Title of Invention | EXHAUST GAS TREATMENT CATALYST AND EXHAUST GAS TREATMENT SYSTEM |
---|---|
Abstract | Provided are an exhaust gas treatment catalyst capable of reducing ammonia leakage rate while keeping a sufficient NOx removal efficiency, said catalyst comprising a coating layer and a catalyst base material, wherein said coating layer has a decreased thickness relative to that of a catalyst base material; and an exhaust gas treatment system using the same. In the exhaust gas treatment catalyst for catalytically removing nitrogen oxides from an exhaust gas by using ammonia as a reducing agent and simulatneously decomposing and removing unreacted ammonia, a coating layer comprising platinum supported on titania is formed on a surface of a porous catalyst base material comprising titania and at least one compound selected from oxides of vanadium (V), oxides of tungsten (W) and oxides of molybdenum (Mo). |
Full Text | FORM 2 THE PATENTS ACT, 1970 (39 of 1970) & THE PATENS RULES, 2003 COMPLETE SPECIFICATION [See section 10, Rule 13] EXHAUST GAS TREATMENT CATALYST AND EXHAUST GAS TREATMENT SYSTEM; MITSUBISHI HEAVY INDUSTRIES, LTD., A JAPANESE CORPORATION, WHOSE ADDRESS IS 16-5, KONAN 2-CHOME, MINATO-KU, TOKYO 108-8215, JAPAN THE FOLLOWING SPECIFICATION PARTICULARLY DESCRIBES THE INVENTION AND THE MANNER IN WHICH IT IS TO BE PERFORMED. 1 DESCRIPTION TECHNICAL FIELD The present invention relates to an exhaust gas treatment catalyst and an exhaust gas treatment system. BACKGROUND ART In order to denitrate combustion exhaust gas, ammonia (NH3) is used as a reducing agent for decomposing nitrogen oxides (NOx) into nitrogen (N2) and water vapor (H2O). In this denization reaction, a DeNOx (denitration) catalyst is used in order to improve the reaction rate and reaction efficiency. For improving the decomposition rate of NOx, it is only necessary to improve a NH3/NOX molar ratio when NH3 is added. When the NH3/NOx molar ratio is increased excessively, however, unreacted ammonia may be mixed into an exhaust gas. The resulting exhaust gas, when released in the atmosphere, may possibly cause secondary pollution or the like due to leaked ammonia. Under such a situation, an exhaust gas purifying catalyst having a catalyst layer for the oxidation of unreacted ammonia is known as is disclosed in JP3436567 B. Such an exhaust gas purifying catalyst comprises a DeNOx catalyst layer as thick as approximately 0.5 mm formed using a DeNOx catalyst slurry. This layer is 2 essential to assure denitration reaction. Thickening of the DeNOx catalyst layer however increases a pressure loss so that the operation efficiency of a plant deteriorates. Another reason for thickening the DeNOx catalyst layer is that the catalyst carrier layer cannot be used as an exhaust gas purifying catalyst. DISCLOSURE OF THE INVENTION PROBLEM TO BE SOLVED BY THE INVENTION In view of the above situation, the present invention has been made. An object of the present invention is to provide an exhaust gas treatment catalyst and an exhaust gas treatment system capable of reducing ammonia leakage rate while keeping a sufficient NOx removal efficiency, comprising a catalyst base material and a coating layer, wherein said coating layer has a decreased thickness relative to that of the catalyst base material. MEANS FOR SOLVING THE PROBLEM To achieve the above object, the present invention may be characterized by an exhaust gas treatment catalyst capable of catalytically removing nitrogen oxides from an exhaust gas by using ammonia as a reducing agent while decomposing and removing unreacted ammonia, the catalyst comprising: a porous catalyst base material comprising titania and at least one compound selected from the group consisting of oxides of vanadium (V), oxides of tungsten (W) and oxides of molybdenum (Mo); and a coating layer formed at a surface of the porous catalyst base material, said coating layer comprising platinum supported on titania. 3 In one aspect, the present invention may be an exhaust gas treatment catalyst capable of catalytically removing nitrogen oxides from an exhaust gas by use of ammonia as a reducing agent while decomposing and removing unreacted ammonia, which is obtained by mixing a first catalyst slurry mixture comprising the platinum supported on titania with a second catalyst slurry prepared from titania and at least one compound selected from oxides of vanadium (V), oxides of tungsten (W) and oxides of molybdenum (Mo) to form a slurry mixture; and applying the slurry mixture to the surface of the porous catalyst base material. It is preferred that the coating layer may comprise platinum in an amount of 0.05 to 0.1 wt.% based on a total amount of the titania and platinum (Pt) comprised by the coating layer. In the exhaust gas treatment catalyst according to the present invention, the thickness of the coating layer may be preferably from 100 to 300 um. In one embodiment of the exhaust gas treatment catalyst according to the present invention, the platinum in the coating layer may be isolated from the oxides of vanadium. In another aspect, the present invention may be characterized by an exhaust gas treatment system capable of catalytically removing nitrogen oxides from an exhaust gas by use of ammonia as a reducing agent while decomposing and removing unreacted ammonia, wherein a DeNOx catalyst is placed on a side upstream of a gas flow and the exhaust gas treatment catalyst of the present invention is placed downstream of the 4 Preparation process of an exhaust gas treatment catalyst having a coating layer The coating layer is prepared by preparing a catalyst slurry, applying it to the porous catalyst base material, and calcining the resulting material. The following is one examples of this process. In one embodiment of this process, spherical titania (having diameter of 2 to 4 mm) is impregnated in an aqueous platinum solution such as an aqueous platinum chloride solution (H2PtCl6) to support from 0.05 to 0.1 wt.% of Pt on the spherical titania. After drying, the resulting titania is calcined at from 450 to 500°C for 3 to 5 hours to obtain Powder catalyst 1. Water is added to the resulting Powdery catalyst 1, followed by wet ball-mill grinding to obtain Catalyst slurry 1 (ammonia oxidation catalyst slurry). Similarly, water is added to Powder catalyst 2 obtained by mixing at least one compound selected from vanadium oxides, tungsten oxides, and molybdenum oxides and titanium oxide and grinding the resulting mixture in a wet ball mill to obtain Catalyst slurry (DeNOx catalyst slurry) 2. In this case it is preferred to mix the oxides at a V/W/Ti atomic ratio of (from 0.1 to 0.6)/(from 3 to 9)/(from 70 to 80) or at a V/Mo/Ti atomic ratio of (from 0.1 to 0.6)/(from 3 to 9)/(from 70 to 80). Catalyst slurry 3 is prepared by mixing from 30 to 40 parts by weight of Catalyst slurry 1 and from 60 to 70 parts by weight of Catalyst slurry 2, each adjusted to an equal slurry concentration. A porous catalyst base material, for example, a porous honeycomb catalyst 7 base material is impregnated in Catalyst slurry 3. After drying the resulting catalyst, it is calcined at from 450 to 500°C for from 3 to 5 hours. Catalyst slurry 3 is applied to the surface of the base material in an amount of from 85 to 115 g (thickness of the coating layer is from 85 to 115 um) per m2 of the surface area of the base material. The bifunctional catalyst thus obtained is an exhaust gas treatment catalyst having, on the porous catalyst base material thereof, a coating layer composed of a single layer containing titania having platinum supported thereon, that is, an ammonia oxidation catalyst and a DeNOx catalyst. When the coating layer is made of a single layer as described above, it is preferred to isolate the platinum from vanadium oxides in order to improve the catalytic activity of platinum upon oxidation of ammonia. The exhaust gas treatment catalyst according to the present invention functions to catalytically remove nitrogen oxides from the exhaust gas by using ammonia as a reducing agent while said catalyst also decomposes and removes unreacted ammonia. In short, it undergoes a denitration reaction and oxidative decomposition of ammonia as described below. Denitration reaction NO + NH3 + l/402 - N2 + 3/2H20 (1) Oxidative decomposition reaction of ammonia NH3 + 3/402 = 1/2N2 + 3/2H20 (2) NH3 + 5/402 = NO + 3/2H20 (3) The exhaust gas treatment catalyst according to the present invention can be 8 employed in an exhaust gas treatment system. Such an exhaust gas treatment system is an exhaust gas treatment system for catalytically removing nitrogen oxides from an exhaust gas by using ammonia as a reducing agent and at the same time, decomposing and removing unreacted ammonia. As a specific mode, an exhaust gas treatment system can be constructed by placing a DeNO* catalyst on the side upstream of a gas flow and then placing the exhaust gas treatment catalyst according to the present invention downstream of the DeNOx catalyst. Such an exhaust gas treatment system has an advantage of reducing a leaked amount of NH3 compared with that using only a DeNOx catalyst. EXAMPLE 1 Spherical titania (having a diameter of from 2 to 4 mm) was impregnated in an aqueous platinum chloride solution (HaPtCU) to support 0.05 wt.% of platinum (Pt) on the spherical titania. After drying, the resulting titania was calcined at 500°C for 5 hours to obtain Powder catalyst 1. Water was added to the resulting Powder catalyst (ammonia oxidation catalyst) 1, followed by grinding in a wet ball mill to obtain Catalyst slurry 1. Similarly, water was added to Powder catalyst (DeNOx catalyst) 2 composed of 0.6 part by weight of vanadium oxides, 9 parts by weight of tungsten oxides, and 80 parts by weight of titanium oxide and the resulting mixture was ground in a ball mill to obtain Catalyst slurry 2. Catalyst slurry 3 was prepared by mixing 35 parts by weight of Catalyst slurry 1 and 65 parts by weight of Catalyst slurry 2, each slurry being adjusted to an equal slurry concentration. A porous honeycomb catalyst base material (functioning as a DeNOx catalyst) serving as a porous catalyst base material and composed of 0.6 part by 9 weight of vanadium oxides, 9 parts by weight of tungsten oxides, and 80 parts by weight of titanium oxide was impregnated in Catalyst slurry 3. The resulting catalyst was dried and then calcined at 500°C for 5 hours. Catalyst slurry 3 was applied to the base material in an amount of 100 g (thickness of coating layer: about 100 um) per m2 of the surface area of the base material and the resulting honeycomb exhaust gas treatment catalyst was designated as Bifunctional catalyst 1. EXAMPLE 2 In a similar manner to that of Bifunctional catalyst 1 employed in Example 1 except a supported amount of platinum (Pt) was changed to 0.1 wt.%, Bifunctional Catalyst 2 was obtained. Comparative Example 1 ATi02-V205-W03 DeNOx catalyst (a Ti02:V205:W03 mass ratio = 80:0.6:9) was prepared in the following manner. To 3600 g of a metatitanic acid slurry (having a Ti02 content of 30 mass%) was added aqueous ammonia having an NH3 content of 25% to adjust the pH to 6.5. To the resulting mixture was added ammonium paratungstate powder to give a WO3 content of 9 mass% and the resulting mixture was wet kneaded for 2 hours. The resulting mass was dried and then calcined at 550°C for 5 hours to obtain powder composed of titanium oxide and tungsten oxide. To the resulting powder was added an aqueous solution of ammonium metavanadate to give a V2Os content of 0.6 mass%. The resulting mixture was mixed fully, dried, and calcined at 450°C for 4 hours to obtain Powder (A) composed of titanium oxide [TiQz], vanadium oxide [V205], and tungsten 10 oxide [WO3]. A kneader was charged with 1000 g of Powder (A), 25 g of carboxymethyl cellulose, and 12.5 g of polyethylene oxide. An adequate amount of water was added to the resulting mixture, followed by kneading for 30 minutes. The resulting kneaded mass was extruded to a 50 mm2 sheet and the sheet was dried and then calcined at 500°C for 5 hours. Comparative Example 2 In a similar manner to that employed in Example 1 except for the use of an aqueous palladium chloride solution instead of the aqueous platinum chloride solution ^PtCU), a catalyst was prepared. Performance test was performed using Bifunctional catalysts 1,2 and 5 and the DeNOx catalyst. The performance test was performed under the following conditions. Exhaust gas temperature: 380°C Exhaust gas flow rate: 2.3 Nm/sec NOx concentration: 500 ppm The results were shown in Table 1. 11 [Table 1] Use of the exhaust gas treatment catalyst according to the present invention enabled to reduce the concentration of leaked ammonia while maintaining the denitration efficiency at 95% and also enabled to decrease the thickness of the coating layer. 12 We Claim: [ 1 ] An exhaust gas treatment catalyst capable of catalytically removing nitrogen oxides from an exhaust gas by using ammonia as a reducing agent while decomposing and removing unreacted ammonia, the catalyst comprising: a porous catalyst base material comprising titania and at least one compound selected from the group consisting of oxides of vanadium (V), oxides of tungsten (W) and oxides of molybdenum (Mo); and a coating layer formed at a surface of the porous catalyst base material, said coating layer comprising platinum supported on titania. [2] The exhaust gas treatment catalyst according to Claim 1, which is obtained by mixing a first catalyst slurry mixture comprising the platinum supported on titania with a second catalyst slurry prepared from titania and at least one compound selected from oxides of vanadium (V), oxides of tungsten (W) and oxides of molybdenum (Mo) to form a slurry mixture; and applying the slurry mixture to the surface of the porous catalyst base material. [3] The exhaust gas treatment catalyst according to Claim 1 or 2, wherein the coating layer comprising the platinum in an amount of from 0.05 to 0.1 wt.% based on a total amount of the titania and platinum (Pt) comprised by the coating layer. [4] The exhaust gas treatment catalyst according to Claim 1, wherein the coating layer has a thickness of from 100 to 300 urn. [5] An exhaust gas treatment system capable of catalytically removing nitrogen oxides from an exhaust gas by using ammonia as a reducing agent while decomposing and removing unreacted ammonia, wherein a DeNOx catalyst is disposed upstream a gas flow and the exhaust gas treatment catalyst as claimed in any one of Claims 1 to 4 is 13 |
---|
Patent Number | 269589 | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Indian Patent Application Number | 1343/MUMNP/2009 | ||||||||||||
PG Journal Number | 44/2015 | ||||||||||||
Publication Date | 30-Oct-2015 | ||||||||||||
Grant Date | 28-Oct-2015 | ||||||||||||
Date of Filing | 16-Jul-2009 | ||||||||||||
Name of Patentee | MITSUBISHI HEAVY INDUSTRIES LTD. | ||||||||||||
Applicant Address | 16-5, KONAN 2-CHOME, MINATO-KU, TOKYO 108-8215, JAPAN | ||||||||||||
Inventors:
|
|||||||||||||
PCT International Classification Number | B01J23/652 | ||||||||||||
PCT International Application Number | PCT/JP2008/64203 | ||||||||||||
PCT International Filing date | 2008-08-07 | ||||||||||||
PCT Conventions:
|