Title of Invention	"ELECTRICAL INSULATION FILM"
Abstract	The present invention relates to a capacitor film comprising a biaxially oriented polypropylene wherein a) said polypropylene has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and b) said polypropylene has an electrical breakdown strength EB63% according to IEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction and in transverse direction of 4.0.

Title of Invention

"ELECTRICAL INSULATION FILM"

Abstract

The present invention relates to a capacitor film comprising a biaxially oriented polypropylene wherein a) said polypropylene has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and b) said polypropylene has an electrical breakdown strength EB63% according to IEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction and in transverse direction of 4.0.

Full Text	Electrical isulation film The present invention relates to electrical insulation films, in particular capacitor films, and their use. Capacitor films must withstand extreme conditions like high temperatures and high electrical breakdown strength. Additionally it is appreciated that capacitor films possess good mechanical properties like a high stiffness. Up to now there is the prevailing opinion in the technical field of capacitor technology that high electrical breakdown strength can be only achieved with a low level of electrical conduction caused by residual metals such as titanium, aluminium and boron. However traditional polypropylenes produced with a Ziegler-Natta catalyst are contaminated with high amounts of residual catalyst components. To achieve the desired very low levels of impurities to make the polypropylene suitable for capacitor films, the polypropylenes must be troublesome washed, a process which is time consuming and cost-intensive. To overcome the washing step polypropylenes produced in the presence of supported single-site catalysts have been developed, as for instance described in WO 02/16455 Al, with low levels of impurities including metallic and non-metallic impurities, like aluminium, titanium, silicon, and halogen (such as CI and F). However to achieve this goal of low levels of impurities the process conditions must be controlled very carefully. Moreover such polypropylenes have the drawback that they cannot be processed in a stable way. In particular films based on polypropylenes produced in the presence of supported single-site catalysts suffer fix)m sagging and break easily when manufactured. Therefore the object of the present invention is to provide a capacitor film withstanding a high electric field strength without causing failure of the same and said film having in particular good mechanical properties, such as a high stiffness. Preferably such a capacitor film has additionally a high temperature resistance. The present invention is based on the finding that an improved breakdown behaviour can be acconpJished by using a polypropylene for the capacitor film featured by a rather high amount of thin lamellae determined by stepwise isothermal segregation technique (SIST). Such a capacitor film reaches a balance of high thermal resistance, high electrical breakdown strength and good mechanical properties. It has been in particular found out that the good properties can be achieved independently fk>m the amount of impurities present, i.e. whether the polypropylene comprises rather high amounts of aluminium, titanium, silicon, halogen (such as CI and F) and/or boron. Accordingly, the object outlined above is solved by providing a capacitor film comprising a biaxially oriented polypropylene wherein a) said polypropylene has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction of 4.0 and at a draw ratio in transverse direction of 4.0. Preferably the capacitor film is further characterized that said film and/or the polypropylene of said film has/have xylene solubles of some extent, i.e. of at least 0.50 wt.-%. Moreover it is preferred, that the biaxially oriented polypropylene as defined in the instant invention is the only polymer component of the capacitor film. Such capacitor films have superior properties compared to the films known in the art. Especially, the inventive capacitor films have high values of electrical breakdown strength also in case relatively high amounts of impurities are present in the film. Thus no troublesome washing steps are necessary as with polypropylenes known in the art. Moreover the capacitor films according to this invention have in addition a high temperature resistance and are obtainable at high process stability and low process temperature. Moreover and surprisingly the inventive film has in addition good mechanical properties at a high stiffness expressed in tensile modulus. Additionally it has been observed that the new capacitor films according to this invention show a significant increase of electrical breakdown strength with increasing the draw ratio. A first requirement of the present invention is that the polypropylene of the capacitor film is biaxially oriented, i.e. has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0. Such ratios are appreciated as commercial biaxially oriented polypropylene films must be stretchable at least to the above defined extent without breaking. The length of the sample increases during stretching in longitudinal direction and the draw ratio in longitudinal direction calculates from the ratio of current length over original sample length. Subsequently, the sample is stretched in transverse direction where the width of the sample is increasing. Hence, the draw ratio calculates from the current width of the sample over the original width of the sample. Preferably the draw ratio in machine direction of the biaxially oriented polypropylene ranges ftom 4.0 to 8.0, more preferably from 4.5 to 6.5. The draw ratio in transverse direction of the biaxially polypropylene ranges preferably from 6.0 to 10.0, more preferably from 7.0 to 9.5. In a preferred embodiment the biaxially polypropylene has a draw ratio in machine direction fix)m, 4.5 to 7.0. in particular from 4.5 to 5.0, and a draw ratio in transverse direction from 6.0 to 10.0, in particular from 8.0 to 10. To obtain such a biaxially polypropylene preferably a process is applied as described below in the instant invention. The second requirement of the present invention is, that the biaxiaily polypropylene and/or said capacitor film has(have) a rather high electrical breakdown strength EB63%, i.e. an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm, at a draw ratio in machine direction and in transverse direction of 4.0. More preferably the electrical breakdown strength EB63% of the biaxiaily polypropylene and/or said capacitor film at a draw ratio in machine direction and in transverse direction of 4.0 is(are) at least 350 kV/mm, still more preferably at least 400 kV/mm and yet more preferably at least 430 kV/mm. Further details about the measurement of the electrical breakdown strength are provided below in the examples. As stated above, the biaxiallly polypropylene is in particular characterized in that the electrical breakdown strength EB63% of the bixially oriented polypropylene disproportionately increases with increase of the stretching ratio, as can be seen in figure 2. Thus it is preferred that the electrical breakdown strength EB63% of the biaxiaily oriented polypropylene and/or of the capacitor film at a draw ratio in machine direction and in transverse direction of 5.0 is(are) at least 500 kV/mm, still more preferably at least 550 kV/mm and yet more preferably at least 580 kV/mra Moreover it is preferred that the capacitor film and/or the polypropylene of said capacitor film has/have xylene solubles of some extent, i.e. of at least 0.50 wt.-%. Xylene solubles are the part of the polymer soluble in cold xylene determined by dissolution in boiling xylene and letting the insoluble part crystallize from the cooling solution (for the method see below in the experimental part). The xylene solubles fraction contains polymer chains of low stereo-regularity and is an indication for the amount of non-crystalline areas. Preferably, the polypropylene component of the film has xylene solubles of more than 0.60 wt.-%. On the other hand, the amount of xylene solubles should not be too high since they represent a potential contamination risk. Accordingly it is preferred that the xylene solubles are not more than 1.00 wt.-% and still more preferably not more than 0.90 wt.-%. In preferred embodiments the xylene solubles are in the range of 0.60 to 1.00 wt.-% and more preferably in the range of 0.60 to 0.90 wt.-%. Preferably, the capacitor film has xylene solubles of more than 0.60 wt.-%. Even more preferred, the capacitor film has xylene solubles of not more than 1.00 wt.-% and more preferably of not more than 0.90 wt.-%. In particular, the film has xylene solubles in the range of 0.60 wt.-% to 1.00 wt.% and more preferably of 0.60 wt.-% to 0.90 wt.-%. Moreover it is preferred that the capacitor film according to this invention is further specified by its lamellar thickness distribution (see figure 7). It has been recognized that higher electrical breakdown strength is achievable in case the polymer comprises rather high amounts of thin lamellae. Thus the acceptance of the film as a capacitor film is independent fix)m the amounts of impurities present in the polypropylene but fix)m its crystalline properties. The stepwise isothermal segregation technique (SIST) provides a possibiUty to determine the lamellar thickness distribution. The exact method is defined in the example section. In the instant invention under lamellar thickness is understood the lamellar thickness of the polymer measured according to the stepwise isothermal segregation technique (SIST) method as defined in the example section. Rather high amounts of polymer fi:actions crystallizing at lower temperatures indicate a rather high amount of thin lamellae. Thus the inventive capacitor film and/or the polypropylene of the film is(are) characterized by a rather high amount of thin lamellae; i.e. a rather high amount of lamellae having a thickness of Accordingly it is preferred that the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 20 wt.-%, more preferred at least 30 wt.-%, yet more preferred at least 35 wt.-%, still more preferred at least 40 wt.-%, still yet more preferred at least 45 vvt.-% and most preferred at least 50 wt.-%, of a fi-action of lamellae with a thickness of More precisely and preferably the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 12 wt.-%, more preferably at least 20 wt.-%, yet more preferably of at least 25 wt.-%, of a fraction of lamellae in the range of 5.55 nm to 7.19 nm. Furthermore it is preferred that the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 5 wt.-%, more preferably at least 7 wt.-%, yet more preferably of at least 10 wt.-%, of a fraction of lamellae in the range of 4.52 nm to 5.55 nm. Thus it is preferred that the inventive capacitor fihn and/or the polypropylene of the fihn (a) comprise(s) at least 20 wt.-%, more preferred at least 30 wt.-%, yet more preferred at least 35 wt.-%, still more preferred at least 40 wt.-%, still yet more preferred at least 45 wt.-% and most preferred at least 50 wt.-%, of a fraction of lamellae with a thickness of (b) said fraction of lamellae with a thickness of (c) at least 5 wt.-%, more preferably at least 7 wt.-%, yet more preferably of at least 10 wt.-%, of a fraction of lamellae in the range of 4.52 nm to 5.55 nm The method for determining the lamellar thickness distribution is described in detail in the example section. The weight percentages are based on the total amount of capacitor film and/or the polypropylene measured by SIST. The molecular weight distribution (MWD) is expressed as the ratio of weight average molecular weight (Mw) and number average molecular weight (Mn). The number average molecular weight (M„) Is an average molecular weight of a polymer expressed as the first moment of a plot of the number of molecules in each molecular weight range against the molecular weight. In effect, this is the total molecular weight of all molecules divided by the number of molecules. In turn, the weight average molecular weight (Mw) is the first moment of a plot of the weight of polymer in each molecular weight range against molecular weight. The number average molecular weight (M„) and the weight average molecular weight (Mw) as well as the molecular weight distribution (MWD) are determined by size exclusion chromatography (SEC) using Waters Alliance GPCV 2000 instrument with online viscometer. The oven temperature is 140 °C. Trichlorobenzene is used as a solvent (ISO 16014). It is preferred that the capacitor film of the present invention comprises a polypropylene which has a weight average molecular weight (Mw) fi'om 10,000 to 2,000,000 &'mol, more preferably from 20,000 to 1,500,000 g/mol. The number average molecular weight (M„) of the polypropylene is preferably in the range of 5,000 to 750,000 g/mol, more preferably from 10,000 to 750,000 g/mol. As a broad molecular weight distribution (MWD) improves the piocessability of the polypropylene the molecular weight distribution (MWD) is preferably up to 20.00, more preferably up to 10.00, still more preferably up to 8.00. However a rather broad molecular weight distribution stimulates sagging. Therefore, in an alternative embodiment the molecular weight distribution (MWD) is preferably between 1.00 to 8.00, still more preferably in the range of 1.00 to 4.00, yet more preferably in the range of 1.00 to 3.50. Furthermore, it is preferred that the polypropylene component of the film of the present invention has a melt flow rate (MFR) given in a specific range. The melt flow rate mainly depends on the average molecular weight. This is due to the fact that long molecules render the material a lower flow tendency than short molecules. An increase in molecular weight means a decrease in the MFR-value. The melt flow rate (MFR) is measured in g/10 min of the polymer discharged through a defined die under specified temperature and pressure conditions and the measure of viscosity of the polymer which, in turn, for each type of polymer is mainly influenced by its molecular weight but also by its degree of branching. The melt flow rate measured under a load of 2.16 kg at 230 °C (ISO 1133) is denoted as MFR2. Accordingly, it is preferred that in the present invention the capacitor film comprises a polypropylene which has an MFR2 up to 10.00 g/lOmin, more preferably up to 6.00 g/lOmin. In another preferred embodiment the polypropylene has MFR2 up to 4 g/lOmin. A preferred range for the MFR2 is 1.00 to 10.00 g/10 min, more preferably in the range of 1.00 to 8.00 g/IOmin, yet more preferably in the range of 1.00 to 6.00 g/lOmin. As cross-linking has a detrimental effect on the extensional flow properties it is preferred that the polypropylene according to this invention is non-cross-linked. More preferably, the polypropylene of the film according to this invention shall have a rather high isotacticity measured by meso pentad concentration (also referred herein as pentad concentration), i.e. higher than 91 %, more preferably higher than 93 %, still more preferably higher than 94 % and most preferably higher than 95 %. On the other hand pentad concentration shall be not higher than 99.5 %. The pentad concentration is an indicator for the narrowness in the regularity distribution of the polypropylene and measured by NMR-spectroscopy. In addition, it is preferred that the polypropylene of the capacitor film has a melting temperature Tm of higher than 148 °C, more preferred higher than 150 °C. In a preferred embodiment, melting temperature Tm of the polypropylene component is higher than 148 °C but below 156 °C. The measuring method for the melting temperature Tm is discussed in the example section. The melting temperature Tm of the capacitor film is preferably at least 148 °C, more preferably at least 150 °C. In a preferred embodiment, the melting temperature Tm of the capacitor film is higher than 150°C but below 160°C. Furthermore a rather high tensile modulus at a draw ratio of 4 in machine direction and a draw ratio of 4 in transverse direction is appreciated since biaxially oriented polypropylene fihns commercially are stretched with a draw ratio of 4 to 8, more preferably 4 to 6, in machine direction and with a draw ratio of 5 to 10, more preferably of 6 to 8, in transverse direction. Thus the polypropylene component of the film of the present invention has a tensile modulus of at least 800 MPa, measured according to ISO 527-3 at a cross head speed of Imm/min (with thickness of 100 \|4,m). More preferably, the polypropylene component has a tensile modulus of at least 850 MPa, even more preferably 900 MPa, and yet more preferably at least 1000 MPa. Preferably, the biaxially oriented polypropylene film of the present invention has a tensile modulus of at least 1800 MPa at a draw ratio of 4.0 in machine direction and in transverse direction, wherein the tensile modulus is measured according to ISO 527-3 at a cross head speed of Imm/min (exact measuring method is provided in the example section). More preferably, the polypropylene film has a tensile modulus of at least 1900 MPa, even more preferably 1950 MPa, and most preferably at least 2200 MPa at a draw ratio of 4.0 in machine direction and in transverse direction. In a preferred embodiment, the film has a stretching stress of at least 2.5 MPa in machine direction and at least 2.5 MPa in transverse direction at a stretching temperature of 152 °C or less and a draw ratio of 4 in machine direction and in transverse direction. Preferably, the stretching temperature mentioned above is at least 2°C, more preferably at least 3°C below the melting temperature of the film. In addition it is appreciated that the inventive capacitor film has good optical properties. Thus it is preferred that capacitor film has a haze of not more than 15, still more preferred not more than 10 measured according to ASTM D 1003-92 (exact measuring method is provided in the example section). In turn the transparency of the film shall be rather high. Thus it is preferred that the capacitor film has a transparency of at least 90 % measured according to ASTM D 1003-92. Preferably the polypropylene of the film according to this invention has low levels of impurities, i.e. low levels of aluminium (Al) residue and/or low levels of silicon residue (Si) and/or low levels of boron (B) residue. Accordingly the aluminium residues of the polypropylene can be lowered to a level of 12.00 ppm. Thus the aluminium residue content of the polypropylene of the film according to this invention is preferably below 20 ppm, more preferably below 18 ppm and yet more preferably 15 ppm. Preferred ranges of aluminium residues are 12 to 20 ppm, more preferred 12 to 18 ppm and yet more preferred 12 to 15 ppm. As stated above the polypropylene of the film according to this invention may comprise low values of silicon residue (Si) and/or boron (B) residue, i.e. below 40 ppm, more preferably below 20 ppm, yet more preferably below 10 ppm. Hence in one preferred embodiment the film according to this invention comprises a polypropylene which is preferably essentially free of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section). Further it is preferred that the polypropylene of the film according to this invention is free of titanium and/or magnesium residues. In other words the polypropylene according to this invention has been preferably not produced with a catalyst system comprising titanium and/or magnesium. On the other hand the properties of this invention are not detrimentally influenced by the presence of residues.. In another preferred embodiment the polypropylene of the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.10 ppm of boron residues and/or silicon residues, still more preferably in amounts of more than 0.20 ppm of boron residues and/or silicon residues, yet more preferably in amounts of more than 0.50 ppm of boron residues and/or silicon residues. In still another preferred embodiment the polypropylene component of the film according to this invention comprises Al residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm, yet more preferred in an amount of more than 25.00 ppm. In yet another prefeiTcd embodiment the polypropylene component of the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.20 ppm of boron residues and/or silicon residues, and aluminium residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm. Moreover preferably the capacitor film according to this invention has low levels of impurities, i.e. low levels of aluminium (Al) residue and/or low levels of silicon residue (Si) and/or low levels of boron (B) residue. Accordingly the aluminium residues of the film can be lowered to a level of 12.00 ppm. Thus the aluminium residue content of the film according to this invention is preferably below 20 ppm, more preferably below 18 ppm and yet more preferably 15 ppm. Preferred ranges of aluminium residues are 12 to 20 ppm, more preferred 12 to 18 ppm and yet more preferred 12 to 15 ppm. As stated above the film according to this invention may comprise low values of silicon residue (Si) and/or boron (B) residue, i.e. below 40 ppm, more preferably below 20 ppm, yet more preferably below 10 ppm. Hence in one preferred embodiment the film according to this invention is preferably essentially fi-ee of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section). Further it is preferred that the film according to this invention is fi-ee of titanium and/or magnesium residues. In other words the polypropylene according to this invention has been preferably not produced with a catalyst system comprising titanium and/or magnesium. On the other hand the properties of this invention are not detrimentally influenced by the presence of residues. Hence in one preferred embodiment the film according to this invention is preferably essentially fi-ee of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section). In another preferred embodiment the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.10 ppm of boron residues and/or silicon residues, still more preferably in amounts of more than 0.20 ppm of boron residues and/or silicon residues, yet more preferably in amounts of more than 0.50 ppm of boron residues and/or silicon residues. In still another preferred embodiment the film according to this invention comprises Al residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm. In yet another preferred embodiment the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.20 ppm of boron residues and/or silicon residues, and aluminium residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm. In a preferred embodiment the polypropylene as defmed above (and fiirther defined below) is preferably unimodal. In another preferred embodiment the polypropylene as defined above (and further defined below) is preferably multimodal, more preferably bimodal. "Muhimodal" or "multimodal distribution" describes a frequency distribution that has several relative maxima (contrary to unimodal having only one maximum). In particular, the expression "modality of a polymer" refers to the forai of its molecular weight distribution (MWD) curve, i.e. the appearance of the graph of the polymer weight fraction as a function of its molecular weight. If the polymer is produced in the sequential step process, i.e. by utilizing reactors coupled in scries, and using different conditions in each reactor, the different polymer fractions produced in the different reactors each have their own molecular weight distribution which may considerably differ from one another. The molecular weight distribution curve of the resulting final polymer can be seen at a super-imposing of the molecular weight distribution curves of the polymer fraction which will, accordingly, show a more distinct maxima, or at least be distinctively broadened compared with the curves for individual fractions. A polymer showing such molecular weight distribution curve is called bimodal or multimodal, respectively. In case the polypropylene of the capacitor film is not unimodal it is preferably bimodal. The polypropylene of the film according to this invention can be a homopolymer or a copolymer. In case the polypropylene is unimodal the polypropylene is preferably a polypropylene homopolymer. In turn in case the polypropylene is multimodal, more preferably bimodal, the polypropylene can be a polypropylene homopolymer as well as a polypropylene copolymer. However it is in particular preferred that in case the polypropylene is multimodal, more preferably bimodal, the polypropylene is a polypropylene homopolymer. Furthermore it is preferred that at least one of the fractions of the multimodal polypropylene is a polypropylene according to this invention, more preferably a polypropylene homopolymer according to the instant invention. The polypropylene of the capacitor film according to this invention is most preferably a unimodal polypropylene homopolymer. The expression polypropylene homopolymer as used in this invention relates to a polypropylene that consists substantially, i.e. of at least 97 wt%, preferably of at least 99 wt%, and most preferably of at least 99.8 wt% of propylene units. In a preferred embodiment only propylene units in the polypropylene homopolymer are detectable. The comonomcr content can be measured with FT infrared spectroscopy. Further details are provided below in the examples. Further it is preferred that the polypropylene of the instant invention is free of units derived from 3-branched a-olefins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms. Even more preferred the inventive film comprises a propylene homopolymer, i.e. firee of units derived from 3-branched a-olefins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms. In case a propylene copolymer is used, than it is preferred that the copolymer is free of units derived from 3-branched a-olcfins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms. In case the polypropylene of the film according to this invention is a multimodal or bimodal polypropylene copolymer, it is preferred that the comonomer is ethylene. However, also other comonomers known in the art are suitable. Preferably, the total amount of comonomer, more preferably ethylene, in the propylene copolymer is up to 30 wt%, more preferably up to 25 wt%. In a preferred embodiment, the multimodal or bimodal polypropylene copolymer is a polypropylene copolymer comprising a polypropylene homopolymer matrix being a polypropylene as defined above and an ethylene-propylene rubber (EPR). The polypropylene homopolymer matrix can be unimodal or multimodal, i.e. bimodal. However it is preferred that polypropylene homopolymer matrix is unimodal. Preferably, the ethylene-propylene rubber (EPR) in the total multimodal or bimodal polypropylene copolymer is up to 50 wt%. More preferably the amount of ethylene-propylene rubber (EPR) in the total multimodal or bimodal polypropylene copolymer is in the range of 10 to 40 wt%, still more preferably in the range of 10 to 30 wt%. In addition, it is preferred that the multimodal or bimodal polypropylene copolymer comprises a polypropylene homopolymer matrix being a polypropylene as defined above and an ethylene-propylene rubber (EPR) with an ethylene-content of up to 50 wt%. In addition, it is preferred that the polypropylene as defined above is produced in the presence of the catalyst as defined below. Furthermore, for the production of the polypropylene as defined above, the process as stated below is preferably used. Moreover from the above defined and further defined capacitor films are preferably the following two embodiments disclaimed: (A) A capacitor film comprising a biaxially oriented polypropylene a) said polypropylene has a draw ratio in machine direction and transverse direction of 4, and b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of 291 or 388 kV/mm at a draw ratio in machine direction and in transverse direction of 4. (B) A capacitor film comprising a biaxially oriented polypropylene a) said polypropylene has a draw ratio in machine direction and transverse direction of 5, and b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of 638 kV/mm at a draw ratio in machine direction and in transverse direction of 5. The polypropylene of the capacitor film according to this invention has been in particular obtained by a new catalyst system. This new catalyst system comprises a symmetric catalyst, whereby the catalyst system has a porosity of less than 1.40 ml/g, more preferably less than 1.30 ml/g and most preferably less than 1.00 ml/g. The porosity has been measured according to DIN 66135 (Na). In another preferred embodiment the porosity is not detectable when determined with the method applied according to DIN 66135 (N2). A symmetric catalyst according to this invention is a mctallocene compound having a C2-symetry. Preferably the Ca-symetric mctallocene comprises two identical organic ligands, still more preferably comprises only two organic ligands which are identical, yet more preferably comprises only two organic ligands which are identical and linked via a bridge. It Is preferred that the rac : meso ratio of the mctallocene compound of the instant invention is at least 20 :1, i.e. 95 % rac. Said symmetric catalyst is preferably a single site catalyst (SSC). Due to the use of the catalyst system with a very low porosity comprising a symmetric catalyst the manufacture of the above defined short-chain branched polypropylene is possible. Furthermore it is preferred, that the catalyst system has a surface area of of lower than 25 mVg, yet more preferred lower than 20 mVg, still more preferred lower than 15 mVg, yet still lower than 10 mVg and most preferred lower than 5 mVg. The surface area according to this invention is measured according to ISO 9277 (N2). It is in particular preferred that the catalytic system according to this invention comprises a symmetric catalyst, i.e. a catalyst as defined above and in further detail below, and has porosity not detectable when applying the method according to DIN 66135 (N2) and has a surface area measured according to ISO 9277 (N2) of less than 5 mVg. Preferably the symmetric catalyst compound, i.e. the C2-symetric metallocene, has the formula (I): (Cp)2R,MX2 (1) wherein M is Zr, Hf or Ti, more preferably Zr, and X is independently a monovalent anionic ligand, such as o-ligand R is a bridging group linking the two Cp ligands Cp is an organic ligand selected from the group consisting of unsubstituted cyclopentadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl, unsubstituted fluorenyl, substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted fluorenyl, with the proviso that both Cp-ligands are selected from the above stated group and both Cp-ligands are chemically the same, i.e. are identical. The term "cr-ligand" is understood in the whole description in a known manner, i.e. a group bonded to the metal at one or more places via a sigma bond. A prefcn'cd monovalent anionic ligand is halogen, in particular chlorine (CI). Preferably, the symmetric catalyst is of formula (I) indicated above, wherein M is Zr and each X is CI. Preferably both identical Cp-ligands are substituted. The optional one or more substituent(s) bonded to cyclopentadienyl, indenyl, tetrahydroindenyl, or fluorenyl may be selected from a group including halogen, hydrocarbyl (e.g. Cj-Cao-alkyl, C2-C2o-alJ More preferably both identical Cp-ligands are indenyl moieties wherein each indenyl moiety bear one or two substituents as defined above. More preferably each of the identical Cp-ligands is an indenyl moiety bearing two substituents as defined above, with the proviso that the substituents are chosen in such are manner that both Cp-ligands are of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety. Still more preferably both identical Cp's are indenyl moieties wherein the indenyl moieties comprise at least at the five membered ring of the indenyl moiety, more preferably at 2-position, a substituent selected from the group consisting of alkyl, such as Ci-Cd alkyl, e.g. methyl, ethyl, isopropyl, and trialkyloxysiloxy, wherein each alkyl is independently selected from Ci-Cg alkyl, such as methyl or ethyl, with proviso that the indenyl moieties of both Cp are of the same chemical structure, i.e both Cp-Iigands have the same substituents bonded to chemically the same indenyl moiety. Still more preferred both identical Cp are indenyl moieties wherein the indenyl moieties comprise at least at the six membered ring of the indenyl moiety, more preferably at 4-position, a substituent selected from the group consisting of a C6-C20 aromatic ring moiety, such as phenyl or naphthyl, preferably phenyl, which is optionally substituted with one or more substitutents, such as Ci-Cg alkyl, and a heteroaromatic ring moiety, with proviso that the indenyl moieties of both Cp are of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety. Yet more preferably both identical Cp are indenyl moieties wherein the indenyl moieties comprise at the five membered ring of the indenyl moiety, more preferably at 2-position, a substituent and at the six membered ring of the indenyl moiety, more preferably at 4-position, a further substituent, wherein the substituent of the five membered ring is selected from the group consisting of alkyl, such as Ci-Ce alkyl, e.g. methyl, ethyl, isopropyl, and trialkyloxysiloxy and the further substituent of the six membered ring is selected from the group consisting of a Ce-Cjo aromatic ring moiety, such as phenyl or naphthyl, preferably phenyl, which is optionally substituted with one or more substituents, such as Ci-Ce alkyl, and a heteroaromatic ring moiety, with proviso that the indenyl moieties of both Cp's arc of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety. Conceming the moiety "R" it is preferred that "R" has the formula (II) -Y(R02- (11) wherein Y is C, Si or Ge, and R' is Ci to C20 alkyl, Ci-Cjz aryl, or C7-C12 arylalkyl or trimethylsilyl. In case both Cp-ligands of the symmetric catalyst as defined above, in particular case of two indenyl moieties, are linked with a bridge member R, the bridge member R is typically placed at 1-position. The bridge member R may contain one or more bridge atoms selected from e.g. C, Si and/or Ge, preferably from C and/or Si. One preferable bridge R is -Si(R')2-, wherein R' is selected independently from one or more of e.g. trimethylsilyl, Ci-Cio alkyl, C1-C20 alkyl, such as Ce-Cn aryl, or C7-C-,o, such as C7-C12 arylalkyl, wherein alkyl as such or as part of arylalkyl is preferably C1-C6 alkyl, such as ethyl or methyl, preferably methyl, and aryl is preferably phenyl. The bridge -Si(R')2- is preferably e.g. -Si(Ci-C6 alkyl)2- -Si(phenyl)2- or -Si(Ci-Ce alkyl)(phenyl)-, such as -Si(Me)2-. In a preferred embodiment the symmetric catalyst, i.e. the C2-symetric metallocene, is defined by the formula (III) (Cp)2R,ZrCl2 (III) wherein both Cp coordinate to M and are selected from the group consisting of unsubstituted cyclopentadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl, unsubstituted fluorenyl, substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted fluorenyl, with the proviso that both Cp-ligands are chemically the same, i.e. are identical, and R is a bridging group linking two ligands L, wherein R is defined by the formula (II) -Y(R')2- (II) wherein Y is C, Si or Ge, and R' is Ci to C20 alkyl, Cc-Cn aryl, or C7-C12 arylalkyl. More preferably the symmetric catalyst is defined by the formula (III), wherein both Cp are selected from the group consisting of substituted cyclopentadienyl, substituted indcnyl, substituted tetrahydroindenyl, and substituted fluorenyl. In a preferred embodiment the symmetric catalyst is dimethylsilandiylbis(2-methyl-4-phenyl-indenyl)zirkonium dichloride. More preferred said symmetric catalyst is non-silica supported. The above described symmetric catalyst components are prepared according to the methods described in WO 01/48034. It is in particular preferred that the symmetric catalyst is obtainable by the emulsion solidification technology as described in WO 03/051934. This document is herewith included in its entirety by reference. Hence the sjmimetric catalyst is preferably in the form of solid catalyst particles, obtainable by a process comprising the steps of a) preparing a solution of one or more symmetric catalyst components; b) dispersing said solution in a solvent immiscible therewith to form an emulsion in which said one or more catalyst components are present in the droplets of the dispersed phase, c) solidifying said dispersed phase to convert said droplets to solid particles and optionally recovering said particles to obtain said catalyst. Preferably a solvent, more preferably an organic solvent, is used to form said solution. Still more preferably the organic solvent is selected from the group consisting of a linear atkane, cyclic alkane, linear alkene, cyclic alkene, aromatic hydrocarbon and halogen-containing hydrocarbon. Moreover the immiscible solvent forming the continuous phase is an inert solvent, more preferably the immiscible solvent comprises a fluorinated organic solvent and/or a flmctionalized derivative thereof, still more preferably the immiscible solvent comprises a semi-, highly- or perfluorinated hydrocarbon and/or a functionalizcd derivative thereof. It is in particular preferred, that said immiscible solvent comprises a perfluorohydrocarbon or a functionalizcd derivative thereof, preferably C3-C30 perfluoroalkanes, -alkenes or -cycloalkanes, more preferred C4-C10 perfluoro-alkanes, -alkenes or -cycloalkanes, particularly preferred perfluorohexane, perfluoroheptanc, pcrfluorooctanc or perfluoro (methylcyclohcxane) or a mixture thereof. Furthermore it Ls preferred that the emulsion comprising said continuous phase and said dispersed phase is a bi-or multiphasic system as known in the art. An emulsifier may be used for forming the emulsion. After the formation of the emulsion system, said catalyst is formed in situ from catalyst components in said solution. In principle, the emulsifying agent may be any suitable agent which contributes to the formation and/or stabilization of the emulsion and which does not have any adverse effect on the catalytic activity of the catalyst. The emulsifying agent may e.g. be a surfactant based on hydrocarbons optionally interrupted with (a) heteroatom(s), preferably halogenated hydrocarbons optionally having a functional group, preferably semi-, highly- or perfluorinated hydrocarbons as known in the art. Alternatively, the emulsifying agent may be prepared during the emulsion preparation, e.g. by reacting a surfactant precursor with a compound of the catalyst solution. Said surfactant precursor may be a halogenated hydrocarbon with at least one fijnctional group, e.g. a highly fluorinated C\ to C30 alcohol, which reacts e.g. with a cocatalyst component, such as aluminoxane. In principle any solidification method can be used for forming the solid particles from the dispersed droplets. According to one preferable embodiment the solidification is effected by a temperature change treatment. Hence the emulsion subjected to gradual temperature change of up to 10 °C/min, preferably 0.5 to 6 °C/min and more preferably 1 to 5 °C/min. Even more preferred the emulsion is subjected to a temperature change of more than 40 °C, preferably more than 50 °C within less than 10 seconds, preferably less than 6 seconds. The recovered particles have preferably an average size range of 5 to 200 \|.im, more preferably 10 to 100\|am. Moreover, the form of solidified particles have preferably a spherical shape, a predetermined particles size distribution and a surface area as mentioned above of preferably less than 25 mVg, still more preferably less than 20 m^/g, yet more preferably less than 15 m^/g, yet still more preferably less than 10 mVg and most preferably less than 5 mVg, wherein said particles arc obtained by the process as described above. For further details, embodiments and examples of the continuous and dispersed phase system, emulsion formation method, emulsifying agent and solidification methods reference is made e.g. to the above cited international patent application WO 03/051934. The above described symmetric catalyst components are prepared according to the methods described in WO 01/48034. As mentioned above the catalyst system may further comprise an activator as a cocatalyst, as described in WO 03/051934, which is enclosed herein with reference. Preferred as cocatalysts for metallocenes and non-metallocenes, if desired, are the aluminoxanes, in particular the Ci-Cio-alkylaluminoxanes, most particularly methylaluminoxane (MAO). Such aluminoxanes can be used as the sole cocatalyst or together with other cocatalyst(s). Thus besides or in addition to aiuminoxanes, other cation complex forming catalysts activators can be used. Said activators are commercially available or can be prepared according to the prior art literature. Further aluminoxane cocatalysts are described i.a. in WO 94/28034 which is incorporated herein by reference. These are linear or cyclic oligomers of having up to 40, preferably 3 to 20, -(A1(R"')0)- repeat units (wherein R'" is hydrogen, Ci-Cio-alkyl (preferably methyl) or C6-Ci8-aryl or mixtures thereof)- The use and amounts of such activators are within the skills of an expexl in the field. As an example, with the boron activators, 5:1 to 1:5, preferably 2:1 to 1:2, such as 1:1, ratio of the transition metal to boron activator may be used. In case of preferred aiuminoxanes, such as methylaluminumoxane (MAO), the amount of Al, provided by aluminoxane, can be chosen to provide a molar ratio of Al:transition metal e.g. in the range of 1 to 10 000, suitably 5 to 8000, preferably 10 to 7000, e.g. 100 to 4000, such as 1000 to 3000. TVpically in case of solid (heterogeneous) catalyst the ratio is preferably below 500. The quantity of cocatalyst to be employed in the catalyst of the invention is thus variable, and depends on the conditions and the particular transition metal compound chosen in a manner well known to a person skilled in the art. Any additional components to be contained in the solution comprising the organotransition compound may be added to said solution before or, alternatively, after the dispersing step. Furthermore, the present invention is related to the use of the above-defined catalyst system for the production of a polypropylene according to this invention. In addition, tlie present invention is related to tiie process for producing the inventive capacitor film comprising the polypropylene, whereby the catalyst system as defined above is employed. Furthermore it is preferred that the process temperature is higher than 60 °C. Preferably, the process is a multi-stage process to obtain multimodal polypropylene as defined above. Multistage processes include also bulk/gas phase reactors known as multizone gas phase reactors for producing multimodal propylene polymer. A preferred multistage process is a "loop-gas phase"-process, such as developed by Boreal is A/S, Denmark (known as BORSTAR® technology) described e.g. in patent literature, such as in EP 0 887 379 or in WO 92/12182. Multimodal polymers can be produced according to several processes which are described, e.g. in WO 92/12182, EP 0 887 379 and WO 97/22633. A multimodal polypropylene according to this invention is produced preferably in a multi-stage process in a muhi-stage reaction sequence as described in WO 92/12182. The contents of this document are included herein by reference. It has previously been known to produce multimodal, in particular bimodal, polypropylene in two or more reactors connected in series, i.e. in different steps (a) and (b). According to the present invention, the main polymerization stages are preferably carried out as a combination of a bulk polymerization/gas phase polymerization. The bulk polymerizations are preferably performed in a so-called loop reactor. In order to produce the multimodal polypropylene according to this invention, a flexible mode is preferred. For this reason, it is preferred that the composition be produced in two main polymerization stages in combination of loop reactor/gas phase reactor. Optionally, and preferably, the process may also comprise a prepolymerization step in a manner known in the field and which may precede the polymerization step (a). If desired, a further elastomeric comonomer component, so called ethylene-propylene rubber (EPR) component as in this invention, may be incorporated into the obtained polypropylene homopolymer matrix to form a propylene copolymer as defined above. The ethylene-propylene rubber (EPR) component may preferably be produced after the gas phase polymerization step (b) in a subsequent second or further gas phase polymerizations using one or more gas phase reactors. The process is preferably a continuous process. Preferably, in the process for producing the propylene polymer as defined above the conditions for the bulk reactor of step (a) may be as follows: the temperature is within the range of 40 °C to 110 °C, preferably between 60 °C and 100 "0,70 to 90 °C, the pressure is within the range of 20 bar to 80 bar, preferably between 30 bar to 60 bar, hydrogen can be added for controlling the molar mass in a manner known per se. Subsequently, the reaction mixture from the bulk (bulk) reactor (step a) is transferred to the gas phase reactor, i.e. to step (b), whereby the conditions in step (b) are preferably as follows: the temperature is within the range of 50 °C to 130 °C, preferably between 60 °C and 100 °C, the pressure is within the range of 5 bar to 50 bar, preferably between 15 bar to 35 bar, hydrogen can be added for controlling the molar mass in a manner known per se. The residence time can vary in both reactor zones. In one embodiment of the process for producing the propylene polymer the residence time in bulk reactor, e.g. loop is in the range 0.5 to 5 hours, e.g. 0.5 to 2 hours and the residence time in gas phase reactor will generally be 1 to 8 hours. If desired, the polymerization may be effected in a known manner under supercritical conditions in the bulk, preferably loop reactor, and/or as a condensed mode in the gas phase reactor. The process of the invention or any embodiments thereof above enable highly feasible means for producing and further tailoring the propylene polymer composition within the invention, e.g. the properties of the polymer composition can be adjusted or controlled in a known manner e.g. with one or more of the following process parameters: temperature, hydrogen feed, comonomer feed, propylene feed e.g. in the gas phase reactor, catalyst, the type and amount of an external donor (if used), split between components. The above process enables very feasible means for obtaining the reactor-made polypropylene as defined above. The capacitor fihn can be prepared by conventional drawing processes known in the art. Accordingly the process for the manufacture of a capacitor film according to this invention comprises the use of the polypropylene as defined herein and its forming into a film preferably by the tenter method known in the art. The tenter method is in particular a method in which the polypropylene as defined herein is melt extruded fi-om a slit die such as a T-die and cooled on a cooling drum obtaining an undrawn sheet. Said sheet is pre-heated for example with a heated metal roil and then drawn in the length direction between a plurality of rolls over which a difference in peripheral speeds is established and then both edges are gripped with grippers and the sheet is drawn in the transverse direction in an oven by means of a tenter resulting in a biaxially drawn film. The temperature of said stretched sheet during the longitudinal drawing is preferably controlled in such a way as to be within the temperature range of the melting point of the polypropylene as defined herein (-15 or + 5°C). The uniformity of the film thickness on transverse drawing can be evaluated with the method in which a fixed region on the film is masked after drawing in the length direction and measuring the actual drawing factor by measuring the spacing of the said masking after transverse drawing. Subsequently, the film can treated by corona discharge in air, nitrogen, carbon dioxide gas or any of the mixtures on the surface to be metallized, lo improve the adhesive strength to the metal to be deposited, and wound by a winder. The obtained film can set in a vacuum metallizer, and the film is preferably coated with an oil to form an insulation groove suitable for the purpose concerned, using a gravure coater, etc. Then, the metal suitable for the purpose concerned is deposited to achieve a predetermined layer resistance. Furthermore, as required, metallization is carried out through a comb-shaped deposition preventive plate to continuously change the resistance value in the transverse direction of the film. The metallized film is slit, to make two metallized reels as a pair for making a capacitor device. Then, the reels are wound to form a device and the device is formed to be fiat by a thermal press, being followed by metal spraying at the ends, attaching of leads, as required impregnation with an insulating oil, and packaging to make a capacitor.Morcover the present invention is directed to the use of the capacitor film as defined herein in a capacitor. In addition, the present invention is directed to a capacitor comprising at least on layer comprising a capacitor film as defined herein. Additionally it is preferred that the capacitor comprises a metal layer, in particular a metal layer obtained by the above described process.The present invention will now be described in fiirther detail by the following examples. Examples 1. Deflnitions/Measuring Methods The following definitions of terms and determination methods apply for the above general description of the invention as well as to the below examples unless otherwise defined. A. Pentad Concentration For the meso pentad concentration analysis, also referred herein as pentad concentration analysis, the assignment analysis is undertaken according to T Hayashi, Pentad concentration. R. Chujo and T. Asakura, Polymer 29 138-43 (1988) and Chujo R, et al., Polymer 21339 (1994) B. Elementary Analysis The below described elementary analysis is used for determining the content of elementary residues which are mainly originating fi«m the catalyst, especially the A1-, B-, and Si-residues in the polymer. Said AI-, B- and Si-residues can be in any form, e.g. in elementary or ionic form, which can be recovered and detected from polypropylene using the below described ICP-method. The method can also be used for determining the Ti-content of the polymer. It is understood that also other known methods can be used which would result in similar results. ICP-Spectrometry (Inductively Coupled Plasma Emission) ICP-instrument: The instrument for determination of A1-, B- nad Si-content is TCP Optima 2000 DV, PSN 620785 (supplier Perkin Elmer Instruments, Belgium) with software of the instrument. Detection limits are 0.10 ppm (Al), 0.10 ppm (B), 0.10 ppm (Si). The polymer sample was first ashed in a known manner, then dissolved in an appropriate acidic solvent. The dilutions of the standards for the calibration curve are dissolved in the same solvent as the sample and the concentrations chosen so that the concentration of the sample would fall within the standard calibration curve. ppm: means parts per million by weight Ash content: Ash content is measured according to ISO 3451-1 (1997) standard. Calculated ash, Al- Si- and B-content: The ash and the above listed elements, Al and/or Si and/or B can also be calculated form a polypropylene based on the polymerization activity of the catalyst as exemplified in the examples. These values would give the upper limit of the presence of said residues originating fiom the catalyst. Thus the estimate catalyst residue is based on catalyst composition and polymerization productivity, catalyst residues in the polymer can be estimated according to: Total catalyst residues [ppm] = 1 / productivity [kgpp/gcataiyst] x 100 Al residues [ppm] = WAI, cawiyst [%] x total catalyst residues [ppm] / 100 Zr residues [ppm] = wzj^, catalyst [%] x total catalyst residues [ppm] /100 (Similar calculations apply also for B, CI and Si residues) Chlorine residues content: The content of Cl-residues is measured from samples in the known manner using X-ray fluorescence (XRF) spectrometry. The instrument was X-ray fluorescention Philips PW2400, PSN 620487, (Supplier: Philips, Belgium) software X47. Detection limit for CI is 1 ppm. C. Particle size distribution Particle size distribution is measured via Coulter Counter LS 200 at room temperature with n-heptane as medium. D. NMR NMR-spectroscopy measurements: The '^C-NMR spectra of polypropylenes were recorded on Bruker 400MHz spectrometer at 130 °C from samples dissolved in l,2,4-trichlorobcnzene/benzenc-d6 (90/10 w/w). For the pentad analysis the assignment is done according to the methods described in literature: (T, Hayashi, Y. Inoue, R. Chiijo, and T. Asakura, Polymer 29 138-43 (1988).and Chujo R, et al,Polymer 35 339 (1994). The NMR-measurement was used for determining the mmmm pentad concentration in a manner well known in the art. E. M„,Mw,MWD Number average molecular weight (Mn), weight average molecular weight (Mw) and molecular weight distribution (MWD) are determined by size exclusion chromatography (SEC) using Waters Alliance GPCV 2000 instrument with online viscometer. The oven temperature is 140 °C. Trichlorobenzene is used as a solvent (ISO 16014). F. Xylene Solubles (XS) The xylene solubles (XS, wt,-%): Analysis according to the known method: 2.0 g of polymer Ls dissolved in 250 ml p-xylenc at 135°C under agitation. After 30±2 minutes the solution is allowed to cool for 15 minutes at ambient temperature and then allowed to settle for 30 minutes at 25±0.5°C. The solution is filtered and evaporated in nitrogen flow and the residue dried under vacuum at 90 °C until constant weight is reached. XS% = (100 X mi X vo) / (mo x vi), wherein mo = initial polymer amount (g) mi = weight of residue (g) vo= initial volume (ml) Vi = volume of analyzed sample (ml) G. Melting temperature Melting temperature Tm, crystallization temperature Tc, and the degree of crystallinity: measured with Mettler TA820 differential scanning calorimetry (DSC) on 5-10 mg samples. Both crystallization and melting curves were obtained during 10 °C/min cooling and heating scans between 30 °C and 225 °C. Melting and crystallization temperatures were taken as the peaks of endothenus and exotherms. Also the melt- and crystallization enthalpy (Hm and He) were measured by the DSC method according to ISO 11357-3. H. Melt Flow Rate I. MFRz: measured according to ISO 1133 (230°C, 2.16 kg load). J. Comonomer content Comonomer content is measured with Fourier transform infrared spectroscopy (FTIR) calibrated with '^C-NMR. When measuring the ethylene content in polypropylene, a thin film of the sample (thickness about 250 (.im) was prepared by hot-pressing. The area of-CH2- absorption peak (800-650 cm') was measured with Perkin Elmer FTIR 1600 spectrometer. The method was calibrated by ethylene content data measured by'^C-NMR. K. Stiffness Stiffness Fibn TD (transversal direction), Stiffness Film MD (machine direction), Elongation at break TD and Elongation at break MD: these are determined according to 1S0527-3 (cross head speed: 1 mm/min). The cast film has a thickness of 100 [im, whereas the thickness of the stretched films are indicated in the tables 3 and 4. L. Haze and transparency: Haze and transparency: are determined: ASTM D1003-92 (thickness 100 \|.im). M. Intrinsic viscosity Intrinsic viscosity: is measured according to DIN ISO 1628/1, October 1999 (in Decalinat 135°C). N. Porosity Porosity: is measured according to DTN 66135. O. Surface area Surface area: is measured according to ISO 9277. P. SIST Stepwise Isothermal Segregation Technique (SIST): The isothermal crystallisation for SIST analysis was performed in a Mettler tA820 DSC on 3±0.5 mg samples at decreasing temperatures between 200°C and 105°C. (i) The samples were melted at 225 °C for 5 min., (ii) then cooled with 80 °C/min to 145 °C (iii) held for 2 hours at 145 °C, (iv) then cooled with 80 °C/min to 135 °C (v) held for 2 hours at 135 °C, (vi) then cooled with 80 °C/min to 125 °C (vii) held for 2 hours at 125 °C, (viii) then cooled with 80 °C/min to 115 °C (ix) held for 2 hours at 115 °C, (x) then cooled with 80 °C/min to 105 °C (xi) held for 2 hours at 105 °C. After the last step the sample was cooled down to ambient temperature, and the melting curve was obtained by heating the cooled sample at a heating rate of 10°C/min up to 200°C. All measurements were performed in a nitrogen atmosphere. The mch enthalpy is recorded as function of temperature and evaluated through measuring the meh enthalpy of fractions melting within temperature intervals as indicated for example E 1 in the table 6 to 8. The melting curve of the material crystallised this way can be used for calculating the lamella thickness distribution according to Thomson-Gibbs equation (Eq 1.). where To=457K, AHo =184xl0^J/m\ a =0,049.6 jW and L is the lamella thickness. Q. Electrical breakdown strength (EB63%) It follows standard lEC 60243- part 1 (1988). The method describes a way to measure the electrical breakdown strength for insulation materials on compression moulded plaques. Definition: The electrical field strength in the test sample at which breakdown occurs. In homogeneous plaques and films this corresponds to the electrical breakdown strength divided by the thickness of the plaque/film (d), unit: kV/mm. The electrical breakdown strength is determined at 50 Hz within a high voUage cabinet using metal rods as electrodes as described in IEC60243-1 (4.1.2). The voltage is raised over the film/plaque at 2 kV/s until a breakdown occurs. 3. Examples Inventive Example 1 (£ 1) Catalyst preparation The catalyst was prepared as described in example 5 of WO 03/051934, with the Al¬and Zr-ratios as given in said example (AJ/Zr = 250). Catalyst characteristics: Al- and Zr- content were analyzed via above mentioned method to 36,27 wt.-% Al and 0,42 %-wt. Zr. The average particle diameter (analyzed via Coulter counter) is 20 ^m and particle size distribution is shown in Fig. 3. Polymerization A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.2 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 15 mmol hydrogen (quality 6.0, supplied by Aga) as chain transfer agent. Reactor temperature was set to 30 °C. 29.1 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 50 minutes at 70 °C, then propylene was flushed out, 5 mmol hydrogen were fed and the reactor pressure was increased to 20 bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 144 minutes, then the reactor was flashed, the polymer was dried and weighted. Polymer yield was weighted to 901 g, that equals a productivity of 31 kgpp/gcataiyst-lOOOppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been melt compounded with a Prism TSE16 lab kneader at 250rpm at a temperature of 220-230°C. Inventive Example 2 (E 2) A catalyst as used in 11 has been used. A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.5 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 50 mmol hydrogen (quaUty 6.0, supplied by Aga) as chain transfer agent. Reactor temperature was set to 30 °C. 19.9 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 40 minutes at 70 °C, then propylene was flushed out, the reactor pressure was increased to 20 bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 273 minutes, then the reactor was flashed, the polymer was dried and weighted. Polymer yield was weighted to 871 g, that equals a productivity of 44 kgpp/gcatsiysc. lOOOppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been meh compounded with a Prism TSE16 lab kneader at 250rpm at a temperature of 220-230°C. Inventive Example 3 (£ 3) A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.1 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 30 mmol hydrogen (quality 6.0, supplied by Aga) as chain transfer agent. Reactor temperature was set to 30 °C. 21.8 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 30 minutes at 70 °C, then propylene was flushed out and subsequently, the reactor pressure was increased to 20 bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 256 minutes, then the reactor was flashed, the polymer was dried and weighted. Polymer yield was weighted to 953 g, that equals a productivity of 43.72 kgpp/gcutniyjt. 1000 ppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been melt compounded with a Prism TSE16 lab kneader at 250 rpm at a temperature of 220 to 230 °C. Comparative Example 1 (CE 1) A commercial polypropylene homopolymer of Borealis has been used. Comparative Example 2 (CE 2) A commercial polypropylene homopolymer of Borealis has been used. In Tables 1,2 and 3, the properties of samples CE 1, CE 2, E 1 and E2 are summarized. Table 1: Properties of polypropylene according to the invention and comparative examples Unit CEl CE2 El E2 E3 Ash ppm 15 13 85 n.a. 74 rac % 98 98 98 MFR g/10' 2,1 2,1 2 5,3 1,1 Mw g/mol 412000 584000 453000 405000 207000 Mw/Mn - 9,9 8,1 2,8 5,3 4,5 XS wt% 1,2 3,5 0,85 0,66 0,70 mmmm - 0,95 0,95 0,95 Tm °C 162 162 150,6 150,8 150,9 Hm J/g 107 100 99,5 100,1 98,7 To °C 115 113 111,9 111,2 105,9 He J/g 101 94 74,6 92,8 90,5 Table 2: Preparation of the cast film and characterization Cast film with OCS equipment, thickness constant at 90-11 On,m. Unit CEl CE2 El E2 E3 Stiffness Film TD MPa 960 756 1011 n.a. 710 Stiffness Film MD MPa 954 752 1059 n.a. 716 Elongation at Break n.a. 601 TD % 789 792 700 Elongation at Break n.a. 723 MD % 733 714 691 Transparency % 94 94 94 n.a. 94 Haze % 24,2 19,9 7,8 n.a. 3 Table 3: Preparation ofBOPP film and characterization VTT Tampere, 4x4 Orientation Code Unit CE1 CE 2 El E2 E3 EB63% kV/mm 210 224 291 388 431 90% LOWER CONF: kV/mm 197 203 267 349 383 90% UPPER CONF: kV/mm 223 244 311 425 480 BETA: none 10,4 6,9 8,3 6,5 Stress MD4 MPa 4,3 3,8 3,6 2,7 ca. 4 Stress TD4 MPa 3,4 3,1 3,0 2.5 ca. 4 Stiffness Film 4x4 MPa 3003 3138 2550 2020 2105 MD Stiffiicss Film 4x4 TD MPa 2943 2691 2824 2554 1835 Elongation at Break % 52 53 80 62 72 Film 4x4 MD Elongation at Break % 50 60 34 41 54 Film 4x4 TD Tm ONSET Film 4x4 °C 141 136 137 n.a. 148 Tm Film (1" melting °C 156 158 154 157 158 4x4) Hm Film (1* melting J/g 56 66 70 92 80 4x4) Tc Film 4x4 °C 111 112 112 114 108 He Film 4x4 J/g 80 78 77 90 96 Tm Film (2"' melting °C 167 165 156 154 153 4x4) Hm Film (Z"** melting J/g 74 73 69 89 96 4x4) Film Thickness ^m 30 30 30 30 30 Table 4: Preparation of BOPP film and characterization VTT Tampere, 5x5 Orientation Code Unit E2 E3 EB63% kV/mm 638 582 90% LOWER CONF: kV/mm 563 579 90% UPPER CONF: kV/mm 707 585 BETA: none 5,6 Stress MD5 MPa 3,5 ca. 4 Stress TD5 MPa 3,4 ca. 4 Stiffness Film 5x5 MD MPa 2271 2055 Stiffness Film 5x5 TD MPa 2445 2464 Elongation at Break Film 5x5 MD % 39 38 Elongation at Break Film 5x5 TD % 19 18 Tm ONSET Film 5x5 °C n.a. 142 Tm Film (1" melting 5x5) °C 152 154 Hm Film (1" melting 5x5) J/g 83 56 Tc Film 5x5 °C 109 109 He Film 5x5 J/g 95 95 Tm Film (2"'melting 5x5) °C 153 151 Hm Film (2"'melting 5x5) J/g 100 93 Film Thickness \|.im 30 30 A biaxiaily oriented film is prepared as follows: In the biaxial stretching Device Bruckner Karo IV, film samples are clamped and extended in both, longitudinal and transverse direction, at constant stretching speed. The length of the sample increases during stretching in longitudinal direction and the stretch ratio in longitudinal direction calculates from the ratio of current length over original sample length. Subsequently, the sample is stretched in transverse direction where the width of the sample is increasing. Hence, the stretch ratio calculates from the current width of the sample over the original width of the sample. In Table 5 the ci7Stallization behaviour of samples is determined via stepwise isothermal segregation technique (SIST). Table 5: Results from stepwise isothermal segregation technique (SIST) -1 El E3 CEl CE2 Peak ID Range m H„ [J/g] H™ [J/g] H„. [J/g] H„ [J/g] 1 2 110-120 3,8 3,6 1,0 1,4 3 120-130 4,8 6,7 2.0 2,6 4 130-140 11,4 19,1 3,9 4,8 5 140-150 27,5 35,0 10,6 12,8 6 150-160 29,2 34,1* 25,4 32,1 7 160-170 16,9 50,7 56,6 8 >170 0,1 37.5 14,3 Hm= melting enthalpy *>150°C Table 6: Results from stepwise isothermal segregation technique (SIST) - II El E3 CEl CE2 T fiom T to H„ [J/g] H„ [J/gl H„ [J/g] H™ [J/g] 0 110 6 6,6 0,6 1 110 120 3,8 3,6 1 1,4 120 130 4,8 6,7 2 2,6 130 140 11,4 19,1 3,9 4,8 140 150 27,5 35 10.6 12,8 150 160 29,2 34,1 25,4 32,1 160 170 16,9 50,7 56,6 170 0,1 37,5 14,3 99,7 105,1 131,7 125,6 Table 7: Results from stepwise isothermal segregation technique (SIST) - III Lfrom Lto Fraction [wt%] m m El E3 CEl CE2 0 3,30E-09 6,0% 6,3% 0.5% 0.8% 3,30E-09 3,81E-09 3,8% 3.4% 0.8% 1,1% 3,81E-09 4,52E-09 4,8% 6,4% 1,5% 2,1% 4,52E-09 5,55E-09 11,4% 18,2% 3.0% 3,8% 5,55E-09 7,19E-09 27,6% 33,3% 8.0% 10,2% 7,19E-09 l,02E-08 29,3% 32.4% 19,3% 25,6% l,02E-08 l,76E-08 17,0% 0,0% 38,5% 45.1% l,76E-08 0,1% 0,0% 28,5% 11,4% 100,0% 100,0% 100,0% 100,0% Table 8: Results from stepwise isothermal segregation technique (SIST) - IV Label El E3 CE1 CE2 3,3nm-3.81nm 4% 3% 1% 1% 3,81nm-4,52nm 5% 6% 2% 2% 4,52nm - 5,55nm 11% 18% 3% 4% 5,55nm-7,19nm 28% 33% 8% 10% 7,19nm-10.21nm 29% 32% 19% 26% 10,21nm-17,57nm 17% 0% 38% 45% >17,57nm 0% 0% 28% 11% New Claims 1. Capacitor film comprising a biaxially oriented propylene homopolymer wherein a) said propylene homopolymer has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and b) said propylene homopolymer and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction and in transverse direction of 4.0. 2. Capacitor film according to claim 1, wherein said propylene homopolymer has a draw ratio in machine direction in the range of 4.0 to 8.0 and a draw ratio in transverse direction of 6.0 to 10.0. 3. Capacitor film according to claim 1 or 2, wherein said propylene homopolymer has electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 500 kV/mm at a draw ratio in machine direction and in transverse direction of 5.0. 4. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have xylene solubles (XS) of at least 0.5 wt.-%. 5. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer comprise(s) at least 20 wt.-% of a fraction of lamellae with a thickness of 6. Capacitor film according to any one of the preceding claims, wherein the film andJor the propylene homopolymer has/have xylene solubles In the range of 0.5 to 1.5 wt.-%. LB;CH:sh 7. Capacitor film according any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have a tensile modules of at least 1800 MPa at a draw ratio of 4.0 in machine direction and a draw ratio of 4.0 in transverse direction, measured according to ISO 527-3 at a cross head speed of 1 mm/min. 8. Capacitor film according any one of the preceding claims, wherein the film has a stretching stress of at least 2.5 MPa in machine direction and transverse direction at a ' stretching temperature of 152 "C or less and a draw ratio of 4.0 in machine direction and transverse direction. 9. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have a melting point Tm of at least 148 °C. 10. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer is multimodal. 11. Capacitor film according to any one of the preceding claims I to 9, wherein the propylene homopolymer is unimodal. 12. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has molecular weight distribution (MWD) measured according to ISO 16014 of not more than 8.00. 13. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has a melt flow rate MFRa measured according to ISO 1133 of up to lOg/lOmin. 14. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has a mmmm pentad concentration of higher than 94 % determined by NMR-spectroscopy. 15. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has been produced in the presence of a catalytic system comprising metallocene complex, wherein the catalytic system has a porosity measured according to DIN 66135 of less than 1.40 ml/g. 16. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has been produced in the presence of a symmetric metallocene complex. 17. Use of the capacitor film according to any one of the preceding claims in a capacitor. 18. Capacitor comprising at least on layer comprising a capacitor film according to any one of the preceding claims I to 16. 19. A process for the preparation of a capacitor film according to any one of the preceding claims 1 to 16, wherein a propylene homopolymer according to any one of the claims 1 to 16 is formed into a biaxially oriented film with a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and wherein the propylene homopolymer is prepared using a catalyst system of low porosity, the catalyst system comprising a symmetric catalyst, wherein the catalyst system has a porosity measured according to DIN 66135 of less than 1.40 ml/g and a surface area of less than 25 mVg measured according to ISO 9277. 20. The process according to claim 19, the catalyst system being a non-silica supported system. 21. The process according to claim 19 or 20, wherein the catalyst system has a porosity below the detection limit of DIN 66135. 22. The process according to any one of the preceding claims 19 to 21, wherein the symmetric catalyst is a transition metal compound of formula (I) wherein M is Zr, Hf or Ti, more preferably Zr X is independently a monovalent anionic ligand, such as a-ligand R is a briding group linking the two Cp ligands Cp is an organic ligand selected from the group consisting of unsubstituted cyclopenadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl, unsubstituted fluorenyl, substituted cyclopenadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted fluorenyl, with the proviso that both Cp-ligands are selected from the above stated group and both Cp-ligands are chemically the same, i.e. are identical.

Full Text

Electrical isulation film
The present invention relates to electrical insulation films, in particular capacitor films, and their use.
Capacitor films must withstand extreme conditions like high temperatures and high electrical breakdown strength. Additionally it is appreciated that capacitor films possess good mechanical properties like a high stiffness. Up to now there is the prevailing opinion in the technical field of capacitor technology that high electrical breakdown strength can be only achieved with a low level of electrical conduction caused by residual metals such as titanium, aluminium and boron. However traditional polypropylenes produced with a Ziegler-Natta catalyst are contaminated with high amounts of residual catalyst components. To achieve the desired very low levels of impurities to make the polypropylene suitable for capacitor films, the polypropylenes must be troublesome washed, a process which is time consuming and cost-intensive. To overcome the washing step polypropylenes produced in the presence of supported single-site catalysts have been developed, as for instance described in WO 02/16455 Al, with low levels of impurities including metallic and non-metallic impurities, like aluminium, titanium, silicon, and halogen (such as CI and F). However to achieve this goal of low levels of impurities the process conditions must be controlled very carefully. Moreover such polypropylenes have the drawback that they cannot be processed in a stable way. In particular films based on polypropylenes produced in the presence of supported single-site catalysts suffer fix)m sagging and break easily when manufactured.
Therefore the object of the present invention is to provide a capacitor film withstanding a high electric field strength without causing failure of the same and said film having in particular good mechanical properties, such as a high stiffness. Preferably such a capacitor film has additionally a high temperature resistance.

The present invention is based on the finding that an improved breakdown behaviour can be acconpJished by using a polypropylene for the capacitor film featured by a rather high amount of thin lamellae determined by stepwise isothermal segregation technique (SIST). Such a capacitor film reaches a balance of high thermal resistance, high electrical breakdown strength and good mechanical properties. It has been in particular found out that the good properties can be achieved independently fk>m the amount of impurities present, i.e. whether the polypropylene comprises rather high amounts of aluminium, titanium, silicon, halogen (such as CI and F) and/or boron.
Accordingly, the object outlined above is solved by providing a capacitor film comprising a biaxially oriented polypropylene wherein
a) said polypropylene has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and
b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction of 4.0 and at a draw ratio in transverse direction of 4.0.
Preferably the capacitor film is further characterized that said film and/or the polypropylene of said film has/have xylene solubles of some extent, i.e. of at least 0.50 wt.-%.
Moreover it is preferred, that the biaxially oriented polypropylene as defined in the instant invention is the only polymer component of the capacitor film.
Such capacitor films have superior properties compared to the films known in the art. Especially, the inventive capacitor films have high values of electrical breakdown strength also in case relatively high amounts of impurities are present in the film. Thus no troublesome washing steps are necessary as with polypropylenes known in

the art. Moreover the capacitor films according to this invention have in addition a high temperature resistance and are obtainable at high process stability and low process temperature. Moreover and surprisingly the inventive film has in addition good mechanical properties at a high stiffness expressed in tensile modulus. Additionally it has been observed that the new capacitor films according to this invention show a significant increase of electrical breakdown strength with increasing the draw ratio.
A first requirement of the present invention is that the polypropylene of the capacitor film is biaxially oriented, i.e. has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0. Such ratios are appreciated as commercial biaxially oriented polypropylene films must be stretchable at least to the above defined extent without breaking. The length of the sample increases during stretching in longitudinal direction and the draw ratio in longitudinal direction calculates from the ratio of current length over original sample length. Subsequently, the sample is stretched in transverse direction where the width of the sample is increasing. Hence, the draw ratio calculates from the current width of the sample over the original width of the sample. Preferably the draw ratio in machine direction of the biaxially oriented polypropylene ranges ft*om 4.0 to 8.0, more preferably from 4.5 to 6.5. The draw ratio in transverse direction of the biaxially polypropylene ranges preferably from 6.0 to 10.0, more preferably from 7.0 to 9.5. In a preferred embodiment the biaxially polypropylene has a draw ratio in machine direction fix)m, 4.5 to 7.0. in particular from 4.5 to 5.0, and a draw ratio in transverse direction from 6.0 to 10.0, in particular from 8.0 to 10.
To obtain such a biaxially polypropylene preferably a process is applied as described below in the instant invention.

The second requirement of the present invention is, that the biaxiaily polypropylene and/or said capacitor film has(have) a rather high electrical breakdown strength EB63%, i.e. an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm, at a draw ratio in machine direction and in transverse direction of 4.0. More preferably the electrical breakdown strength EB63% of the biaxiaily polypropylene and/or said capacitor film at a draw ratio in machine direction and in transverse direction of 4.0 is(are) at least 350 kV/mm, still more preferably at least 400 kV/mm and yet more preferably at least 430 kV/mm. Further details about the measurement of the electrical breakdown strength are provided below in the examples.
As stated above, the biaxiallly polypropylene is in particular characterized in that the electrical breakdown strength EB63% of the bixially oriented polypropylene disproportionately increases with increase of the stretching ratio, as can be seen in figure 2. Thus it is preferred that the electrical breakdown strength EB63% of the biaxiaily oriented polypropylene and/or of the capacitor film at a draw ratio in machine direction and in transverse direction of 5.0 is(are) at least 500 kV/mm, still more preferably at least 550 kV/mm and yet more preferably at least 580 kV/mra
Moreover it is preferred that the capacitor film and/or the polypropylene of said capacitor film has/have xylene solubles of some extent, i.e. of at least 0.50 wt.-%. Xylene solubles are the part of the polymer soluble in cold xylene determined by dissolution in boiling xylene and letting the insoluble part crystallize from the cooling solution (for the method see below in the experimental part). The xylene solubles fraction contains polymer chains of low stereo-regularity and is an indication for the amount of non-crystalline areas.
Preferably, the polypropylene component of the film has xylene solubles of more than 0.60 wt.-%. On the other hand, the amount of xylene solubles should not be too

high since they represent a potential contamination risk. Accordingly it is preferred that the xylene solubles are not more than 1.00 wt.-% and still more preferably not more than 0.90 wt.-%. In preferred embodiments the xylene solubles are in the range of 0.60 to 1.00 wt.-% and more preferably in the range of 0.60 to 0.90 wt.-%.
Preferably, the capacitor film has xylene solubles of more than 0.60 wt.-%. Even more preferred, the capacitor film has xylene solubles of not more than 1.00 wt.-% and more preferably of not more than 0.90 wt.-%. In particular, the film has xylene solubles in the range of 0.60 wt.-% to 1.00 wt.% and more preferably of 0.60 wt.-% to 0.90 wt.-%.
Moreover it is preferred that the capacitor film according to this invention is further specified by its lamellar thickness distribution (see figure 7). It has been recognized that higher electrical breakdown strength is achievable in case the polymer comprises rather high amounts of thin lamellae. Thus the acceptance of the film as a capacitor film is independent fix)m the amounts of impurities present in the polypropylene but fix)m its crystalline properties. The stepwise isothermal segregation technique (SIST) provides a possibiUty to determine the lamellar thickness distribution. The exact method is defined in the example section. In the instant invention under lamellar thickness is understood the lamellar thickness of the polymer measured according to the stepwise isothermal segregation technique (SIST) method as defined in the example section. Rather high amounts of polymer fi:actions crystallizing at lower temperatures indicate a rather high amount of thin lamellae.
Thus the inventive capacitor film and/or the polypropylene of the film is(are) characterized by a rather high amount of thin lamellae; i.e. a rather high amount of lamellae having a thickness of
Accordingly it is preferred that the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 20 wt.-%, more preferred at least 30 wt.-%, yet more preferred at least 35 wt.-%, still more preferred at least 40 wt.-%, still yet more preferred at least 45 vvt.-% and most preferred at least 50 wt.-%, of a fi-action of lamellae with a thickness of More precisely and preferably the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 12 wt.-%, more preferably at least 20 wt.-%, yet more preferably of at least 25 wt.-%, of a fraction of lamellae in the range of 5.55 nm to 7.19 nm. Furthermore it is preferred that the inventive capacitor film and/or the polypropylene of the film comprise(s) at least 5 wt.-%, more preferably at least 7 wt.-%, yet more preferably of at least 10 wt.-%, of a fraction of lamellae in the range of 4.52 nm to 5.55 nm.
Thus it is preferred that the inventive capacitor fihn and/or the polypropylene of the fihn
(a) comprise(s) at least 20 wt.-%, more preferred at least 30 wt.-%, yet more preferred at least 35 wt.-%, still more preferred at least 40 wt.-%, still yet more preferred at least 45 wt.-% and most preferred at least 50 wt.-%, of a fraction of lamellae with a thickness of (b) said fraction of lamellae with a thickness of (c) at least 5 wt.-%, more preferably at least 7 wt.-%, yet more preferably of at least 10 wt.-%, of a fraction of lamellae in the range of 4.52 nm to 5.55 nm
The method for determining the lamellar thickness distribution is described in detail in the example section. The weight percentages are based on the total amount of capacitor film and/or the polypropylene measured by SIST.

The molecular weight distribution (MWD) is expressed as the ratio of weight average molecular weight (Mw) and number average molecular weight (Mn). The number average molecular weight (M„) Is an average molecular weight of a polymer expressed as the first moment of a plot of the number of molecules in each molecular weight range against the molecular weight. In effect, this is the total molecular weight of all molecules divided by the number of molecules. In turn, the weight average molecular weight (Mw) is the first moment of a plot of the weight of polymer in each molecular weight range against molecular weight.
The number average molecular weight (M„) and the weight average molecular weight (Mw) as well as the molecular weight distribution (MWD) are determined by size exclusion chromatography (SEC) using Waters Alliance GPCV 2000 instrument with online viscometer. The oven temperature is 140 °C. Trichlorobenzene is used as a solvent (ISO 16014).
It is preferred that the capacitor film of the present invention comprises a polypropylene which has a weight average molecular weight (Mw) fi'om 10,000 to 2,000,000 &'mol, more preferably from 20,000 to 1,500,000 g/mol.
The number average molecular weight (M„) of the polypropylene is preferably in the range of 5,000 to 750,000 g/mol, more preferably from 10,000 to 750,000 g/mol.
As a broad molecular weight distribution (MWD) improves the piocessability of the polypropylene the molecular weight distribution (MWD) is preferably up to 20.00, more preferably up to 10.00, still more preferably up to 8.00. However a rather broad molecular weight distribution stimulates sagging. Therefore, in an alternative embodiment the molecular weight distribution (MWD) is preferably between 1.00 to 8.00, still more preferably in the range of 1.00 to 4.00, yet more preferably in the range of 1.00 to 3.50.

Furthermore, it is preferred that the polypropylene component of the film of the present invention has a melt flow rate (MFR) given in a specific range. The melt flow rate mainly depends on the average molecular weight. This is due to the fact that long molecules render the material a lower flow tendency than short molecules. An increase in molecular weight means a decrease in the MFR-value. The melt flow rate (MFR) is measured in g/10 min of the polymer discharged through a defined die under specified temperature and pressure conditions and the measure of viscosity of the polymer which, in turn, for each type of polymer is mainly influenced by its molecular weight but also by its degree of branching. The melt flow rate measured under a load of 2.16 kg at 230 °C (ISO 1133) is denoted as MFR2. Accordingly, it is preferred that in the present invention the capacitor film comprises a polypropylene which has an MFR2 up to 10.00 g/lOmin, more preferably up to 6.00 g/lOmin. In another preferred embodiment the polypropylene has MFR2 up to 4 g/lOmin. A preferred range for the MFR2 is 1.00 to 10.00 g/10 min, more preferably in the range of 1.00 to 8.00 g/IOmin, yet more preferably in the range of 1.00 to 6.00 g/lOmin.
As cross-linking has a detrimental effect on the extensional flow properties it is preferred that the polypropylene according to this invention is non-cross-linked.
More preferably, the polypropylene of the film according to this invention shall have a rather high isotacticity measured by meso pentad concentration (also referred herein as pentad concentration), i.e. higher than 91 %, more preferably higher than 93 %, still more preferably higher than 94 % and most preferably higher than 95 %. On the other hand pentad concentration shall be not higher than 99.5 %. The pentad concentration is an indicator for the narrowness in the regularity distribution of the polypropylene and measured by NMR-spectroscopy.
In addition, it is preferred that the polypropylene of the capacitor film has a melting temperature Tm of higher than 148 °C, more preferred higher than 150 °C. In a

preferred embodiment, melting temperature Tm of the polypropylene component is higher than 148 °C but below 156 °C. The measuring method for the melting temperature Tm is discussed in the example section.
The melting temperature Tm of the capacitor film is preferably at least 148 °C, more preferably at least 150 °C. In a preferred embodiment, the melting temperature Tm of the capacitor film is higher than 150°C but below 160°C.
Furthermore a rather high tensile modulus at a draw ratio of 4 in machine direction and a draw ratio of 4 in transverse direction is appreciated since biaxially oriented polypropylene fihns commercially are stretched with a draw ratio of 4 to 8, more preferably 4 to 6, in machine direction and with a draw ratio of 5 to 10, more preferably of 6 to 8, in transverse direction.
Thus the polypropylene component of the film of the present invention has a tensile modulus of at least 800 MPa, measured according to ISO 527-3 at a cross head speed of Imm/min (with thickness of 100 |4,m). More preferably, the polypropylene component has a tensile modulus of at least 850 MPa, even more preferably 900 MPa, and yet more preferably at least 1000 MPa.
Preferably, the biaxially oriented polypropylene film of the present invention has a tensile modulus of at least 1800 MPa at a draw ratio of 4.0 in machine direction and in transverse direction, wherein the tensile modulus is measured according to ISO 527-3 at a cross head speed of Imm/min (exact measuring method is provided in the example section). More preferably, the polypropylene film has a tensile modulus of at least 1900 MPa, even more preferably 1950 MPa, and most preferably at least 2200 MPa at a draw ratio of 4.0 in machine direction and in transverse direction.
In a preferred embodiment, the film has a stretching stress of at least 2.5 MPa in machine direction and at least 2.5 MPa in transverse direction at a stretching

temperature of 152 °C or less and a draw ratio of 4 in machine direction and in transverse direction. Preferably, the stretching temperature mentioned above is at least 2°C, more preferably at least 3°C below the melting temperature of the film.
In addition it is appreciated that the inventive capacitor film has good optical properties. Thus it is preferred that capacitor film has a haze of not more than 15, still more preferred not more than 10 measured according to ASTM D 1003-92 (exact measuring method is provided in the example section). In turn the transparency of the film shall be rather high. Thus it is preferred that the capacitor film has a transparency of at least 90 % measured according to ASTM D 1003-92.
Preferably the polypropylene of the film according to this invention has low levels of impurities, i.e. low levels of aluminium (Al) residue and/or low levels of silicon residue (Si) and/or low levels of boron (B) residue. Accordingly the aluminium residues of the polypropylene can be lowered to a level of 12.00 ppm. Thus the aluminium residue content of the polypropylene of the film according to this invention is preferably below 20 ppm, more preferably below 18 ppm and yet more preferably 15 ppm. Preferred ranges of aluminium residues are 12 to 20 ppm, more preferred 12 to 18 ppm and yet more preferred 12 to 15 ppm. As stated above the polypropylene of the film according to this invention may comprise low values of silicon residue (Si) and/or boron (B) residue, i.e. below 40 ppm, more preferably below 20 ppm, yet more preferably below 10 ppm. Hence in one preferred embodiment the film according to this invention comprises a polypropylene which is preferably essentially free of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section). Further it is preferred that the polypropylene of the film according to this invention is free of titanium and/or magnesium residues. In other words the polypropylene according to this invention has been preferably not produced with a catalyst system comprising titanium and/or magnesium. On the other hand the

properties of this invention are not detrimentally influenced by the presence of residues.. In another preferred embodiment the polypropylene of the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.10 ppm of boron residues and/or silicon residues, still more preferably in amounts of more than 0.20 ppm of boron residues and/or silicon residues, yet more preferably in amounts of more than 0.50 ppm of boron residues and/or silicon residues. In still another preferred embodiment the polypropylene component of the film according to this invention comprises Al residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm, yet more preferred in an amount of more than 25.00 ppm. In yet another prefeiTcd embodiment the polypropylene component of the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.20 ppm of boron residues and/or silicon residues, and aluminium residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm.
Moreover preferably the capacitor film according to this invention has low levels of impurities, i.e. low levels of aluminium (Al) residue and/or low levels of silicon residue (Si) and/or low levels of boron (B) residue. Accordingly the aluminium residues of the film can be lowered to a level of 12.00 ppm. Thus the aluminium residue content of the film according to this invention is preferably below 20 ppm, more preferably below 18 ppm and yet more preferably 15 ppm. Preferred ranges of aluminium residues are 12 to 20 ppm, more preferred 12 to 18 ppm and yet more preferred 12 to 15 ppm. As stated above the film according to this invention may comprise low values of silicon residue (Si) and/or boron (B) residue, i.e. below 40 ppm, more preferably below 20 ppm, yet more preferably below 10 ppm. Hence in one preferred embodiment the film according to this invention is preferably essentially fi-ee of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section).

Further it is preferred that the film according to this invention is fi-ee of titanium and/or magnesium residues. In other words the polypropylene according to this invention has been preferably not produced with a catalyst system comprising titanium and/or magnesium. On the other hand the properties of this invention are not detrimentally influenced by the presence of residues. Hence in one preferred embodiment the film according to this invention is preferably essentially fi-ee of any boron and/or silicon residues, i.e. residues thereof are not detectable (The analysis of residue contents is defined in the example section). In another preferred embodiment the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.10 ppm of boron residues and/or silicon residues, still more preferably in amounts of more than 0.20 ppm of boron residues and/or silicon residues, yet more preferably in amounts of more than 0.50 ppm of boron residues and/or silicon residues. In still another preferred embodiment the film according to this invention comprises Al residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm. In yet another preferred embodiment the film according to this invention comprises boron and/or silicon in detectable amounts, i.e. in amounts of more than 0.20 ppm of boron residues and/or silicon residues, and aluminium residues in an amount of more than 12.00 ppm, even more preferred in an amount of more than 20.00 ppm and yet more preferred in an amount of more than 25.00 ppm.
In a preferred embodiment the polypropylene as defmed above (and fiirther defined below) is preferably unimodal. In another preferred embodiment the polypropylene as defined above (and further defined below) is preferably multimodal, more preferably bimodal.
"Muhimodal" or "multimodal distribution" describes a frequency distribution that has several relative maxima (contrary to unimodal having only one maximum). In

particular, the expression "modality of a polymer" refers to the forai of its molecular weight distribution (MWD) curve, i.e. the appearance of the graph of the polymer weight fraction as a function of its molecular weight. If the polymer is produced in the sequential step process, i.e. by utilizing reactors coupled in scries, and using different conditions in each reactor, the different polymer fractions produced in the different reactors each have their own molecular weight distribution which may considerably differ from one another. The molecular weight distribution curve of the resulting final polymer can be seen at a super-imposing of the molecular weight distribution curves of the polymer fraction which will, accordingly, show a more distinct maxima, or at least be distinctively broadened compared with the curves for individual fractions.
A polymer showing such molecular weight distribution curve is called bimodal or multimodal, respectively.
In case the polypropylene of the capacitor film is not unimodal it is preferably bimodal.
The polypropylene of the film according to this invention can be a homopolymer or a copolymer. In case the polypropylene is unimodal the polypropylene is preferably a polypropylene homopolymer. In turn in case the polypropylene is multimodal, more preferably bimodal, the polypropylene can be a polypropylene homopolymer as well as a polypropylene copolymer. However it is in particular preferred that in case the polypropylene is multimodal, more preferably bimodal, the polypropylene is a polypropylene homopolymer. Furthermore it is preferred that at least one of the fractions of the multimodal polypropylene is a polypropylene according to this invention, more preferably a polypropylene homopolymer according to the instant invention.

The polypropylene of the capacitor film according to this invention is most preferably a unimodal polypropylene homopolymer.
The expression polypropylene homopolymer as used in this invention relates to a polypropylene that consists substantially, i.e. of at least 97 wt%, preferably of at least 99 wt%, and most preferably of at least 99.8 wt% of propylene units. In a preferred embodiment only propylene units in the polypropylene homopolymer are detectable. The comonomcr content can be measured with FT infrared spectroscopy. Further details are provided below in the examples.
Further it is preferred that the polypropylene of the instant invention is free of units derived from 3-branched a-olefins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms. Even more preferred the inventive film comprises a propylene homopolymer, i.e. firee of units derived from 3-branched a-olefins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms. In case a propylene copolymer is used, than it is preferred that the copolymer is free of units derived from 3-branched a-olcfins having 6 or more carbon atoms and/or vinylcycloalkanes having 6 or more carbon atoms.
In case the polypropylene of the film according to this invention is a multimodal or bimodal polypropylene copolymer, it is preferred that the comonomer is ethylene. However, also other comonomers known in the art are suitable. Preferably, the total amount of comonomer, more preferably ethylene, in the propylene copolymer is up to 30 wt%, more preferably up to 25 wt%.
In a preferred embodiment, the multimodal or bimodal polypropylene copolymer is a polypropylene copolymer comprising a polypropylene homopolymer matrix being a polypropylene as defined above and an ethylene-propylene rubber (EPR).

The polypropylene homopolymer matrix can be unimodal or multimodal, i.e. bimodal. However it is preferred that polypropylene homopolymer matrix is unimodal.
Preferably, the ethylene-propylene rubber (EPR) in the total multimodal or bimodal polypropylene copolymer is up to 50 wt%. More preferably the amount of ethylene-propylene rubber (EPR) in the total multimodal or bimodal polypropylene copolymer is in the range of 10 to 40 wt%, still more preferably in the range of 10 to 30 wt%.
In addition, it is preferred that the multimodal or bimodal polypropylene copolymer comprises a polypropylene homopolymer matrix being a polypropylene as defined above and an ethylene-propylene rubber (EPR) with an ethylene-content of up to 50 wt%.
In addition, it is preferred that the polypropylene as defined above is produced in the presence of the catalyst as defined below. Furthermore, for the production of the polypropylene as defined above, the process as stated below is preferably used.
Moreover from the above defined and further defined capacitor films are preferably the following two embodiments disclaimed:
(A) A capacitor film comprising a biaxially oriented polypropylene
a) said polypropylene has a draw ratio in machine direction and transverse direction of 4, and
b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of 291 or 388 kV/mm at a draw ratio in machine direction and in transverse direction of 4.
(B) A capacitor film comprising a biaxially oriented polypropylene

a) said polypropylene has a draw ratio in machine direction and transverse direction of 5, and
b) said polypropylene and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of 638 kV/mm at a draw ratio in machine direction and in transverse direction of 5.
The polypropylene of the capacitor film according to this invention has been in particular obtained by a new catalyst system. This new catalyst system comprises a symmetric catalyst, whereby the catalyst system has a porosity of less than 1.40 ml/g, more preferably less than 1.30 ml/g and most preferably less than 1.00 ml/g. The porosity has been measured according to DIN 66135 (Na). In another preferred embodiment the porosity is not detectable when determined with the method applied according to DIN 66135 (N2).
A symmetric catalyst according to this invention is a mctallocene compound having a C2-symetry. Preferably the Ca-symetric mctallocene comprises two identical organic ligands, still more preferably comprises only two organic ligands which are identical, yet more preferably comprises only two organic ligands which are identical and linked via a bridge.
It Is preferred that the rac : meso ratio of the mctallocene compound of the instant invention is at least 20 :1, i.e. 95 % rac.
Said symmetric catalyst is preferably a single site catalyst (SSC).
Due to the use of the catalyst system with a very low porosity comprising a symmetric catalyst the manufacture of the above defined short-chain branched polypropylene is possible.

Furthermore it is preferred, that the catalyst system has a surface area of of lower than 25 mVg, yet more preferred lower than 20 mVg, still more preferred lower than 15 mVg, yet still lower than 10 mVg and most preferred lower than 5 mVg. The surface area according to this invention is measured according to ISO 9277 (N2).
It is in particular preferred that the catalytic system according to this invention comprises a symmetric catalyst, i.e. a catalyst as defined above and in further detail below, and has porosity not detectable when applying the method according to DIN 66135 (N2) and has a surface area measured according to ISO 9277 (N2) of less than 5 mVg.
Preferably the symmetric catalyst compound, i.e. the C2-symetric metallocene, has the formula (I):
(Cp)2R,MX2 (1) wherein
M is Zr, Hf or Ti, more preferably Zr, and X is independently a monovalent anionic ligand, such as o-ligand R is a bridging group linking the two Cp ligands Cp is an organic ligand selected from the group consisting of unsubstituted cyclopentadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl, unsubstituted fluorenyl, substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted fluorenyl,
with the proviso that both Cp-ligands are selected from the above stated group and both Cp-ligands are chemically the same, i.e. are identical.
The term "cr-ligand" is understood in the whole description in a known manner, i.e. a group bonded to the metal at one or more places via a sigma bond. A prefcn'cd monovalent anionic ligand is halogen, in particular chlorine (CI). Preferably, the symmetric catalyst is of formula (I) indicated above,

wherein M is Zr and each X is CI.
Preferably both identical Cp-ligands are substituted.
The optional one or more substituent(s) bonded to cyclopentadienyl, indenyl, tetrahydroindenyl, or fluorenyl may be selected from a group including halogen, hydrocarbyl (e.g. Cj-Cao-alkyl, C2-C2o-alJ More preferably both identical Cp-ligands are indenyl moieties wherein each indenyl moiety bear one or two substituents as defined above. More preferably each of the identical Cp-ligands is an indenyl moiety bearing two substituents as defined above, with the proviso that the substituents are chosen in such are manner that both Cp-ligands are of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety.
Still more preferably both identical Cp's are indenyl moieties wherein the indenyl moieties comprise at least at the five membered ring of the indenyl moiety, more preferably at 2-position, a substituent selected from the group consisting of alkyl, such as Ci-Cd alkyl, e.g. methyl, ethyl, isopropyl, and trialkyloxysiloxy, wherein each alkyl is independently selected from Ci-Cg alkyl, such as methyl or ethyl, with proviso that the indenyl moieties of both Cp are of the same chemical structure, i.e

both Cp-Iigands have the same substituents bonded to chemically the same indenyl moiety.
Still more preferred both identical Cp are indenyl moieties wherein the indenyl moieties comprise at least at the six membered ring of the indenyl moiety, more preferably at 4-position, a substituent selected from the group consisting of a C6-C20 aromatic ring moiety, such as phenyl or naphthyl, preferably phenyl, which is optionally substituted with one or more substitutents, such as Ci-Cg alkyl, and a heteroaromatic ring moiety, with proviso that the indenyl moieties of both Cp are of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety.
Yet more preferably both identical Cp are indenyl moieties wherein the indenyl moieties comprise at the five membered ring of the indenyl moiety, more preferably at 2-position, a substituent and at the six membered ring of the indenyl moiety, more preferably at 4-position, a further substituent, wherein the substituent of the five membered ring is selected from the group consisting of alkyl, such as Ci-Ce alkyl, e.g. methyl, ethyl, isopropyl, and trialkyloxysiloxy and the further substituent of the six membered ring is selected from the group consisting of a Ce-Cjo aromatic ring moiety, such as phenyl or naphthyl, preferably phenyl, which is optionally substituted with one or more substituents, such as Ci-Ce alkyl, and a heteroaromatic ring moiety, with proviso that the indenyl moieties of both Cp's arc of the same chemical structure, i.e both Cp-ligands have the same substituents bonded to chemically the same indenyl moiety.
Conceming the moiety "R" it is preferred that "R" has the formula (II)
-Y(R02- (11) wherein Y is C, Si or Ge, and

R' is Ci to C20 alkyl, Ci-Cjz aryl, or C7-C12 arylalkyl or trimethylsilyl.
In case both Cp-ligands of the symmetric catalyst as defined above, in particular case of two indenyl moieties, are linked with a bridge member R, the bridge member R is typically placed at 1-position. The bridge member R may contain one or more bridge atoms selected from e.g. C, Si and/or Ge, preferably from C and/or Si. One preferable bridge R is -Si(R')2-, wherein R' is selected independently from one or more of e.g. trimethylsilyl, Ci-Cio alkyl, C1-C20 alkyl, such as Ce-Cn aryl, or C7-C-,o, such as C7-C12 arylalkyl, wherein alkyl as such or as part of arylalkyl is preferably C1-C6 alkyl, such as ethyl or methyl, preferably methyl, and aryl is preferably phenyl. The bridge -Si(R')2- is preferably e.g. -Si(Ci-C6 alkyl)2- -Si(phenyl)2- or -Si(Ci-Ce alkyl)(phenyl)-, such as -Si(Me)2-.
In a preferred embodiment the symmetric catalyst, i.e. the C2-symetric metallocene, is defined by the formula (III)
(Cp)2R,ZrCl2 (III) wherein
both Cp coordinate to M and are selected from the group consisting of unsubstituted cyclopentadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl, unsubstituted fluorenyl, substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted fluorenyl, with the proviso that both Cp-ligands are chemically the same, i.e. are identical, and
R is a bridging group linking two ligands L, wherein R is defined by the formula (II)
-Y(R')2- (II) wherein
Y is C, Si or Ge, and R' is Ci to C20 alkyl, Cc-Cn aryl, or C7-C12 arylalkyl.

More preferably the symmetric catalyst is defined by the formula (III), wherein both Cp are selected from the group consisting of substituted cyclopentadienyl, substituted indcnyl, substituted tetrahydroindenyl, and substituted fluorenyl.
In a preferred embodiment the symmetric catalyst is dimethylsilandiylbis(2-methyl-4-phenyl-indenyl)zirkonium dichloride. More preferred said symmetric catalyst is non-silica supported.
The above described symmetric catalyst components are prepared according to the methods described in WO 01/48034.
It is in particular preferred that the symmetric catalyst is obtainable by the emulsion solidification technology as described in WO 03/051934. This document is herewith included in its entirety by reference. Hence the sjmimetric catalyst is preferably in the form of solid catalyst particles, obtainable by a process comprising the steps of
a) preparing a solution of one or more symmetric catalyst components;
b) dispersing said solution in a solvent immiscible therewith to form an emulsion in which said one or more catalyst components are present in the droplets of the dispersed phase,
c) solidifying said dispersed phase to convert said droplets to solid particles and optionally recovering said particles to obtain said catalyst.
Preferably a solvent, more preferably an organic solvent, is used to form said solution. Still more preferably the organic solvent is selected from the group consisting of a linear atkane, cyclic alkane, linear alkene, cyclic alkene, aromatic hydrocarbon and halogen-containing hydrocarbon.
Moreover the immiscible solvent forming the continuous phase is an inert solvent, more preferably the immiscible solvent comprises a fluorinated organic solvent

and/or a flmctionalized derivative thereof, still more preferably the immiscible solvent comprises a semi-, highly- or perfluorinated hydrocarbon and/or a functionalizcd derivative thereof. It is in particular preferred, that said immiscible solvent comprises a perfluorohydrocarbon or a functionalizcd derivative thereof, preferably C3-C30 perfluoroalkanes, -alkenes or -cycloalkanes, more preferred C4-C10 perfluoro-alkanes, -alkenes or -cycloalkanes, particularly preferred perfluorohexane, perfluoroheptanc, pcrfluorooctanc or perfluoro (methylcyclohcxane) or a mixture thereof.
Furthermore it Ls preferred that the emulsion comprising said continuous phase and said dispersed phase is a bi-or multiphasic system as known in the art. An emulsifier may be used for forming the emulsion. After the formation of the emulsion system, said catalyst is formed in situ from catalyst components in said solution.
In principle, the emulsifying agent may be any suitable agent which contributes to the formation and/or stabilization of the emulsion and which does not have any adverse effect on the catalytic activity of the catalyst. The emulsifying agent may e.g. be a surfactant based on hydrocarbons optionally interrupted with (a) heteroatom(s), preferably halogenated hydrocarbons optionally having a functional group, preferably semi-, highly- or perfluorinated hydrocarbons as known in the art. Alternatively, the emulsifying agent may be prepared during the emulsion preparation, e.g. by reacting a surfactant precursor with a compound of the catalyst solution. Said surfactant precursor may be a halogenated hydrocarbon with at least one fijnctional group, e.g. a highly fluorinated C\ to C30 alcohol, which reacts e.g. with a cocatalyst component, such as aluminoxane.
In principle any solidification method can be used for forming the solid particles from the dispersed droplets. According to one preferable embodiment the solidification is effected by a temperature change treatment. Hence the emulsion

subjected to gradual temperature change of up to 10 °C/min, preferably 0.5 to 6 °C/min and more preferably 1 to 5 °C/min. Even more preferred the emulsion is subjected to a temperature change of more than 40 °C, preferably more than 50 °C within less than 10 seconds, preferably less than 6 seconds.
The recovered particles have preferably an average size range of 5 to 200 |.im, more preferably 10 to 100|am.
Moreover, the form of solidified particles have preferably a spherical shape, a predetermined particles size distribution and a surface area as mentioned above of preferably less than 25 mVg, still more preferably less than 20 m^/g, yet more preferably less than 15 m^/g, yet still more preferably less than 10 mVg and most preferably less than 5 mVg, wherein said particles arc obtained by the process as described above.
For further details, embodiments and examples of the continuous and dispersed phase system, emulsion formation method, emulsifying agent and solidification methods reference is made e.g. to the above cited international patent application WO 03/051934.
The above described symmetric catalyst components are prepared according to the methods described in WO 01/48034.
As mentioned above the catalyst system may further comprise an activator as a cocatalyst, as described in WO 03/051934, which is enclosed herein with reference.
Preferred as cocatalysts for metallocenes and non-metallocenes, if desired, are the aluminoxanes, in particular the Ci-Cio-alkylaluminoxanes, most particularly methylaluminoxane (MAO). Such aluminoxanes can be used as the sole cocatalyst or

together with other cocatalyst(s). Thus besides or in addition to aiuminoxanes, other cation complex forming catalysts activators can be used. Said activators are commercially available or can be prepared according to the prior art literature.
Further aluminoxane cocatalysts are described i.a. in WO 94/28034 which is incorporated herein by reference. These are linear or cyclic oligomers of having up to 40, preferably 3 to 20, -(A1(R"')0)- repeat units (wherein R'" is hydrogen, Ci-Cio-alkyl (preferably methyl) or C6-Ci8-aryl or mixtures thereof)-
The use and amounts of such activators are within the skills of an expexl in the field. As an example, with the boron activators, 5:1 to 1:5, preferably 2:1 to 1:2, such as 1:1, ratio of the transition metal to boron activator may be used. In case of preferred aiuminoxanes, such as methylaluminumoxane (MAO), the amount of Al, provided by aluminoxane, can be chosen to provide a molar ratio of Al:transition metal e.g. in the range of 1 to 10 000, suitably 5 to 8000, preferably 10 to 7000, e.g. 100 to 4000, such as 1000 to 3000. TVpically in case of solid (heterogeneous) catalyst the ratio is preferably below 500.
The quantity of cocatalyst to be employed in the catalyst of the invention is thus variable, and depends on the conditions and the particular transition metal compound chosen in a manner well known to a person skilled in the art.
Any additional components to be contained in the solution comprising the organotransition compound may be added to said solution before or, alternatively, after the dispersing step.
Furthermore, the present invention is related to the use of the above-defined catalyst system for the production of a polypropylene according to this invention.

In addition, tlie present invention is related to tiie process for producing the inventive capacitor film comprising the polypropylene, whereby the catalyst system as defined above is employed. Furthermore it is preferred that the process temperature is higher than 60 °C. Preferably, the process is a multi-stage process to obtain multimodal polypropylene as defined above.
Multistage processes include also bulk/gas phase reactors known as multizone gas phase reactors for producing multimodal propylene polymer.
A preferred multistage process is a "loop-gas phase"-process, such as developed by Boreal is A/S, Denmark (known as BORSTAR® technology) described e.g. in patent literature, such as in EP 0 887 379 or in WO 92/12182.
Multimodal polymers can be produced according to several processes which are described, e.g. in WO 92/12182, EP 0 887 379 and WO 97/22633.
A multimodal polypropylene according to this invention is produced preferably in a multi-stage process in a muhi-stage reaction sequence as described in WO 92/12182. The contents of this document are included herein by reference.
It has previously been known to produce multimodal, in particular bimodal, polypropylene in two or more reactors connected in series, i.e. in different steps (a) and (b).
According to the present invention, the main polymerization stages are preferably carried out as a combination of a bulk polymerization/gas phase polymerization.
The bulk polymerizations are preferably performed in a so-called loop reactor.

In order to produce the multimodal polypropylene according to this invention, a flexible mode is preferred. For this reason, it is preferred that the composition be produced in two main polymerization stages in combination of loop reactor/gas phase reactor.
Optionally, and preferably, the process may also comprise a prepolymerization step in a manner known in the field and which may precede the polymerization step (a).
If desired, a further elastomeric comonomer component, so called ethylene-propylene rubber (EPR) component as in this invention, may be incorporated into the obtained polypropylene homopolymer matrix to form a propylene copolymer as defined above. The ethylene-propylene rubber (EPR) component may preferably be produced after the gas phase polymerization step (b) in a subsequent second or further gas phase polymerizations using one or more gas phase reactors.
The process is preferably a continuous process.
Preferably, in the process for producing the propylene polymer as defined above the conditions for the bulk reactor of step (a) may be as follows:
the temperature is within the range of 40 °C to 110 °C, preferably between
60 °C and 100 "0,70 to 90 °C,
the pressure is within the range of 20 bar to 80 bar, preferably between 30 bar
to 60 bar,
hydrogen can be added for controlling the molar mass in a manner known per
se.
Subsequently, the reaction mixture from the bulk (bulk) reactor (step a) is transferred to the gas phase reactor, i.e. to step (b), whereby the conditions in step (b) are preferably as follows:

the temperature is within the range of 50 °C to 130 °C, preferably between
60 °C and 100 °C,
the pressure is within the range of 5 bar to 50 bar, preferably between 15 bar
to 35 bar,
hydrogen can be added for controlling the molar mass in a manner known per
se.
The residence time can vary in both reactor zones. In one embodiment of the process for producing the propylene polymer the residence time in bulk reactor, e.g. loop is in the range 0.5 to 5 hours, e.g. 0.5 to 2 hours and the residence time in gas phase reactor will generally be 1 to 8 hours.
If desired, the polymerization may be effected in a known manner under supercritical conditions in the bulk, preferably loop reactor, and/or as a condensed mode in the gas phase reactor.
The process of the invention or any embodiments thereof above enable highly feasible means for producing and further tailoring the propylene polymer composition within the invention, e.g. the properties of the polymer composition can be adjusted or controlled in a known manner e.g. with one or more of the following process parameters: temperature, hydrogen feed, comonomer feed, propylene feed e.g. in the gas phase reactor, catalyst, the type and amount of an external donor (if used), split between components.
The above process enables very feasible means for obtaining the reactor-made polypropylene as defined above.
The capacitor fihn can be prepared by conventional drawing processes known in the art. Accordingly the process for the manufacture of a capacitor film according to this

invention comprises the use of the polypropylene as defined herein and its forming into a film preferably by the tenter method known in the art.
The tenter method is in particular a method in which the polypropylene as defined herein is melt extruded fi-om a slit die such as a T-die and cooled on a cooling drum obtaining an undrawn sheet. Said sheet is pre-heated for example with a heated metal roil and then drawn in the length direction between a plurality of rolls over which a difference in peripheral speeds is established and then both edges are gripped with grippers and the sheet is drawn in the transverse direction in an oven by means of a tenter resulting in a biaxially drawn film. The temperature of said stretched sheet during the longitudinal drawing is preferably controlled in such a way as to be within the temperature range of the melting point of the polypropylene as defined herein (-15 or + 5°C). The uniformity of the film thickness on transverse drawing can be evaluated with the method in which a fixed region on the film is masked after drawing in the length direction and measuring the actual drawing factor by measuring the spacing of the said masking after transverse drawing.
Subsequently, the film can treated by corona discharge in air, nitrogen, carbon dioxide gas or any of the mixtures on the surface to be metallized, lo improve the adhesive strength to the metal to be deposited, and wound by a winder.
The obtained film can set in a vacuum metallizer, and the film is preferably coated with an oil to form an insulation groove suitable for the purpose concerned, using a gravure coater, etc. Then, the metal suitable for the purpose concerned is deposited to achieve a predetermined layer resistance. Furthermore, as required, metallization is carried out through a comb-shaped deposition preventive plate to continuously change the resistance value in the transverse direction of the film. The metallized film is slit, to make two metallized reels as a pair for making a capacitor device. Then, the reels are wound to form a device and the device is formed to be fiat by a

thermal press, being followed by metal spraying at the ends, attaching of leads, as required impregnation with an insulating oil, and packaging to make a capacitor.Morcover the present invention is directed to the use of the capacitor film as defined herein in a capacitor.
In addition, the present invention is directed to a capacitor comprising at least on layer comprising a capacitor film as defined herein. Additionally it is preferred that the capacitor comprises a metal layer, in particular a metal layer obtained by the above described process.The present invention will now be described in fiirther detail by the following examples.
Examples
1. Deflnitions/Measuring Methods
The following definitions of terms and determination methods apply for the above general description of the invention as well as to the below examples unless otherwise defined.
A. Pentad Concentration
For the meso pentad concentration analysis, also referred herein as pentad concentration analysis, the assignment analysis is undertaken according to T Hayashi, Pentad concentration. R. Chujo and T. Asakura, Polymer 29 138-43 (1988) and Chujo R, et al., Polymer 21339 (1994)
B. Elementary Analysis
The below described elementary analysis is used for determining the content of elementary residues which are mainly originating fi«m the catalyst, especially the A1-, B-, and Si-residues in the polymer. Said AI-, B- and Si-residues can be in any

form, e.g. in elementary or ionic form, which can be recovered and detected from polypropylene using the below described ICP-method. The method can also be used for determining the Ti-content of the polymer. It is understood that also other known methods can be used which would result in similar results.
ICP-Spectrometry (Inductively Coupled Plasma Emission)
ICP-instrument: The instrument for determination of A1-, B- nad Si-content is TCP
Optima 2000 DV, PSN 620785 (supplier Perkin Elmer Instruments, Belgium) with
software of the instrument.
Detection limits are 0.10 ppm (Al), 0.10 ppm (B), 0.10 ppm (Si).
The polymer sample was first ashed in a known manner, then dissolved in an
appropriate acidic solvent. The dilutions of the standards for the calibration curve are
dissolved in the same solvent as the sample and the concentrations chosen so that the
concentration of the sample would fall within the standard calibration curve.
ppm: means parts per million by weight
Ash content: Ash content is measured according to ISO 3451-1 (1997) standard.
Calculated ash, Al- Si- and B-content:
The ash and the above listed elements, Al and/or Si and/or B can also be calculated
form a polypropylene based on the polymerization activity of the catalyst as
exemplified in the examples. These values would give the upper limit of the presence
of said residues originating fiom the catalyst.
Thus the estimate catalyst residue is based on catalyst composition and
polymerization productivity, catalyst residues in the polymer can be estimated
according to:
Total catalyst residues [ppm] = 1 / productivity [kgpp/gcataiyst] x 100
Al residues [ppm] = WAI, cawiyst [%] x total catalyst residues [ppm] / 100

Zr residues [ppm] = wzj^, catalyst [%] x total catalyst residues [ppm] /100 (Similar calculations apply also for B, CI and Si residues)
Chlorine residues content: The content of Cl-residues is measured from samples in the known manner using X-ray fluorescence (XRF) spectrometry. The instrument was X-ray fluorescention Philips PW2400, PSN 620487, (Supplier: Philips, Belgium) software X47. Detection limit for CI is 1 ppm.
C. Particle size distribution
Particle size distribution is measured via Coulter Counter LS 200 at room temperature with n-heptane as medium.
D. NMR
NMR-spectroscopy measurements:
The '^C-NMR spectra of polypropylenes were recorded on Bruker 400MHz spectrometer at 130 °C from samples dissolved in l,2,4-trichlorobcnzene/benzenc-d6 (90/10 w/w). For the pentad analysis the assignment is done according to the methods described in literature: (T, Hayashi, Y. Inoue, R. Chiijo, and T. Asakura, Polymer 29 138-43 (1988).and Chujo R, et al,Polymer 35 339 (1994). The NMR-measurement was used for determining the mmmm pentad concentration in a manner well known in the art.
E. M„,Mw,MWD
Number average molecular weight (Mn), weight average molecular weight (Mw) and molecular weight distribution (MWD) are determined by size exclusion chromatography (SEC) using Waters Alliance GPCV 2000 instrument with online viscometer. The oven temperature is 140 °C. Trichlorobenzene is used as a solvent (ISO 16014).

F. Xylene Solubles (XS)
The xylene solubles (XS, wt,-%): Analysis according to the known method: 2.0 g of
polymer Ls dissolved in 250 ml p-xylenc at 135°C under agitation. After 30±2
minutes the solution is allowed to cool for 15 minutes at ambient temperature and
then allowed to settle for 30 minutes at 25±0.5°C. The solution is filtered and
evaporated in nitrogen flow and the residue dried under vacuum at 90 °C until
constant weight is reached.
XS% = (100 X mi X vo) / (mo x vi), wherein
mo = initial polymer amount (g)
mi = weight of residue (g)
vo= initial volume (ml)
Vi = volume of analyzed sample (ml)
G. Melting temperature
Melting temperature Tm, crystallization temperature Tc, and the degree of crystallinity: measured with Mettler TA820 differential scanning calorimetry (DSC) on 5-10 mg samples. Both crystallization and melting curves were obtained during 10 °C/min cooling and heating scans between 30 °C and 225 °C. Melting and crystallization temperatures were taken as the peaks of endothenus and exotherms. Also the melt- and crystallization enthalpy (Hm and He) were measured by the DSC method according to ISO 11357-3.
H. Melt Flow Rate
I. MFRz: measured according to ISO 1133 (230°C, 2.16 kg load).
J. Comonomer content
Comonomer content is measured with Fourier transform infrared spectroscopy (FTIR) calibrated with '^C-NMR. When measuring the ethylene content in polypropylene, a thin film of the sample (thickness about 250 (.im) was prepared by

hot-pressing. The area of-CH2- absorption peak (800-650 cm') was measured with Perkin Elmer FTIR 1600 spectrometer. The method was calibrated by ethylene content data measured by'^C-NMR.
K. Stiffness
Stiffness Fibn TD (transversal direction), Stiffness Film MD (machine direction), Elongation at break TD and Elongation at break MD: these are determined according to 1S0527-3 (cross head speed: 1 mm/min). The cast film has a thickness of 100 [im, whereas the thickness of the stretched films are indicated in the tables 3 and 4.
L. Haze and transparency:
Haze and transparency: are determined: ASTM D1003-92 (thickness 100 |.im).
M. Intrinsic viscosity
Intrinsic viscosity: is measured according to DIN ISO 1628/1, October 1999 (in Decalinat 135°C).
N. Porosity
Porosity: is measured according to DTN 66135.
O. Surface area
Surface area: is measured according to ISO 9277.
P. SIST
Stepwise Isothermal Segregation Technique (SIST): The isothermal crystallisation
for SIST analysis was performed in a Mettler tA820 DSC on 3±0.5 mg samples at
decreasing temperatures between 200°C and 105°C.
(i) The samples were melted at 225 °C for 5 min.,
(ii) then cooled with 80 °C/min to 145 °C

(iii) held for 2 hours at 145 °C,
(iv) then cooled with 80 °C/min to 135 °C
(v) held for 2 hours at 135 °C,
(vi) then cooled with 80 °C/min to 125 °C
(vii) held for 2 hours at 125 °C,
(viii) then cooled with 80 °C/min to 115 °C
(ix) held for 2 hours at 115 °C,
(x) then cooled with 80 °C/min to 105 °C
(xi) held for 2 hours at 105 °C.
After the last step the sample was cooled down to ambient temperature, and the
melting curve was obtained by heating the cooled sample at a heating rate of
10°C/min up to 200°C. All measurements were performed in a nitrogen atmosphere.
The mch enthalpy is recorded as function of temperature and evaluated through
measuring the meh enthalpy of fractions melting within temperature intervals as
indicated for example E 1 in the table 6 to 8.
The melting curve of the material crystallised this way can be used for calculating
the lamella thickness distribution according to Thomson-Gibbs equation (Eq 1.).

where To=457K, AHo =184xl0^J/m\ a =0,049.6 jW and L is the lamella thickness.
Q. Electrical breakdown strength (EB63%)
It follows standard lEC 60243- part 1 (1988).
The method describes a way to measure the electrical breakdown strength for
insulation materials on compression moulded plaques.
Definition:

The electrical field strength in the test sample at which breakdown occurs. In homogeneous plaques and films this corresponds to the electrical breakdown strength divided by the thickness of the plaque/film (d), unit: kV/mm. The electrical breakdown strength is determined at 50 Hz within a high voUage cabinet using metal rods as electrodes as described in IEC60243-1 (4.1.2). The voltage is raised over the film/plaque at 2 kV/s until a breakdown occurs.
3. Examples
Inventive Example 1 (£ 1) Catalyst preparation
The catalyst was prepared as described in example 5 of WO 03/051934, with the Al¬and Zr-ratios as given in said example (AJ/Zr = 250). Catalyst characteristics:
Al- and Zr- content were analyzed via above mentioned method to 36,27 wt.-% Al and 0,42 %-wt. Zr. The average particle diameter (analyzed via Coulter counter) is 20 ^m and particle size distribution is shown in Fig. 3. Polymerization
A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.2 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 15 mmol hydrogen (quality 6.0, supplied by Aga) as chain transfer agent. Reactor temperature was set to 30 °C. 29.1 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 50 minutes at 70 °C, then propylene was flushed out, 5 mmol hydrogen were fed and the reactor pressure was increased to 20

bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 144 minutes, then the reactor was flashed, the polymer was dried and weighted. Polymer yield was weighted to 901 g, that equals a productivity of 31 kgpp/gcataiyst-lOOOppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been melt compounded with a Prism TSE16 lab kneader at 250rpm at a temperature of 220-230°C.
Inventive Example 2 (E 2)
A catalyst as used in 11 has been used.
A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.5 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 50 mmol hydrogen (quaUty 6.0, supplied by Aga) as chain transfer agent. Reactor temperature was set to 30 °C. 19.9 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 40 minutes at 70 °C, then propylene was flushed out, the reactor pressure was increased to 20 bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 273 minutes, then the reactor was flashed, the polymer was dried and weighted.
Polymer yield was weighted to 871 g, that equals a productivity of 44 kgpp/gcatsiysc. lOOOppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been meh compounded with a Prism TSE16 lab kneader at 250rpm at a temperature of 220-230°C.
Inventive Example 3 (£ 3)
A 5 liter stainless steel reactor was used for propylene polymerizations. 1100 g of liquid propylene (Borealis polymerization grade) was fed to reactor. 0.1 ml triethylaluminum (100%, purchased from Crompton) was fed as a scavenger and 30 mmol hydrogen (quality 6.0, supplied by Aga) as chain transfer agent. Reactor

temperature was set to 30 °C. 21.8 mg catalyst were flushed into to the reactor with nitrogen overpressure. The reactor was heated up to 70 °C in a period of about 14 minutes. Polymerization was continued for 30 minutes at 70 °C, then propylene was flushed out and subsequently, the reactor pressure was increased to 20 bars by feeding (gaseous-) propylene. Polymerization continued in gas-phase for 256 minutes, then the reactor was flashed, the polymer was dried and weighted. Polymer yield was weighted to 953 g, that equals a productivity of 43.72 kgpp/gcutniyjt. 1000 ppm of a commercial stabilizer Irganox B 215 (FF) (Ciba) have been added to the powder. The powder has been melt compounded with a Prism TSE16 lab kneader at 250 rpm at a temperature of 220 to 230 °C.
Comparative Example 1 (CE 1)
A commercial polypropylene homopolymer of Borealis has been used.
Comparative Example 2 (CE 2)
A commercial polypropylene homopolymer of Borealis has been used. In Tables 1,2 and 3, the properties of samples CE 1, CE 2, E 1 and E2 are summarized.

Table 1: Properties of polypropylene according to the invention and
comparative examples
Unit CEl CE2 El E2 E3
Ash ppm 15 13 85 n.a. 74
rac % 98 98 98
MFR g/10' 2,1 2,1 2 5,3 1,1
Mw g/mol 412000 584000 453000 405000 207000
Mw/Mn - 9,9 8,1 2,8 5,3 4,5
XS wt% 1,2 3,5 0,85 0,66 0,70
mmmm - 0,95 0,95 0,95
Tm °C 162 162 150,6 150,8 150,9
Hm J/g 107 100 99,5 100,1 98,7
To °C 115 113 111,9 111,2 105,9
He J/g 101 94 74,6 92,8 90,5

Table 2: Preparation of the cast film and characterization
Cast film with OCS equipment, thickness constant at 90-11 On,m.
Unit CEl CE2 El E2 E3
Stiffness Film TD MPa 960 756 1011 n.a. 710
Stiffness Film MD MPa 954 752 1059 n.a. 716
Elongation at Break n.a. 601
TD % 789 792 700
Elongation at Break n.a. 723
MD % 733 714 691
Transparency % 94 94 94 n.a. 94
Haze % 24,2 19,9 7,8 n.a. 3

Table 3: Preparation ofBOPP film and characterization
VTT Tampere, 4x4 Orientation
Code Unit CE1 CE 2 El E2 E3
EB63% kV/mm 210 224 291 388 431
90% LOWER CONF: kV/mm 197 203 267 349 383
90% UPPER CONF: kV/mm 223 244 311 425 480
BETA: none 10,4 6,9 8,3 6,5
Stress MD4 MPa 4,3 3,8 3,6 2,7 ca. 4
Stress TD4 MPa 3,4 3,1 3,0 2.5 ca. 4
Stiffness Film 4x4
MPa 3003 3138 2550 2020 2105
MD
Stiffiicss Film 4x4 TD MPa 2943 2691 2824 2554 1835
Elongation at Break
% 52 53 80 62 72
Film 4x4 MD
Elongation at Break
% 50 60 34 41 54
Film 4x4 TD
Tm ONSET Film 4x4 °C 141 136 137 n.a. 148
Tm Film (1"* melting
°C 156 158 154 157 158
4x4)
Hm Film (1* melting
J/g 56 66 70 92 80
4x4)
Tc Film 4x4 °C 111 112 112 114 108
He Film 4x4 J/g 80 78 77 90 96
Tm Film (2"' melting
°C 167 165 156 154 153
4x4)
Hm Film (Z"** melting
J/g 74 73 69 89 96
4x4)
Film Thickness ^m 30 30 30 30 30

Table 4: Preparation of BOPP film and characterization
VTT Tampere, 5x5 Orientation
Code Unit E2 E3
EB63% kV/mm 638 582
90% LOWER CONF: kV/mm 563 579
90% UPPER CONF: kV/mm 707 585
BETA: none 5,6
Stress MD5 MPa 3,5 ca. 4
Stress TD5 MPa 3,4 ca. 4
Stiffness Film 5x5 MD MPa 2271 2055
Stiffness Film 5x5 TD MPa 2445 2464
Elongation at Break Film 5x5 MD % 39 38
Elongation at Break Film 5x5 TD % 19 18
Tm ONSET Film 5x5 °C n.a. 142
Tm Film (1" melting 5x5) °C 152 154
Hm Film (1" melting 5x5) J/g 83 56
Tc Film 5x5 °C 109 109
He Film 5x5 J/g 95 95
Tm Film (2"'melting 5x5) °C 153 151
Hm Film (2"'melting 5x5) J/g 100 93
Film Thickness |.im 30 30

A biaxiaily oriented film is prepared as follows:
In the biaxial stretching Device Bruckner Karo IV, film samples are clamped and extended in both, longitudinal and transverse direction, at constant stretching speed. The length of the sample increases during stretching in longitudinal direction and the stretch ratio in longitudinal direction calculates from the ratio of current length over original sample length. Subsequently, the sample is stretched in transverse direction where the width of the sample is increasing. Hence, the stretch ratio calculates from the current width of the sample over the original width of the sample. In Table 5 the ci7Stallization behaviour of samples is determined via stepwise isothermal segregation technique (SIST).
Table 5: Results from stepwise isothermal segregation technique (SIST) -1
El E3 CEl CE2
Peak ID Range m H„ [J/g] H™ [J/g] H„. [J/g] H„ [J/g]
1 2 110-120 3,8 3,6 1,0 1,4
3 120-130 4,8 6,7 2.0 2,6
4 130-140 11,4 19,1 3,9 4,8
5 140-150 27,5 35,0 10,6 12,8
6 150-160 29,2 34,1* 25,4 32,1
7 160-170 16,9 50,7 56,6
8 >170 0,1 37.5 14,3
Hm= melting enthalpy
*>150°C

Table 6: Results from stepwise isothermal segregation technique (SIST) - II
El E3 CEl CE2
T fiom T to H„ [J/g] H„ [J/gl H„ [J/g] H™ [J/g]
0 110 6 6,6 0,6 1
110 120 3,8 3,6 1 1,4
120 130 4,8 6,7 2 2,6
130 140 11,4 19,1 3,9 4,8
140 150 27,5 35 10.6 12,8
150 160 29,2 34,1 25,4 32,1
160 170 16,9 50,7 56,6
170 0,1 37,5 14,3
99,7 105,1 131,7 125,6
Table 7: Results from stepwise isothermal segregation technique (SIST) - III
Lfrom Lto Fraction [wt%]
m m El E3 CEl CE2
0 3,30E-09 6,0% 6,3% 0.5% 0.8%
3,30E-09 3,81E-09 3,8% 3.4% 0.8% 1,1%
3,81E-09 4,52E-09 4,8% 6,4% 1,5% 2,1%
4,52E-09 5,55E-09 11,4% 18,2% 3.0% 3,8%
5,55E-09 7,19E-09 27,6% 33,3% 8.0% 10,2%
7,19E-09 l,02E-08 29,3% 32.4% 19,3% 25,6%
l,02E-08 l,76E-08 17,0% 0,0% 38,5% 45.1%
l,76E-08 0,1% 0,0% 28,5% 11,4%
100,0% 100,0% 100,0% 100,0%

Table 8: Results from stepwise isothermal segregation technique (SIST) - IV
Label El E3 CE1 CE2
3,3nm-3.81nm 4% 3% 1% 1%
3,81nm-4,52nm 5% 6% 2% 2%
4,52nm - 5,55nm 11% 18% 3% 4%
5,55nm-7,19nm 28% 33% 8% 10%
7,19nm-10.21nm 29% 32% 19% 26%
10,21nm-17,57nm 17% 0% 38% 45%
>17,57nm 0% 0% 28% 11%

New Claims
1. Capacitor film comprising a biaxially oriented propylene homopolymer wherein
a) said propylene homopolymer has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and
b) said propylene homopolymer and/or said capacitor film has(have) an electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction and in transverse direction of 4.0.

2. Capacitor film according to claim 1, wherein said propylene homopolymer has a draw ratio in machine direction in the range of 4.0 to 8.0 and a draw ratio in transverse direction of 6.0 to 10.0.
3. Capacitor film according to claim 1 or 2, wherein said propylene homopolymer has electrical breakdown strength EB63% according to lEC 60243-part 1 (1988) of at least 500 kV/mm at a draw ratio in machine direction and in transverse direction of 5.0.
4. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have xylene solubles (XS) of at least 0.5 wt.-%.
5. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer comprise(s) at least 20 wt.-% of a fraction of lamellae with a thickness of 6. Capacitor film according to any one of the preceding claims, wherein the film andJor the propylene homopolymer has/have xylene solubles In the range of 0.5 to 1.5 wt.-%.
LB;CH:sh

7. Capacitor film according any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have a tensile modules of at least 1800 MPa at a draw ratio of 4.0 in machine direction and a draw ratio of 4.0 in transverse direction, measured according to ISO 527-3 at a cross head speed of 1 mm/min.
8. Capacitor film according any one of the preceding claims, wherein the film has a stretching stress of at least 2.5 MPa in machine direction and transverse direction at a
' stretching temperature of 152 "C or less and a draw ratio of 4.0 in machine direction
and transverse direction.
9. Capacitor film according to any one of the preceding claims, wherein the film and/or the propylene homopolymer has/have a melting point Tm of at least 148 °C.
10. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer is multimodal.
11. Capacitor film according to any one of the preceding claims I to 9, wherein the propylene homopolymer is unimodal.
12. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has molecular weight distribution (MWD) measured according to ISO 16014 of not more than 8.00.
13. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has a melt flow rate MFRa measured according to ISO 1133 of up to lOg/lOmin.
14. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has a mmmm pentad concentration of higher than 94 % determined by NMR-spectroscopy.

15. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has been produced in the presence of a catalytic system comprising metallocene complex, wherein the catalytic system has a porosity measured according to DIN 66135 of less than 1.40 ml/g.
16. Capacitor film according to any one of the preceding claims, wherein the propylene homopolymer has been produced in the presence of a symmetric metallocene complex.
17. Use of the capacitor film according to any one of the preceding claims in a capacitor.
18. Capacitor comprising at least on layer comprising a capacitor film according to any one of the preceding claims I to 16.
19. A process for the preparation of a capacitor film according to any one of the preceding claims 1 to 16, wherein a propylene homopolymer according to any one of the claims 1 to 16 is formed into a biaxially oriented film with a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and wherein the propylene homopolymer is prepared using a catalyst system of low porosity, the catalyst system comprising a symmetric catalyst, wherein the catalyst system has a porosity measured according to DIN 66135 of less than 1.40 ml/g and a surface area of less than 25 mVg measured according to ISO 9277.
20. The process according to claim 19, the catalyst system being a non-silica supported system.
21. The process according to claim 19 or 20, wherein the catalyst system has a porosity below the detection limit of DIN 66135.

22. The process according to any one of the preceding claims 19 to 21, wherein the symmetric catalyst is a transition metal compound of formula (I)

wherein
M is Zr, Hf or Ti, more preferably Zr
X is independently a monovalent anionic ligand, such as a-ligand
R is a briding group linking the two Cp ligands
Cp is an organic ligand selected from the group consisting of unsubstituted
cyclopenadienyl, unsubstituted indenyl, unsubstituted tetrahydroindenyl,
unsubstituted fluorenyl, substituted cyclopenadienyl, substituted indenyl,
substituted tetrahydroindenyl, and substituted fluorenyl,
with the proviso that both Cp-ligands are selected from the above stated group
and both Cp-ligands are chemically the same, i.e. are identical.

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=KeMYlundpUdWBahXeQU0iA==&loc=egcICQiyoj82NGgGrC5ChA==

« Previous Patent

Next Patent »

Patent Number

269203

Indian Patent Application Number

6551/CHENP/2009

PG Journal Number

42/2015

Publication Date

16-Oct-2015

Grant Date

09-Oct-2015

Date of Filing

06-Nov-2009

Name of Patentee

BOREALIS TECHNOLOGY OY

Applicant Address

P.O.BOX 330, FI-06101 PORVOO,

Inventors:

#	Inventor's Name	Inventor's Address
1	STADLBAUER, MANFRED	DORNACHERSTRASSE 15, A-4040 LINZ,
2	ERNST,EBERHARD	HATTMANNSDORF 6, A-4210 UNTERWEITERSDORF
3	HUHTANEN, LAURI	PEIKKOVUORENTIE 13, FIN-07940 LOVIISA
4	DANIELS, YVO	ENGSTEGENSEWEG 24, B-3520 ZONHOVEN
5	JACOBS, FRANCK	REIBROEKSTRAAT 58, B-9940 EVERGEM

PCT International Classification Number

C08F10/06

PCT International Application Number

PCT/EP08/55663

PCT International Filing date

2008-05-07

PCT Conventions: