Title of Invention

"SLIP- AND LEVELLING AGENT"

Abstract

The invention relates to a slip- and leveling agent characterized in that it comprises a copolymer which is obtained by copolymerizing A at least one unit of a mono- or di perfluoroester of an unsaturated dicarboxylic-acid; B at least one terminal reactive polysiloxane unit; C at least one alkyl(meth)acrylate unit or cycloalkyl(meth)acrylate unit and/or (meth)acrylic acid and/or other units originating from vinylic compounds that can form radicals.

Full Text

Slip- and leveling agent The invention relates to a new slip- and leveling agent containing perfluoralkyi dicarboxylic acid /siloxane moieties and to its use as slip-and leveling agent and anti-cratering agent for a variety of applications. Difficulties related to the application of liquid resin solutions (liquid systems) such as paint, printing ink, plastic compounds and the like, to solid substrates are generally known in the art, in particular when the surface tension of the liquid system is high, and the surface tension of the solid substrate is lower. Such liquid systems are typically composed of solvents, resins, and optionally pigments, extenders and additives. In particular, modern synthetic resins have a higher intrinsic surface tension by design and function, in comparison to traditional resins based on natural fatty acids and oils. Thus, it may be more difficult to apply modern liquid systems such as modern 2-component systems like epoxies, polyester/melamines or polyurethanes, than to apply (conventional) alkyds. If water is employed as a solvent, the surface tension of the liquid formulation is high by definition. This obligates the technician to use leveling and anti-crater agents to obtain an aesthetic surface, which ensures its protective function through an uniform film. By reduction of the surface tension of the liquid system to a value below the surface tension of the substrate, spreading of the liquid is improved and the surface may level out to obtain an aesthetically more attractive film. Craters are caused by contaminates, which enter the liquid film from the outside, or are already present on the substrate. In order to avoid cratering, the liquid systems need to have a lower surface tension than the contaminate itself, usually silicone or mineral oil droplets. For the purpose of slip, leveling, substrate wetting and anti-cratering, the market offers a variety of products, ranging from organically modified polysiloxanes to fluorocarbons, waxes and other anionic, cationic or electroneutral organic surfactants, which however show well-known disadvantages such as foam formation, foam stabilisation, surface slip, overcoatability problems, and incompatibility in the liquid systems, causing craters, haze, loss of gloss, migration, sweating and poor storage stability. US 6,710,127 (Byk) describes a leveling agent which is a branched polymer comprising a polymeric backbone molecule into which macromonomeric units such as polydimethyl-siloxanes or perfluoroalkyl acrylates have been incorporated. WO03/033603 (EFKA) corresponding to US2004236007 describes the use of a polymer as a leveling agent or anti-cratering agent, said polymer comprising units of certain ester moieties of unsaturated dicarboxylic-acids with certain fluorinated units. Preferred co-monomers include alkyl(meth)acrylate units and/or (meth)acrylic acid and/or other vinylic compounds. WO03/033603 does not contain a monomeric unit containing a terminal reactive poly-siloxane. There is still a need for improved slip- and leveling agents having enhanced surface properties such as a good anti-cratering performance, a low coefficient of friction, a good intercoat adhesion and in addition show a good foam control. It has now been found that particular copolymers comprising perfluoroester units of an unsaturated dicarboxylic-acid; monoethylenically unsaturated polydimethylsiloxane units and common co-monomer units are very suitable slip- and leveling agents. Especially improved slip properties are obtained compared to leveling agents containing perfluoroester units of an unsaturated dicarboxylic-acid and (meth)acrylate units as disclosed in WO03/033603. Accordingly, the present invention relates to a slip- and leveling agent characterized in that it comprises a copolymer which is obtained by copolymerizing A at least one unit of a mono- or di perfluoroester of an unsaturated dicarboxylic-acid; B at least one terminal reactive polysiloxane unit; C at least one alkyl(meth)acrylate unit or cycloalkyl(meth)acrylate unit and/or (meth)acrylic acid and/or other units originating from vinylic compounds that can form radicals. Advantage: The use of a slip- and leveling according to the invention gives benefits such as a low coefficient of friction, excellent slip, complete wetting of the substrate. It helps to prevent the formation of craters and pin-holes, to provide a smooth and/or equal leveling of the paint film without orange peel leading to improved aesthetics of the dry film. Also, edge crawling, air-draft sensitivity, fish eyes and/or other dewetting effects of the liquid resin solution during the drying stage may be avoided or at least reduced significantly. Additionally, it has been found that such a slip-and levelling agent exhibits low foam properties. All this may be achieved without loosing overcoatability of the dry film. Definitions A) Perfluoroester of unsaturated dicarboxylic-acids are mono- or diesters of fluoroalcohols or mixtures of fluoroalcohols or are as disclosed in WO03/033603 and thus may be represented by formula I, In a preferred embodiment the one or more fluorinated units A are represented by formula I wherein n is 4 -14, more preferably 4-10. Very good results have been achieved when using a copolymer wherein at least 50%, preferably 70 - 100% of the fluorinated units of the copolymer are represented by formula I wherein n is 4-14, preferably 4 -10 , and particularly wherein n is 4 or 6 or 8. In another preferred embodiment the number of CH2 units (m) in R1 and optionally in R2 is 1, 2, or 3. More preferably m in R1 and/or R2 is 2. In another preferred embodiment the number of -(OCH2CHR5) units (p) in R1 and optionally in R2 is O, 6, 7 or 8. In a preferred embodiment of the invention at least 50%f preferably 90 - 100% of the fluorinated monomeric units are mono-esters. An advantage of using a copolymer with a high level of monoesters, is related to the ease of manufacturing such esters. Another advantage of such a polymer is the fact that it can be rendered water-soluble in an efficient way through neutralisation of the remaining C02H-groups. Very goods results have also been achieved with a copolymer wherein at least the majority of the R1 moieties and optionally at least the majority of the R2 moieties represent a linear fluoroalkyl moiety. Examples of particularly preferred fluorinated units (R1, R2) are (1H,1H,2H,2H)-pentadeca-fluorooctyl, (1H,1H,2H,2H)-heptadecafluorodecyl, (1H,1H,9H)-hexadecafluorononyl, (1H, 1H, 7H)-dodecafluoroheptyl, /V-butyl and N-ethyl perfluorooctane sulphonamido ethyl, (1H,1H,2H,2H)-pentadecafluorooctyl heptaethoxylate and (1H,1H,2H,2H)-heptadecafluoro-decyl heptaethoxylate. An especially preferred unit is the N-CrC6alkyl perfluorobutane sulphonamide ethyl group (CF3-CF2-CF2-CF2-S02-N(Ci-C6alkyl)-CH2-CH2"). The alkyl group is preferably methyl or ethyl. Suitable unsaturated dicarboxylic acid monomers include, for example, maleic acid, maleic anhydride, methylmaleic anhydride, fumaric acid, methylfumaric acid and alkali and metal salts thereof. Maleic acid is preferred. Fluoroalcohols are various tetrafluoroethylene based telomer fluoroalcohols such as those commercially available from Dupont as Zonyl, from Clariant as Fluowet, from Elf-Atochem as Foralkyl 6HN, and the like. C14H29 Fluowet EA800: linear fluoroalcohol C8F17CH2CH20H > 98% with MW of 464 g/mol; originating from Clariant. Fluowet EA 612: mixture of linear fluoroalcohols RfCH2CH2OH with Rf = C6F13 42 +/- 4%, C8Fi7 31 +/- 3%, C10F21 14,5 +/- 2,5% and fluorinated compounds > C12F25 less than 10% and the average MW of the mixture is 448 g/mol; the mixture is originating from Clariant. Foralkyl EON-6N-LW: mixture of linear fluoroalcohols RfCH2CH2OH with Rf = C6F13 45 +/-10%, C8F17 36 +/-10%, C10F21 12 +/- 5% and fluorinated compounds .>_ C12F25 less than 10% and the average MW of the mixture is 475 g/mol; the mixture is originating from Atofina. Fluorad FC 10: mixture of linear fluoroalcohols: /V-ethyl perfluorooctane sulphonamidoethyl alcohol 85 +/- 5%, /V-ethyl perfluoro C4-C7-alkyl sulphonamidoethyl alcohols 15 +/- 5% and the average MW of the mixture is ca. 575 g/mol; the mixture is originating from 3M. Fluoroalcohol L-19547: N-methyl perfluorobutane sulphonamidoethyl alcohol with the MW of ca. 357 g/mol; the material is originating from 3M. The terminal reactive polysiloxane compound has at least one polymerizable unsaturated group such as an acryloxy group, methacryloxy group, vinyl group, propenyl group, butadienyl group, styryl group, ethynyl group, maleate group or acrylamide group. Polydimethylsiloxane compounds are preferable in view of easy availability. The terminal reactive polysiloxane may be prepared by a known method, or it is commercially available. Examples of commercial products are Silaplane FM-0711, FM-0721, FM-0725, FM-0511, FM-0521, FM-0525, TM-0701, TMO701T (manufactured by Chisso Corp.), and the like can be given. To prepare the reactive polysiloxanes, a mono-OH functional silicone compound, for example, those commercially available under the trade names of, Silaplane FM-0411, FM-0421, FM-0425, FM-D411, FM-D421, FM-D425, FM-DA11, FM-DA21, FM-DA25 (manufactured by Chisso Corp.), can be reacted with a compound having a polymerizable unsaturated group as defined above, for example reaction with (meth)acryloyl chloride, allylchloride; or by esterifying them with (meth)acrylic acid or maleic acid. Examples of mono-OH functional groups are 3-(2'-hydroxyethoxy)propyl, 3-(2'-ethyl-2'-hydroxymethyl-3-- hydroxy)propyl or 3-(2,-hydroxy-3,-isopropylamino)propyl. Alkyl(meth)acrylate or cycloalkyl(meth)acrylate units and/or (meth)acrylic acid and/or other units originating from vinylic compounds that can form radicals are e.g. styrene, n-propyl methacrylate, 2-methyl cyclohexyl methacrylate, ethylene glycol mono-methacrylate, tert-butylacrylate, iso-butyl methacrylate, iso-butyl acrylate, o-cresyl methacrylate, t-butyl methacrylate, n-butyl acrylate, n-butyl methacrylate, methylacrylate, methyl methacrylate, ethylacrylate, propylacrylate, iso-propyl methacrylate, 3-methyl-1-pentylacrylate, octyl-acrylate, tetradecylacrylate, s-butylacrylate, s-butyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, 2-methoxyethyI acrylate, phenyl acrylate, cyclohexylacrylate, cyclohexylmethacrylate, acrylic acid, methacrylic acid 1,3-butadiene, isoprene, vinyl pyrrolidone, acrylonitrile, methacrylonitrile, vinylimidazole and vinylpyridine, p-methylstyrene, 3,4-dimethyl styrene, m-ethyl styrene, p-butyl styrene, o-methoxy styrene, p-methoxystyrene, 2,6-dimethoxy styrene, isopropyl vinyl ether, isobutyl vinyl ether, vinyl 2-methoxy ethyl ether, n-hexyl vinyl ether, 2-ethylbutyl vinyl ether, n-octadecyl vinyl ether, .alpha.-methylvinyl ethyl ether, cyclohexanol vinyl ether, benzyl alcohol vinyl ether, vinyl phenyl ether, vinyl acetate, vinyl methoxyacetate, vinyl isobutyrate, vinyl oleate, vinyl benzoate, vinyloctylphthalate). Particularly preferred are alkyl(meth)acrylates or cyclo alkyl(meth)acrylates including n-propyl(meth)acrylate, iso-propyl(meth)acrylate, n-butyl(meth)acrylate, sec-butyl(meth)-acrylate, tert-butyl(meth)acrylate, iso-butyl(meth)acrylate, ethylhexyl(meth)acrylate, cyclo-hexyl(meth)acrylate) and (meth)acrylic acid. The slip-and levelling agent according to the invention may, for example, be a random copolymer, an alternating copolymer or a block copolymer. Preferably the co-polymer is a random copolymer. A preferred slip- and leveling agent is characterized in that it comprises a copolymer which is obtained by copolymerizing A at least one unit of a mono- or di perfluoroester of maleic acid; B a mono-(meth)acrylic functional polydimethylsiloxane or a mono-maleic functional polydimethylsiloxane; and C an alkyl(meth)acrylate unit, cycloalkyl(meth)acrylate unit or a styrene unit, especially an alkyl(meth)acrylate unit or a cycloalkyl(meth)acrylate unit Use: The slip- and leveling agent according to the invention may be used in a variety of applications, e.g. in coatings and inks and plastics. Examples are aqueous systems (e.g. emulsion laquers, such as lacquers based upon polyurethane, alkyds, acrylics, polyester-melamine), water-reducible systems (2K-poly-urethane, alkyd, acrylic, epoxy, vinyl copolymers), (organic) solvent based systems (e.g. polyurethane-based, stoving alkyd/melamine- or polyester/melamine-based, epoxy-based, air-drying alkyds, nitrocellulose, CAB, unsaturated polyesters, acrylics, silicone resins, UV/EB-curing resins, vinyl copolymers, chlorinated rubber) and plastic compounds (hot and ambient curing unsaturated polyesters, epoxy, polyurethanes, polyvinylchloride). The slip- and leveling agent according to the invention may be present in a product (e.g. such as specified above) within a wide concentration range, of which the skilled professional will be able to determine a suitable concentration for a particular application. When the slip- and leveling agent is used in aqueous or organic solvent based systems very good results have been achieved with a product comprising A 0.1-10 wt%, preferably 0.2 - 2.5 wt%, more preferably 0.4 - 1.5 wt% of a mono- or di perfluoroester of an unsaturated dicarboxylic-acid; B 1-20wt%, preferably 1-10wt%, more preferably 1-5wt% of the terminal reactive polysiloxane compound; C 50-99wt% alkyl(meth)acrylate units and/or (meth)acrylic acid and/or other unit originating from vinylic compounds that can form radicals. A copolymer according to the invention or a copolymer used in accordance to the invention preferably has a number average molecular weight in the range of 1,000 to 50,000 g/mol, more preferably in the range of 2,000 to 20,000 g/mol, e.g. in the range of 2,500 to 4,000 g/mol. Very good results have also been achieved with a copolymer having a polydispersity (Mw/Mn) in the range of 1 -4, e.g. 1.1-2. The slip-and levelling agent may be a living copolymer, e.g. obtained by anionic polymerisation, atom transfer mechanism, nitroxide mediated techniques or other controlled polymerisation techniques. A benefit of a living copolymer is its tailor-made molecular architecture, combined with a narrower molecular weight distribution leading to smaller melting ranges and lower viscosities. Very good results have also been obtained with a copolymer in the form of a liquid or a solid (e.g. a powder), which is soluble in an organic solvent or in water, or made water-soluble after neutralization of acidic moieties. Such a system is particularly suitable for water-based systems. Suitable neutralizing agents for neutralising acidic moieties are e.g. dimethyl-ethanolamine, ammonia, other primary, secondary or tertiary amines or alkali hydroxides. An advantage of using a volatile amine neutralizing agent is that during the drying phase of a paint film, the amine neutralizing agent evaporates, leaving behind a more water resistant copolymer. In principle, the copolymer according to the invention may be prepared in any way, e.g. by a thermal radical, controlled radical, anionic or cationic polymerisation technique, of which the skilled professional will know how to employ them. The monomer employed are generally commercially available and/or may be prepared readily according to methods familiar to those skilled in the art. The perfluoroesters are commercially available or may be prepared according to WO03/033603 In order to prepare the leveling agent of the invention the monomers C are copolymerized with monomers A and B. e.g. using thermal random solution polymerisation or using controlled polymerisation. The invention further relates to compositions comprising a slip- and leveling agent according to the invention. Such a composition may, for example, further comprise one or more pigments, e.g. chosen from the group consisting of phthalocyanines, carbon black, titanium dioxide, ferrous oxides, alumino silicates, quinacridones, anthroquinones, diketopyrrolo-pyrrole, benzimidazolones and isoindolinones, one or more extenders, e.g. calcium carbonate, barium sulphate, silicium dioxide, alumium trihydoxide, organic fibres, glass and optionally one or more dispersants, e.g. polyurethane dispersants, polyester dispersants, polyacrylate dispersants, polyether derivatives, fatty acid derivatives, alkylsulphates. The slip-and leveling agents of the invention may very suitably be used in a dispersion, comprising 0-85 %, by weight, preferably 3 to 70%, of pigment and/or extender, 0.1 - 5% by weight, preferably 0.2 to 2% of a copolymer according to the invention, 10 - 95% by weight, preferably 25 to 40% of a resin, 0 - 90% by weight preferably 20 to 50% of water and/or non-aqueous liquid and 0 -15% by weight preferably 1 to 5% of dispersant. The invention will now be illustrated by some examples. Experimental: 1. Preparation of the terminal reactive polvsiloxane unit (intermediate) Intermediate A: Under a nitrogen atmosphere, maleic anhydride (3 g, 1,02 equivalent) and Silaplane FM-0411 (Mn ~ 1.000 g/mol, 30 g, 1 equivalent) were placed in a reactor at ambient temperature and heated to 120 °C in one hour. No solvent or catalyst were added. After three hours the intermediate A was obtained as a yellowish liquid. In a similar way the intermediates B and C were prepared: Intermediate B: 0,72 g of maleic anhydride, 36 g Silaplane FM-0421 (Mn ~ 5.000 g/mol), slightly yellowish liquid. Intermediate C: 0,6 g of maleic anhydride, 60 g Silaplane FM-0425 (Mn ~ 10.000 g/mol), almost colorless liquid. Commercially available silicones: Silaplane FM-0411: mono-hydroxyl functional polysiloxane with an average Mn of about 1.000 g/mol, originating from CHISSO CORPORATION Silaplane FM-0421: mono-hydroxyl functional polysiloxane with an average Mn of about 5.000 g/mol, originating from CHISSO CORPORATION Silaplane FM-0425: mono-hydroxyl functional polysiloxane with an average Mn of about 10.000 g/mol, originating from CHISSO CORPORATION Silaplane FM-0711: mono-methacrylic functional polysiloxane with an average Mn of about 1.000 g/mol, originating from CHISSO CORPORATION Silaplane FM-0721: mono-methacrylic functional polysiloxane with an average Mn of about 5.000 g/mol, originating from CHISSO CORPORATION Silaplane FM-0725: mono-methacrylic functional polysiloxane with an average Mn of about 10.000 g/mol, originating from CHISSO CORPORATION Silaplane TM-0701: mono-methacrylic functional polysiloxane with an average Mn of about 423 g/mol, originating from CHISSO CORPORATION Methacryl Siloxane SLM 446008-50: mono-methacrylic functional polysiloxane with an average Mn of about 4.000 g/mol, originating from WACKER CHEMIE GmbH X-24-8201: mono-methacrylic functional polysiloxane with an average Mn of about 2.100 g/mol, originating from SHIN-ETSU Chemicals Co., Ltd. X-22-174DX: mono-methacrylic functional polysiloxane with an average Mn of about 4.600 g/mol, originating from SHIN-ETSU Chemicals Co., Ltd. X-22-2426: mono-methacrylic functional polysiloxane with an average Mn of about 12.000 g/mol, originating from SHIN-ETSU Chemicals Co., Ltd. 2. Preparation of the Slip-and Leveling agent: Comparative example according to WO03/033603. Xylene (29,5 g) was placed in a three-necked flask under nitrogen atmosphere and heated to reflux (140 °C). The premix consisting of 40,00 g n-butyl acrylate, 13,33 g octyl acrylate, 10,Og of i-butyl methacrylate, 4,79 g cyclohexyl methacrylate 1,02 g of Zonyl Ba-L-maleate and 1,37 g of di-tert-butyl peroxide was metered in over the course of 3 hours. After addition of the premix, the reaction was carried out for 4 hours more at 140 °C. The solid content was corrected to 70 % by addition of xylene to obtain a yellowish clear liquid. In the following examples a similar polymerisation procedure was followed. Preparation of the slip-and leveling agent using controlled polymerisation General procedure for synthesis of acrylic polymers [Controlled polymers: examples 22-301: In a 3-necked 250ml round bottom flask with magnetic stirring bar, cooler, thermometer and septum 68,44 g n-butyl acrylate (128.17g/mol), 0.34g of perfluoroalkyl-modified maleate (described as intermediate G in WO03/033603, 1030 g/mol), 2,23 g regulator 1-(1»phenylethoxy)-2f3,6-trimethyl-2,6-diethyl-4oxopiperidine (317.48g/mol; described as compound 112 in GB 2335190) and methacrylic modified siloxanes (amount see table) were added, three times degassed with N2/vacuum and polymerized at 115 °C with a ramp of 20 °C under N2 until a conversion around 80% is reached. Residual monomers and were distilled of at 95°C and 12 mbar. The solid content was ajusted to 50 % by addition of xylene to obtain clear yellow liquids. Intermediate G in WO03/033603 is prepared as follows: Under a nitrogen atmosphere, maleic anhydride (5.66 g, 1 equivalent), xylene (60 g), Foralkyl® EON-6N-LW (54.83 g, MW ca. 475, 2 equivalents) and toluene-4-sulphonic acid (0.5 g) are refluxed. The reaction water is distilled off under azeotropic conditions. The esterification is complete when the calculated amount of reaction water is separated. After the solvent removal, the intermediate G is obtained as a yellowish wax. 2) Formulations for testing the silicone modified acrylic slip-and leveling agent Table 2 1 2 3 4 5 6 7 1) 2 pack PU (g) 74.00 73.82 73.63 73.45 73.26 72.89 72.52 2) Example 1 - 26 (g) 0.00 0.25 0.50 0.75 1.00 1.50 2.00 3) Desmodur N 75 (g) Polyisocyanate resin 26.00 25.94 25.87 25.81 25.74 25.61 25.48 Total 100.00 100.00 100.00 100.00 100.00 100.00 100.00 Position 1 till 3 will be mixed by spatula till homogeneous mixture. After mixing, let the samples rest for 1 hour before preparing the draw down. 3) Application, Prepare draw downs (75 µm) of the samples 1 till 7. 4) Results, Table 3; 1 = no craters; 8 = a lot of craters. Table 6 Dynamic COF comparative Ex.1 Ex.2 Ex.3 Ex.4 Ex.5 Ex.6 1) 0.25% 0.33 0.21 0.30 0.26 0.22 0.30 0.27 2) 0.5% 0.33 0.19 0.28 0.26 0.21 0.24 0.26 3) 1.0% 0.31 0.19 0.27 0.25 0.20 0.22 0.24 Dynamic COF Ex.7 Ex.8 Ex.9 Ex.10 Ex.11 Ex.12 Ex.13 1) 0.25% 0.24 0.25 0.27 0.29 0.25 0.26 0.24 2) 0.5% 0.23 0.24 0.25 0.29 0.22 0.22 0.23 3) 1.0% 0.22 0.26 0.23 0.28 0.23 0.20 0.23 I Dynamic COF Ex.14 Ex.15 Ex.16 Ex.17 Ex.18 Ex.19 Ex.20 1) 0.25% 0.29 0.28 0.23 0.24 0.27 0.28 0.25 2) 0.5% 0.28 0.26 0.21 0.23 0.27 0.26 0.22 3) 1.0% 0.26 0.25 0.20 0.22 0.26 0.24 0.22 Dynamic COF Ex.21 Ex.22 Ex.23 Ex.24 Ex.25 Ex.26 Ex.27 Ex.28 Ex.29 Ex.30 1) 0.25% 0.29 0,28 0,27 0,27 0,26 0.31 0.30 0.28 0.27 0.28 2) 0.5% 0.29 0,25 0,24 0,25 0,22 0.27 0.20 0.15 0.21 0.20 3) 1.0% 0.18 0,23 0,21 0,22 0,19 0.23 0.19 0.16 0.19 0.19 » Prepare draw downs (75 µm) of the shaken samples on glass plate. Flush off for 10 min. and bake draw down for 20 min. @ 135 °C . Cool down the glass panel. Add few drops of blue colorant to white stoving enamel with additive. Prepare over the white draw down a new draw down of the blue paint. Flush off for 10 min. and bake draw down for 30 min. @ 135 °C. Cool down the glass panel. Test intercoat adhesion by making use of the cross cutter. 1. A slip- and leveling agent characterized in that it comprises a copolymer which is obtained by copolymerizing A at least one unit of a mono- or di perfluoroester of an unsaturated dicarboxylic-acid; B at least one terminal reactive polysiloxane unit; C at least one alkyl(meth)acrylate unit or cycloalkyl(meth)acrylate unit and/or (meth)acrylic acid and/or other units originating from vinylic compounds that can form radicals. 2. A slip-and levelling agent according to claim 1, characterized in that it comprises a copolymer which is obtained by copolymerizing A 0.1-10 wt.% of a mono- or di perfluoroester of an unsaturated dicarboxylic-acid; B 1-20wt% of the terminal reactive polysiloxane compound; C 50-99wt% alkyl(meth)acrylate units and/or (meth)acrylic acid and/or other unit originating from vinylic compounds that can form radicals. consisting of H, CI, Br, I, C1-12 alkyls and OC1-12 alkyls, wherein 4 6. A slip-and levelling agent according to any one of claims 1-5, which is obtained by polymerizing A at least one unit of a mono- or di perfluoroester of maleic acid; B a mono-(meth)acrylic functional polydimethylsiloxane or a mono-maleic functional polydimethylsiloxane; and C an alkyl(meth)acrylate unit, cycloalkyl(meth)acrylate unit or a styrene unit. 7. Coating, printing ink or plastic compound comprising a slip- and leveling agent according to any of the claims 1-6, a pigment and optionally a dispersant. 8. A dispersion, comprising 0 - 85% by weight of pigment and/or extender, 0.1-5 % by weight of a copolymer according to any of the claims 1-6,10 - 95 % by weight of a resin, 0 - 90% by weight of water and/or non-aqueous liquid and 0 -15% by weight of dispersant. 9. The use of a copolymer obtainable as described in any one of claims 1-6 as siip-and levelling agent. 10. The use of a copolymer obtainable as described in any one of claims 1-6 as siip-and levelling agent for coatings, printing inks and plastics. Dated this 26 day of November 2007

Documents:

5352-CHENP-2007 CORRESPONDENCE OTHERS 13-01-2015.pdf

5352-CHENP-2007 AMENDED CLAIMS 15-12-2014.pdf

5352-CHENP-2007 AMENDED PAGES OF SPECIFICATION 15-12-2014.pdf

5352-CHENP-2007 FORM-1 15-12-2014.pdf

5352-CHENP-2007 POWER OF ATTORNEY 15-12-2014.pdf

5352-chenp-2007 correspondance others.pdf

5352-CHENP-2007 CORRESPONDENCE OTHERS 19-02-2014.pdf

5352-CHENP-2007 CORRESPONDENCE OTHERS 22-11-2013.pdf

5352-CHENP-2007 EXAMINATION REPORT REPLY RECEIVED 31-12-2014.pdf

5352-CHENP-2007 EXAMINATION REPORT REPLY RECIEVED 15-12-2014.pdf

5352-chenp-2007 form-18.pdf

5352-CHENP-2007 FORM-3 22-11-2013.pdf

5352-CHENP-2007 (FORM 13).pdf

5352-CHENP-2007 (FORM 3).pdf

5352-CHENP-2007 (HIGHLIGHTED FORMS 1 AND 5).pdf

5352-CHENP-2007 (PETITION FOR FORM 3).pdf

5352-CHENP-2007 (PETITION FOR POR).pdf

5352-CHENP-2007 AMENDED CLAIMS 04-02-2015.pdf

5352-CHENP-2007 EXAMINATION REPORT REPLY RECEIVED 04-02-2015.pdf

5352-CHENP-2007 FRESH FORMS 1 AND 5).pdf

5352-chenp-2007-abstract.pdf

5352-chenp-2007-claims.pdf

5352-chenp-2007-correspondnece-others.pdf

5352-chenp-2007-description(complete).pdf

5352-chenp-2007-form 1.pdf

5352-chenp-2007-form 26.pdf

5352-chenp-2007-form 3.pdf

5352-chenp-2007-form 5.pdf

5352-chenp-2007-pct.pdf