnetocaloric material so as to increase the entropy change and to increase the temperature range over which the entropy change occurs. This enables smaller applied magnetic fields to be used to achieve sufficient cooling and a stable reT frigeration cycle to be achieved over a larger temperature range. These measures aim to simplify the design of the heat exchange system since smaller magnetic fields can be produced by a permanent magnet rather than an electromagnet or even a superconducting magnet. The magnetic refrigerant working material may also be provided in the form of a composite. For example, US 6,826,915 discloses a regenerative bed comprising a magnetic refrigeration material including a binder comprising a metal or alloy of high ductility and a magnetocaloric material of the NiAs-type. However, further improvements are desirable to enable a more extensive application of magnetic heat exchange technology. It is an object of the invention to provide a composite article comprising magnetocal-orically active material which can be reliably and cost effectively manufactured. It is a further object to provide methods by which the composite article may be produced. This object is solved by the subject matter of the independent claims. Further advantageous improvements are the subject matter of the dependent claims. The invention provides a composite article comprising a plurality of inclusions of a magnetocalorically active material embedded in a matrix of a magnetocalorically passive material. The inclusions and the matrix have a microstructure characteristic of a compacted powder. Herein, the term matrix is defined as the magnetocalorically passive material, irrespective of its volume fraction and distribution. A magnetocalorically active material is defined herein as a material which undergoes a change in entropy when it is subjected to a magnetic field. The entropy change may be the result of a change from ferromagnetic to paramagnetic behaviour, for example. The magnetocalorically active material may exhibit in only a part of a temperature region an inflection point at which the sign of the second derivative of magnetization with respect to an applied magnetic field changes from positive to negative. A magnetocalorically passive material is defined herein as a material which exhibits no significant change in entropy when it is subjected to a magnetic field. Inclusion is defined herein as a particle or grain having a first composition which is at least partially embedded in the matrix comprising a different second composition. Inclusion also includes an agglomerate of particles or grains of a first composition which is at least partially embedded in the matrix comprising a second different composition material. A particle or agglomerate which has a portion exposed from the matrix, for example this exposed portion may provide an outer surface of the composite article, is included in this definition of inclusion. A microstructure characteristic of a compacted powder can be identified by examining a polished cross-section of the composite article using light microscopy or Scanning Electron Microscopy. A compacted powder has a microstructure which comprises a plurality of particles which at least in part touch their immediate neighbours, i.e. the contiguous particles, without interdiffusion of atoms between the contiguous particles. The particles of a compacted powder also have lattice structure which exhibits strain and/or fractures which have occurred as a result of the pressure applied during compaction. These structural defects can be observed using Transmission Electron Microscopy. The composite article according to the invention has the advantage that it can be simply produced by mixing together a first powder of a magnetocalorically active material and a second powder of a magnetocalorically passive material and then compacting the powder mixture to form a composite article. The composite article may be used in a magnetic heat exchange system as the magnetic working material without going a subsequent heat treatment. Therefore, the inclusions and the matrix of the composite article have a microstructure characteristic of a compacted powder. The matrix of the composite article may be thought of as a binder which holds the inclusions of magnetically active material together to form a composite article. Thus magnetocalorically active material, which, particularly in the case of materials such as Gd, La(Fe1-bSib)13-based phases, Gd5(Si,Ge)4-based phases, Mn(As,Sb)-based phases, MnFe(P,As)-based phases, Tb-Gd-based phases, (La, Ca, Pr,Nd,Sr)MnO3-based phases, Co-Mn-(Si, Ge)- based phases and Pr2(Fe,Co)17-based phases is brittle, can be formed into a composite article having sufficient mechanical stability to be used in a heat exchanger system due to the matrix of magnetocalorically passive material. The composite article has the advantage that the magnetocalorically active material and magnetocalorically passive material may be fabricated using known techniques and be fabricated separately from one another before being mixed together to form the starting mixture for the composite article. Consequently, the fabrication of the two powders can be optimised separately from the optimisation of the composite article. By controlling the compaction process appropriately, the composite article can be produced having the dimensions desired for a particular magnetic heat exchange system. The composite article may be produced having a near-net shape simply by compacting the powder mixture. The composite article is, therefore, easily produced using a simple, cost-effective manufacturing process. The magnetocalorically active material may be used as supplied or as fabricated or may be given an additional heat treatment in order to improve the magnetocaloric properties of the powder before it is mixed with the magnetocalorically passive powder which later forms the matrix. The first embodiment, the matrix has an average particle size of less than 1000 μm (micrometer). In a further embodiment, the inclusions have an average diameter of less than 1000 μm (micrometer). The average particle size of the matrix is defined herein as the mean of the longest dimension of each of 20 randomly selected particles in a polished cross-section of the composite article. The average diameter of the inclusions is defined herein as the mean of the longest dimension of each of 20 randomly selected inclusions in a polished cross-section of the composite article. In a further embodiment of the invention, a composite article is provided which comprises a plurality of inclusions of a magnetocaloricalry active material embedded in a matrix of a magnetocalorically passive material. In this embodiment, the matrix has a microstructure characteristic of a sintered powder. A microstructure characteristic of a sintered powder can be identified by examining a polished cross-section of the composite article using light microscopy or Scanning Electron Microscopy. A sintered powder has a microstructure which comprises a plurality of particles which at least in part touch their immediate neighbours, i.e. the contiguous particles, wherein the interface between contiguous particles comprises in-terdiffusion of atoms of the contiguous particles. Furthermore, as a result of the sintering process, the particles have undergone strain relief. This strain relief can be observed using Transmission Electron Microscopy techniques since the dislocation density and lattice strain within the grains is lower than that of compacted unsintered powder. The composite article comprising a matrix having a microstructure characteristic of a sintered powder has the advantage that the mechanical strength of the composite article is increased due to the sintering process. This simplifies the handling of the composite article during any later production steps, for example surface finishing of the composite article, during storage and delivery of the composite article as well as during the assembly of the composite article into a magnetic heat exchange system. Furthermore, in the case that the magnetic heat exchange system is of the type in which the magnets remain stationary and the magnetic working material is physically moved relative to the magnets, the likelihood of cracking and damage to the magnetic working material as a result of this movement is reduced. The composite article comprising a matrix having a microstructure characteristic of a sintered powder is also easily produced using known powder processing techniques. For example, a powder of a magnetocalorically passive material may be mixed with magnetocalorically active material, the powder mixture is compacted and then sintered by applying heat. This embodiment has the advantage that the composite article may be manufactured by embedding magnetocalorically active material in powder of a magnetocalorically passive material. This intermediate may then be sintered to produce the composite article. In an embodiment, the inclusions comprising a magnetocalorically active material are provided in the form of a powder. In this embodiment, the inclusions as well as the matrix have a microstructure characteristic of a sintered powder. Alternatively, the inclusions may be provided in forms other than that of powder. For example, the inclusions may be provided in the form of a skeleton structure which is embedded in powder of a magnetocalorically passive material or in the form of a series of foils, flakes, filaments or tapes which are embedded in powder of a magnetocalorically passive material which forms the matrix of the composite article. The matrix and possibly the inclusions may have a grain structure characteristic of a sintered powder. This characteristic grain structure can be identified using light microscopy and or Scanning Electron Microscopy techniques. The most appropriate technique may depend on the average grain size. The grain structure of a sintered powder is characterised by the grain boundaries between adjacent grains, in particular between contiguous grains comprising the same material. These grains are atomically joined to one another due to interdiffusion between the contiguous grains at the interface and have a misorientation with respect to one another. The microstructure of the grains and of the grain boundaries can be observed using Transmission Electron Microscopy techniques. The average grain size of the sintered composite article, in particular of the matrix, is also typically greater than the average particle size from which the article was produced. For example, the average grain size of the matrix is greater than the average particle size of the magnetocalorically passive powder. In an embodiment, the magnetocalorically active material has a Curie temperature Tc in the range 220K to 345K. The operating temperature of the magnetocalorically active material, when used in a magnetic heat exchange system, is approximately that of its Curie temperature. A magnetocalorically active material with a Curie temperature in the range 220K to 345K is suitable for applications such as domestic and commercial freezer systems, refrigeration, air conditioning or climate control systems depending on the desired operating temperature and operating temperature range. The magnetocalorically active material is one of Gd, a La(Fe1-bSib)13-based phase, a Gd5(Si,Ge)4-based phase, a Mn(As,Sb)-based phase, a MnFe(P,As)-based phase, a Tb-Gd-based phase, a (La, Ca, Pr,Nd,Sr)MnCybased phase, a Co-Mn-(Si,Ge)-based phase and a Pr2(Fe,Co)17-based phase. These basic compositions may further comprise further chemical elements which may substitute partially or in full for the listed elements. These phases may also comprise elements which are accommodated at least in part in-terstitially within the crystal structure, for example, hydrogen. These phases may also include impurity elements and small amounts of elements such as oxygen. The matrix may comprise a variety of materials. In an embodiment, the matrix comprises a material which has a higher thermal conductivity than the thermal con- ductivity of the inclusions of the magnetocalorically active material. This has the advantage that the efficiency of the heat exchange between the magnetocalorically active material and the heat exchange medium is increased. In an embodiment, the matrix comprises a metal or an alloy which may comprise one or more of the elements Al, Cu, Ti, Mg, Zn, Sn, Bi and Pb. The matrix may also comprise a ceramic such as one or more of BeO, A1N, BN and graphite. In a further embodiment, the matrix comprises a metal or alloy and a ceramic. The ceramic may be provided in the form of inclusions within a metal or alloy matrix. In a further embodiment, the inclusions comprise a metallic corrosion protection coating. This corrosion protection coating may comprise one or more of Al, Cu and Sn. The corrosion protection coating may be applied to increase the working life of the magnetocalorically active phase since the corrosion and degradation of the magnetocalorically active material into non-magnetocalorically active phases is at least slowed, or even prevented entirely over the working lifetime of the magntocalorically active material, due to the corrosion protection coating. In a further embodiment, the inclusions comprise an outer coating of an electrically isolating material. In the case of a composite article comprising inclusions and matrix having a microstructure characteristic of a compacted powder, the particles of the matrix may also comprise an outer coating of an electrically isolating material. In the case of a composite article having a matrix with a microstructure characteristic of a sintered powder, the grain boundaries between the grains of the matrix as well as between the inclusions and the matrix may comprise an electrically isolating layer. The electrically isolating material may comprise a polymer or a ceramic such as BeO, A1N, BN or inorganic compounds such as silicates, oxides and phosphates. A mixture of a ceramic and a metal or alloy for the matrix or in the form of an outer coating of the inclusions and/or particle or grains of the matrix has the advantage that the average electrical resistivity of the matrix is increased. This reduces the effect of eddy currents during the application and removal of the magnetic field which further increases the efficiency of the magnetic heat exchange system. The electrically isolating coating may also provide corrosion protection for the magnetocalorically active material since it provides a physical barrier between the magnetocalorically active particle and the surrounding environment. An electrically isolating coating has the advantage that the layer thickness may be small. Therefore, a thin ceramic coating may be provided on the particles to electrically isolate the particles from the contiguous particles without increasing the brittleness of the matrix. The material of the matrix may be selected in order to optimise a variety of additional properties. For example, the material of the matrix may be selected so as to be easily worked by mechanical deformation techniques such as extrusion, rolling, drawing and swaging, for example. The material may, therefore, be ductile and easily workable at room temperature with or without intermediate annealing at temperatures of a few hundred °C. This matrix material enables a composite article to be fabricated which can be easily worked after the initial fabrication of the composite article. This has the advantage that the composite article may be formed by mechanical deformation techniques into the desired final form. Alternatively, or in addition, the material or the matrix may have a high thermal conductivity. This has the advantage that the efficiency of the heat transfer from the mag-netocalorically active material to the heat exchange medium which is in contact with outer surfaces of the composite article during the operation of the composite article in a magnetic heat exchange system is increased. The mechanical properties of the matrix may also be adjusted by selection of a single material or by selection of a mixture of materials, for example one or more ceramics and one or more metals or alloys. Thus the mechanical strength of the composite article can be increased in order to further limit possible damage to the composite article during its use in a magnetic heat exchange system. The composite article comprising at least a matrix having a microstructure characteristic of sintered powder may have a matrix comprising an average grain size of less than 1000 μm (micrometer) and/or inclusions having an average diameter of less than 1000 μm (micrometer). The relative proportions of the magnetocalorically active material and of the mag-netocaloricaUy passive material may also be selected to provide the desired heat exchange characteristics for a desired total volume of the composite article. For example, the lower limit of the volume fraction of magnetocalorically active material may be limited by the desired heat exchange capacity, whether that be cooling capacity or heating capacity. The upper limit of the volume fraction of magnetocalorically active material may be limited by the production of the composite article and/or its workability and/or corrosion stability. For example, if the volume fraction of the magnetocalorically passive material is too low, then the advantages produced by using a ductile material in order to improve the workability of the compacted article and/or the sintered composite article may not be achieved to the desired degree. If the magnetocalorically active material corrodes in the heat exchange medium, the matrix may not provide a sufficiently good coverage of the inclusions in order to prevent the magnetocalorically active material coming into contact with the heat exchange medium if the fraction of the magnetocalorically passive material providing the matrix is too low and the volume fraction of the magnetocalorically active material is too high. The volume fraction of inclusions may be between 25% and 98%, preferably between 60% and 95%. In a further embodiment, the matrix comprises a soft magnetic material. This has the advantage that the effective magnetic air gap between the magnets and the composite article in the magnetic heat exchange system is reduced. Therefore, the cooling and/or heating effect provided by the magnetocalorically active material of the composite article can be increased. The soft magnetic material may comprise one or more of Fe, FeSi, Co and Ni. In a further embodiment, the composite article comprises a plurality of magnetocalorically active materials, each having a different Curie temperature. This may be provided by adjusting the composition of a single phase or by providing different phases. In a first arrangement, the plurality of magnetocalorically active materials are distributed essentially homogeneously throughout the volume of the composite article. In another embodiment, the composite article comprises a plurality of layers, each layer comprising inclusions of a magnetocalorically active material having a Tc which is different to the Tc of the magnetocalorically active material in an adjacent layer. In a further embodiment, the magnetocalorically active material of each of the layers is selected, along with the order in which the materials are arranged, in order that the Tc progressively increases from one end of the composite article to the other. The use of composite articles comprising a plurality of magnetocalorically active materials having different Tc's, has the advantage that the operating range of the heat exchanger in which the composite article is used is increased. The Curie temperature T c translates to the operating temperature and, since a range of Tc's are provided, the operating range of the heat exchanger is increased. This enables the heat exchanger to provide cooling and/or heating over a wider operating temperature range and to provide cooling and/heating from a starting temperature to a smaller/ larger lowermost/ uppermost temperature, respectively, than that possible using magnetocalorically active material having a single Tc. The composite article may further comprise an effective porosity. Effective porosity is used herein to describe a porosity of the composite article which has a measurable effect on the efficiency of the magnetic heat exchange. The effective porosity comprises at least one channel within the body of the composite article in flow communication from a first side of the composite article to a second side of the composite article. The porosity may be in the range of 10 vol.% to 60 vol.%. The effective porosity may be provided in the form of a series of interconnected channels in flow communication with each other forming a hollow network of skeleton type structure within the body of the composite article. The heat exchange fluid can then flow through the hollow network from one side of the composite article to the other. The effective porosity may be provided by loosely compacting the powder or by loosely compacting the powder followed by sintering to form in each case a body with a density of less than 100% such that the unoccupied volume provides an interconnected hollow network though which the heat exchange medium can flow. These embodiments of a composite article have the advantage that the surface area of the composite is increased. The heat exchange fluid is in contact with inner surfaces, that is the surfaces of the channels providing the porosity which are positioned within the body of the composite article, as well as with the overall outer surface of the composite article. Thus, the contact area between the composite article and the heat exchange fluid is increased. Consequently, the efficiency of the magnetic heat exchange may be further increased. The composite article may further comprise at least one channel. The channel may be provided in the form of a through-hole which is surrounded by the composite article or may be provided in the form of a channel in an outer surface of the composite article. One or more channels have the advantage of increasing the surface area of the composite article which can further improve the heat exchange efficiency between the composite article and the heat exchange medium. The channel may be formed by extrusion or profile rolling, for example. In a further embodiment, the channel is adapted to direct the flow of the heat exchange medium. The position of the channel is determined by the design of the heat exchange system in which the composite article is to operate. The channel may be adapted to direct the flow of the heat exchange medium with reduced or, optimally, minimum turbulence in order to increase the efficiency of the heat exchange. The article may be a component of a heat exchanger, a cooling system, an air conditioning unit for a building or a vehicle, in particular an automobile, or a climate control device for a building or an automobile. The climate control device may be used as a heater in winter and as a cooler in summer by reversing the direction of the fluid coolant or heat exchanger medium. This is particularly advantageous for automobiles and other vehicles as the space available within the chassis for accommodating the climate control system is limited by the design of the vehicle. The composite article may also comprise an outer protective coating. The outer protective coating may comprise a metal, an alloy or a polymer. The material of the outer protective coating may be chosen so as to be chemically, as well as mechanically, stable during the lifetime operation of the composite article in the heat exchange medium. If the coating is applied to the finished article, it is not subjected to higher temperatures, for example during sintering, or working of the composite article. In this case, a polymer with a relatively low decomposition temperature or melting temperature may be used. The heat exchange medium may comprise ethanol or glycol, mixtures of water, ethanol or glycol or an alternative material with a high thermal conductivity in order to increase the efficiency of the heat exchange between the heat exchange medium and the composite article. The heat exchange medium may be corrosive to the magnetocal-orically active material and/or the magnetocalorically passive material of the matrix. Therefore, an additional outer protective coating may be used to provide additional protection. The invention also provides methods of manufacturing a composite article. A method comprises: - providing a first powder comprising a magnetocalorically active material, - providing a second powder comprising a magnetocalorically passive material, - mixing the first powder and the second powder together to form a powder mixture, and - compacting the powder mixture to form a composite article. The first powder and the second powder may be mixed using known powder mixing techniques such as ball mixing and attrition milling. The average particle size of the first powder and the second powder may also be reduced as a result of the mixing process. The powder mixture may be compacted to form the composite article using known methods. For example, the powder may be placed into a die and compacted by applying pressure. The powder may also be compacted by rolling the powder mixture itself, by rolling a partially compacted or pre-compacted article or by rolling an encapsulated perform containing the powder mixture or an at least partially compacted powder mixture. To produce a perform, the powder mixture may be enveloped in a mantle before compaction using a method such as a powder-in-tube type method. The composite article comprising a mixture of compacted powders of differing compositions may be referred to as a green body since the composite article has not been subjected to a heat treatment process. In the first embodiment, the compacted powder mixture is not subjected to further heat treatment after its production and is used in a magnetic heat exchanger in this unsintered condition. This method has the advantage that the composite article is formed directly from a powder mixture without additional heat treatment. The manufacturing process is simple and cost-effective since the use of one or more additional heat treatments on the composite article is avoided. In an embodiment, the first powder comprises a plurality of particles which are coated with a metallic corrosion protection coating before the first powder is mixed with the second powder. The metallic corrosion protection coating may be applied to the first powder by electro-plating or electroless plating for example. In a further embodiment, the particles of the first powder are coated with an electrically isolating material before the first powder is mixed with the second powder. If it is desired to electrically isolate the particles or grains of the matrix this can be performed by coating the particles of the second powder with an electrically isolating material before the second powder is mixed with the first powder. In order to reduce the effect of eddy currents further the particles of both the first and second powder may comprise an electrically isolating layer. This can be applied to the powders before they are mixed together. The composition of the electrically isolating layer of the first powder may differ from the composition of the electrically isolating layer of the second powder. This enables the coating to be selected specifically for the differing compositions of the two powders. This may be advantageous to improve the adhesion of the coating to the particle by the appropriate selection of the composition of the electrically isolating material. Alternatively, the first powder may be mixed with the second powder and afterwards the particles of the powder mixture are coated with the electrically isolating material. In this case both the particles of the first and second powder comprise an electrically isolating layer of the same composition. In an embodiment, additionally one or more of a lubricant, an organic binder and a dispersant are added to the powder mixture. These additive components may be used to improve mixing of the first powder and the second powder in the case of a binder and/ or dispersant and/or to improve the density of compaction which is achieved during the compaction step in the case of a lubricant. The lubricant can, for example, enable the particles to slide over one another more effectively, thus increasing the density of the compacted powder mixture and the density of the composite article both in the compacted state as well as in the sintered state. The powder mixture may be compacted under a pressure in the range of 10 MPa to 3000 MPa. The density of the composite article generally increases with increasing applied pressure. This relationship is, however, not linear so that a practical upper limit to the pressure may arise above which the increase in density is not outweighed by the increased complexity of applying the higher pressure. If the pressure applied is too low, then the compacted composite article may not have the desired mechanical integrity for reliable use in a magnetic heat exchange system. The pressure may be applied using a method such as rolling or pressing. In a further embodiment, the powder mixture is enveloped in a mantel before the powder mixture is compacted. The powder mixture may also be partially compacted to form a self supporting body before being enveloped in the mantel and further compacted. The powder mixture may be impacted at room temperature. Alternatively, the powder may be compacted as a temperature of between 30°C to 250°C. An elevated temperature has the advantage that the density of the green body can be increased. Dependent on the temperature, a degree of sintering may also occur during the compaction process so that the mechanical integrity of the composite article is further increased. If additives are provided in the powder mixture, they may also be removed during the compaction process at an elevated temperature due to their evaporation and/or decomposition into gaseous components. The invention also provides methods to provide a composite article in which at least the second powder providing the matrix is sintered and has a microstructure characteristic of a sintered powder. In a further embodiment, after the powder mixture is compacted to form a green composite article, a heat treatment is carried out on the compacted composite article. The heat treatment may be carried out such that the powder particles of the matrix sinter together, thus improving the mechanical strength of the composite article. The heat treatment may be carried out at temperatures between 300°C and 1200°C for a time of between two hours and 10 hours. The temperature and time may be selected so as to optimise the sintering process and densification of the composite article and, typically, depends on the material used for the magnetocalorically active material and of the magnetocalorically passive material. The heat treatment may also be performed in order to improve the magnetocaloric properties of the magnetocalorically active material. For example, the Tc may be increased or the sharpness of the transition providing the entropy change can be increased. This heat treatment may be carried out under vacuum or in a protective atmosphere. A protective atmosphere may be provided by a noble gas, such as argon, or by a gas which is inert with respect to the composite article. The gas may be selected so as to avoid degradation of the magnetocalorically active material and/or magnetocalorically passive material due to be elevated temperature used for the heat treatment. The gas may also be selected so that residual undesired elements such as oxygen and carbon are removed during the heat treatment. During the heat treatment, the composition of the magnetocalorically active material may be modified by the interstitial incorporation of elements such as hydrogen and nitrogen delivered by the atmosphere. In a further embodiment, a second compaction process is carried out on the composite article. The second compaction process may be carried out on the compacted composite article, that is the green body, or on the composite article after it has been subjected to a heat treatment and sintered. A second compaction process may be used to further increase the density of the composite article. A second compaction process may be advantageous if additives such as a lubricant, binder and/or dispersant are used in the powder mixture which is removed or burnt out during the first heat treatment. This can result in porosity within the composite article which can be reduced by means of a second compaction process. The degree of compaction achieved during a second compaction or sizing process may range from 5% to 50%. Therefore, in a method, the compacted composite article is first given a heat treatment at a relatively low temperature to remove these additives, and then given a second compaction process and a second heat treatment at a higher temperature during which sintering takes place in order to produce a composite article in which at least the matrix has a microstructure characteristic of a sintered powder. After the production of a composite article, whether it comprises compacted powder or sintered powder, one or more further finishing procedures may be carried out. A finishing procedure may be one in which the final profile of the composite article is produced. The final profile may be produced by grinding and/or polishing the outer surface of the composite article, for example. A further possible finishing procedure may comprise further working of the composite article in order to form the final desired dimensions. For example, the composite article may be subjected to the further mechanical deformation process such as extruding, rolling, drawing and/or swaging, for example. One or more channels for directing the flow of the heat exchange medium may be formed in the composite article during one of these finishing procedures. The composite article may be also be coated with an outer protective coating. This outer protective coating may be applied by dipping, spraying or electroplating. The outer protective coating may be applied to the composite article after the sintering heat treatment is carried out This has the advantage that thermally sensitive materials may be used for the protective coating since the coating is not subjected to the sintering heat treatment. In a further embodiment, the outer protective coating is applied to the compacted composite article. This method may be used when the composite article is to remain unsintered. If the composite article is to be sintered, the protective coating may be applied before the sintering heat treatment in order to protect the intermediate product. Embodiments of the invention will now be described with reference to the drawings. Figure 1 illustrates a composite article according to a first embodiment, Figure 2 illustrates a composite article according to a second embodiment, Figure 3 illustrates a cross-sectional view along the line A-A of the composite article of Figure 2, Figure 4 illustrates a composite article according to a third embodiment, Figure 5 illustrates a composite article according to a fourth embodiment. Figure 1 illustrates a composite article 1 according to a first embodiment of the invention. The composite article 1 comprises a first powder 2 comprising a mag-netocalorically active material and a second powder 3 comprising a magnetocalorically passive powder. The magnetocalorically active powder 2 consists essentially of La(Fe 1-a-bCoaSib)13 with a Tc of 20°C and the magnetocalorically passive powder 3 consists essentially of copper. Copper has a high thermal conductivity and is ductile so that the composite article 1 can be worked by mechanical deformation processes if desired. The two powders 2, 3 are mixed together and compacted in a press to produce composite article 1 which is self-supporting and has a sufficient degree of mechanical strength to be used as the working component in a non-illustrated magnetic heat exchange system. The magnetic heat exchange system may be of a known type. The copper particles 3 providing the magnetocalorically passive powder provide a matrix 4 in which inclusions 5 of magnetocalorically active powder 2 are embedded. The inclusions 5 are distributed and embedded within the matrix 4. Some of the inclusions 5 of magnetocalorically active material 2 have portions 6 which are exposed from the matrix 4 and provide regions of the outer surface 7 of the composite article 1. The inclusions 5 and the matrix 4 each have a microstructure which is characteristic of a compacted powder. The copper powder 3 providing the matrix 4 has a higher thermal conductivity than the magnetocalorically active material 2. The matrix 4, in addition to a binder function, also improves the heat exchange efficiency between the magnetocalorically active inclusions 5 and the heat exchange medium within which the composite article 1 is positioned when it is in use in a magnetic heat exchange system. Figure 2 illustrates a composite article 10 according to a second embodiment of the invention. The composite article 10 comprises three layers 11, 12, 13. Each layer 11, 12,13 comprises a plurality of inclusions 14, each consisting essentially of a magnetocalorically active material, which is embedded in a matrix 15 comprising magnetocalorically passive material 16. In this embodiment, the magnetocalorically passive material 16 providing the matrix 15 of each of the layers 11,12,13 consists essentially of copper. The boundary between adjacent layers is indicated in the figure by a dashed line 17. In this embodiment, the composite article 10 is built up from three layers 11,12,13. The lower layer 13 comprises inclusions 14 of a first magnetocalorically active material 18 with a Tc of 3°C. The second layer 12 is positioned on the first layer 13 and comprises inclusions 14 of magnetocalorically active material 19 with a Tc of 15°C which is greater than the Tc of 3°C of the first magnetocalorically active material 18 of the first layer 13. The third layer 13, which is positioned on the second layer 12, comprises inclusions 14 of a magnetocalorically active phase 20 having a Tc of 29°C which is greater than the Tc 15°C of the second layer. The Tc of the magnetocalorically active material 14 of the composite 10 increases from one side of the composite article 10 to the other, from bottom to top in the view of Figure 2. The composite article 10 also comprises an outer coating 21 which comprises a • polymer. The polymer was applied to the composite article 10 after the sintering process by spraying the composite article 10 with the polymer. The outer coating 21 provides a protective coating which prevents the magnetocalorically active materials 18, 19 and 20 coming into contact with the atmosphere and heat exchange medium of the heat exchange system thus preventing corrosion of the magnetocalorically active materials 18, 19 and 20 and the composite article 10. The use of a plurality layers 11,12,13 each having a progressively higher Tc has the advantage that the operating temperature range of the composite article 10 is increased over a composite article comprising a magnetocalorically active material having a single Tc. In a further embodiment not illustrated in the figures, the composite article comprises a plurality of materials each having a different Tc. These plurality of materials are mixed throughout the volume of the composite article rather than being arranged in layers as illustrated in figure 2. In contrast to the embodiment of figure 1, the composite article 10 is subjected to a heat treatment which results in sintering of the powder 15 and the matrix 16. Therefore, in this embodiment, the matrix 16 has a microstructure characteristic of a sintered powder. The composite article 10 is fabricated by first fabricating three different powder mixtures. The first powder mixture comprises magnetocalorically active material 18 with a Tc of 3°C and copper powder 15, the second powder comprises magnetocalorically active material 19 with a Tc of 15°C and copper powder 15 and the third powder mixture comprises magnetocalorically active material 20 with a Tc of 29°C and copper powder 15. A layer 11 of the first powder mixture is placed into a die, followed by a layer 12 of the second powder mixture and finally followed by a layer 13 of the third powder mixture. The layered arrangement of the powder mixtures was compacted under an pressure of 600 MPa and then given a sintering heat treatment at 1000°C in order to produce a sintered composite article 10. A plurality of generally parallel channels 22 was then formed in the outer surface of the composite article 23 by profile rolling. The channels 22 are illustrated in Figure 3. The channels 22 each have dimensions and are arranged in the outer surface so as to be adapted to direct the flow of a heat exchange medium in the direction of the desired heat transfer when the composite article 10 is positioned in a non-illustrated heat exchange system. The channels 22 are arranged to extend from the low Tc first layer 11 to the high Tc third layer 13. The composite article 10 was then sprayed with a polymer to provide the outer protective coating 21. In a further non-illustrated embodiment, additionally, one or more of a lubricant, an organic binder and a dispersant are added to the powder mixture before its compaction, preferably before the mixing procedure. A lubricant can help to increase the density of the compacted composite article 1,10. A binder and/or a dispersant can help to provide a uniform distribution of inclusions 5,14 within the matrix 4, 15. Although the layered structure has been illustrated in figure 2 as comprising three layers, any number of layers, including only a single layer, is also provided by the invention for a sintered composite article. Similarly, a compacted unsintered green composite article with layers comprising magnetocalorically active material of different Tc may also be produced using this layered process of the different powders. The process differs from that described in connection with the embodiment of Figure 2 in that no heat treatment is performed on the layered composite article after the compaction process. Figure 4 illustrates a composite article 30 according to a third embodiment. The composite article 30 is similar to the composite article 1 of the first embodiment illustrated in Figure 1, but differs from the composite article 1 of the first embodiment in that the inclusions 5 of magnetocalorically active powder 2 as well as the copper particles 3 are coated with an electrically isolating material 31. For clarity of illustration, in Figure 4 the inclusions 5 of the magnetocalorically active powder 2 are shaded black while the magnetocalorically passive copper particles 3 of the matrix 4 are unshaded. It should also be noted that the thickness of the electrically isolating coating as well as the size of the particles has been exaggerated for illustrative purposes. The inclusions 5 and the copper particles 3 of the matrix 4 are electrically isolated from one another by the electrically isolating coating 31. The provision of the electrically isolating coating 31 has the advantage that the production of eddy currents during the application and removal of a magnetic field are reduced which leads to an increase in the efficiency of the magnetic heat exchange system. The electrically isolating coating 31 may be a polymer or a ceramic, for example. The particles of the two powders 2, 3 may be coated with an electrically isolating material before they are mixed together or the two powders 2, 3 may first mixed together and the electrically isolating coating 31 applied to the outer surfaces of the particles of the powder mixture. In a further embodiment, the composite article 30 is subjected to a heat treatment which results in sintering of the powder 3 providing the matrix 4 so that the matrix 4 has a microstructure characteristic of a sintered powder. In this embodiment, the electrically isolating coating 31 is present at the grain boundaries between the grains of the sintered matrix 4 as well as at the grain boundaries between the inclusions 5 and the sintered matrix 4. The electrically isolating coating 31 may also provide protection against corrosion. This is particularly advantageous for composites in which the inclusions 5 of the mag-netocalorically active material are coated with an electrical isolation layer since some magnetocalorically active materials tend to corrode upon exposure to the atmosphere as well as upon exposure to the heat transfer medium. Figure 5 illustrates a composite article 40 according to a fourth embodiment. The composite article 40 differs from the previous embodiments in that the composite article further comprises an effective porosity 41. For clarity of illustration, in Figure 5 the inclusions 5 of the magnetocalorically active powder 2 are shaded black while the magnetocalorically passive copper particles 3 are unshaded. In the fourth embodiment, the composite article 40 comprises an effective porosity which enables the heat exchange fluid to pass through the composite article 40. The porosity 41 comprises a plurality of interconnected channels 42 providing a skeleton type structure of channels 42 throughout the composite article 40. A sufficient number of which are open at one or two ends at the outer surface 7 of the composite article 40. The heat exchange medium is able to flow from one side 43 of the composite article 41 to the opposite side 44 as indicated by the arrows through the network of channels 42. In Figure 5 only one through channel 42 and a branch channel 47 from the through channel 42 of the network providing the porosity 41 are illustrated. The heat exchange fluid is able to contact the inner surfaces 45 provided by the porous structure 42 as well as the outer surface 7 of the composite article 40. The surface area of the composite article 40 is increased due to the presence of the porosity 42 and, furthermore, the contact area between the composite article 40 and the heat exchange medium is increased. Consequently, the efficiency of the magnetic heat exchange may be further increased. In the fourth embodiment, the inclusions 5 comprising magnetocalorically active material further comprise a metallic corrosion protection coating 46. The corrosion protection coating 46 is copper and is arranged between the outer surface of the mag-netocalorically active material of the individual inclusions 5 and the electrically isolating coating 31. The inclusions 5, therefore, comprise two coatings. This has the advantage that the properties of each layer can be optimized separately. An additional corrosion protection layer 46 is useful in a composite article 40 having an effective porosity 41 since some of the inclusions 5 border on the channels 42 and form a portion of the surface 45 of the channel 42. The corrosion protection coating 46 provides additional protection for these portions of the inclusions 5 which are not embedded in the matrix 3 and which come into contact with the environment and the heat exchange fluid. It should also be noted that the thickness of the corrosion protection coating 46 and the electrically isolating coating 31 as well as the size of the particles 3, 5 and the channels 42, 47 has been exaggerated for illustrative purposes in Figure 5. In a further non-illustrated embodiment, the inclusions 5 include only a metallic corrosion protection coating 46, that is the inclusions 5 are not provided with an additional outer electrically isolating layer 31. The composite article 1; 10; 30; 40 may be used as the working component of a heat exchanger, a refrigeration system, a climate control device, an air-conditioning unit, or an industrial, commercial or domestic freezer. Reference numbers 1 first composite article 2 first powder comprising a magnetocalorically active material 3 second powder comprising a magnetocalorically passive material 4 matrix 5 inclusion 6 exposed portion of inclusion 7 outer surface of composite article 10 second composite article 11 first layer 12 second layer 13 third layer 14 inclusion 15 matrix 16 magnetocalorically passive material 17 boundary between adjacent layers 18 first magnetocalorically active material 19 second magnetocalorically active material 20 third magnetocalorically active material 21 outer coating 22 channel 23 outer surface 30 third composite article 31 electrically isolating coating 40 fourth composite article 41 porosity 42 channel of porosity 43 first side 44 second opposing side 45 surface of porosity 46 corrosion protection layer 47 second channel We Claim; [1] Composite article (1), comprising a plurality of inclusions (5) of a magnetocalorically active material embedded in a matrix (4) of a magnetocalorically passive material, wherein the inclusions (5) and the matrix (4) have a microstructure characteristic of a compacted powder. [2] Composite article(l) according to claim 1, characterized in that the matrix (4) has an average particle size of less than 1000 urn (micrometer). [3] Composite article (1) according claim 1 or claim 2, characterized in that the inclusions (5) have an average diameter of less than 1000 urn (micrometer). [4] Composite article (40) according to one of claims 1 to 3, characterized in that the inclusions (5) comprise a metallic corrosion protection coating (46). [5] Composite article (40) according to claim 4, characterized in that the corrosion protection coating (46) comprises one or more of Al, Cu and Sn. [6] Composite article (1) according to one of claims 1 to 5, characterized in that the inclusions (5) comprise an outer coating (31) of an electrically isolating material. [7] Composite article (1) according to one of claims 1 to 6, characterized in that the particles of the matrix (4) comprise an outer coating (31) of an electrically isolating material. [8] Composite article (1) according to claim 6 or claim 7, characterized in that the electrically isolating material comprises a polymer or a ceramic or an inorganic compound. [9] Composite article (10), comprising a plurality of inclusions (14) of a magnetocalorically active material (18, 19,20) embedded in a matrix (15) of a magnetocalorically passive material (16), wherein the matrix (15) has a microstructure characteristic of a sintered powder. [10] Composite article (10) according to claim 9, characterized in that the inclusions (14) and the matrix (15) have a microstructure characteristic of a sintered powder. [11] Composite article (10) according to claim 9 or claim 10, characterized in that the inclusions (14) and the matrix (15) have a grain structure characteristic of a sintered powder. [12] Composite article (40) according to one of claims 9 to 11, characterized in that the inclusions (5) comprise a metallic corrosion protection coating (46). [13] Composite article (40) according to claim 12, characterized in that the corrosion protection coating (46) comprises one or more of Al, Cu and Sn. [14] Composite article (10) according to one of claims 9 to 13, characterized in that the inclusions (5) comprise an outer coating (31) of an electrically isolating material. [15] Composite article (10) according to one of claims 9 to 14, characterized in that the particles of the matrix (4) comprise an outer coating (31) of an electrically isolating material. [16] Composite article (10) according to claim 14 or claim 15, characterized in that the electrically isolating material comprises a polymer or a ceramic. [17] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the magnetocalorically active material (2; 18,19,20) has a Curie temperature Tc in the range 220K to 345K. [18] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the magnetocalorically active material (2; 18, 19, 20) is one or more of Gd, a La(Fe1-bSib)13-based phase, a Gds(Si,Ge)4-based phase, a Mn(As,Sb)-based phase, a MnFe(P,As)-based phase, a Tb-Gd-based phase, a (La, Ca, Pr,Nd,Sr)MnO3 - based phase, a Co-Mn-(Si,Ge)-based phase and a Pr2(Fe,Co)17-based phase. [19] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the matrix (4; 15) comprises one or more of the elements, A1, Cu, Ti, Mg, Zn, Sn, Bi and Pb. [20] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the matrix comprises one or more of BeO, A1N, BN and graphite. [21] Composite article (10) according to one of claims 9 to 20, characterized in that the matrix (15) has an average grain size of less than 1000 μm (micrometer). [22] Composite article (10) according to one claims 9 to 21, characterized in that the inclusions (14) have an average diameter of less than 1000 μm (micrometer). [23] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the volume fraction of inclusions (5; 14) is between 25% and 98%. [24] Composite article (1; 10; 40) according to claim 13, characterized in that the volume fraction of inclusions (5; 14) is between 60% and 95%. [25] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the matrix (5; 14) comprises a soft magnetic material. [26] Composite article (1; 10; 40) according to claim 25, characterized in that the soft magnetic material comprises one or more of Fe, FeSi, Co and Ni. [27] Composite article (10) according to one of the previous claims, characterized in that the composite article (10) comprises a plurality of layers (11,12,13), each layer (11, 12, 13) comprising inclusions (14) of a magnetocalorically active material (18,19, 20) having a Tc which is different to the Tc of the magnetocalorically active material in an adjacent layer (11,12,13). [28] Composite article (10) according to one of the previous claims, characterized in that the composite article (10) further comprises at least one channel (22) in a surface. [29] Composite article (10) according to claim 28, characterized in that the channel (22) is adapted to direct the flow of a heat exchange medium. [30] Composite article (1; 10; 40) according to one of claims 1 to 29 further comprising an outer protective coating (21). [31 ] Composite article (1; 10; 40) according to claim 30, characterized in that the outer protective coating (21) comprises a polymer or a metal or an alloy. [32] Composite article (1; 10; 40) according to one of the previous claims further comprising an effective porosity (41). [33] Composite article (40) according to claim 32, characterized in that the effective porosity (41) comprises at least one channel (42) within the body of the composite article (40) providing flow communication from a first side (43) of the composite article (40) to a second side (44) of the composite article (40). [34] Composite article (40) according to claim 32 or claim 33, characterized in that the effective porosity (41) comprises 10 vol.% to 60 vol.% of the composite article (40). [35] Composite article (1; 10; 40) according to one of the previous claims, characterized in that the composite article (1; 10) is a component of a heat exchanger, a refrigeration system, a climate control device, an air-conditioning unit, or an industrial, commercial or domestic freezer. [36] Heat exchanger comprising at least one composite article according to one of claims 1 to 34. [37] Method of manufacturing a composite article (1; 10; 40), comprising - providing a first powder (2) comprising a magnetocalorically active material, - providing a second powder (3) comprising a magnetocalorically passive material, - mixing the first powder (2) and the second powder (3) together to form a powder mixture, - compacting the powder mixture to form a composite article (1). [38] Method according to claim 37, characterized in that additionally one or more of a lubricant, an organic binder and a dispersant are added to the powder mixture. [39] Method according to claim 37 or claim 38, characterized in that the first powder (2) comprises a plurality of particles which are coated with a metallic corrosion protection coating (46) before the first powder (2) is mixed with the second powder (3). [40] Method according to one of claims 37 to 39, characterized in that the first powder (2) comprises a plurality of particles which are coated with an electrically isolating material before the first powder (2) is mixed with the second powder (3). [41] Method according to one of claims 37 to 40, characterized in that the second powder (3) comprises a plurality of particles which are coated with an electrically isolating material before the second powder (3) is mixed with the first powder (2). [42] Method according to claim 40 or claim 41, characterized in that the first powder (2) comprises a plurality of particles and the second powder (3) comprises a plurality of particles which are coated with an electrically isolating material after the first powder (2) is mixed with the second powder (3). [43] Method according to one of claims 37 to 42, characterized in that the powder mixture is compacted under a pressure of 10 MPa to 3000 MPa. [44] Method according to one of claims 37 to 42, characterized in that the powder mixture is compacted by one of rolling and pressing. [45] Method according to one of claims 37 to 44, characterized in that before compaction the powder mixture is enveloped in a mantle. [46] Method according to one of claims 37 to 45, characterized in that the powder mixture is compacted at one of room temperature or at a temperature between 30°C to 250°C. [47] Method according to one of claims 37 to 46, characterized in that a heat treatment is carried out on the compacted composite article (10). [48] Method according to claim 47, characterized in that the heat treatment is carried out at a temperature between 300°C and 1200°C for a time between 2 hours and 10 hours. [49] Method according to claim 47 or claim 48, characterized in that the heat treatment is carried out under vacuum or in a protective atmosphere. [50] Method according to one of claims 37 to 49, characterized in that a second compaction process is carried out on the composite article. [51] Method according to one of claims 37 to 50, characterized in that a finishing procedure is carried out. [52] Method according to one of claims 37 to 51, further comprising applying an outer protective coating (21) to the composite article (1; 10). [53] Method according to claim 52, characterized in that the outer protective coating (21) is applied by dipping, spraying or electro-de position. [54] Method according to claim 52 to claim 53, characterized in that the outer protective coating (21) is applied after the sintering heat treatment is carried out. [55] Method according to one of claims 52 to 56, characterized in that the outer protective coating (21)is applied to the compacted composite article (1). Composite article with magnetocalorically active material and method for its production A composite article (1; 10; 40) comprises a plurality of inclusions (5) of a magnetocalorically active material embedded in a matrix (4) of a magnetocalorically passive material. The inclusions (5) and the matrix (4) have a microstructure characteristic of a compacted powder.

Full Text

Description Composite article with magnetocalorically active material and
method for its production
The invention relates to a composite article with magnetocalorically active material and to methods for producing a composite article with magnetocalorically active material.
The magnetocaloric effect describes the adiabatic conversion of a magnetically induced entropy change to the evolution or absorption of heat. Therefore, by applying a magnetic field to a magnetocaloric material, an entropy change can be induced which results in the evolution or absorption of heat. This effect can be harnessed to provide refrigeration and/or heating.
In recent years, materials such as La(Fe1-aSia)13, Gd5(Si,Ge)4, Mn (As,Sb) and MnFe(P,As) have been developed which have a Curie Temperature, Tc, at or near room temperature. The Curie Temperature translates to the operating temperature of the material in a magnetic heat exchange system. Consequently, these materials are suitable for use in applications such as building climate control, domestic and in-dustrial refrigerators and freezers as well as automotive climate control.
Magnetic heat exchange technology has the advantage that magnetic heat exchangers are, in principle, more energy efficient than gas compression/expansion cycle systems. Furthermore, magnetic heat exchangers are environmentally friendly as ozone depleting chemicals such as CFC's are not used.
Consequently, magnetic heat exchanger systems are being developed in order to practically realise the advantages provided by the newly developed magnetocaloric materials. Magnetic heat exchangers, such as that disclosed in US 6,676,772, typically include a pumped recirculation system, a heat exchange medium such as a fluid coolant, a chamber packed with particles of a magnetic refrigerant working material which displays the magnetocaloric effect and a means for applying a magnetic field to the chamber.
Further developments of these systems have been directed towards optimizing the composition of the magnetocaloric material so as to increase the entropy change and to increase the temperature range over which the entropy change occurs. This enables smaller applied magnetic fields to be used to achieve sufficient cooling and a stable reT frigeration cycle to be achieved over a larger temperature range.
These measures aim to simplify the design of the heat exchange system since smaller magnetic fields can be produced by a permanent magnet rather than an electromagnet or even a superconducting magnet.

The magnetic refrigerant working material may also be provided in the form of a composite. For example, US 6,826,915 discloses a regenerative bed comprising a magnetic refrigeration material including a binder comprising a metal or alloy of high ductility and a magnetocaloric material of the NiAs-type.
However, further improvements are desirable to enable a more extensive application of magnetic heat exchange technology.
It is an object of the invention to provide a composite article comprising magnetocal-orically active material which can be reliably and cost effectively manufactured. It is a further object to provide methods by which the composite article may be produced.
This object is solved by the subject matter of the independent claims. Further advantageous improvements are the subject matter of the dependent claims.
The invention provides a composite article comprising a plurality of inclusions of a magnetocalorically active material embedded in a matrix of a magnetocalorically passive material. The inclusions and the matrix have a microstructure characteristic of a compacted powder.
Herein, the term matrix is defined as the magnetocalorically passive material, irrespective of its volume fraction and distribution.
A magnetocalorically active material is defined herein as a material which undergoes a change in entropy when it is subjected to a magnetic field. The entropy change may be the result of a change from ferromagnetic to paramagnetic behaviour, for example. The magnetocalorically active material may exhibit in only a part of a temperature region an inflection point at which the sign of the second derivative of magnetization with respect to an applied magnetic field changes from positive to negative.
A magnetocalorically passive material is defined herein as a material which exhibits no significant change in entropy when it is subjected to a magnetic field.
Inclusion is defined herein as a particle or grain having a first composition which is at least partially embedded in the matrix comprising a different second composition. Inclusion also includes an agglomerate of particles or grains of a first composition which is at least partially embedded in the matrix comprising a second different composition material. A particle or agglomerate which has a portion exposed from the matrix, for example this exposed portion may provide an outer surface of the composite article, is included in this definition of inclusion.
A microstructure characteristic of a compacted powder can be identified by examining a polished cross-section of the composite article using light microscopy or Scanning Electron Microscopy. A compacted powder has a microstructure which comprises a plurality of particles which at least in part touch their immediate neighbours, i.e. the contiguous particles, without interdiffusion of atoms between the contiguous particles.

The particles of a compacted powder also have lattice structure which exhibits strain and/or fractures which have occurred as a result of the pressure applied during compaction. These structural defects can be observed using Transmission Electron Microscopy.
The composite article according to the invention has the advantage that it can be simply produced by mixing together a first powder of a magnetocalorically active material and a second powder of a magnetocalorically passive material and then compacting the powder mixture to form a composite article. The composite article may be used in a magnetic heat exchange system as the magnetic working material without going a subsequent heat treatment. Therefore, the inclusions and the matrix of the composite article have a microstructure characteristic of a compacted powder.
The matrix of the composite article may be thought of as a binder which holds the inclusions of magnetically active material together to form a composite article. Thus magnetocalorically active material, which, particularly in the case of materials such as Gd, La(Fe1-bSib)13-based phases, Gd5(Si,Ge)4-based phases, Mn(As,Sb)-based phases, MnFe(P,As)-based phases, Tb-Gd-based phases, (La, Ca, Pr,Nd,Sr)MnO3-based phases, Co-Mn-(Si, Ge)- based phases and Pr2(Fe,Co)17-based phases is brittle, can be formed into a composite article having sufficient mechanical stability to be used in a heat exchanger system due to the matrix of magnetocalorically passive material.
The composite article has the advantage that the magnetocalorically active material and magnetocalorically passive material may be fabricated using known techniques and be fabricated separately from one another before being mixed together to form the starting mixture for the composite article. Consequently, the fabrication of the two powders can be optimised separately from the optimisation of the composite article.
By controlling the compaction process appropriately, the composite article can be produced having the dimensions desired for a particular magnetic heat exchange system. The composite article may be produced having a near-net shape simply by compacting the powder mixture. The composite article is, therefore, easily produced using a simple, cost-effective manufacturing process.
The magnetocalorically active material may be used as supplied or as fabricated or may be given an additional heat treatment in order to improve the magnetocaloric properties of the powder before it is mixed with the magnetocalorically passive powder which later forms the matrix.
The first embodiment, the matrix has an average particle size of less than 1000 μm (micrometer). In a further embodiment, the inclusions have an average diameter of less than 1000 μm (micrometer).
The average particle size of the matrix is defined herein as the mean of the longest dimension of each of 20 randomly selected particles in a polished cross-section of the

composite article.
The average diameter of the inclusions is defined herein as the mean of the longest dimension of each of 20 randomly selected inclusions in a polished cross-section of the composite article.
In a further embodiment of the invention, a composite article is provided which comprises a plurality of inclusions of a magnetocaloricalry active material embedded in a matrix of a magnetocalorically passive material. In this embodiment, the matrix has a microstructure characteristic of a sintered powder.
A microstructure characteristic of a sintered powder can be identified by examining a polished cross-section of the composite article using light microscopy or Scanning Electron Microscopy. A sintered powder has a microstructure which comprises a plurality of particles which at least in part touch their immediate neighbours, i.e. the contiguous particles, wherein the interface between contiguous particles comprises in-terdiffusion of atoms of the contiguous particles.
Furthermore, as a result of the sintering process, the particles have undergone strain relief. This strain relief can be observed using Transmission Electron Microscopy techniques since the dislocation density and lattice strain within the grains is lower than that of compacted unsintered powder.
The composite article comprising a matrix having a microstructure characteristic of a sintered powder has the advantage that the mechanical strength of the composite article is increased due to the sintering process. This simplifies the handling of the composite article during any later production steps, for example surface finishing of the composite article, during storage and delivery of the composite article as well as during the assembly of the composite article into a magnetic heat exchange system. Furthermore, in the case that the magnetic heat exchange system is of the type in which the magnets remain stationary and the magnetic working material is physically moved relative to the magnets, the likelihood of cracking and damage to the magnetic working material as a result of this movement is reduced.
The composite article comprising a matrix having a microstructure characteristic of a sintered powder is also easily produced using known powder processing techniques. For example, a powder of a magnetocalorically passive material may be mixed with magnetocalorically active material, the powder mixture is compacted and then sintered by applying heat.
This embodiment has the advantage that the composite article may be manufactured by embedding magnetocalorically active material in powder of a magnetocalorically passive material. This intermediate may then be sintered to produce the composite article.
In an embodiment, the inclusions comprising a magnetocalorically active material are

provided in the form of a powder. In this embodiment, the inclusions as well as the matrix have a microstructure characteristic of a sintered powder.
Alternatively, the inclusions may be provided in forms other than that of powder. For example, the inclusions may be provided in the form of a skeleton structure which is embedded in powder of a magnetocalorically passive material or in the form of a series of foils, flakes, filaments or tapes which are embedded in powder of a magnetocalorically passive material which forms the matrix of the composite article.
The matrix and possibly the inclusions may have a grain structure characteristic of a sintered powder. This characteristic grain structure can be identified using light microscopy and or Scanning Electron Microscopy techniques. The most appropriate technique may depend on the average grain size. The grain structure of a sintered powder is characterised by the grain boundaries between adjacent grains, in particular between contiguous grains comprising the same material. These grains are atomically joined to one another due to interdiffusion between the contiguous grains at the interface and have a misorientation with respect to one another. The microstructure of the grains and of the grain boundaries can be observed using Transmission Electron Microscopy techniques.
The average grain size of the sintered composite article, in particular of the matrix, is also typically greater than the average particle size from which the article was produced. For example, the average grain size of the matrix is greater than the average particle size of the magnetocalorically passive powder.
In an embodiment, the magnetocalorically active material has a Curie temperature Tc in the range 220K to 345K. The operating temperature of the magnetocalorically active material, when used in a magnetic heat exchange system, is approximately that of its Curie temperature. A magnetocalorically active material with a Curie temperature in the range 220K to 345K is suitable for applications such as domestic and commercial freezer systems, refrigeration, air conditioning or climate control systems depending on the desired operating temperature and operating temperature range.
The magnetocalorically active material is one of Gd, a La(Fe1-bSib)13-based phase, a Gd5(Si,Ge)4-based phase, a Mn(As,Sb)-based phase, a MnFe(P,As)-based phase, a Tb-Gd-based phase, a (La, Ca, Pr,Nd,Sr)MnCybased phase, a Co-Mn-(Si,Ge)-based phase and a Pr2(Fe,Co)17-based phase. These basic compositions may further comprise further chemical elements which may substitute partially or in full for the listed elements. These phases may also comprise elements which are accommodated at least in part in-terstitially within the crystal structure, for example, hydrogen. These phases may also include impurity elements and small amounts of elements such as oxygen.
The matrix may comprise a variety of materials. In an embodiment, the matrix comprises a material which has a higher thermal conductivity than the thermal con-

ductivity of the inclusions of the magnetocalorically active material. This has the advantage that the efficiency of the heat exchange between the magnetocalorically active material and the heat exchange medium is increased.
In an embodiment, the matrix comprises a metal or an alloy which may comprise one or more of the elements Al, Cu, Ti, Mg, Zn, Sn, Bi and Pb.
The matrix may also comprise a ceramic such as one or more of BeO, A1N, BN and graphite. In a further embodiment, the matrix comprises a metal or alloy and a ceramic. The ceramic may be provided in the form of inclusions within a metal or alloy matrix.
In a further embodiment, the inclusions comprise a metallic corrosion protection coating. This corrosion protection coating may comprise one or more of Al, Cu and Sn. The corrosion protection coating may be applied to increase the working life of the magnetocalorically active phase since the corrosion and degradation of the magnetocalorically active material into non-magnetocalorically active phases is at least slowed, or even prevented entirely over the working lifetime of the magntocalorically active material, due to the corrosion protection coating.
In a further embodiment, the inclusions comprise an outer coating of an electrically isolating material. In the case of a composite article comprising inclusions and matrix having a microstructure characteristic of a compacted powder, the particles of the matrix may also comprise an outer coating of an electrically isolating material.
In the case of a composite article having a matrix with a microstructure characteristic of a sintered powder, the grain boundaries between the grains of the matrix as well as between the inclusions and the matrix may comprise an electrically isolating layer. The electrically isolating material may comprise a polymer or a ceramic such as BeO, A1N, BN or inorganic compounds such as silicates, oxides and phosphates.
A mixture of a ceramic and a metal or alloy for the matrix or in the form of an outer coating of the inclusions and/or particle or grains of the matrix has the advantage that the average electrical resistivity of the matrix is increased. This reduces the effect of eddy currents during the application and removal of the magnetic field which further increases the efficiency of the magnetic heat exchange system.
The electrically isolating coating may also provide corrosion protection for the magnetocalorically active material since it provides a physical barrier between the magnetocalorically active particle and the surrounding environment.
An electrically isolating coating has the advantage that the layer thickness may be small. Therefore, a thin ceramic coating may be provided on the particles to electrically isolate the particles from the contiguous particles without increasing the brittleness of the matrix.
The material of the matrix may be selected in order to optimise a variety of additional properties. For example, the material of the matrix may be selected so as to be easily

worked by mechanical deformation techniques such as extrusion, rolling, drawing and swaging, for example. The material may, therefore, be ductile and easily workable at room temperature with or without intermediate annealing at temperatures of a few hundred °C. This matrix material enables a composite article to be fabricated which can be easily worked after the initial fabrication of the composite article. This has the advantage that the composite article may be formed by mechanical deformation techniques into the desired final form.
Alternatively, or in addition, the material or the matrix may have a high thermal conductivity. This has the advantage that the efficiency of the heat transfer from the mag-netocalorically active material to the heat exchange medium which is in contact with outer surfaces of the composite article during the operation of the composite article in a magnetic heat exchange system is increased.
The mechanical properties of the matrix may also be adjusted by selection of a single material or by selection of a mixture of materials, for example one or more ceramics and one or more metals or alloys. Thus the mechanical strength of the composite article can be increased in order to further limit possible damage to the composite article during its use in a magnetic heat exchange system.
The composite article comprising at least a matrix having a microstructure characteristic of sintered powder may have a matrix comprising an average grain size of less than 1000 μm (micrometer) and/or inclusions having an average diameter of less than 1000 μm (micrometer).
The relative proportions of the magnetocalorically active material and of the mag-netocaloricaUy passive material may also be selected to provide the desired heat exchange characteristics for a desired total volume of the composite article. For example, the lower limit of the volume fraction of magnetocalorically active material may be limited by the desired heat exchange capacity, whether that be cooling capacity or heating capacity.
The upper limit of the volume fraction of magnetocalorically active material may be limited by the production of the composite article and/or its workability and/or corrosion stability. For example, if the volume fraction of the magnetocalorically passive material is too low, then the advantages produced by using a ductile material in order to improve the workability of the compacted article and/or the sintered composite article may not be achieved to the desired degree.
If the magnetocalorically active material corrodes in the heat exchange medium, the matrix may not provide a sufficiently good coverage of the inclusions in order to prevent the magnetocalorically active material coming into contact with the heat exchange medium if the fraction of the magnetocalorically passive material providing the matrix is too low and the volume fraction of the magnetocalorically active material

is too high. The volume fraction of inclusions may be between 25% and 98%, preferably between 60% and 95%.
In a further embodiment, the matrix comprises a soft magnetic material. This has the advantage that the effective magnetic air gap between the magnets and the composite article in the magnetic heat exchange system is reduced. Therefore, the cooling and/or heating effect provided by the magnetocalorically active material of the composite article can be increased. The soft magnetic material may comprise one or more of Fe, FeSi, Co and Ni.
In a further embodiment, the composite article comprises a plurality of magnetocalorically active materials, each having a different Curie temperature. This may be provided by adjusting the composition of a single phase or by providing different phases.
In a first arrangement, the plurality of magnetocalorically active materials are distributed essentially homogeneously throughout the volume of the composite article.
In another embodiment, the composite article comprises a plurality of layers, each layer comprising inclusions of a magnetocalorically active material having a Tc which is different to the Tc of the magnetocalorically active material in an adjacent layer. In a further embodiment, the magnetocalorically active material of each of the layers is selected, along with the order in which the materials are arranged, in order that the Tc progressively increases from one end of the composite article to the other.
The use of composite articles comprising a plurality of magnetocalorically active materials having different Tc's, has the advantage that the operating range of the heat exchanger in which the composite article is used is increased. The Curie temperature T c translates to the operating temperature and, since a range of Tc's are provided, the operating range of the heat exchanger is increased. This enables the heat exchanger to provide cooling and/or heating over a wider operating temperature range and to provide cooling and/heating from a starting temperature to a smaller/ larger lowermost/ uppermost temperature, respectively, than that possible using magnetocalorically active material having a single Tc.
The composite article may further comprise an effective porosity. Effective porosity is used herein to describe a porosity of the composite article which has a measurable effect on the efficiency of the magnetic heat exchange.
The effective porosity comprises at least one channel within the body of the composite article in flow communication from a first side of the composite article to a second side of the composite article. The porosity may be in the range of 10 vol.% to 60 vol.%.
The effective porosity may be provided in the form of a series of interconnected channels in flow communication with each other forming a hollow network of skeleton

type structure within the body of the composite article. The heat exchange fluid can then flow through the hollow network from one side of the composite article to the other.
The effective porosity may be provided by loosely compacting the powder or by loosely compacting the powder followed by sintering to form in each case a body with a density of less than 100% such that the unoccupied volume provides an interconnected hollow network though which the heat exchange medium can flow.
These embodiments of a composite article have the advantage that the surface area of the composite is increased. The heat exchange fluid is in contact with inner surfaces, that is the surfaces of the channels providing the porosity which are positioned within the body of the composite article, as well as with the overall outer surface of the composite article. Thus, the contact area between the composite article and the heat exchange fluid is increased. Consequently, the efficiency of the magnetic heat exchange may be further increased.
The composite article may further comprise at least one channel. The channel may be provided in the form of a through-hole which is surrounded by the composite article or may be provided in the form of a channel in an outer surface of the composite article. One or more channels have the advantage of increasing the surface area of the composite article which can further improve the heat exchange efficiency between the composite article and the heat exchange medium. The channel may be formed by extrusion or profile rolling, for example.
In a further embodiment, the channel is adapted to direct the flow of the heat exchange medium. The position of the channel is determined by the design of the heat exchange system in which the composite article is to operate. The channel may be adapted to direct the flow of the heat exchange medium with reduced or, optimally, minimum turbulence in order to increase the efficiency of the heat exchange.
The article may be a component of a heat exchanger, a cooling system, an air conditioning unit for a building or a vehicle, in particular an automobile, or a climate control device for a building or an automobile. The climate control device may be used as a heater in winter and as a cooler in summer by reversing the direction of the fluid coolant or heat exchanger medium. This is particularly advantageous for automobiles and other vehicles as the space available within the chassis for accommodating the climate control system is limited by the design of the vehicle.
The composite article may also comprise an outer protective coating. The outer protective coating may comprise a metal, an alloy or a polymer. The material of the outer protective coating may be chosen so as to be chemically, as well as mechanically, stable during the lifetime operation of the composite article in the heat exchange medium. If the coating is applied to the finished article, it is not subjected to higher

temperatures, for example during sintering, or working of the composite article. In this case, a polymer with a relatively low decomposition temperature or melting temperature may be used.
The heat exchange medium may comprise ethanol or glycol, mixtures of water, ethanol or glycol or an alternative material with a high thermal conductivity in order to increase the efficiency of the heat exchange between the heat exchange medium and the composite article. The heat exchange medium may be corrosive to the magnetocal-orically active material and/or the magnetocalorically passive material of the matrix. Therefore, an additional outer protective coating may be used to provide additional protection.
The invention also provides methods of manufacturing a composite article. A method comprises:
- providing a first powder comprising a magnetocalorically active material,
- providing a second powder comprising a magnetocalorically passive material,
- mixing the first powder and the second powder together to form a powder mixture, and
- compacting the powder mixture to form a composite article.
The first powder and the second powder may be mixed using known powder mixing techniques such as ball mixing and attrition milling. The average particle size of the first powder and the second powder may also be reduced as a result of the mixing process.
The powder mixture may be compacted to form the composite article using known methods. For example, the powder may be placed into a die and compacted by applying pressure. The powder may also be compacted by rolling the powder mixture itself, by rolling a partially compacted or pre-compacted article or by rolling an encapsulated perform containing the powder mixture or an at least partially compacted powder mixture. To produce a perform, the powder mixture may be enveloped in a mantle before compaction using a method such as a powder-in-tube type method.
The composite article comprising a mixture of compacted powders of differing compositions may be referred to as a green body since the composite article has not been subjected to a heat treatment process. In the first embodiment, the compacted powder mixture is not subjected to further heat treatment after its production and is used in a magnetic heat exchanger in this unsintered condition.
This method has the advantage that the composite article is formed directly from a powder mixture without additional heat treatment. The manufacturing process is simple and cost-effective since the use of one or more additional heat treatments on the composite article is avoided.
In an embodiment, the first powder comprises a plurality of particles which are

coated with a metallic corrosion protection coating before the first powder is mixed with the second powder. The metallic corrosion protection coating may be applied to the first powder by electro-plating or electroless plating for example.
In a further embodiment, the particles of the first powder are coated with an electrically isolating material before the first powder is mixed with the second powder.
If it is desired to electrically isolate the particles or grains of the matrix this can be performed by coating the particles of the second powder with an electrically isolating material before the second powder is mixed with the first powder.
In order to reduce the effect of eddy currents further the particles of both the first and second powder may comprise an electrically isolating layer. This can be applied to the powders before they are mixed together. The composition of the electrically isolating layer of the first powder may differ from the composition of the electrically isolating layer of the second powder. This enables the coating to be selected specifically for the differing compositions of the two powders. This may be advantageous to improve the adhesion of the coating to the particle by the appropriate selection of the composition of the electrically isolating material.
Alternatively, the first powder may be mixed with the second powder and afterwards the particles of the powder mixture are coated with the electrically isolating material. In this case both the particles of the first and second powder comprise an electrically isolating layer of the same composition.
In an embodiment, additionally one or more of a lubricant, an organic binder and a dispersant are added to the powder mixture. These additive components may be used to improve mixing of the first powder and the second powder in the case of a binder and/ or dispersant and/or to improve the density of compaction which is achieved during the compaction step in the case of a lubricant. The lubricant can, for example, enable the particles to slide over one another more effectively, thus increasing the density of the compacted powder mixture and the density of the composite article both in the compacted state as well as in the sintered state.
The powder mixture may be compacted under a pressure in the range of 10 MPa to 3000 MPa. The density of the composite article generally increases with increasing applied pressure. This relationship is, however, not linear so that a practical upper limit to the pressure may arise above which the increase in density is not outweighed by the increased complexity of applying the higher pressure. If the pressure applied is too low, then the compacted composite article may not have the desired mechanical integrity for reliable use in a magnetic heat exchange system. The pressure may be applied using a method such as rolling or pressing.
In a further embodiment, the powder mixture is enveloped in a mantel before the powder mixture is compacted. The powder mixture may also be partially compacted to

form a self supporting body before being enveloped in the mantel and further compacted.
The powder mixture may be impacted at room temperature. Alternatively, the powder may be compacted as a temperature of between 30°C to 250°C.
An elevated temperature has the advantage that the density of the green body can be increased. Dependent on the temperature, a degree of sintering may also occur during the compaction process so that the mechanical integrity of the composite article is further increased. If additives are provided in the powder mixture, they may also be removed during the compaction process at an elevated temperature due to their evaporation and/or decomposition into gaseous components.
The invention also provides methods to provide a composite article in which at least the second powder providing the matrix is sintered and has a microstructure characteristic of a sintered powder.
In a further embodiment, after the powder mixture is compacted to form a green composite article, a heat treatment is carried out on the compacted composite article. The heat treatment may be carried out such that the powder particles of the matrix sinter together, thus improving the mechanical strength of the composite article.
The heat treatment may be carried out at temperatures between 300°C and 1200°C for a time of between two hours and 10 hours. The temperature and time may be selected so as to optimise the sintering process and densification of the composite article and, typically, depends on the material used for the magnetocalorically active material and of the magnetocalorically passive material.
The heat treatment may also be performed in order to improve the magnetocaloric properties of the magnetocalorically active material. For example, the Tc may be increased or the sharpness of the transition providing the entropy change can be increased.
This heat treatment may be carried out under vacuum or in a protective atmosphere. A protective atmosphere may be provided by a noble gas, such as argon, or by a gas which is inert with respect to the composite article. The gas may be selected so as to avoid degradation of the magnetocalorically active material and/or magnetocalorically passive material due to be elevated temperature used for the heat treatment. The gas may also be selected so that residual undesired elements such as oxygen and carbon are removed during the heat treatment.
During the heat treatment, the composition of the magnetocalorically active material may be modified by the interstitial incorporation of elements such as hydrogen and nitrogen delivered by the atmosphere.
In a further embodiment, a second compaction process is carried out on the composite article. The second compaction process may be carried out on the

compacted composite article, that is the green body, or on the composite article after it has been subjected to a heat treatment and sintered. A second compaction process may be used to further increase the density of the composite article. A second compaction process may be advantageous if additives such as a lubricant, binder and/or dispersant are used in the powder mixture which is removed or burnt out during the first heat treatment. This can result in porosity within the composite article which can be reduced by means of a second compaction process.
The degree of compaction achieved during a second compaction or sizing process may range from 5% to 50%.
Therefore, in a method, the compacted composite article is first given a heat treatment at a relatively low temperature to remove these additives, and then given a second compaction process and a second heat treatment at a higher temperature during which sintering takes place in order to produce a composite article in which at least the matrix has a microstructure characteristic of a sintered powder.
After the production of a composite article, whether it comprises compacted powder or sintered powder, one or more further finishing procedures may be carried out. A finishing procedure may be one in which the final profile of the composite article is produced. The final profile may be produced by grinding and/or polishing the outer surface of the composite article, for example.
A further possible finishing procedure may comprise further working of the composite article in order to form the final desired dimensions. For example, the composite article may be subjected to the further mechanical deformation process such as extruding, rolling, drawing and/or swaging, for example. One or more channels for directing the flow of the heat exchange medium may be formed in the composite article during one of these finishing procedures.
The composite article may be also be coated with an outer protective coating. This outer protective coating may be applied by dipping, spraying or electroplating.
The outer protective coating may be applied to the composite article after the sintering heat treatment is carried out This has the advantage that thermally sensitive materials may be used for the protective coating since the coating is not subjected to the sintering heat treatment.
In a further embodiment, the outer protective coating is applied to the compacted composite article. This method may be used when the composite article is to remain unsintered. If the composite article is to be sintered, the protective coating may be applied before the sintering heat treatment in order to protect the intermediate product.
Embodiments of the invention will now be described with reference to the drawings.
Figure 1 illustrates a composite article according to a first embodiment,
Figure 2 illustrates a composite article according to a second embodiment,

Figure 3 illustrates a cross-sectional view along the line A-A of the composite article of Figure 2,
Figure 4 illustrates a composite article according to a third embodiment,
Figure 5 illustrates a composite article according to a fourth embodiment.
Figure 1 illustrates a composite article 1 according to a first embodiment of the invention. The composite article 1 comprises a first powder 2 comprising a mag-netocalorically active material and a second powder 3 comprising a magnetocalorically passive powder. The magnetocalorically active powder 2 consists essentially of La(Fe 1-a-bCoaSib)13 with a Tc of 20°C and the magnetocalorically passive powder 3 consists essentially of copper. Copper has a high thermal conductivity and is ductile so that the composite article 1 can be worked by mechanical deformation processes if desired.
The two powders 2, 3 are mixed together and compacted in a press to produce composite article 1 which is self-supporting and has a sufficient degree of mechanical strength to be used as the working component in a non-illustrated magnetic heat exchange system. The magnetic heat exchange system may be of a known type.
The copper particles 3 providing the magnetocalorically passive powder provide a matrix 4 in which inclusions 5 of magnetocalorically active powder 2 are embedded. The inclusions 5 are distributed and embedded within the matrix 4. Some of the inclusions 5 of magnetocalorically active material 2 have portions 6 which are exposed from the matrix 4 and provide regions of the outer surface 7 of the composite article 1.
The inclusions 5 and the matrix 4 each have a microstructure which is characteristic of a compacted powder.
The copper powder 3 providing the matrix 4 has a higher thermal conductivity than the magnetocalorically active material 2. The matrix 4, in addition to a binder function, also improves the heat exchange efficiency between the magnetocalorically active inclusions 5 and the heat exchange medium within which the composite article 1 is positioned when it is in use in a magnetic heat exchange system.
Figure 2 illustrates a composite article 10 according to a second embodiment of the invention.
The composite article 10 comprises three layers 11, 12, 13. Each layer 11, 12,13 comprises a plurality of inclusions 14, each consisting essentially of a magnetocalorically active material, which is embedded in a matrix 15 comprising magnetocalorically passive material 16. In this embodiment, the magnetocalorically passive material 16 providing the matrix 15 of each of the layers 11,12,13 consists essentially of copper. The boundary between adjacent layers is indicated in the figure by a dashed line 17.
In this embodiment, the composite article 10 is built up from three layers 11,12,13. The lower layer 13 comprises inclusions 14 of a first magnetocalorically active

material 18 with a Tc of 3°C. The second layer 12 is positioned on the first layer 13 and comprises inclusions 14 of magnetocalorically active material 19 with a Tc of 15°C which is greater than the Tc of 3°C of the first magnetocalorically active material 18 of the first layer 13. The third layer 13, which is positioned on the second layer 12, comprises inclusions 14 of a magnetocalorically active phase 20 having a Tc of 29°C which is greater than the Tc 15°C of the second layer. The Tc of the magnetocalorically active material 14 of the composite 10 increases from one side of the composite article 10 to the other, from bottom to top in the view of Figure 2.
The composite article 10 also comprises an outer coating 21 which comprises a • polymer. The polymer was applied to the composite article 10 after the sintering process by spraying the composite article 10 with the polymer. The outer coating 21 provides a protective coating which prevents the magnetocalorically active materials 18, 19 and 20 coming into contact with the atmosphere and heat exchange medium of the heat exchange system thus preventing corrosion of the magnetocalorically active materials 18, 19 and 20 and the composite article 10.
The use of a plurality layers 11,12,13 each having a progressively higher Tc has the advantage that the operating temperature range of the composite article 10 is increased over a composite article comprising a magnetocalorically active material having a single Tc.
In a further embodiment not illustrated in the figures, the composite article comprises a plurality of materials each having a different Tc. These plurality of materials are mixed throughout the volume of the composite article rather than being arranged in layers as illustrated in figure 2.
In contrast to the embodiment of figure 1, the composite article 10 is subjected to a heat treatment which results in sintering of the powder 15 and the matrix 16. Therefore, in this embodiment, the matrix 16 has a microstructure characteristic of a sintered powder.
The composite article 10 is fabricated by first fabricating three different powder mixtures. The first powder mixture comprises magnetocalorically active material 18 with a Tc of 3°C and copper powder 15, the second powder comprises magnetocalorically active material 19 with a Tc of 15°C and copper powder 15 and the third powder mixture comprises magnetocalorically active material 20 with a Tc of 29°C and copper powder 15.
A layer 11 of the first powder mixture is placed into a die, followed by a layer 12 of the second powder mixture and finally followed by a layer 13 of the third powder mixture. The layered arrangement of the powder mixtures was compacted under an pressure of 600 MPa and then given a sintering heat treatment at 1000°C in order to produce a sintered composite article 10.

A plurality of generally parallel channels 22 was then formed in the outer surface of the composite article 23 by profile rolling. The channels 22 are illustrated in Figure 3.
The channels 22 each have dimensions and are arranged in the outer surface so as to be adapted to direct the flow of a heat exchange medium in the direction of the desired heat transfer when the composite article 10 is positioned in a non-illustrated heat exchange system. The channels 22 are arranged to extend from the low Tc first layer 11 to the high Tc third layer 13.
The composite article 10 was then sprayed with a polymer to provide the outer protective coating 21.
In a further non-illustrated embodiment, additionally, one or more of a lubricant, an organic binder and a dispersant are added to the powder mixture before its compaction, preferably before the mixing procedure. A lubricant can help to increase the density of the compacted composite article 1,10. A binder and/or a dispersant can help to provide a uniform distribution of inclusions 5,14 within the matrix 4, 15.
Although the layered structure has been illustrated in figure 2 as comprising three layers, any number of layers, including only a single layer, is also provided by the invention for a sintered composite article. Similarly, a compacted unsintered green composite article with layers comprising magnetocalorically active material of different Tc may also be produced using this layered process of the different powders. The process differs from that described in connection with the embodiment of Figure 2 in that no heat treatment is performed on the layered composite article after the compaction process.
Figure 4 illustrates a composite article 30 according to a third embodiment. The composite article 30 is similar to the composite article 1 of the first embodiment illustrated in Figure 1, but differs from the composite article 1 of the first embodiment in that the inclusions 5 of magnetocalorically active powder 2 as well as the copper particles 3 are coated with an electrically isolating material 31.
For clarity of illustration, in Figure 4 the inclusions 5 of the magnetocalorically active powder 2 are shaded black while the magnetocalorically passive copper particles 3 of the matrix 4 are unshaded. It should also be noted that the thickness of the electrically isolating coating as well as the size of the particles has been exaggerated for illustrative purposes.
The inclusions 5 and the copper particles 3 of the matrix 4 are electrically isolated from one another by the electrically isolating coating 31. The provision of the electrically isolating coating 31 has the advantage that the production of eddy currents during the application and removal of a magnetic field are reduced which leads to an increase in the efficiency of the magnetic heat exchange system.
The electrically isolating coating 31 may be a polymer or a ceramic, for example.

The particles of the two powders 2, 3 may be coated with an electrically isolating material before they are mixed together or the two powders 2, 3 may first mixed together and the electrically isolating coating 31 applied to the outer surfaces of the particles of the powder mixture.
In a further embodiment, the composite article 30 is subjected to a heat treatment which results in sintering of the powder 3 providing the matrix 4 so that the matrix 4 has a microstructure characteristic of a sintered powder. In this embodiment, the electrically isolating coating 31 is present at the grain boundaries between the grains of the sintered matrix 4 as well as at the grain boundaries between the inclusions 5 and the sintered matrix 4.
The electrically isolating coating 31 may also provide protection against corrosion. This is particularly advantageous for composites in which the inclusions 5 of the mag-netocalorically active material are coated with an electrical isolation layer since some magnetocalorically active materials tend to corrode upon exposure to the atmosphere as well as upon exposure to the heat transfer medium.
Figure 5 illustrates a composite article 40 according to a fourth embodiment. The composite article 40 differs from the previous embodiments in that the composite article further comprises an effective porosity 41.
For clarity of illustration, in Figure 5 the inclusions 5 of the magnetocalorically active powder 2 are shaded black while the magnetocalorically passive copper particles 3 are unshaded.
In the fourth embodiment, the composite article 40 comprises an effective porosity which enables the heat exchange fluid to pass through the composite article 40. The porosity 41 comprises a plurality of interconnected channels 42 providing a skeleton type structure of channels 42 throughout the composite article 40. A sufficient number of which are open at one or two ends at the outer surface 7 of the composite article 40. The heat exchange medium is able to flow from one side 43 of the composite article 41 to the opposite side 44 as indicated by the arrows through the network of channels 42. In Figure 5 only one through channel 42 and a branch channel 47 from the through channel 42 of the network providing the porosity 41 are illustrated.
The heat exchange fluid is able to contact the inner surfaces 45 provided by the porous structure 42 as well as the outer surface 7 of the composite article 40.
The surface area of the composite article 40 is increased due to the presence of the porosity 42 and, furthermore, the contact area between the composite article 40 and the heat exchange medium is increased. Consequently, the efficiency of the magnetic heat exchange may be further increased.
In the fourth embodiment, the inclusions 5 comprising magnetocalorically active material further comprise a metallic corrosion protection coating 46. The corrosion

protection coating 46 is copper and is arranged between the outer surface of the mag-netocalorically active material of the individual inclusions 5 and the electrically isolating coating 31. The inclusions 5, therefore, comprise two coatings. This has the advantage that the properties of each layer can be optimized separately.
An additional corrosion protection layer 46 is useful in a composite article 40 having an effective porosity 41 since some of the inclusions 5 border on the channels 42 and form a portion of the surface 45 of the channel 42. The corrosion protection coating 46 provides additional protection for these portions of the inclusions 5 which are not embedded in the matrix 3 and which come into contact with the environment and the heat exchange fluid.
It should also be noted that the thickness of the corrosion protection coating 46 and the electrically isolating coating 31 as well as the size of the particles 3, 5 and the channels 42, 47 has been exaggerated for illustrative purposes in Figure 5.
In a further non-illustrated embodiment, the inclusions 5 include only a metallic corrosion protection coating 46, that is the inclusions 5 are not provided with an additional outer electrically isolating layer 31.
The composite article 1; 10; 30; 40 may be used as the working component of a heat exchanger, a refrigeration system, a climate control device, an air-conditioning unit, or an industrial, commercial or domestic freezer.
Reference numbers
1 first composite article
2 first powder comprising a magnetocalorically active material
3 second powder comprising a magnetocalorically passive material
4 matrix
5 inclusion
6 exposed portion of inclusion
7 outer surface of composite article

10 second composite article
11 first layer
12 second layer
13 third layer
14 inclusion
15 matrix
16 magnetocalorically passive material
17 boundary between adjacent layers
18 first magnetocalorically active material
19 second magnetocalorically active material
20 third magnetocalorically active material

21 outer coating
22 channel
23 outer surface

30 third composite article
31 electrically isolating coating

40 fourth composite article
41 porosity
42 channel of porosity
43 first side
44 second opposing side
45 surface of porosity
46 corrosion protection layer
47 second channel

We Claim;
[1] Composite article (1), comprising
a plurality of inclusions (5) of a magnetocalorically active material embedded in
a matrix (4) of a magnetocalorically passive material, wherein
the inclusions (5) and the matrix (4) have a microstructure characteristic of a
compacted powder.
[2] Composite article(l) according to claim 1,
characterized in that
the matrix (4) has an average particle size of less than 1000 urn (micrometer).
[3] Composite article (1) according claim 1 or claim 2,
characterized in that
the inclusions (5) have an average diameter of less than 1000 urn (micrometer).
[4] Composite article (40) according to one of claims 1 to 3,
characterized in that
the inclusions (5) comprise a metallic corrosion protection coating (46).
[5] Composite article (40) according to claim 4,
characterized in that
the corrosion protection coating (46) comprises one or more of Al, Cu and Sn.
[6] Composite article (1) according to one of claims 1 to 5,
characterized in that
the inclusions (5) comprise an outer coating (31) of an electrically isolating
material.
[7] Composite article (1) according to one of claims 1 to 6,
characterized in that
the particles of the matrix (4) comprise an outer coating (31) of an electrically
isolating material.
[8] Composite article (1) according to claim 6 or claim 7,
characterized in that
the electrically isolating material comprises a polymer or a ceramic or an
inorganic compound.
[9] Composite article (10), comprising
a plurality of inclusions (14) of a magnetocalorically active material (18, 19,20)
embedded in a matrix (15) of a magnetocalorically passive material (16),
wherein
the matrix (15) has a microstructure characteristic of a sintered powder.
[10] Composite article (10) according to claim 9,
characterized in that

the inclusions (14) and the matrix (15) have a microstructure characteristic of a
sintered powder.
[11] Composite article (10) according to claim 9 or claim 10,
characterized in that
the inclusions (14) and the matrix (15) have a grain structure characteristic of a
sintered powder.
[12] Composite article (40) according to one of claims 9 to 11,
characterized in that
the inclusions (5) comprise a metallic corrosion protection coating (46).
[13] Composite article (40) according to claim 12,
characterized in that
the corrosion protection coating (46) comprises one or more of Al, Cu and Sn.
[14] Composite article (10) according to one of claims 9 to 13,
characterized in that
the inclusions (5) comprise an outer coating (31) of an electrically isolating
material.
[15] Composite article (10) according to one of claims 9 to 14,
characterized in that
the particles of the matrix (4) comprise an outer coating (31) of an electrically
isolating material.
[16] Composite article (10) according to claim 14 or claim 15,
characterized in that
the electrically isolating material comprises a polymer or a ceramic.
[17] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the magnetocalorically active material (2; 18,19,20) has a Curie temperature Tc
in the range 220K to 345K.
[18] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the magnetocalorically active material (2; 18, 19, 20) is one or more of Gd, a
La(Fe1-bSib)13-based phase, a Gds(Si,Ge)4-based phase, a Mn(As,Sb)-based phase,
a MnFe(P,As)-based phase, a Tb-Gd-based phase, a (La, Ca, Pr,Nd,Sr)MnO3 -
based phase, a Co-Mn-(Si,Ge)-based phase and a Pr2(Fe,Co)17-based phase.
[19] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the matrix (4; 15) comprises one or more of the elements, A1, Cu, Ti, Mg, Zn, Sn,
Bi and Pb.
[20] Composite article (1; 10; 40) according to one of the previous claims,

characterized in that
the matrix comprises one or more of BeO, A1N, BN and graphite.
[21] Composite article (10) according to one of claims 9 to 20,
characterized in that
the matrix (15) has an average grain size of less than 1000 μm (micrometer).
[22] Composite article (10) according to one claims 9 to 21,
characterized in that
the inclusions (14) have an average diameter of less than 1000 μm (micrometer).
[23] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the volume fraction of inclusions (5; 14) is between 25% and 98%.
[24] Composite article (1; 10; 40) according to claim 13,
characterized in that
the volume fraction of inclusions (5; 14) is between 60% and 95%.
[25] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the matrix (5; 14) comprises a soft magnetic material.
[26] Composite article (1; 10; 40) according to claim 25,
characterized in that
the soft magnetic material comprises one or more of Fe, FeSi, Co and Ni.
[27] Composite article (10) according to one of the previous claims,
characterized in that
the composite article (10) comprises a plurality of layers (11,12,13), each layer
(11, 12, 13) comprising inclusions (14) of a magnetocalorically active material
(18,19, 20) having a Tc which is different to the Tc of the magnetocalorically
active material in an adjacent layer (11,12,13).
[28] Composite article (10) according to one of the previous claims,
characterized in that
the composite article (10) further comprises at least one channel (22) in a
surface.
[29] Composite article (10) according to claim 28,
characterized in that
the channel (22) is adapted to direct the flow of a heat exchange medium.
[30] Composite article (1; 10; 40) according to one of claims 1 to 29 further
comprising an outer protective coating (21).
[31 ] Composite article (1; 10; 40) according to claim 30,
characterized in that
the outer protective coating (21) comprises a polymer or a metal or an alloy.

[32] Composite article (1; 10; 40) according to one of the previous claims further
comprising an effective porosity (41).
[33] Composite article (40) according to claim 32,
characterized in that
the effective porosity (41) comprises at least one channel (42) within the body of
the composite article (40) providing flow communication from a first side (43) of
the composite article (40) to a second side (44) of the composite article (40).
[34] Composite article (40) according to claim 32 or claim 33,
characterized in that
the effective porosity (41) comprises 10 vol.% to 60 vol.% of the composite
article (40).
[35] Composite article (1; 10; 40) according to one of the previous claims,
characterized in that
the composite article (1; 10) is a component of a heat exchanger, a refrigeration
system, a climate control device, an air-conditioning unit, or an industrial,
commercial or domestic freezer.
[36] Heat exchanger comprising at least one composite article according to one of
claims 1 to 34.
[37] Method of manufacturing a composite article (1; 10; 40), comprising
- providing a first powder (2) comprising a magnetocalorically active material,
- providing a second powder (3) comprising a magnetocalorically passive material,
- mixing the first powder (2) and the second powder (3) together to form a powder mixture,
- compacting the powder mixture to form a composite article (1).
[38] Method according to claim 37,
characterized in that
additionally one or more of a lubricant, an organic binder and a dispersant are
added to the powder mixture.
[39] Method according to claim 37 or claim 38,
characterized in that
the first powder (2) comprises a plurality of particles which are coated with a
metallic corrosion protection coating (46) before the first powder (2) is mixed
with the second powder (3).
[40] Method according to one of claims 37 to 39,
characterized in that
the first powder (2) comprises a plurality of particles which are coated with an
electrically isolating material before the first powder (2) is mixed with the

second powder (3).
[41] Method according to one of claims 37 to 40,
characterized in that
the second powder (3) comprises a plurality of particles which are coated with an
electrically isolating material before the second powder (3) is mixed with the
first powder (2).
[42] Method according to claim 40 or claim 41,
characterized in that
the first powder (2) comprises a plurality of particles and the second powder (3)
comprises a plurality of particles which are coated with an electrically isolating
material after the first powder (2) is mixed with the second powder (3).
[43] Method according to one of claims 37 to 42,
characterized in that
the powder mixture is compacted under a pressure of 10 MPa to 3000 MPa.
[44] Method according to one of claims 37 to 42,
characterized in that
the powder mixture is compacted by one of rolling and pressing.
[45] Method according to one of claims 37 to 44,
characterized in that
before compaction the powder mixture is enveloped in a mantle.
[46] Method according to one of claims 37 to 45,
characterized in that
the powder mixture is compacted at one of room temperature or at a temperature
between 30°C to 250°C.
[47] Method according to one of claims 37 to 46,
characterized in that
a heat treatment is carried out on the compacted composite article (10).
[48] Method according to claim 47,
characterized in that
the heat treatment is carried out at a temperature between 300°C and 1200°C for
a time between 2 hours and 10 hours.
[49] Method according to claim 47 or claim 48,
characterized in that
the heat treatment is carried out under vacuum or in a protective atmosphere.
[50] Method according to one of claims 37 to 49,
characterized in that
a second compaction process is carried out on the composite article.
[51] Method according to one of claims 37 to 50,

characterized in that
a finishing procedure is carried out.
[52] Method according to one of claims 37 to 51, further comprising applying an
outer protective coating (21) to the composite article (1; 10).
[53] Method according to claim 52,
characterized in that
the outer protective coating (21) is applied by dipping, spraying or electro-de
position.
[54] Method according to claim 52 to claim 53,
characterized in that
the outer protective coating (21) is applied after the sintering heat treatment is
carried out.
[55] Method according to one of claims 52 to 56,
characterized in that
the outer protective coating (21)is applied to the compacted composite article (1).

Composite article with magnetocalorically active material and method for its production A composite article (1; 10; 40) comprises a plurality of inclusions (5) of a magnetocalorically active material embedded in a matrix (4) of a magnetocalorically passive material. The inclusions (5) and the matrix (4) have a microstructure characteristic of a compacted powder.

Documents:

3167-KOLNP-2009-(16-12-2014)-CLAIMS.pdf

3167-KOLNP-2009-(16-12-2014)-CORRESPONDENCE.pdf

3167-KOLNP-2009-(16-12-2014)-OTHERS.pdf

3167-KOLNP-2009-(18-02-2014)-CLAIMS.pdf

3167-KOLNP-2009-(18-02-2014)-CORRESPONDENCE.pdf

3167-KOLNP-2009-(18-02-2014)-FORM-3.pdf

3167-KOLNP-2009-(18-02-2014)-OTHERS.pdf

3167-KOLNP-2009-(18-02-2014)-PETITION UNDER RULE 137.pdf

3167-KOLNP-2009-(19-08-2013)-CORRESPONDENCE.pdf

3167-KOLNP-2009-(19-08-2013)-FORM-3.pdf

3167-kolnp-2009-abstract.pdf

3167-kolnp-2009-claims.pdf

3167-KOLNP-2009-CORRESPONDENCE 1.1.pdf

3167-KOLNP-2009-CORRESPONDENCE 1.2.pdf

3167-kolnp-2009-correspondence.pdf

3167-kolnp-2009-description (complete).pdf

3167-kolnp-2009-drawings.pdf

3167-KOLNP-2009-FORM 1.1.1.pdf

3167-kolnp-2009-form 1.pdf

3167-KOLNP-2009-FORM 18.pdf

3167-kolnp-2009-form 2.pdf

3167-KOLNP-2009-FORM 3.1.1.pdf

3167-kolnp-2009-form 3.pdf

3167-kolnp-2009-form 5.pdf

3167-kolnp-2009-international publication.pdf

3167-kolnp-2009-international search report.pdf

3167-KOLNP-2009-PA.pdf

3167-kolnp-2009-specification.pdf

abstract-3167-kolnp-2009.jpg

« Previous Patent

Next Patent »

Patent Number

264329

Indian Patent Application Number

3167/KOLNP/2009

PG Journal Number

52/2014

Publication Date

26-Dec-2014

Grant Date

22-Dec-2014

Date of Filing

07-Sep-2009

Name of Patentee

VACUUMSCHMELZE GMBH & CO., KG

Applicant Address

GRUENER WEG 37 63450 HANAU GERMANY

Inventors:

#	Inventor's Name	Inventor's Address
1	MATTHIAS KATTER	AM BACHGRABEN 8 63755 ALZENAU GERMANY
2	GEORG WERNER REPPEL	GOLDBERGSTR. 4 63456 HAMMERSBACH GERMANY

PCT International Classification Number

H01F 1/01,F25B 21/00

PCT International Application Number

PCT/IB2007/055316

PCT International Filing date

2007-12-27