Title of Invention	SPHEROIDAL CAST ALLOY AND METHOD FOR PRODUCING CAST PARTS FROM SAID SPHEROIDAL CAST ALLOY
Abstract	The invention relates to a spheroidal cast alloy for producing cast iron products with great mechanical strength, high wear-resistance and a high degree of ductility. Said alloy comprises the following as non-iron components: between 2.5 and 3.8 wt. % C, between 2.4 and 3.4 wt. % Si, between 0.02 and 0.08 wt. % P, between 0.02 and 0.06 wt. % Mg, between 0.01 and 0.05 wt. % Cr, between 0.002 and 0.02 wt. % Al, between 0.0005 and 0.015 wt. % S, between 0.0002 and 0.002 wt. % B and conventional impurities. According to the invention, the alloy contains between 3.0 and 3.7 wt. % C, between 2.6 and 3.4 wt. % Si, between 0.02 and 0.05 wt. % P, between 0.025 and 0.045 wt. % Mg, between 0.01 and 0.03 wt. % Cr, between 0.003 and 0.017 wt. % Al, between 0.0005 and 0.012 wt. % S and between 0.0004 and 0.002 wt. % B. The alloy is used for example to produce chassis parts or brake discs in the automobile industry.

Title of Invention

SPHEROIDAL CAST ALLOY AND METHOD FOR PRODUCING CAST PARTS FROM SAID SPHEROIDAL CAST ALLOY

Abstract

The invention relates to a spheroidal cast alloy for producing cast iron products with great mechanical strength, high wear-resistance and a high degree of ductility. Said alloy comprises the following as non-iron components: between 2.5 and 3.8 wt. % C, between 2.4 and 3.4 wt. % Si, between 0.02 and 0.08 wt. % P, between 0.02 and 0.06 wt. % Mg, between 0.01 and 0.05 wt. % Cr, between 0.002 and 0.02 wt. % Al, between 0.0005 and 0.015 wt. % S, between 0.0002 and 0.002 wt. % B and conventional impurities. According to the invention, the alloy contains between 3.0 and 3.7 wt. % C, between 2.6 and 3.4 wt. % Si, between 0.02 and 0.05 wt. % P, between 0.025 and 0.045 wt. % Mg, between 0.01 and 0.03 wt. % Cr, between 0.003 and 0.017 wt. % Al, between 0.0005 and 0.012 wt. % S and between 0.0004 and 0.002 wt. % B. The alloy is used for example to produce chassis parts or brake discs in the automobile industry.

Full Text	WO 2006/056334 PCT/EP2005/012160 Spheroidal cast alloy and method for producing cast parts from said spheroidal cast alloy The invention relates to a spheroidal cast alloy for cast iron products with great mechanical strength, high wear resistance and at the same time a high degree of ductility, comprising as non-iron constituents 2.5 to 3.8% by weight C, 2.4 to 3.4% by weight Si, 0.02 to 0.08% by weight P, 0.02 to 0.06% by weight Mg, 0.01 to 0.05% by weight Cr, 0.002 to 0.02% by weight Al, 0.0005 to 0.015% by weight S, 0.0002 to 0.002% by weight B and the conventional impurities. In motor vehicle construction, cast iron alloys are used for producing cast parts that must have high wear resistance, for example brake disks, which during the braking operation have to convert the kinetic energy of the vehicle into thermal energy. The brake disks can in this case reach temperatures of up to about 850°C. During the braking operation, not only the brake linings but also the brake disks are worn. Brake disks have irregular wear and often have to be replaced while still under warranty, involving high costs for the automobile manufacturer. In order that the wear on the surface of the brake disk takes place as evenly as possible, high demands are made of the crystalline structure and the homogeneity of the structure. The homogeneity can be improved by a suitable casting process. GB 832 666 discloses a cast iron alloy comprising as non-iron constituents 1.0 to 2.5% by weight C, 1.5 to 3.2% by weight Si, less than 1.15% by weight Mn, less than 0.5% by weight S and 0.001 to 0.05% by weight B. After casting, the graphite component takes on the compact form. Because the alloy does not contain any Mg there is no spheroidal graphite or vermicular graphite present, but rather a graphite formation that WO 2006/056334 PCT/EP2005/012160 - 2 - resembles temper carbon nodes of malleable cast iron predominates. The alloy contains 5 to 10% carbides in a predominantly pearlitic matrix, which has the consequence that the elongation at rupture becomes relatively low. In order to limit the formation of lamellar graphite, and consequently improve the modulus of elasticity, tellurium and bismuth are admixed as alloying elements. Higher elongation at rupture values are achieved by a subsequent heat treatment. US 2004/0112479-A1 discloses a further cast iron alloy, which preferably contains 3.7% by weight C, 2.5% by weight Si, 1.85% by weight Ni, 0.85% by weight Cu and 0.05% by weight Mo. This material is distinguished by an elongation of 20 to 16% with a tensile strength of 500 to 900 MPa and by a Brinell hardness of 180 to 290 HB. These properties are achieved after a time-consuming heat treatment, which comprises the following successive steps: 10 to 360 minutes of austenitizing at temperatures between 750 and 790°C, rapid cooling in a salt bath at a temperature between 300 and 400°C, 1 to 3 hours of austempering at temperatures between 3 00 and 400°C and cooling to room temperature. After this treatment, the material has a structure with an austenitic and ferritic microstructure. The material is distinguished by easier machinability than a cast iron that has been subjected to a conventional type of austempering. On the basis of this prior art, the object of the invention is to provide a cast iron alloy which is produced from elements that are as inexpensive as possible, the cast parts having the highest or greatest possible heat resistance and strength, in particular wear resistance, and at the same time a very high degree of ductility, without an additional heat treatmen3t. WO 2006/056334 PCT/EP2005/012160 - 3 - This object is achieved by a spheroidal cast alloy for cast iron products with great mechanical strength, high wear resistance and at the same time a high degree of ductility, comprising as non-iron constituents 2.5 to 3.8% by weight C, 2.4 to 3.4% by weight Si, 0.02 to 0.08% by weight P, 0.02 to 0.06% by weight Mg, 0.01 to 0.05% by weight Cr, 0.002 to 0.02% by weight Al, 0.0005 to 0.015% by weight S, 0.0002 to 0.002% by weight B and the conventional impurities, the alloy containing 3.0 to 3.7% by weight C, 2.6 to 3.4% by weight Si, 0.02 to 0.05% by weight P, 0.025 to 0.045% by weight Mg, 0.01 to 0.03% by weight Cr, 0.003 to 0.017% by weight Al, 0.0005 to 0.012% by weight S and 0.0004 to 0.002% by weight B. Preferred developments of the invention are provided by the dependent claims. It is of advantage that the alloy has the best possible strength-strain behavior. This is achieved by the spheroidal cast alloy containing 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight Cu. This is also achieved by the alloy containing 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn. It is also of advantage that the alloy has the best possible wear behavior. This is achieved by the alloy containing 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight Cu and 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn. This is also achieved by the alloy containing 0.1 to 1.5% by weight Mn, preferably 0.5 to 1.0% by weight Mn, and 0.05 to 1.0% by weight Cu, preferably 0.05 to 0.2% by weight Cu. The essential idea of the invention is to provide a cast iron alloy which has a Brinell hardness of over 22 0 and which is worn as evenly as possible when used WO 2006/056334 PCT/EP2005/012160 - 4 - as a brake disk. The graphite in the cast iron alloy may be of a spheroidal or vermicular, but not lamellar form. Although brake disks with lamellar graphite are inexpensive, they have lower resistance to temperature changes. As a result, so-called fire cracks can already occur after a short time in use, rapidly growing and leading to irregularities of the surface. An irregular surface in turn leads to irregular thermal loading, irregular wear and so-called brake juddering. Further applications of the spheroidal cast alloy according to the invention are axle and chassis parts for trucks and for passenger cars, such as for example wishbones, wheel carriers and pivot bearings, which are exposed to high mechanical and dynamic loads and in the case of a collision of the motor vehicle must plastically deform and must not rupture. Example 1 A brake disk was produced from the spheroidal cast alloy according to the invention. The chemical composition was 3.34% by weight C, 2.92% by weight Si, 0.62% by weight Cu, 0.17% by weight Mn, 0.038% by weight Mg, 0.025% by weight P, 0.021% by weight Cr, 0.01% by weight Al, 0.001% by weight S and 0.0008% by weight B, the remainder Fe and the conventional impurities. The brake disk was investigated for the number of spherulites, graphite content, graphite form and graphite size, pearlite content and Brinell hardness. Specimens from the brake disk were subjected to a tensile test in order to establish the strength-strain behavior. The number of spherulites is 384 +/-76 spherulites per mm2. The graphite content is 9.7 +/- 0.7%. The graphite form in accordance with DIN EN ISO 945 is 97.9% of the form VI. The size distribution in accordance with DIN EN ISO 945 is 45% of size 8, 42% of size 7 and 13% of size 6. The pearlite content is WO 2006/056334 PCT/EP2005/012160 - 5 - 84 +/- 1%. The Brinell hardness is 248 +/- 3 HB. In the tensile test, the following values were established: yield strength Rp0.2 = 474 MPa, tensile strength Rm = 778 MPa, elongation at rupture A5 = 11.4% and modulus of elasticity E = 165 to 170 kN/mm2. In comparison with the known materials for brake disks, it was possible to establish a much better oxidation behavior (see Figure 1) and a greatly reduced tendency to fire cracking (see Figures 2 and 3) . The oxidation behavior, and consequently also the wear behavior, is greatly improved by the addition of a mixture of copper and/or manganese to the spheroidal cast alloy. In Figure 1, the weight increase in grams per square meter and per day caused by oxidation at 700°C in air is represented. The material according to the invention shows a weight increase of about 9 g/m2.d, in comparison with a cast iron material for conventional brake disks with a weight increase of about 21 g/m2.d. The tests to test for fire cracking were carried out as follows: a sample with the dimensions 40 x 20 x 7 mm is subjected to at least 100 cycles comprising 7 seconds of heating up to 700°C and 6 seconds of quenching in water. Subsequently, transverse sections are produced and examined under a microscope and photographed. Figure 2 shows a microphoto of a commercially available brake disk with a fire crack 0.4 mm deep. Figure 3 shows a further microphoto of the brake disk according to the invention, to the same magnification, with a fire crack 0.14 mm deep. Example 2 A wishbone for passenger cars was produced from the spheroidal cast alloy according to the invention. The WO 2006/056334 PCT/EP2005/012160 - 6 - chemical composition was 3.5% by weight C, 2.85% by weight Si, 0.63% by weight Cu, 0.18% by weight Mn, 0.038% by weight Mg, 0.026% by weight P, 0.029% by weight Cr, 0.004% by weight Al, 0.001% by weight S and 0.0007% by weight B, the remainder Fe and the conventional impurities. In the tensile test, the following values were established: yield strength Rp0.2 = 465 MPa, tensile strength Rm = 757 MPa, elongation at rupture A5 = 11.1% and modulus of elasticity E = 165 to 170 kN/mm2. The Brinell hardness is 258 +/- 3 HB. Example 3 A wheel carrier for passenger cars was produced from the spheroidal cast alloy according to the invention. The chemical composition was 3.43% by weight C, 3.38% by weight Si, 0.71% by weight Cu, 0.2% by weight Mn, 0.037% by weight Mg, 0.047% by weight P, 0.043% by weight Cr, 0.012% by weight Al, 0.004% by weight S and 0.0008% by weight B, the remainder Fe and the conventional impurities. In the tensile test, the following values were established: yield strength Rp0.2 = 558 MPa, tensile strength Rm = 862 MPa and elongation at rupture A5 = 6.1%. The Brinell hardness is 288 HB. The number of spherulites in the microstructure was determined as 455 spherulites per mm2. Figure 4 shows the elongation at rupture A5 as a function of the tensile strength Rm. The solid line indicates the minimum values in accordance with the standard EN 1563 for cast iron with spheroidal graphite of types produced in the cast state. The measurements of the material according to the invention are entered in accordance with Examples 1 to 3 presented above. Figure 5 shows the elongation at rupture A5 as a function of the yield strength Rp0.2. The solid line indicates the minimum values in accordance with the WO 2006/056334 PCT/EP2005/012160 - 7 - standard EN 1563 for cast iron with spheroidal graphite of types produced in the cast state. The measurements of the material according to the invention are entered in accordance with Examples 1 to 3 presented above. The material properties of the spheroidal cast iron according to the invention are consequently far above the European standard EN 1563 for cast iron with spheroidal graphite and even reach the values of ADI (= Austempered Ductile Iron) , a cast iron material standardized in Europe under EN 1564 which is produced by a very complex heat treatment in relatively great wall thicknesses that can only be obtained by alloying the expensive elements nickel and/or molybdenum, and is consequently correspondingly expensive. Figure 6 shows the strength ranges against the elongation at rupture of the materials aluminum cast alloys, cast iron with spheroidal graphite, ADI and the material according to the invention with Examples 1 to 3 entered. The uniformity of the structure is also achieved by a novel casting process. The casting mold is divided horizontally instead of vertically, the brake disks being arranged horizontally and the filling of the casting mold being carried out from the middle toward the edge of the brake disk. This has the consequence that the casting mold is filled rotationally symmetrically and that the brake disk is uniformly cooled from the inside to the outside after casting. As a result, a uniform, homogeneous structure is created over the entire circumference of the brake disk. A subsequent heat treatment, which is time-consuming and incurs costs, is no longer required. WO 2006/056334 PCT/EP2005/012160 - 8 - Patent claims 1. A spheroidal cast alloy for cast iron products with great mechanical strength, high wear resistance and at the same time a high degree of ductility, comprising as non-iron constituents 2.5 to 3.8% by weight C, 2.4 to 3.4% by weight Si, 0.02 to 0.08% by weight P, 0.02 to 0.06% by weight Mg, 0.01 to 0.05% by weight Cr, 0.002 to 0.02% by weight Al, 0.0005 to 0.015% by weight S, 0.0002 to 0.002% by weight B and the conventional impurities, characterized in that the spheroidal cast alloy contains 3.0 to 3.7% by weight C, 2.6 to 3.4% by weight Si, 0.02 to 0.05% by weight P, 0.025 to 0.045% by weight Mg, 0.01 to 0.03% by weight Cr, 0.003 to 0.017% by weight Al, 0.0005 to 0.009% by weight S and 0.0004 to 0.002% by weight B. 2. The spheroidal cast alloy as claimed in claim 1, characterized in that the alloy contains 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight Cu. 3. The spheroidal cast alloy as claimed in claim 1, characterized in that the alloy contains 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn. 4. The spheroidal cast alloy as claimed in claim 1, characterized in that the alloy contains 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight WO 2006/056334 PCT/EP2005/012160 - 9 - Cu, and 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn. 5. The spheroidal cast alloy as claimed in claim 1, characterized in that the alloy contains 0.1 to 1.5% by weight Mn, preferably 0.5 to 1.0% by weight Mn, and 0.05 to 1.0% by weight Cu, preferably 0.05 to 0.2% by weight Cu. 6. The spheroidal cast alloy as claimed in at least one of claims 1 to 5, characterized in that, immediately after casting and cooling, the graphite component is of a spheroidal and/or vermicular form in respect of over 90% of the graphite present. 7. The spheroidal cast alloy as claimed in at least one of claims 1 to 6, characterized in that, immediately after casting and cooling, the crystalline structure of the cast part is of a pearlitic form in respect of 70 to 90%. 8. The spheroidal cast alloy as claimed in at least one of claims 1 to 7, characterized in that, immediately after casting and cooling, the crystalline structure of the cast part has 200 to 700 spherulites per mm2. 9. The spheroidal cast alloy as claimed in at least one of claims 1 to 8, characterized in that the cast part has a Brinell hardness of over 220. 10. The spheroidal cast alloy as claimed in at least one of claims 1 to 9, characterized in that the graphite particles have a size distribution of at least 30% of size 8, 10% to 70% of size 7 and at most 20% of size 6 in accordance with DIN EN ISO 945. WO 2006/056334 PCT/EP2005/012160 - 10 - 11. The spheroidal cast alloy as claimed in at least one of claims 1 to 10, characterized in that the cast part has an elongation at rupture A5 of 5 to 14% with a tensile strength Rm of 900 to 600 MPa. 12. The spheroidal cast alloy as claimed in at least one of claims 1 to 11, characterized in that the cast part has an elongation at rupture A5 of 5 to 14% with a yield strength Rp0.2 of 600 to 400 MPa. 13. The spheroidal cast alloy as claimed in at least one of claims 1 to 12, characterized in that it is used for chassis parts in motor vehicles. 14. The spheroidal cast alloy as claimed in at least one of claims 1 to 12, characterized in that it is used for wishbones in motor vehicles. 15. The spheroidal cast alloy as claimed in at least one of claims 1 to 12, characterized in that it is used for wheel carriers in motor vehicles. 16. The spheroidal cast alloy as claimed in at least one of claims 1 to 12, characterized in that it is used for pivot bearings in motor vehicles. 17. The spheroidal cast alloy as claimed in at least one of claims 1 to 12, characterized in that it is used for brake disks in motor vehicles. 18. A method for producing a cast part from a spheroidal cast alloy as claimed in one of claims 1 to 17, characterized in that, after the casting and cooling of the cast part, no heat treatment of the cast part is performed. 19. A method for producing a cast part as claimed in one of claims 1 to 18, characterized in that the WO 2006/056334 PCT/EP2005/012160 - 11 - casting mold is divided horizontally, the cast part being arranged horizontally in the casting mold. 20. A method for producing a rotationally symmetrical cast part as claimed in one of claims 1 to 19, characterized in that the casting mold is filled rotationally symmetrically from the middle point of the cast part. The invention relates to a spheroidal cast alloy for producing cast iron products with great mechanical strength, high wear-resistance and a high degree of ductility. Said alloy comprises the following as non-iron components: between 2.5 and 3.8 wt. % C, between 2.4 and 3.4 wt. % Si, between 0.02 and 0.08 wt. % P, between 0.02 and 0.06 wt. % Mg, between 0.01 and 0.05 wt. % Cr, between 0.002 and 0.02 wt. % Al, between 0.0005 and 0.015 wt. % S, between 0.0002 and 0.002 wt. % B and conventional impurities. According to the invention, the alloy contains between 3.0 and 3.7 wt. % C, between 2.6 and 3.4 wt. % Si, between 0.02 and 0.05 wt. % P, between 0.025 and 0.045 wt. % Mg, between 0.01 and 0.03 wt. % Cr, between 0.003 and 0.017 wt. % Al, between 0.0005 and 0.012 wt. % S and between 0.0004 and 0.002 wt. % B. The alloy is used for example to produce chassis parts or brake discs in the automobile industry.

Full Text

WO 2006/056334 PCT/EP2005/012160
Spheroidal cast alloy and method for producing cast parts from said spheroidal cast alloy
The invention relates to a spheroidal cast alloy for cast iron products with great mechanical strength, high wear resistance and at the same time a high degree of ductility, comprising as non-iron constituents 2.5 to 3.8% by weight C, 2.4 to 3.4% by weight Si, 0.02 to 0.08% by weight P, 0.02 to 0.06% by weight Mg, 0.01 to 0.05% by weight Cr, 0.002 to 0.02% by weight Al, 0.0005 to 0.015% by weight S, 0.0002 to 0.002% by weight B and the conventional impurities.
In motor vehicle construction, cast iron alloys are used for producing cast parts that must have high wear resistance, for example brake disks, which during the braking operation have to convert the kinetic energy of the vehicle into thermal energy. The brake disks can in this case reach temperatures of up to about 850°C. During the braking operation, not only the brake linings but also the brake disks are worn. Brake disks have irregular wear and often have to be replaced while still under warranty, involving high costs for the automobile manufacturer. In order that the wear on the surface of the brake disk takes place as evenly as possible, high demands are made of the crystalline structure and the homogeneity of the structure. The homogeneity can be improved by a suitable casting process.
GB 832 666 discloses a cast iron alloy comprising as non-iron constituents 1.0 to 2.5% by weight C, 1.5 to 3.2% by weight Si, less than 1.15% by weight Mn, less than 0.5% by weight S and 0.001 to 0.05% by weight B. After casting, the graphite component takes on the compact form. Because the alloy does not contain any Mg there is no spheroidal graphite or vermicular graphite present, but rather a graphite formation that

WO 2006/056334 PCT/EP2005/012160
- 2 -
resembles temper carbon nodes of malleable cast iron predominates. The alloy contains 5 to 10% carbides in a predominantly pearlitic matrix, which has the consequence that the elongation at rupture becomes relatively low. In order to limit the formation of lamellar graphite, and consequently improve the modulus of elasticity, tellurium and bismuth are admixed as alloying elements. Higher elongation at rupture values are achieved by a subsequent heat treatment.
US 2004/0112479-A1 discloses a further cast iron alloy, which preferably contains 3.7% by weight C, 2.5% by weight Si, 1.85% by weight Ni, 0.85% by weight Cu and 0.05% by weight Mo. This material is distinguished by an elongation of 20 to 16% with a tensile strength of 500 to 900 MPa and by a Brinell hardness of 180 to 290 HB. These properties are achieved after a time-consuming heat treatment, which comprises the following successive steps: 10 to 360 minutes of austenitizing at temperatures between 750 and 790°C, rapid cooling in a salt bath at a temperature between 300 and 400°C, 1 to 3 hours of austempering at temperatures between 3 00 and 400°C and cooling to room temperature. After this treatment, the material has a structure with an austenitic and ferritic microstructure. The material is distinguished by easier machinability than a cast iron that has been subjected to a conventional type of austempering.
On the basis of this prior art, the object of the invention is to provide a cast iron alloy which is produced from elements that are as inexpensive as possible, the cast parts having the highest or greatest possible heat resistance and strength, in particular wear resistance, and at the same time a very high degree of ductility, without an additional heat treatmen3t.

WO 2006/056334 PCT/EP2005/012160
- 3 -
This object is achieved by a spheroidal cast alloy for cast iron products with great mechanical strength, high wear resistance and at the same time a high degree of ductility, comprising as non-iron constituents 2.5 to 3.8% by weight C, 2.4 to 3.4% by weight Si, 0.02 to 0.08% by weight P, 0.02 to 0.06% by weight Mg, 0.01 to 0.05% by weight Cr, 0.002 to 0.02% by weight Al, 0.0005 to 0.015% by weight S, 0.0002 to 0.002% by weight B and the conventional impurities, the alloy containing 3.0 to 3.7% by weight C, 2.6 to 3.4% by weight Si, 0.02 to 0.05% by weight P, 0.025 to 0.045% by weight Mg, 0.01 to 0.03% by weight Cr, 0.003 to 0.017% by weight Al, 0.0005 to 0.012% by weight S and 0.0004 to 0.002% by weight B.
Preferred developments of the invention are provided by the dependent claims.
It is of advantage that the alloy has the best possible strength-strain behavior. This is achieved by the spheroidal cast alloy containing 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight Cu. This is also achieved by the alloy containing 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn.
It is also of advantage that the alloy has the best possible wear behavior. This is achieved by the alloy containing 0.1 to 1.5% by weight Cu, preferably 0.5 to 0.8% by weight Cu and 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn. This is also achieved by the alloy containing 0.1 to 1.5% by weight Mn, preferably 0.5 to 1.0% by weight Mn, and 0.05 to 1.0% by weight Cu, preferably 0.05 to 0.2% by weight Cu.
The essential idea of the invention is to provide a cast iron alloy which has a Brinell hardness of over 22 0 and which is worn as evenly as possible when used

WO 2006/056334 PCT/EP2005/012160
- 4 -
as a brake disk. The graphite in the cast iron alloy may be of a spheroidal or vermicular, but not lamellar form. Although brake disks with lamellar graphite are inexpensive, they have lower resistance to temperature changes. As a result, so-called fire cracks can already occur after a short time in use, rapidly growing and leading to irregularities of the surface. An irregular surface in turn leads to irregular thermal loading, irregular wear and so-called brake juddering.
Further applications of the spheroidal cast alloy according to the invention are axle and chassis parts for trucks and for passenger cars, such as for example wishbones, wheel carriers and pivot bearings, which are exposed to high mechanical and dynamic loads and in the case of a collision of the motor vehicle must plastically deform and must not rupture.
Example 1
A brake disk was produced from the spheroidal cast alloy according to the invention. The chemical composition was 3.34% by weight C, 2.92% by weight Si, 0.62% by weight Cu, 0.17% by weight Mn, 0.038% by weight Mg, 0.025% by weight P, 0.021% by weight Cr, 0.01% by weight Al, 0.001% by weight S and 0.0008% by weight B, the remainder Fe and the conventional impurities. The brake disk was investigated for the number of spherulites, graphite content, graphite form and graphite size, pearlite content and Brinell hardness. Specimens from the brake disk were subjected to a tensile test in order to establish the strength-strain behavior. The number of spherulites is 384 +/-76 spherulites per mm2. The graphite content is 9.7 +/- 0.7%. The graphite form in accordance with DIN EN ISO 945 is 97.9% of the form VI. The size distribution in accordance with DIN EN ISO 945 is 45% of size 8, 42% of size 7 and 13% of size 6. The pearlite content is

WO 2006/056334 PCT/EP2005/012160
- 5 -
84 +/- 1%. The Brinell hardness is 248 +/- 3 HB. In the tensile test, the following values were established: yield strength Rp0.2 = 474 MPa, tensile strength Rm = 778 MPa, elongation at rupture A5 = 11.4% and modulus of elasticity E = 165 to 170 kN/mm2.
In comparison with the known materials for brake disks, it was possible to establish a much better oxidation behavior (see Figure 1) and a greatly reduced tendency to fire cracking (see Figures 2 and 3) . The oxidation behavior, and consequently also the wear behavior, is greatly improved by the addition of a mixture of copper and/or manganese to the spheroidal cast alloy.
In Figure 1, the weight increase in grams per square meter and per day caused by oxidation at 700°C in air is represented. The material according to the invention shows a weight increase of about 9 g/m2.d, in comparison with a cast iron material for conventional brake disks with a weight increase of about 21 g/m2.d.
The tests to test for fire cracking were carried out as follows: a sample with the dimensions 40 x 20 x 7 mm is subjected to at least 100 cycles comprising 7 seconds of heating up to 700°C and 6 seconds of quenching in water. Subsequently, transverse sections are produced and examined under a microscope and photographed.
Figure 2 shows a microphoto of a commercially available brake disk with a fire crack 0.4 mm deep. Figure 3 shows a further microphoto of the brake disk according to the invention, to the same magnification, with a fire crack 0.14 mm deep.
Example 2
A wishbone for passenger cars was produced from the spheroidal cast alloy according to the invention. The

WO 2006/056334 PCT/EP2005/012160
- 6 -
chemical composition was 3.5% by weight C, 2.85% by weight Si, 0.63% by weight Cu, 0.18% by weight Mn, 0.038% by weight Mg, 0.026% by weight P, 0.029% by weight Cr, 0.004% by weight Al, 0.001% by weight S and 0.0007% by weight B, the remainder Fe and the conventional impurities. In the tensile test, the following values were established: yield strength Rp0.2 = 465 MPa, tensile strength Rm = 757 MPa, elongation at rupture A5 = 11.1% and modulus of elasticity E = 165 to 170 kN/mm2. The Brinell hardness is 258 +/- 3 HB.
Example 3
A wheel carrier for passenger cars was produced from the spheroidal cast alloy according to the invention. The chemical composition was 3.43% by weight C, 3.38% by weight Si, 0.71% by weight Cu, 0.2% by weight Mn, 0.037% by weight Mg, 0.047% by weight P, 0.043% by weight Cr, 0.012% by weight Al, 0.004% by weight S and 0.0008% by weight B, the remainder Fe and the conventional impurities. In the tensile test, the following values were established: yield strength Rp0.2 = 558 MPa, tensile strength Rm = 862 MPa and elongation at rupture A5 = 6.1%. The Brinell hardness is 288 HB. The number of spherulites in the microstructure was determined as 455 spherulites per mm2.
Figure 4 shows the elongation at rupture A5 as a function of the tensile strength Rm. The solid line indicates the minimum values in accordance with the standard EN 1563 for cast iron with spheroidal graphite of types produced in the cast state. The measurements of the material according to the invention are entered in accordance with Examples 1 to 3 presented above.
Figure 5 shows the elongation at rupture A5 as a function of the yield strength Rp0.2. The solid line indicates the minimum values in accordance with the

WO 2006/056334 PCT/EP2005/012160
- 7 -
standard EN 1563 for cast iron with spheroidal graphite of types produced in the cast state. The measurements of the material according to the invention are entered in accordance with Examples 1 to 3 presented above.
The material properties of the spheroidal cast iron according to the invention are consequently far above the European standard EN 1563 for cast iron with spheroidal graphite and even reach the values of ADI (= Austempered Ductile Iron) , a cast iron material standardized in Europe under EN 1564 which is produced by a very complex heat treatment in relatively great wall thicknesses that can only be obtained by alloying the expensive elements nickel and/or molybdenum, and is consequently correspondingly expensive.
Figure 6 shows the strength ranges against the elongation at rupture of the materials aluminum cast alloys, cast iron with spheroidal graphite, ADI and the material according to the invention with Examples 1 to 3 entered.
The uniformity of the structure is also achieved by a novel casting process. The casting mold is divided horizontally instead of vertically, the brake disks being arranged horizontally and the filling of the casting mold being carried out from the middle toward the edge of the brake disk. This has the consequence that the casting mold is filled rotationally symmetrically and that the brake disk is uniformly cooled from the inside to the outside after casting. As a result, a uniform, homogeneous structure is created over the entire circumference of the brake disk. A subsequent heat treatment, which is time-consuming and incurs costs, is no longer required.

WO 2006/056334 PCT/EP2005/012160
- 8 -
Patent claims
1. A spheroidal cast alloy for cast iron products with
great mechanical strength, high wear resistance and
at the same time a high degree of ductility,
comprising as non-iron constituents
2.5 to 3.8% by weight C,
2.4 to 3.4% by weight Si,
0.02 to 0.08% by weight P,
0.02 to 0.06% by weight Mg,
0.01 to 0.05% by weight Cr,
0.002 to 0.02% by weight Al,
0.0005 to 0.015% by weight S,
0.0002 to 0.002% by weight B and the conventional impurities, characterized in that the spheroidal cast alloy contains 3.0 to 3.7% by weight C,
2.6 to 3.4% by weight Si,
0.02 to 0.05% by weight P,
0.025 to 0.045% by weight Mg,
0.01 to 0.03% by weight Cr,
0.003 to 0.017% by weight Al,
0.0005 to 0.009% by weight S and
0.0004 to 0.002% by weight B.
2. The spheroidal cast alloy as claimed in claim 1,
characterized in that the alloy contains 0.1 to
1.5% by weight Cu, preferably 0.5 to 0.8% by weight
Cu.
3. The spheroidal cast alloy as claimed in claim 1,
characterized in that the alloy contains 0.1 to
1.0% by weight Mn, preferably 0.15 to 0.2% by
weight Mn.
4. The spheroidal cast alloy as claimed in claim 1,
characterized in that the alloy contains 0.1 to
1.5% by weight Cu, preferably 0.5 to 0.8% by weight

WO 2006/056334 PCT/EP2005/012160
- 9 -
Cu, and 0.1 to 1.0% by weight Mn, preferably 0.15 to 0.2% by weight Mn.
5. The spheroidal cast alloy as claimed in claim 1,
characterized in that the alloy contains 0.1 to
1.5% by weight Mn, preferably 0.5 to 1.0% by weight
Mn, and 0.05 to 1.0% by weight Cu, preferably 0.05
to 0.2% by weight Cu.
6. The spheroidal cast alloy as claimed in at least
one of claims 1 to 5, characterized in that,
immediately after casting and cooling, the graphite
component is of a spheroidal and/or vermicular form
in respect of over 90% of the graphite present.
7. The spheroidal cast alloy as claimed in at least
one of claims 1 to 6, characterized in that,
immediately after casting and cooling, the
crystalline structure of the cast part is of a
pearlitic form in respect of 70 to 90%.
8. The spheroidal cast alloy as claimed in at least
one of claims 1 to 7, characterized in that,
immediately after casting and cooling, the
crystalline structure of the cast part has 200 to
700 spherulites per mm2.
9. The spheroidal cast alloy as claimed in at least
one of claims 1 to 8, characterized in that the
cast part has a Brinell hardness of over 220.
10. The spheroidal cast alloy as claimed in at least
one of claims 1 to 9, characterized in that the
graphite particles have a size distribution of at
least 30% of size 8, 10% to 70% of size 7 and at
most 20% of size 6 in accordance with DIN EN ISO
945.

WO 2006/056334 PCT/EP2005/012160
- 10 -
11. The spheroidal cast alloy as claimed in at least
one of claims 1 to 10, characterized in that the
cast part has an elongation at rupture A5 of 5 to
14% with a tensile strength Rm of 900 to 600 MPa.
12. The spheroidal cast alloy as claimed in at least
one of claims 1 to 11, characterized in that the
cast part has an elongation at rupture A5 of 5 to
14% with a yield strength Rp0.2 of 600 to 400 MPa.
13. The spheroidal cast alloy as claimed in at least
one of claims 1 to 12, characterized in that it is
used for chassis parts in motor vehicles.
14. The spheroidal cast alloy as claimed in at least
one of claims 1 to 12, characterized in that it is
used for wishbones in motor vehicles.
15. The spheroidal cast alloy as claimed in at least
one of claims 1 to 12, characterized in that it is
used for wheel carriers in motor vehicles.
16. The spheroidal cast alloy as claimed in at least
one of claims 1 to 12, characterized in that it is
used for pivot bearings in motor vehicles.
17. The spheroidal cast alloy as claimed in at least
one of claims 1 to 12, characterized in that it is
used for brake disks in motor vehicles.
18. A method for producing a cast part from a
spheroidal cast alloy as claimed in one of claims 1
to 17, characterized in that, after the casting and
cooling of the cast part, no heat treatment of the
cast part is performed.
19. A method for producing a cast part as claimed in
one of claims 1 to 18, characterized in that the

WO 2006/056334 PCT/EP2005/012160
- 11 -
casting mold is divided horizontally, the cast part being arranged horizontally in the casting mold.
20. A method for producing a rotationally symmetrical cast part as claimed in one of claims 1 to 19, characterized in that the casting mold is filled rotationally symmetrically from the middle point of the cast part.

The invention relates to a spheroidal cast alloy for producing cast iron products with great mechanical strength, high wear-resistance and a high degree of ductility. Said alloy comprises the following as non-iron components: between 2.5 and 3.8 wt. % C, between 2.4 and 3.4 wt. % Si, between 0.02 and 0.08 wt. % P, between 0.02 and 0.06 wt. % Mg, between 0.01 and 0.05 wt. % Cr, between 0.002 and 0.02 wt. % Al, between 0.0005 and 0.015 wt. % S, between 0.0002 and 0.002 wt. % B and conventional impurities. According to the invention, the alloy contains between 3.0 and 3.7 wt. % C, between 2.6 and 3.4 wt. % Si, between 0.02 and 0.05 wt. % P, between 0.025 and 0.045 wt. % Mg, between 0.01 and 0.03 wt. % Cr, between 0.003 and 0.017 wt. % Al, between 0.0005 and 0.012 wt. % S and between 0.0004 and 0.002 wt. % B. The alloy is used for example to produce chassis parts or brake discs in the automobile industry.

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=AxdCXJWmPRywHXgWh8wgRw==&loc=wDBSZCsAt7zoiVrqcFJsRw==

« Previous Patent

Next Patent »

Patent Number

271217

Indian Patent Application Number

669/KOLNP/2007

PG Journal Number

07/2016

Publication Date

12-Feb-2016

Grant Date

09-Feb-2016

Date of Filing

23-Feb-2007

Name of Patentee

GEORG FISCHER AUTOMOTIVE AG.

Applicant Address

MUHLENTALSTRASSE 65, 8201 SCHAFFHAUSEN.

Inventors:

#	Inventor's Name	Inventor's Address
1	WERNER MENK	PILATUSSTRASSE 33, 8200 SCHAFFHAUSEN.
2	ANDREAS HECKER	WUHRSTRASSE 7, 78267 AACH.
3	TORSTEN RIECK	KARL-THEODOR-STRASSE 4, 40878 RATINGEN.
4	ROLF RIETZSCHER	BRAHMSSTRASSE 13, 40822 METTMANN.

PCT International Classification Number

C22C 37/04

PCT International Application Number

PCT/EP2005/012160

PCT International Filing date

2005-11-14

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	102004056331.4	2004-11-22	Germany