Indian Patents. 271938:METHOD AND DEVICE FOR THE PRODUCTION OF MOLDED BODIES

Title of Invention	METHOD AND DEVICE FOR THE PRODUCTION OF MOLDED BODIES
Abstract	The invention relates to a method for the production of molded bodied from a base substance, wherein the base substance is mixed with a solution for producing a molding solution, and said solution subsequently is at least partially removed from the mixture, and the molding solution is fed to a unit for molding, wherein the molding solution is diluted before molding.

Full Text	FORM 2 THE PATENT ACT 197° (39 of 1970) & The Patents Rules, 2003 COMPLETE SPECIFICATION (See Section 10, and rule 13) 1. TITLE OF INVENTION METHOD AND DEVICE FOR THE PRODUCTION OF MOLDED BODIES 2. APPLICANT(S) b) Nationality : SWISS Company c) Address : 24, BERSTELSTRASSE, CH-4422 ARISDORF, SWITZERLAND 3. PREAMBLE TO THE DESCRIPTION The following specification particularly describes the invention and the manned in which it is to be performed : - The present invention relates to a method for producing molded bodies from a base substance wherein the base substance for producing a molding solution is mixed with a solvent and subsequently this solvent is at least partly removed from the mixture and the molding solution is fed to a means for molding, and also to a device therefor. PRIOR ART In the present case, the term "molded bodies" subsumes all possible bodies obtainable from a natural or artificial base substance. This is generally accomplished with the aid of a molding tool whereby the base substance is brought into a mold for the molded bodies. An example which may be mentioned, purely for illustration and in no way exhaustive, is viscose fiber. Viscose fibers are fibers consisting of cellulose as base material and industrially produced via the viscose process. The chemical nature of viscose fibers resembles that of cotton fibers. Modal fibers are a similar product to viscose fibers. They likewise consist 100% of cellulose and, just like viscose fibers, are produced from natural pulp. However, a somewhat different process results in higher fiber strength and improved fiber properties being achieved. The class of cellulosic fibers further includes Tencel and lyocell fibers. In the case of lyocell fibers, the nontoxic solvent NMMO (N-methylmorpholine N-oxide) is used to dissolve the pulp directly, without prior reaction with caustic soda and derivatization to the xanthate. Lyocell fibers are spun in a dilute aqueous NMMO bath by going below the solubility limit of the cellulose and thereby forming a thread. For this purpose, the corresponding spinning solution is pressed through spinneret dies. This lyocell process is described for example in DE1 713 486, US-A-3 447 939 or GB 8 216 566. The suitable spinning solution is produced for example in a horizontal kneading reactor as shown in DE198 37 210 or WO02/20885 Al. In these devices and according to the known methods, the spinning solution is produced in the further processable viscosity necessary for the spinning process and the associated cellulose concentration. However, the corresponding means for spinning can only process a spinning solution having low viscosity, but this significantly reduces the effectivity of the process for producing the spinning solution. Specific applications require very low viscosities and hence low cellulose contents, and this spinning solution can no longer be effectively produced using the known technology. OBJECT It is an object of the present invention to significantly improve the effectivity of the molding solution production and the production of the molded bodies. ACHIEVEMENT OF OBJECT The object is achieved when the molding solution is diluted prior to the molding operation. The principle of the idea is to separate the production of the molding solution = eg, spinning solution and the molding/spinning and to operate each at the optimal viscosity or cellulose concentration. Since the known kneading reactors are in principle distinctly more efficient at high viscosities, this stage is operated at higher cellulose concentration and it is only after production of the spinning solution that the diluting is effected, with the corresponding concentrated amine oxide monohydrate, to the level of the viscosity, or cellulose concentration, needed for the spinning plant. In terms of plant engineering, the separation of production of the molding solution from the molding step is characterized particularly in that between the actual kneading reactor and the means for molding there is interposed a mixer in which the high-viscosity molding solution is diluted. The separation of these two processing stages is further sharpened through appropriate interposed buffering containers. Which molded body is produced is of minor importance. Preference is given to producing filaments, fibrous nonwoven webs or filament yarn. However, it is also possible to produce films, hollow fibers, membranes or the like. The molding of the solution into a desired cellulosic molded body can be effected using known spinneret dies for producing fibers, slot dies or hollow-fiber spinneret dies. After molding, ie, prior to being introduced into the coagulation bath, the molded solution can also be stretched. The solvent used is preferably-a tertiary amine oxide, more particularly an amine oxide monohydrate, However, the invention shall not be restricted thereto. Nor is the invention restricted to cellulose, but also comprises materials such as proteins, polylactides or starch or a mixture thereof. The material to be dissolved shall have a significant water content of 1% to 80% at the start of the process. The material to be dissolved is then dissolved with the solvent. The water content is reduced in the process to the concentration of the solubility window. At the end of the first stage of the process, the spinning solution, for example, shall have a 12% to 28% concentration in amine oxide monohydrate of the material to be dissolved. This spinning solution, then, is however not necessarily intermediately stored in a buffering container. If it is then provided for spirining, it is diluted, preferably again with amine oxide monohydrate, to a solution which is readily spinnable in the spinning plants. To this end, in accordance with a proposal of the present invention, the spinning solution is conveyed under overpressure by means of a volumetric pump, while amine oxide monohydrate is metered into the stream by means of a second volumetric pump. The two pumps are mutually adjusted such that the spinning solution produced has a desired low concentration of 4% to 14% in amine oxide monohydrate of the dissolved material. The dilute spinning solution is treated in a mixer of any desired design. This mixer optionally additionally serves as buffer. Optionally, the homogenized molding solution downstream of the mixer is pressed, with or without pressure-enhancing pump, through a molding solution filter and is homogenized once more in the process. The filter has a mesh size of 1 to 500 mµ,. To police the spinning solution, the refractive index and the temperature of the spinning solution and also of the amine oxide monohydrate is policed upstream of the mixer and downstream of the mixer. The refractive index should be between 1.48 and 1.49. To prevent any change in the consistency of the spinning solution, all pipelines, pumps, mixers, ie, ideally all plant components with which the spinning solution comes into contact in whatever state and also the lines of the amine oxide monohydrate should be heated. The temperature chosen is a range from 80°C to 120°C. Furthermore, all plant components that contain spinning solution, amine oxide monohydrate and/or dilute spinning solution shall be monitored by pressure and temperature sensors and secured against any unallowable overpressure. This can be accomplished by means of bursting disks for example. In the case of intermediate storage in buffering containers, care must be taken to ensure that these too are heated and that the spinning solution is introduced and discharged bubblelessly. Discharging is preferably accomplished under an admission pressure produced for example by pressurization with nitrogen on the product surface. This nitrogen should additionally be slightly humidified. FIGURE DESCRIPTION Further advantages, features and details of the invention will be apparent from the following description of preferred illustrative embodiments and also from reference to the drawing. This shows in its single figure a schematic block diagram for the inventive method for producing molded bodies from renewable raw materials. The cellulose needed for this is fed via supply line 1 to a kneading reactor 2. Such kneading reactors are known for example from DE199 40 521 Al or DE 4118 884. However, the invention is not restricted to these kneading reactors. The invention comprises all treating means in which renewable raw materials can be subjected to a treatment for later spinning. In the present illustrative embodiment, the renewable raw material is treated by means of a solvent, preferably amine oxide monohydrate, which is fed to the kneading reactor via a further supply line 3. In the kneading reactor 2, heat is added to effect intensive commixing of the raw material with the solvent and also evaporation of the solvent to form a relatively high-viscosity spinning solution. This spinning solution is then fed, via a discharge means 4, to a buffering container 5. There it is intermediately stored with or without heating. As soon as spinning solution is needed, the relatively high-viscosity spinning solution is removed from the buffering container 5 by a volumetric pump 6, and the pump 6 conveys the spinning solution into a mixer 7. On the way there or directly into the mixer, the stream has added to it, likewise via a volumetric pump 8, a solvent, preferably amine oxide monohydrate. This is accomplished via the supply line 9. In the mixer 7, then, the added amine oxide monohydrate effects a dilution of the spinning solution, for which the nature of the mixing and of the mixer itself are of minor importance. A dilute spinning solution is then discharged from the mixer 7 and pressed by means of a pump 13 through a spinning solution filter 10. This effects a further homogenization of the spinning solution. Thereafter/ the spinning solution can be intermediately stored in a further buffering container 11, if necessary. The actual spinning then takes place in a means 12. List of reference symbols 1 Supply line 34 67 2 Kneading reactor 35 68 3 Supply line 36 69 4 Discharging means 37 70 5 Buffering container 38 71 6 Pump 39 72 7 Mixer 40 73 8 Pump 41 74 9 Supply line 42 75 10 Spinning solution filter 43 76 11 Buffering container 44 77 12 Means for spinning 45 78 13 Pump 46 79 14 47 15 48 16 49 17 50 18 51 E 19 52 20 53 21 54 22 55 23 56 24 57 25 58 26 59 27 60 28 61 29 62 30 63 31 64 32 65 33 66 WE CLAIM: 1. A method for producing molded bodies from a base substance wherein the base substance for producing a molding solution is mixed with a solvent and subsequently this solvent is at least partly removed from the mixture and the molding solution is fed to a means for molding, characterized in that the molding solution is diluted prior to molding. 2. The method according to claim 1, characterized in that a tertiary amine oxide is used as solvent. 3. The method according to claim2, characterized in that amine oxide monohydrate is used as solvent. 4. The method according to any one of claims 1 to 3, characterized in that the materials to be dissolved consist of cellulose, proteins, polylactides or starch or a mixture thereof. 5. The method according to at least one of claims 1 to 4, characterized in that the material to be dissolved has a significant water content of 1 to 80% at the start of the process and is dissolved with the solvent. 6. The method according to at least one of claims 1 to 5, characterized in that the molding solution in the form of a spinning solution contains 12 to 28% of the raw material in amine oxide monohydrate. 7. The method according to at least one of claims 1 to 6, characterized in that the molding solution in the form of a spinning solution is diluted again with amine oxide monohydrate prior to spinning. 8. The method according to at least one of claims 1 to 7, characterized in that the as-produced molding solution is conveyed under overpressure by means of a volumetric pump (6) and amine oxide monohydrate is metered into the stream with a second volumetric pump (8). 9. The method according to claim 8, characterized in that the two volumetrically conveying pumps (6, 8) are mutually adjusted so as to form a molding solution having the desired low concentrations in amine oxide monohydrate of 4 to 14% of material to be dissolved. 10. The method according to at least one of claims 1 to 9, characterized in that the dilute molding solution is treated in a static or dynamic stirred mixer (7) installed either directly online in a subsequent distribution line or disposed separately therefrom, wherein this mixer (7) optionally additionally serves as buffer. 11. The method according to claim 10/characterized in that the homogenized molding solution downstream of the mixer (7) is pressed, with or without pressure-enhancing pump, through a molding solution filter (10) and is homogenized once more in the process,, wherein the filter (10) has a mesh size of 1 to 500 urn. 12. The method according to claim 11, characterized in that the refractive index and the temperature of the molding solution and also of the amine oxide monohydrate is policed online upstream of the mixer (7) and downstream of the mixer. 13. The method according to claim 12, characterized in that the refractive index is between 1.48 and 1.49. 14. The method according to at least one of claims 1 to 13, characterized in that at least some of the pipelines, pumps, mixers, etc. that contain concentrated molding solution, amine oxide monohydrate or dilute molding solutions are heated to about 80 to 120°C. 15. The method according to at least one of claims 1 to 14, characterized in that at least some of the plant components that contain molding solution, amine oxide monohydrate or dilute molding solutions are monitored by pressure and temperature sensors and/or secured by bursting disks against unallowable overpressure. 16. The method according to at least one of claims 1 to 15, characterized in that the concentrated molding solution is stored in a buffering container (5) or is fed to the mixer directly via a pump (6). 17. The method according to at least one of claims 1 to 15, characterized in that the dilute molding solution is stored in a buffering container (11) or is fed directly to the means (12) for molding. 18. The method according to claim 16, characterized in that the molding solution is heated in the buffering container (11). 19. The method according to claim 16, 17 or 18, characterized in that the dilute molding solution is introduced to the buffering container (5,11) bubblelessly from below, sideways or from above, and is discharged bubblelessly in the downward direction. 20. The method according to at least one of claims 16 to 19, characterized in that the fill level in the buffering container (5, 11) is measured online, preferably using a radar probe. 21. The method according to at least one of claims 16 to 19, characterized in that the molding solution in the buffering container (5, 11) is subjected to an admission pressure on its product surface. 22. The method according to claim 21, characterized in that the admission pressure is generated by nitrogen. 23. The method according to claim 22, characterized in that the nitrogen is slightly humidified. 24. A device for carrying out the method according to at least one of claims 1 to 23, characterized in that between a kneading reactor (2) and the means (12) for molding the molding solution there is interposed a mixer (7) for reducing the viscosity of the molding solution. 25. The device according to claim 24, characterized in that between kneading reactor (2) and/ or mixer (7) and means (12) for molding the molding solution there is provided a buffering container (6,8). 26. The device according to claim 24 or 25, characterized in that the mixer (7) is followed on its downstream side by a molding solution filter (10).

Full Text

FORM 2
THE PATENT ACT 197° (39 of 1970)
&
The Patents Rules, 2003 COMPLETE SPECIFICATION (See Section 10, and rule 13)
1. TITLE OF INVENTION
METHOD AND DEVICE FOR THE PRODUCTION OF MOLDED BODIES
2. APPLICANT(S)
b) Nationality : SWISS Company
c) Address : 24, BERSTELSTRASSE,
CH-4422 ARISDORF, SWITZERLAND
3. PREAMBLE TO THE DESCRIPTION
The following specification particularly describes the invention and the manned in which it is to be performed : -

The present invention relates to a method for producing molded bodies from a base substance wherein the base substance for producing a molding solution is mixed with a solvent and subsequently this solvent is at least partly removed from the mixture and the molding solution is fed to a means for molding, and also to a device therefor.
PRIOR ART
In the present case, the term "molded bodies" subsumes all possible bodies obtainable from a natural or artificial base substance. This is generally accomplished with the aid of a molding tool whereby the base substance is brought into a mold for the molded bodies. An example which may be mentioned, purely for illustration and in no way exhaustive, is viscose fiber.
Viscose fibers are fibers consisting of cellulose as base material and industrially produced via the viscose process. The chemical nature of viscose fibers resembles that of cotton fibers.
Modal fibers are a similar product to viscose fibers. They likewise consist 100% of cellulose and, just like viscose fibers, are produced from natural pulp. However, a somewhat different process results in higher fiber strength and improved fiber properties being achieved.
The class of cellulosic fibers further includes Tencel and lyocell fibers. In the case of lyocell fibers, the nontoxic solvent NMMO (N-methylmorpholine N-oxide) is used to dissolve the pulp directly, without prior reaction with caustic soda and derivatization to the xanthate. Lyocell fibers are spun in a dilute aqueous NMMO bath by going below the solubility limit of the cellulose and thereby forming a thread. For this purpose, the corresponding spinning solution is pressed through spinneret dies. This lyocell process is described for example in DE1 713 486, US-A-3 447 939 or GB 8 216 566. The suitable spinning solution is produced for

example in a horizontal kneading reactor as shown in DE198 37 210 or WO02/20885 Al.
In these devices and according to the known methods, the spinning solution is produced in the further processable viscosity necessary for the spinning process and the associated cellulose concentration. However, the corresponding means for spinning can only process a spinning solution having low viscosity, but this significantly reduces the effectivity of the process for producing the spinning solution. Specific applications require very low viscosities and hence low cellulose contents, and this spinning solution can no longer be effectively produced using the known technology.
OBJECT
It is an object of the present invention to significantly improve the effectivity of the molding solution production and the production of the molded bodies.
ACHIEVEMENT OF OBJECT
The object is achieved when the molding solution is diluted prior to the molding operation.
The principle of the idea is to separate the production of the molding solution = eg, spinning solution and the molding/spinning and to operate each at the optimal viscosity or cellulose concentration. Since the known kneading reactors are in principle distinctly more efficient at high viscosities, this stage is operated at higher cellulose concentration and it is only after production of the spinning solution that the diluting is effected, with the corresponding concentrated amine oxide monohydrate, to the level of the viscosity, or cellulose concentration, needed for the spinning plant.

In terms of plant engineering, the separation of production of the molding solution from the molding step is characterized particularly in that between the actual kneading reactor and the means for molding there is interposed a mixer in which the high-viscosity molding solution is diluted. The separation of these two processing stages is further sharpened through appropriate interposed buffering containers.
Which molded body is produced is of minor importance. Preference is given to producing filaments, fibrous nonwoven webs or filament yarn. However, it is also possible to produce films, hollow fibers, membranes or the like. The molding of the solution into a desired cellulosic molded body can be effected using known spinneret dies for producing fibers, slot dies or hollow-fiber spinneret dies. After molding, ie, prior to being introduced into the coagulation bath, the molded solution can also be stretched.
The solvent used is preferably-a tertiary amine oxide, more particularly an amine oxide monohydrate, However, the invention shall not be restricted thereto. Nor is the invention restricted to cellulose, but also comprises materials such as proteins, polylactides or starch or a mixture thereof.
The material to be dissolved shall have a significant water content of 1% to 80% at the start of the process. The material to be dissolved is then dissolved with the solvent. The water content is reduced in the process to the concentration of the
solubility window.
At the end of the first stage of the process, the spinning solution, for example, shall have a 12% to 28% concentration in amine oxide monohydrate of the material to be dissolved. This spinning solution, then, is however not necessarily intermediately stored in a buffering container. If it is then provided for spirining, it is diluted, preferably again with amine oxide monohydrate, to a solution which is readily spinnable in the spinning plants. To this end, in accordance with a proposal of the present invention, the spinning solution is conveyed under overpressure by means

of a volumetric pump, while amine oxide monohydrate is metered into the stream by means of a second volumetric pump. The two pumps are mutually adjusted such that the spinning solution produced has a desired low concentration of 4% to 14% in amine oxide monohydrate of the dissolved material. The dilute spinning solution is treated in a mixer of any desired design. This mixer optionally additionally serves as buffer.
Optionally, the homogenized molding solution downstream of the mixer is pressed, with or without pressure-enhancing pump, through a molding solution filter and is homogenized once more in the process. The filter has a mesh size of 1 to 500 mµ,.
To police the spinning solution, the refractive index and the temperature of the spinning solution and also of the amine oxide monohydrate is policed upstream of the mixer and downstream of the mixer. The refractive index should be between 1.48 and 1.49.
To prevent any change in the consistency of the spinning solution, all pipelines, pumps, mixers, ie, ideally all plant components with which the spinning solution comes into contact in whatever state and also the lines of the amine oxide monohydrate should be heated. The temperature chosen is a range from 80°C to 120°C.
Furthermore, all plant components that contain spinning solution, amine oxide monohydrate and/or dilute spinning solution shall be monitored by pressure and temperature sensors and secured against any unallowable overpressure. This can be accomplished by means of bursting disks for example.
In the case of intermediate storage in buffering containers, care must be taken to ensure that these too are heated and that the spinning solution is introduced and discharged bubblelessly. Discharging is preferably accomplished under an admission pressure produced for example by pressurization with nitrogen on the

product surface. This nitrogen should additionally be slightly humidified.
FIGURE DESCRIPTION
Further advantages, features and details of the invention will be apparent from the following description of preferred illustrative embodiments and also from reference to the drawing. This shows in its single figure a schematic block diagram for the inventive method for producing molded bodies from renewable raw materials.
The cellulose needed for this is fed via supply line 1 to a kneading reactor 2. Such kneading reactors are known for example from DE199 40 521 Al or DE 4118 884. However, the invention is not restricted to these kneading reactors. The invention comprises all treating means in which renewable raw materials can be subjected to a treatment for later spinning.
In the present illustrative embodiment, the renewable raw material is treated by means of a solvent, preferably amine oxide monohydrate, which is fed to the kneading reactor via a further supply line 3.
In the kneading reactor 2, heat is added to effect intensive commixing of the raw material with the solvent and also evaporation of the solvent to form a relatively high-viscosity spinning solution. This spinning solution is then fed, via a discharge means 4, to a buffering container 5. There it is intermediately stored with or without heating. As soon as spinning solution is needed, the relatively high-viscosity spinning solution is removed from the buffering container 5 by a volumetric pump 6, and the pump 6 conveys the spinning solution into a mixer 7. On the way there or directly into the mixer, the stream has added to it, likewise via a volumetric pump 8, a solvent, preferably amine oxide monohydrate. This is accomplished via the supply line 9.

In the mixer 7, then, the added amine oxide monohydrate effects a dilution of the spinning solution, for which the nature of the mixing and of the mixer itself are of minor importance.
A dilute spinning solution is then discharged from the mixer 7 and pressed by means of a pump 13 through a spinning solution filter 10. This effects a further homogenization of the spinning solution. Thereafter/ the spinning solution can be intermediately stored in a further buffering container 11, if necessary. The actual spinning then takes place in a means 12.

List of reference symbols

1 Supply line 34 67
2 Kneading reactor 35 68
3 Supply line 36 69
4 Discharging means 37 70
5 Buffering container 38 71
6 Pump 39 72
7 Mixer 40 73
8 Pump 41 74
9 Supply line 42 75
10 Spinning solution filter 43 76
11 Buffering container 44 77
12 Means for spinning 45 78
13 Pump 46 79
14 47
15 48
16 49
17 50
18 51 E
19 52
20 53
21 54
22 55
23 56
24 57
25 58
26 59
27 60
28 61
29 62
30 63
31 64
32 65
33 66

WE CLAIM:
1. A method for producing molded bodies from a base substance wherein the
base substance for producing a molding solution is mixed with a solvent and
subsequently this solvent is at least partly removed from the mixture and the
molding solution is fed to a means for molding,
characterized in that
the molding solution is diluted prior to molding.
2. The method according to claim 1, characterized in that a tertiary amine oxide is used as solvent.
3. The method according to claim2, characterized in that amine oxide monohydrate is used as solvent.
4. The method according to any one of claims 1 to 3, characterized in that the materials to be dissolved consist of cellulose, proteins, polylactides or starch or a mixture thereof.
5. The method according to at least one of claims 1 to 4, characterized in that the material to be dissolved has a significant water content of 1 to 80% at the start of the process and is dissolved with the solvent.
6. The method according to at least one of claims 1 to 5, characterized in that the molding solution in the form of a spinning solution contains 12 to 28% of the raw material in amine oxide monohydrate.
7. The method according to at least one of claims 1 to 6, characterized in that the molding solution in the form of a spinning solution is diluted again with amine oxide monohydrate prior to spinning.

8. The method according to at least one of claims 1 to 7, characterized in that the as-produced molding solution is conveyed under overpressure by means of a volumetric pump (6) and amine oxide monohydrate is metered into the stream with a second volumetric pump (8).
9. The method according to claim 8, characterized in that the two volumetrically conveying pumps (6, 8) are mutually adjusted so as to form a molding solution having the desired low concentrations in amine oxide monohydrate of 4 to 14% of material to be dissolved.
10. The method according to at least one of claims 1 to 9, characterized in that the dilute molding solution is treated in a static or dynamic stirred mixer (7) installed either directly online in a subsequent distribution line or disposed separately therefrom, wherein this mixer (7) optionally additionally serves as buffer.
11. The method according to claim 10/characterized in that the homogenized molding solution downstream of the mixer (7) is pressed, with or without pressure-enhancing pump, through a molding solution filter (10) and is homogenized once more in the process,, wherein the filter (10) has a mesh size of 1 to 500 urn.
12. The method according to claim 11, characterized in that the refractive index and the temperature of the molding solution and also of the amine oxide monohydrate is policed online upstream of the mixer (7) and downstream of the mixer.
13. The method according to claim 12, characterized in that the refractive index is between 1.48 and 1.49.

14. The method according to at least one of claims 1 to 13, characterized in that at least some of the pipelines, pumps, mixers, etc. that contain concentrated molding solution, amine oxide monohydrate or dilute molding solutions are heated to about 80 to 120°C.
15. The method according to at least one of claims 1 to 14, characterized in that at least some of the plant components that contain molding solution, amine oxide monohydrate or dilute molding solutions are monitored by pressure and temperature sensors and/or secured by bursting disks against unallowable overpressure.
16. The method according to at least one of claims 1 to 15, characterized in that the concentrated molding solution is stored in a buffering container (5) or is fed to the mixer directly via a pump (6).
17. The method according to at least one of claims 1 to 15, characterized in that the dilute molding solution is stored in a buffering container (11) or is fed directly to the means (12) for molding.
18. The method according to claim 16, characterized in that the molding solution is heated in the buffering container (11).
19. The method according to claim 16, 17 or 18, characterized in that the dilute molding solution is introduced to the buffering container (5,11) bubblelessly from below, sideways or from above, and is discharged bubblelessly in the downward direction.
20. The method according to at least one of claims 16 to 19, characterized in that the fill level in the buffering container (5, 11) is measured online, preferably using a radar probe.

21. The method according to at least one of claims 16 to 19, characterized in that the molding solution in the buffering container (5, 11) is subjected to an admission pressure on its product surface.
22. The method according to claim 21, characterized in that the admission pressure is generated by nitrogen.
23. The method according to claim 22, characterized in that the nitrogen is slightly humidified.
24. A device for carrying out the method according to at least one of claims 1 to 23, characterized in that between a kneading reactor (2) and the means (12) for molding the molding solution there is interposed a mixer (7) for reducing the viscosity of the molding solution.
25. The device according to claim 24, characterized in that between kneading reactor (2) and/ or mixer (7) and means (12) for molding the molding solution there is provided a buffering container (6,8).
26. The device according to claim 24 or 25, characterized in that the mixer (7) is followed on its downstream side by a molding solution filter (10).

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=CfZ4rfOHDxHDVQQVoXrIRA==&loc=vsnutRQWHdTHa1EUofPtPQ==

« Previous Patent

Next Patent »

Patent Number

271938

Indian Patent Application Number

1678/MUMNP/2010

PG Journal Number

11/2016

Publication Date

11-Mar-2016

Grant Date

10-Mar-2016

Date of Filing

06-Aug-2010

Name of Patentee

LIST HOLDING AG

Applicant Address

24, BERSTELSTRASSE, CH-4422 ARISDORF, SWITZERLAND

Inventors:

#	Inventor's Name	Inventor's Address
1	SCHILDKNECHT, HELMUT	9829 ABRELL WALK, CHARLOTTE NC 28226, U.S.A.
2	TRETZACK, OLIVER	34, AUF DER WEGSCHEIDE, 79686 HASEL, GERMANY
3	DIENER, ANDREAS	129, HAUPTSTRASSE, 09603 GROSSSCHIRMA, GERMANY
4	WITTE, DANIEL	LOERRACHERSTRASSE 33C, 79639 GRENZACH-WYHLEN, GERMANY

PCT International Classification Number

C08B1/00

PCT International Application Number

PCT/EP2009/000837

PCT International Filing date

2009-02-06

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	102008023064.2	2008-05-09	Germany
2	102008008342.9	2008-02-08	Germany