Indian Patents. 272495:"A METHOD FOR MANUFACTURING BRAKE PADS"

Title of Invention	"A METHOD FOR MANUFACTURING BRAKE PADS"
Abstract	A brake pad is, in order to reduce stock keeping and for flexible adjustement to varying demands regarding the dimensions, manufactured by providing a plate (10) the dimensions of which are essentially larger than the dimensions of the smallest brake pad to be manufactured. From that plate a brake pad Is cut comprising at least partially its final dimensions. (Figure 1)

Full Text	Method and product for manufacturing brake pads The invention is concerned with manufacturing brake pads, in particular for disc brakes. According to the art, brake pads for disc brakes usually are composed of a carrier plate, e.g. made from steel, and a brake lining which is pressed against the disc in order to generate braking action. According to the prior art such brake pads are manufactured by producing first a carrier plate comprising its final dimensions (i.e. the dimensions in the final brake pad) and, thereafter, the lining is attached to the carrier plate, wherein the lining also has already its final dimensions. The attachment is e.g. obtained by a glue. According to this known method of manufacture, each brake pad is completely finished at the manufacturer's premises and then shipped to the distributors and final users. This causes a complex and laborious stockkeeping of several sizes of brake pads. The technical problem underlying the present invention is to provide a method and a product for manufacturing brake pads reducing the stockkeeping requirements and allowing a less laborious adjustment as to varying size requirements at the market place. Also, the transportation from the manufacturer to the distributor and other users shall be reduced. To this end, the invention teaches a method for manufacturing brake pads comprising the following steps: - providing a plate comprising a lining, said plate having dimensions substantially larger than the dimensions of the smallest brake pad to be manufactured, and - cutting the brake pad to be manufactured from said plate, at least partially in accordance with the final dimensions of the brake pad. According to the invention, therefore, a manufacturer can produce said plates and deliver them to customers, wherein the customer can produce from said plates with relatively simple equipment brake pads for vehicle brakes. This manufacturing process comprises good flexibility regarding varying local demands. The present invention is most suitable in connection with so-called "Fast-Fit-Workshops". Such workshops can manufacture with relatively inexpensive equipment and with practically neglectable stockkeeping different brake pads, depending on the local actual demand. The prior art brake pads, in particular for disc brakes, comprise regularly a carrier plate, typically made from steel and a friction lining made from a different material since the mechanical requirements regarding the carrier plate, which shall transfer the strong braking forces into the brake carrier, on the one hand, and the requirements regarding the lining, on the other hand, are substantially different. If the method according to the present invention is applied to such brake pads, said step of cutting the plate comprises, according to one embodiment, that the material of the carrier plate, e.g. steel, is cut to its final dimensions, i.e. the dimensions in the completed brake pad. During that cut the layer of lining material of the plate also obtains the contour (outline) on the carrier plate. Thereafter, the material of the lining on the carrier plate is formed into its final shape. During that formation normally an area is obtained at the edge of the carrier plate not covered by lining material. According to another embodiment of the method of the present invention for manufacturing brake pads, initially part of the friction lining layer is removed from the plate, e.g. by milling, approximately following the outline (contour) of the brake pad to be manufactured such that a part of the carrier plate layer of the plate is free from lining material, corresponding the contour of the carrier plate to be manufactured, such that thereafter the carrier plate layer can be cut in accordance with that contour, for example by means of a laser beam or a water jet. The invention is also concerned with a plate for manufacturing brake pads, said plate being an "intermediate product", i.e. a plate that has dimensions essentially larger than the dimensions of the brake pad to be manufactured, said plate comprising friction lining material as a layer. If a conventional brake pad is manufactured comprising a carrier plate made of steel or the like and a friction lining made of a material having a large friction coefficient, said plate comprises the above-mentioned two layers, namely a carrier plate layer and a lining layer. Furthermore, the plate has e.g. dimensions sufficient to manufacture two or more brake pads from that plate. In the following embodiments of the invention are explained with regard to the figures: Figure 1 shows a plate for manufacturing two brake pads: Figure 2 shows a cross section of the plate according to figure 1 along the line MI; and Figure 3 shows a complete brake pad. According to figure 1, a plate 10 is large enough so that two brake pads can be manufactured from that plate. According to figure 3 the brake pad to be manufactured comprises in a conventional manner a carrier plate 12 and a friction lining 26. The friction lining has a contour (outline, presented in figure 3 as a darkened area) smaller than contour of the carrier plate. Figure 2 shows the plate of figure 1 in cross section along the line I-II. As is shown in figure 2, the plate 10 of figure 1 is composed of two layers, namely a layer of friction material 22 and a layer of carrier plate material 24. Initially, both said layers of friction material 22 and carrier plate material 24 are continuous along the entire plate 10 according to figure 1. Figure 1 shows in continuous lines the contours (outlines) of two carrier plates 12,14 as these carrier plates are formed in the final complete product. As is known as such in the-art, the carrier plates 12, 14 comprise a protrusion with a hole 16 for receiving a mounting spring 28 (cf. figure 3). Dashed lines in figure 1 show an outer contour 18 and an inner contour 20 which run outside and, respectively, inside the contour of the carrier plate 12 to be manufactured. In figure 1 these dashed lines are shown only in connection with carrier plate 12, however, with regard to the other carrier plate 14 corresponding dashed lines can be drawn (not shown). According to a first method of manufacturing brake pads from plate 10 in its initial state, as described above, an appropriate cutting means, e.g. a focussed laser beam, a water beam or a milling machine can be used to cut the plate 10 along the continuous line. As a result, that method yields a blank for a brake pad comprising a carrier plate 12 already essentially in its final contour, apart from polishing the edge or deburring (if any), whereas the layer of friction material has not yet its final shape which is indicated by line 20 (see figures 1 and 3). Accordingly, the blank is further processed such that along the edge of that plate the friction material is removed. As a result, a brake pad in accordance with figure 3 is obtained. According to another embodiment of the method of manufacturing a brake pad, the plate 10 in its initial state is processed such that lining friction material 22 in between the dashed lines of the outer contour 18 and the inner contour 20, respectively, is removed, e.g. by millcut Thereafter, the area between the dashed lines of figure 1 is free from friction material and the carrier plate material 24 (figure 2) is exposed, wherein the lining to be manufactured has already obtained its final form. Thereafter, only the carrier plate material 24 must be cut, e.g. using a water beam or a laser beam, along the continuous line of figure 1, corresponding to the final shape of the carrier plate, in order to obtain a brake pad as shown in figure 3, in which the mounting spring 28 is inserted into the hole 16. Although described above with respect to a steel carrier plate it should be appreciated that other materials can be used for the carrier plate, e.g. Aluminium, Plastics, Metal Composites either on their own or as part of sandwich design. Depending on the material chosen for the carrier plate the exposed surfaces thereof may be subjected to an anti-corrosion treatment e.g. painting. The dimensions of the plate 10 are such that two or more brake pads can be cut from a single plate. This applies to all brake pads to be manufactured from such plates, in particular to the brake pads having the largest dimensions. Claims 1. Manufacturing process for brake pads, said process comprising the following steps: a plate (10) is manufactured at a first location, said plate comprising a friction lining (26) and dimensions which are essentially larger than the dimensions of the smallest brake pad to be manufactured, shipping that plate (10) to a customer at another location, wherein said customer cuts said plate (10) such that brake pads are manufactured comprising their final dimensions. 2. A method for manufacturing brake pads from a plate (10) comprising lining friction material (22) and having dimensions such that at least two brake pads can be manufactured from the plate (10), wherein part of the friction lining layer is removed from the plate following the outline of the brake pad to be manufactured such that a part of a carrier plate layer of the plate (10) is free from lining material, corresponding the contour of the carrier plate to be manufactured, such that thereafter the carrier plate layer can be cut in accordance with that contour. 3. Manufacturing process according to claim 1, wherein the plate has dimensions such that at least two brake pads can be manufactured from that plate (10). 4. Manufacturing process according to claim 1, wherein the plate comprises (10) comprises two layers: a first layer of lining friction material (22), and a second layer of a material (24) for a carrier plate of the brake pad. 5. Manufacturing process according to claim 4, characterized in that during the step of cutting the second layer is cut to its final dimensions of the carrier plate of the brake pad.

Full Text

Method and product for manufacturing brake pads
The invention is concerned with manufacturing brake pads, in particular for disc brakes.
According to the art, brake pads for disc brakes usually are composed of a carrier plate, e.g. made from steel, and a brake lining which is pressed against the disc in order to generate braking action.
According to the prior art such brake pads are manufactured by producing first a carrier plate comprising its final dimensions (i.e. the dimensions in the final brake pad) and, thereafter, the lining is attached to the carrier plate, wherein the lining also has already its final dimensions. The attachment is e.g. obtained by a glue.
According to this known method of manufacture, each brake pad is completely finished at the manufacturer's premises and then shipped to the distributors and final users. This causes a complex and laborious stockkeeping of several sizes of brake pads.
The technical problem underlying the present invention is to provide a method and a product for manufacturing brake pads reducing the stockkeeping requirements and allowing a less laborious adjustment as to varying size requirements at the market place. Also, the transportation from the manufacturer to the distributor and other users shall be reduced.
To this end, the invention teaches a method for manufacturing brake pads comprising the following steps:
- providing a plate comprising a lining, said plate having dimensions substantially larger than the dimensions of the smallest brake pad to be manufactured, and
- cutting the brake pad to be manufactured from said plate, at least partially in accordance with the final dimensions of the brake pad.
According to the invention, therefore, a manufacturer can produce said plates and deliver them to customers, wherein the customer can produce from said plates with relatively simple equipment brake pads for vehicle brakes. This manufacturing process comprises good flexibility regarding varying local demands. The present invention is most suitable in connection with so-called "Fast-Fit-Workshops". Such workshops can manufacture with relatively inexpensive equipment and with practically neglectable stockkeeping different brake pads, depending on the local actual demand.
The prior art brake pads, in particular for disc brakes, comprise regularly a carrier plate, typically made from steel and a friction lining made from a different material since the mechanical requirements regarding the carrier plate, which shall transfer the strong braking forces into the brake carrier, on the one hand, and the requirements regarding the lining, on the other hand, are substantially different. If the method according to the present invention is applied to such brake pads, said step of cutting the plate comprises, according to one embodiment, that the material of the carrier plate, e.g. steel, is cut to its final dimensions, i.e. the dimensions in the completed brake pad. During that cut the layer of lining material of the plate also obtains the contour (outline) on the carrier plate. Thereafter, the material of the lining on the carrier plate is formed into its final shape. During that formation normally an area is obtained at the edge of the carrier plate not covered by lining material.
According to another embodiment of the method of the present invention for manufacturing brake pads, initially part of the friction lining layer is removed from the plate, e.g. by milling, approximately following the outline (contour) of the brake pad to be manufactured such that a part of the carrier plate layer of the plate is free from lining material, corresponding the contour of the carrier plate to be
manufactured, such that thereafter the carrier plate layer can be cut in accordance with that contour, for example by means of a laser beam or a water jet.
The invention is also concerned with a plate for manufacturing brake pads, said plate being an "intermediate product", i.e. a plate that has dimensions essentially larger than the dimensions of the brake pad to be manufactured, said plate comprising friction lining material as a layer. If a conventional brake pad is manufactured comprising a carrier plate made of steel or the like and a friction lining made of a material having a large friction coefficient, said plate comprises the above-mentioned two layers, namely a carrier plate layer and a lining layer. Furthermore, the plate has e.g. dimensions sufficient to manufacture two or more brake pads from that plate.
In the following embodiments of the invention are explained with regard to the figures:
Figure 1 shows a plate for manufacturing two brake pads:
Figure 2 shows a cross section of the plate according to figure 1 along the line MI; and
Figure 3 shows a complete brake pad.
According to figure 1, a plate 10 is large enough so that two brake pads can be manufactured from that plate. According to figure 3 the brake pad to be manufactured comprises in a conventional manner a carrier plate 12 and a friction lining 26. The friction lining has a contour (outline, presented in figure 3 as a darkened area) smaller than contour of the carrier plate.
Figure 2 shows the plate of figure 1 in cross section along the line I-II. As is shown in figure 2, the plate 10 of figure 1 is composed of two layers, namely a layer of friction material 22 and a layer of carrier plate material 24. Initially, both said layers
of friction material 22 and carrier plate material 24 are continuous along the entire plate 10 according to figure 1.
Figure 1 shows in continuous lines the contours (outlines) of two carrier plates 12,14 as these carrier plates are formed in the final complete product. As is known as such in the-art, the carrier plates 12, 14 comprise a protrusion with a hole 16 for receiving a mounting spring 28 (cf. figure 3). Dashed lines in figure 1 show an outer contour 18 and an inner contour 20 which run outside and, respectively, inside the contour of the carrier plate 12 to be manufactured. In figure 1 these dashed lines are shown only in connection with carrier plate 12, however, with regard to the other carrier plate 14 corresponding dashed lines can be drawn (not shown).
According to a first method of manufacturing brake pads from plate 10 in its initial state, as described above, an appropriate cutting means, e.g. a focussed laser beam, a water beam or a milling machine can be used to cut the plate 10 along the continuous line.
As a result, that method yields a blank for a brake pad comprising a carrier plate 12 already essentially in its final contour, apart from polishing the edge or deburring (if any), whereas the layer of friction material has not yet its final shape which is indicated by line 20 (see figures 1 and 3). Accordingly, the blank is further processed such that along the edge of that plate the friction material is removed. As a result, a brake pad in accordance with figure 3 is obtained.
According to another embodiment of the method of manufacturing a brake pad, the plate 10 in its initial state is processed such that lining friction material 22 in between the dashed lines of the outer contour 18 and the inner contour 20, respectively, is removed, e.g. by millcut Thereafter, the area between the dashed lines of figure 1 is free from friction material and the carrier plate material 24 (figure 2) is exposed, wherein the lining to be manufactured has already obtained its final form. Thereafter, only the carrier plate material 24 must be cut, e.g. using a water beam or a laser
beam, along the continuous line of figure 1, corresponding to the final shape of the carrier plate, in order to obtain a brake pad as shown in figure 3, in which the mounting spring 28 is inserted into the hole 16.
Although described above with respect to a steel carrier plate it should be appreciated that other materials can be used for the carrier plate, e.g. Aluminium, Plastics, Metal Composites either on their own or as part of sandwich design.
Depending on the material chosen for the carrier plate the exposed surfaces thereof may be subjected to an anti-corrosion treatment e.g. painting. The dimensions of the plate 10 are such that two or more brake pads can be cut from a single plate. This applies to all brake pads to be manufactured from such plates, in particular to the brake pads having the largest dimensions.

Claims
1. Manufacturing process for brake pads, said process comprising the following steps:
a plate (10) is manufactured at a first location, said plate comprising a friction lining (26) and dimensions which are essentially larger than the dimensions of the smallest brake pad to be manufactured, shipping that plate (10) to a customer at another location, wherein said customer cuts said plate (10) such that brake pads are manufactured comprising their final dimensions.
2. A method for manufacturing brake pads from a plate (10) comprising lining friction material (22) and having dimensions such that at least two brake pads can be manufactured from the plate (10), wherein part of the friction lining layer is removed from the plate following the outline of the brake pad to be manufactured such that a part of a carrier plate layer of the plate (10) is free from lining material, corresponding the contour of the carrier plate to be manufactured, such that thereafter the carrier plate layer can be cut in accordance with that contour.
3. Manufacturing process according to claim 1, wherein the plate has dimensions
such that at least two brake pads can be manufactured from that plate (10).
4. Manufacturing process according to claim 1, wherein the plate comprises (10)
comprises two layers:
a first layer of lining friction material (22), and
a second layer of a material (24) for a carrier plate of the brake pad.

5. Manufacturing process according to claim 4, characterized in that during the step of cutting the second layer is cut to its final dimensions of the carrier plate of the brake pad.

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=9VymPAOThm7MOO9S1pl1Ig==&loc=+mN2fYxnTC4l0fUd8W4CAA==

« Previous Patent

Next Patent »

Patent Number

272495

Indian Patent Application Number

6448/DELNP/2006

PG Journal Number

15/2016

Publication Date

08-Apr-2016

Grant Date

05-Apr-2016

Date of Filing

01-Nov-2006

Name of Patentee

TRW KFZ-AUSRUSTUNG GMBH

Applicant Address

RUDOLF-DIESEL-STRASSE 7, 56556 NEUWIED, GERMANY

Inventors:

#	Inventor's Name	Inventor's Address
1	AUGNET, FRANCOIS	BIRGELER KOPF WEG 6, 53424 REMAGEN-OBERWINTER, GERMANY

PCT International Classification Number

F16D 65/092

PCT International Application Number

PCT/EP2005/005910

PCT International Filing date

2005-06-01

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	04013123.7	2004-06-03	EUROPEAN UNION