Title of Invention	DISTRIBUTOR DEVICE FOR METAL CASTING
Abstract	Distributor (1) for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the wall comprising a first and a second longitudinal wall portion (20, 21) and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture (7, 8, 9) and the first and second cross wall portion having a first front aperture (U} and a second front aperture (12) respectively, whereby the distributor further comprises a first and a second deflector plate (17, 18) , the first deflector plate (17) extending between the bottom aperture (7, 8, 9) and the first longitudinal wall portion and the second deflector plate (18) extending between the bottom aperture (7, 8, 9) and the second longitudinal wall portion (21) whereby the bottom and the wall are made of a rigid material.

Title of Invention

DISTRIBUTOR DEVICE FOR METAL CASTING

Abstract

Distributor (1) for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the wall comprising a first and a second longitudinal wall portion (20, 21) and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture (7, 8, 9) and the first and second cross wall portion having a first front aperture (U} and a second front aperture (12) respectively, whereby the distributor further comprises a first and a second deflector plate (17, 18) , the first deflector plate (17) extending between the bottom aperture (7, 8, 9) and the first longitudinal wall portion and the second deflector plate (18) extending between the bottom aperture (7, 8, 9) and the second longitudinal wall portion (21) whereby the bottom and the wall are made of a rigid material.

Full Text	DISTRIBUTOR DEVICE FOR USE IK METAL CASTING The invention relates to a distributor for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the waif comprising a first and a second longitudinal wall portion and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture and the first and second cross wall portion having a first front aperture and a second font aperture respectively. Such distributor is often used in the aluminium industry where aluminium, as the molten metal, is cast into ingots of a desired shape. The distributor is positioned inside a casting mould and molten metal is fed, mostly through a casting pipe, into the distributor. The function of the distributor is to control the velocity and recirculation and the solidification processes of the molten metal in the mould with the object to obtain a homogeneous ingot. The most common fonn of a distributor is a bag in the form of a box made of woven glass cloth. The bottom and walls are made of glass cloth, which is because of the density with which it is woven, impenneable for the molten mental. The various apertures are covered with open woven glass cloth, which acts as a filter to prevent inclusions from entenng into (he Ingot. A problem with the known distributor in the form of a flexible bag is that, because of its flexibility, the flow of moilen melal from (he distributor into the mould is difficult to control. In particular, macro-segregation wherein the concentrations of the additives and alloying elements change over the cross section of the ingot is a problem. Macro-segregation is caused by insufficient stirring of the hot metal in the mould, through insufficient control of the flow through the various apertures in the distributor and the unstable shape of the bag during casting. Another problem with the flexible bag is that it can only be used for casting a single ingot after which the bag has to be discarded. This leads to high costs and waste, which is unwanted from an environmental point of view. It is an object of the present invention to provide a distributor, which gives better control of the flow in the mould when casting a hot metal into an ingot. I( is another object of the present invention lo provide a distributor which prevents or at least reduces unwanted flows in the mould. It is a further object of the present invention lo provide a distributor, which can be used for casting a plurality of ingots. It is still a fijrther object of the present invention to provide a distributor which prevents or at least reduces macro-segregation in the mould. These objects and further objects and advantages are obtained with a distributor, which according to the invention is characterised in that the distributor further comprises a first and a second deflector plate, the first deflector plate extending between the bottom aperture and the first longitudinal wall portion and the second deflector plale extending between the bottom aperture and the second longitudinal wall portion whereby the bottom and the wall are made of a rigid material. The deflector plates guide the flow of molten metal. By suitably selecting the position and shape of the deflector plates, the flow through the or each of the bottom apertures can be controlled. Because the bottom and the wall are made of a rigid material, the shape of the distributor is stable and constant during casting. In one embodiment of the distributor of the invention the rigid material is a refractory material, reinforced with glass fibres if desired. A distributor made of a rigid material can after casting an ingot easily be cleaned from remnants of aluminium which stayed behind, The distributor can be re-used many times, which saves money and limits environmental pollution, In a further embodiment the first and second deflector plate are made of a rigid material. In this embodiment the deflector plates are not distorted during the casting process, which further contributes to an improved control of the flow in the mould. Rigid deflection plates can also be cleaned easily after each casting and can be re-used for a number of castings. In a preferred embodiment wherein the first and second deflector plate extend tapering in the direction of a cross wall portion. Preferably the deflector plates enclose a gap or slil near the cross wail portion. The tapered position of the deflector plates increases the flow resistance in the direction of tapering. One result thereof is that the velocity of the flow of molten metal in the vincinity of the or each bottom apenure is reduced which leads to an increased flow through the or each bottom aperture in the direction of the mould. The increase in flow resistance also causes an increase in the level of the bath of aluminium in the distributor between the detlector plates in the direction of the tapering and hence also in a higher hydrostatic pressure at the level of the bottom and at the slit between the deflection plates at the tapering near the cross wall portion. The higher hydrostatic pressure increases the flow through the or each bottom aperture and the quantity of metal flowing through the slil into the direction of the aperture in the cross wall. The higher hydrostatic pressure has a self-stabilizing and self-conlroJling effecl on the quantity of meial flowing through the apertures in the distributor and through the slit. A fiirther embodiment of the distributor according to the invention is characterised in that the first and second deflector plate are provided with a passage near the entry area to allow hot meta! to flow in the direction of the longitudinal wall portions and wherein each of the first and the second longitudinal wall is provided with at least one side exit port. With l)ie known distributor, hot metal leaves the distributor through the apertures in the cross wall portions and in the bottom. The meniscus of the hot metal in the mould between the side wails of the mould and the wall of the distributor has a lower temperature than the hot metal entering the mould through the bottom apenure. This hot metal has a lower specific density than the hot metal at the meniscus and therefor has the tendency to rise up. This leads to a flow of hot metal in (he mould along the bottom of the distributor. However to prevent macro-segregation il is desired that the hot metal which enters the mould through the bottom aperture penetrates into the molten metal in the mould and rises in the so-called mushy zone along the solidified shell of metal in the mould. In that situation the rising flow entails solidified highly pure metal such as aluminium particles which have sunk to the lowest point of the pool of molten aluminium back into the direction of the meniscus. (n a case wherein there is a substantial flow of molten metai closely under the bottom in the direction of the meniscus, the highly pure metal, such as aluminium particles, are not entrained in the directioti of the meniscus, but remain in the centre. Then there will be a great difference between the chemical composition at the center of the ingot and the sidewalls thereof This embodiment of the inventions prevents or reduces this segregation. The flow of hot metal leaving the distnbutor through the apertures in the longitudinal wall of the distributor is directed to the longitudinal wall of the mould and heats up the meniscus thereby raising the temperature thereof and suppressing a difference in specific ^avity between the molten metal of the meniscus and in the centre of the mould. This suppresses an uptlow of hot metal along the longitudinal wall of the mould, thereby preventing harmftil macro-segregation. A further embodiment of the distributor according to the invention is characterised in that the bottom is provided with a dcfleclor positioned downstream, in use, of the bottom aperture. In particular in an embodiment of the distributor having a plurality of bottom apertures, wherein the bottom apertures are positioned one behind the other in the direction of the main flow of the metal, the velocity of the flow of molten metal along the bottom in the direction of (be cross wall may be so high that the hot metal tends to pass at least the first aperture seen in the direction of the flow, and does not enter into the aperture. The deflector locally brakes the flow of molten metal and directs it into the bottom aperture in front of the deflector. In that way, the deflector contributes to a desired partem of flow of molten metal from the distributor into the mould. The effect of the deflector can be further improved in an embodiment wherein the deflector is tilted in the, m use, upstream direction of the flow of hot metal. In another embodiment the deflector has a generally triangular cross section. The triangular cross section gives the deflector great strength to withstand the forces exerted by the impact of the flow of hot metal, while, at the same time, this shape creates (he desired flow around the deflector !o direct hot melaJ into the bottom aperture in from. In cross section. Ehc top ponion of ihe ingot being cast shows a solified pari enclosing a cavity filled with molten metal. The transition area in the mould between the solidified part and the bath of molten metal also called mushy zone, is a mixiure of solid metal and molten metal. To prevent macro-segieyation ii is desired io stir the bath and the metal in the mushy zone. Tests have shown that an effective stirring can be achieved with an embodiment of the distributor of the invention, which is characterised in (hat the bottom at the entry area is provided with at least one throuyh-hole. When casting certain molten meials, such as molten aluminium, part of the molten metal inevitably oxidises by contact with the air and often forms sohd particles, which should nol enter into the ingot. To prevent solid particles from cnienng the ingot a further embodiment of the invention is characterised in that at least one, preferably all apertures, exit ports or trough holes in the distributor are provided with u mesh cover. The invention will tjow be illustrated ivJJb reference lo the non-Jimiting drawing in which Fig. } shows one halfof a symmetric distribiitor according to the prior art. Fig. 2 shows in a schematic form one half of a symmetric distributor according to the invention. Fig. 3 shows in a schematic form a part of a distributor which is according to an embodiment of the invention provided with a deflector. Fig. 4 shows in a schematic form a part of a distributor which is according to an embodiment of the invention provided with adeilector of a differetit shape. Fig. 5 shows m a schematic fomi a part of a distributor which is according to an embodiment of the invention provided with a deflector of a further different shape. The same numerals in the figures indicate the same items,or item with the same or an identical function. In Fig. !, the numeral 1 indicates in general a distributor according to the prior art. The distributor is made of a woven glass cloth, A casting pipe 2, which is commonly not pari of a distributor reaches into the distributor I. In Fig. 1 only one half of the disiribulor 1 and the casting pipe 2 is shown. Both components are symmetrical with respect to a plane through lines 3 and 5. The bottom 6 is provided with a pJurality of bottom aperture^- 7, S and 9. First front wall portion 10 is provided with first front apertures 1 I and 12. in use, molten metal such as molten aluminium is fed e.g. from a melting ftimace (not shown} thnaugh casting pipe 2 into the distributor I, Molten metal leaves the distributor 1 through bottom apertures 7, 8 and Q and first front apertures ! I and 12. The flow through the first front apertures 11 and 12 is directed to one of the small sides of a rectangular casting mould and supplies molten metal to the small sides and comers of the casting mould. It has shown that in practice it is difficult to control the flow of molten metal through the various apertures 7, S, 9, i 1 and (2 of a distributor made of woven glass cloth. In particular the distribution of the quantity of molten metal flowing through each of the hottom apertures is a problem. Because of the insufficient control of the quantities, macro-segregation in the cast ingot may occor. Fig. 2 shows a distributor in which the present invention is embodied. Numeral 1 again indicates m genera! a distributor suitable for use in a method of casting a metal ingot such as an aluminium ingot. The distributor is manufactured fr'om a refractory material and has a rigid box shape of rectangular nature. The distributor is provided with bottom apertures 7, S and 9 and with first (rant apertures 11 and 12, Further the distributor has side exit parts 13 and 14 in the first longitudinal wall 20 and side exit ports 15 and 16 in the second longitudinal wall 2!. fn use, molten metal such as moiten aluminium is fed e.g. from a melting furnace (not shown) through casting pipe 2 into the distributor ! at entry area 30. A first part of the molten metal flowing into the distributor flows into the space between the deflector plates 17 and 18. A first effect of the deflector plates is that only part of the molten metal flowing into the distributor is available for flowing through the bottom apertures. A second part of the molten metal flowing into the distributor flows into the space between the first longitudinal wall 20 and deflector plate 17 and into the space between the second longitudinal wall 21 and deflector plate 18. Because of the tapered position of the deflector plates 17 and IS the level of the molten metal in the space between the deflector plates 17 and I 8 increases in the direction of the taper. Therefore, the hydrostatic pressure on the botloin increases in the direction from bottom aperture 7, through bottom aperture 8 to bottom aperture 9. The increasing hydrostatic pressure results in an increased flow through bottom apertures 8 and 9 of the embodiment of the invention as compared to the flow through bottom apeilures S and '^ of the distributor of the prior art. The distributor therefore contributes to a better distrihuhon of the flow through the bottom apertures of the distributor of the invention as compared to the distributor of the prior art. A proportion of the first part passes through the slit 22 between the deflector plates 17 and 18 at the side of the taper and leaves the distributor through first front apertures 11 and 12 in the direction of a short wall of a casting mould (not shown). Tests and mathematical simulat:ons have shown that the tlow in the mould has the tendency to be directed along the bottom of the distributor and then upwardly along the long sides of the casting mould (not shown). To limit this upwardly directed flow ihe first longitudinal wall 20 is provided with side exit pons 13 and 14 and the second longitudinal wall 21 is provided with side exit ports ! 5 and 16, A proportion of the second pari of the tlow of molten metal entering the space between the deflector plates and the longitudiua! walls leaves the distributor through the side exit ports 13, 14, 15 and 16 and surjiresses the upwardly directed flow. In this way, the side exit ports provide the possibility lo further .'itabilize and control the flow of molten metal in the casting mould. The bottom is also provided with through holes 26 and 27 which are positioned at the entry area 30 under the casting pipe 2, Molten metal leaving the distributor through the through holes 26 and 27 enters the mould in a basically vertical direction and have a beneficial stirrig effect on the pool of molten metal in the casting mould, more in particular on the '■inusliy zone" whidx is the (ransition area between the liquid and Ihe solidified metal in Ihe casting mould. As shown, fust front apertures 11 and 12 arc covered with a mesh 4 of e,g. glass fiber. The mesh acts as a fitter for solid particles and smoothes the flow of molten metal through the apertures. Et}iialiy, one or more of the bottom apertures, one or more of the side exit ports and one or more of the through holes may be covered with a mesh. Fig. 3 shows in a schematic tbrni a part of a distributor in which a deflector 25 is applied in the form of a flat baffle. The deflector reduces the horizontal velocity of the molten metal near bottom aperture 7 and deflects a proportion of the lirsi part of molten metal flowing into the distributor in a vertical direction thereby increasing the vertical velocity of the molten metal flowing through bottom aperture 7 into the mould. This results in an even further stabilisation and control of the flow of molten metal in the casting mould. Fig. 4 shows an embodiment of the invention wherein the deflector is tilled in the direction opposite to the direction of the horizontal flow of molten metal along the bottom of the distributor. By selecting the angle al which the deflector is tilted, the vertical velocity can be given a desired value dependent on process parameters. Fig. 5 shows an embodiment wherein the deflector has a basically triangular cross section. This embodiment has the advantage of mechanical strength and less disturbance of the horizonta! flow of molten metal downstream of the deflector. CLAIMS 1. Distributor for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the wall comprising a first and a second longitudinal wall portion and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture and the first and second cross wall portion having a first front aperture and a second front aperture respectively, characterised in that the distributor further comprises a first and a second deflector plate, the first deflector plate extending between the bottom aperture and the first longitudinal wall portion and the second deflector plate extending between the bottom aperture and the second longitudinal wall portion whereby the bottom and the wall are made of a rigid materia!. 2. Distributor according the claim 1 wherein the first and second deflector plate are made of a rigid material. 3. Distributor according lo claim 1 or 2 wherein the first and second deflector plate extend tapering in the direction of a cross wall portion. 4. Distributor according to any of the preceding claims wherein the first and second deflector plate are provided with a passage near the entry area to allow hot metal to flow in the direction of the longitudinal wall portions and wherein each of the first and the second longitudinal wail is provided with at least one side exit port. 5. Distributor according to any of the preceding claims wherein the bottom is provided with a deflector positioned downstream, in use, of the bottom aperture- - 10 - 6. Distributor according to claim 5 wherein the deflector is tilled in the, in use, upstream direction of the flow of hot metal. 7. Distributor according to claim 5 or claim 6 wherein the deflector has a generally triangular cross section. 8. Distributor according to any of the preceding claims wherein the bottom at the entry area is provided with at least one through-hole. 9. Distributor according to any of the preceding claims wherein at least one, preferably all apertures, exit ports or trough holes in the distributor are provided with a mesh cover.

Full Text

DISTRIBUTOR DEVICE FOR USE IK METAL CASTING
The invention relates to a distributor for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the waif comprising a first and a second longitudinal wall portion and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture and the first and second cross wall portion having a first front aperture and a second font aperture respectively.
Such distributor is often used in the aluminium industry where aluminium, as the molten metal, is cast into ingots of a desired shape. The distributor is positioned inside a casting mould and molten metal is fed, mostly through a casting pipe, into the distributor. The function of the distributor is to control the velocity and recirculation and the solidification processes of the molten metal in the mould with the object to obtain a homogeneous ingot.
The most common fonn of a distributor is a bag in the form of a box made of woven glass cloth. The bottom and walls are made of glass cloth, which is because of the density with which it is woven, impenneable for the molten mental.
The various apertures are covered with open woven glass cloth, which acts as a filter to prevent inclusions from entenng into (he Ingot.
A problem with the known distributor in the form of a flexible bag is that, because of its flexibility, the flow of moilen melal from (he distributor into the mould is difficult to control. In particular, macro-segregation wherein the concentrations of the additives and alloying elements change over the cross section of the ingot is a problem. Macro-segregation is caused by insufficient stirring of the hot metal in the mould, through insufficient control of the flow through the various apertures in the distributor and the unstable shape of the bag during casting.
Another problem with the flexible bag is that it can only be used for casting a single ingot after which the bag has to be discarded. This leads to high costs and waste, which is unwanted from an environmental point of view.
It is an object of the present invention to provide a distributor, which gives better control of the flow in the mould when casting a hot metal into an ingot.

I( is another object of the present invention lo provide a distributor which prevents or at least reduces unwanted flows in the mould.
It is a further object of the present invention lo provide a distributor, which can be used for casting a plurality of ingots.
It is still a fijrther object of the present invention to provide a distributor which prevents or at least reduces macro-segregation in the mould.
These objects and further objects and advantages are obtained with a distributor, which according to the invention is characterised in that the distributor further comprises a first and a second deflector plate, the first deflector plate extending between the bottom aperture and the first longitudinal wall portion and the second deflector plale extending between the bottom aperture and the second longitudinal wall portion whereby the bottom and the wall are made of a rigid material.
The deflector plates guide the flow of molten metal. By suitably selecting the position and shape of the deflector plates, the flow through the or each of the bottom apertures can be controlled.
Because the bottom and the wall are made of a rigid material, the shape of the distributor is stable and constant during casting.
In one embodiment of the distributor of the invention the rigid material is a refractory material, reinforced with glass fibres if desired.
A distributor made of a rigid material can after casting an ingot easily be cleaned from remnants of aluminium which stayed behind,
The distributor can be re-used many times, which saves money and limits environmental pollution,
In a further embodiment the first and second deflector plate are made of a rigid material.
In this embodiment the deflector plates are not distorted during the casting process, which further contributes to an improved control of the flow in the mould.
Rigid deflection plates can also be cleaned easily after each casting and can be re-used for a number of castings.
In a preferred embodiment wherein the first and second deflector plate extend tapering in the direction of a cross wall portion.

Preferably the deflector plates enclose a gap or slil near the cross wail portion.
The tapered position of the deflector plates increases the flow resistance in the direction of tapering. One result thereof is that the velocity of the flow of molten metal in the vincinity of the or each bottom apenure is reduced which leads to an increased flow through the or each bottom aperture in the direction of the mould. The increase in flow resistance also causes an increase in the level of the bath of aluminium in the distributor between the detlector plates in the direction of the tapering and hence also in a higher hydrostatic pressure at the level of the bottom and at the slit between the deflection plates at the tapering near the cross wall portion.
The higher hydrostatic pressure increases the flow through the or each bottom aperture and the quantity of metal flowing through the slil into the direction of the aperture in the cross wall. The higher hydrostatic pressure has a self-stabilizing and self-conlroJling effecl on the quantity of meial flowing through the apertures in the distributor and through the slit.
A fiirther embodiment of the distributor according to the invention is characterised in that the first and second deflector plate are provided with a passage near the entry area to allow hot meta! to flow in the direction of the longitudinal wall portions and wherein each of the first and the second longitudinal wall is provided with at least one side exit port.
With l)ie known distributor, hot metal leaves the distributor through the apertures in the cross wall portions and in the bottom.
The meniscus of the hot metal in the mould between the side wails of the mould and the wall of the distributor has a lower temperature than the hot metal entering the mould through the bottom apenure. This hot metal has a lower specific density than the hot metal at the meniscus and therefor has the tendency to rise up. This leads to a flow of hot metal in (he mould along the bottom of the distributor. However to prevent macro-segregation il is desired that the hot metal which enters the mould through the bottom aperture penetrates into the molten metal in the mould and rises in the so-called mushy zone along the solidified shell of metal in the mould. In that situation the rising flow entails solidified highly pure metal such as aluminium particles which have sunk to the lowest point of the pool of molten aluminium back into the direction of the meniscus.

(n a case wherein there is a substantial flow of molten metai closely under the bottom in the direction of the meniscus, the highly pure metal, such as aluminium particles, are not entrained in the directioti of the meniscus, but remain in the centre. Then there will be a great difference between the chemical composition at the center of the ingot and the sidewalls thereof This embodiment of the inventions prevents or reduces this segregation.
The flow of hot metal leaving the distnbutor through the apertures in the longitudinal wall of the distributor is directed to the longitudinal wall of the mould and heats up the meniscus thereby raising the temperature thereof and suppressing a difference in specific ^avity between the molten metal of the meniscus and in the centre of the mould. This suppresses an uptlow of hot metal along the longitudinal wall of the mould, thereby preventing harmftil macro-segregation.
A further embodiment of the distributor according to the invention is characterised in that the bottom is provided with a dcfleclor positioned downstream, in use, of the bottom aperture.
In particular in an embodiment of the distributor having a plurality of bottom apertures, wherein the bottom apertures are positioned one behind the other in the direction of the main flow of the metal, the velocity of the flow of molten metal along the bottom in the direction of (be cross wall may be so high that the hot metal tends to pass at least the first aperture seen in the direction of the flow, and does not enter into the aperture.
The deflector locally brakes the flow of molten metal and directs it into the bottom aperture in front of the deflector. In that way, the deflector contributes to a desired partem of flow of molten metal from the distributor into the mould.
The effect of the deflector can be further improved in an embodiment wherein the deflector is tilted in the, m use, upstream direction of the flow of hot metal.
In another embodiment the deflector has a generally triangular cross section.
The triangular cross section gives the deflector great strength to withstand the forces exerted by the impact of the flow of hot metal, while, at the same time, this shape creates (he desired flow around the deflector !o direct hot melaJ into the bottom aperture in from.

In cross section. Ehc top ponion of ihe ingot being cast shows a solified pari enclosing a cavity filled with molten metal.
The transition area in the mould between the solidified part and the bath of molten metal also called mushy zone, is a mixiure of solid metal and molten metal.
To prevent macro-segieyation ii is desired io stir the bath and the metal in the mushy zone.
Tests have shown that an effective stirring can be achieved with an embodiment of the distributor of the invention, which is characterised in (hat the bottom at the entry area is provided with at least one throuyh-hole.
When casting certain molten meials, such as molten aluminium, part of the molten metal inevitably oxidises by contact with the air and often forms sohd particles, which should nol enter into the ingot.
To prevent solid particles from cnienng the ingot a further embodiment of the invention is characterised in that at least one, preferably all apertures, exit ports or trough holes in the distributor are provided with u mesh cover.
The invention will tjow be illustrated ivJJb reference lo the non-Jimiting drawing in which
Fig. } shows one halfof a symmetric distribiitor according to the prior art.
Fig. 2 shows in a schematic form one half of a symmetric distributor according to the invention.
Fig. 3 shows in a schematic form a part of a distributor which is according to an embodiment of the invention provided with a deflector.
Fig. 4 shows in a schematic form a part of a distributor which is according to an embodiment of the invention provided with adeilector of a differetit shape.
Fig. 5 shows m a schematic fomi a part of a distributor which is according to an embodiment of the invention provided with a deflector of a further different shape.
The same numerals in the figures indicate the same items,or item with the same or an identical function.
In Fig. !, the numeral 1 indicates in general a distributor according to the prior art. The distributor is made of a woven glass cloth, A casting pipe 2, which is commonly not pari of a distributor reaches into the distributor I.

In Fig. 1 only one half of the disiribulor 1 and the casting pipe 2 is shown. Both components are symmetrical with respect to a plane through lines 3 and 5. The bottom 6 is provided with a pJurality of bottom aperture^- 7, S and 9. First front wall portion 10 is provided with first front apertures 1 I and 12.
in use, molten metal such as molten aluminium is fed e.g. from a melting ftimace (not shown} thnaugh casting pipe 2 into the distributor I, Molten metal leaves the distributor 1 through bottom apertures 7, 8 and Q and first front apertures ! I and 12. The flow through the first front apertures 11 and 12 is directed to one of the small sides of a rectangular casting mould and supplies molten metal to the small sides and comers of the casting mould.
It has shown that in practice it is difficult to control the flow of molten metal through the various apertures 7, S, 9, i 1 and (2 of a distributor made of woven glass cloth. In particular the distribution of the quantity of molten metal flowing through each of the hottom apertures is a problem.
Because of the insufficient control of the quantities, macro-segregation in the cast ingot may occor.
Fig. 2 shows a distributor in which the present invention is embodied.
Numeral 1 again indicates m genera! a distributor suitable for use in a method of casting a metal ingot such as an aluminium ingot. The distributor is manufactured fr'om a refractory material and has a rigid box shape of rectangular nature.
The distributor is provided with bottom apertures 7, S and 9 and with first (rant apertures 11 and 12, Further the distributor has side exit parts 13 and 14 in the first longitudinal wall 20 and side exit ports 15 and 16 in the second longitudinal wall 2!.
fn use, molten metal such as moiten aluminium is fed e.g. from a melting furnace (not shown) through casting pipe 2 into the distributor ! at entry area 30. A first part of the molten metal flowing into the distributor flows into the space between the deflector plates 17 and 18. A first effect of the deflector plates is that only part of the molten metal flowing into the distributor is available for flowing through the bottom apertures. A second part of the molten metal flowing into the distributor flows into the space between the first longitudinal wall 20 and deflector plate 17 and into the space between the second longitudinal wall 21 and deflector plate 18. Because of the tapered position of the deflector plates 17 and IS the level of

the molten metal in the space between the deflector plates 17 and I 8 increases in the direction of the taper.
Therefore, the hydrostatic pressure on the botloin increases in the direction from bottom aperture 7, through bottom aperture 8 to bottom aperture 9.
The increasing hydrostatic pressure results in an increased flow through bottom apertures 8 and 9 of the embodiment of the invention as compared to the flow through bottom apeilures S and '^ of the distributor of the prior art.
The distributor therefore contributes to a better distrihuhon of the flow through the bottom apertures of the distributor of the invention as compared to the distributor of the prior art.
A proportion of the first part passes through the slit 22 between the deflector plates 17 and 18 at the side of the taper and leaves the distributor through first front apertures 11 and 12 in the direction of a short wall of a casting mould (not shown).
Tests and mathematical simulat:ons have shown that the tlow in the mould has the tendency to be directed along the bottom of the distributor and then upwardly along the long sides of the casting mould (not shown).
To limit this upwardly directed flow ihe first longitudinal wall 20 is provided with side exit pons 13 and 14 and the second longitudinal wall 21 is provided with side exit ports ! 5 and 16,
A proportion of the second pari of the tlow of molten metal entering the space between the deflector plates and the longitudiua! walls leaves the distributor through the side exit ports 13, 14, 15 and 16 and surjiresses the upwardly directed flow.
In this way, the side exit ports provide the possibility lo further .'itabilize and control the flow of molten metal in the casting mould.
The bottom is also provided with through holes 26 and 27 which are positioned at the entry area 30 under the casting pipe 2, Molten metal leaving the distributor through the through holes 26 and 27 enters the mould in a basically vertical direction and have a beneficial stirrig effect on the pool of molten metal in the casting mould, more in particular on the '■inusliy zone" whidx is the (ransition area between the liquid and Ihe solidified metal in Ihe casting mould.
As shown, fust front apertures 11 and 12 arc covered with a mesh 4 of e,g. glass fiber. The mesh acts as a fitter for solid particles and smoothes the flow of

molten metal through the apertures. Et}iialiy, one or more of the bottom apertures, one or more of the side exit ports and one or more of the through holes may be covered with a mesh.
Fig. 3 shows in a schematic tbrni a part of a distributor in which a deflector 25 is applied in the form of a flat baffle.
The deflector reduces the horizontal velocity of the molten metal near bottom aperture 7 and deflects a proportion of the lirsi part of molten metal flowing into the distributor in a vertical direction thereby increasing the vertical velocity of the molten metal flowing through bottom aperture 7 into the mould. This results in an even further stabilisation and control of the flow of molten metal in the casting mould.
Fig. 4 shows an embodiment of the invention wherein the deflector is tilled in the direction opposite to the direction of the horizontal flow of molten metal along the bottom of the distributor. By selecting the angle al which the deflector is tilted, the vertical velocity can be given a desired value dependent on process parameters.
Fig. 5 shows an embodiment wherein the deflector has a basically triangular cross section. This embodiment has the advantage of mechanical strength and less disturbance of the horizonta! flow of molten metal downstream of the deflector.

CLAIMS
1. Distributor for use in a method of casting molten metal into a metal ingot, comprising a bottom and a wall of a generally rectangular shape, the wall comprising a first and a second longitudinal wall portion and a first and a second cross wall portion, the bottom having an entry area at which in use the hot metal is fed into the distributor and at least one bottom aperture and the first and second cross wall portion having a first front aperture and a second front aperture respectively, characterised in that the distributor further comprises a first and a second deflector plate, the first deflector plate extending between the bottom aperture and the first longitudinal wall portion and the second deflector plate extending between the bottom aperture and the second longitudinal wall portion whereby the bottom and the wall are made of a rigid materia!.
2. Distributor according the claim 1 wherein the first and second deflector plate are made of a rigid material.
3. Distributor according lo claim 1 or 2 wherein the first and second deflector plate extend tapering in the direction of a cross wall portion.
4. Distributor according to any of the preceding claims wherein the first and second deflector plate are provided with a passage near the entry area to allow hot metal to flow in the direction of the longitudinal wall portions and wherein each of the first and the second longitudinal wail is provided with at least one side exit port.
5. Distributor according to any of the preceding claims wherein the bottom is provided with a deflector positioned downstream, in use, of the bottom aperture-

- 10 -
6. Distributor according to claim 5 wherein the deflector is tilled in the, in use,
upstream direction of the flow of hot metal.
7. Distributor according to claim 5 or claim 6 wherein the deflector has a
generally triangular cross section.
8. Distributor according to any of the preceding claims wherein the bottom at the
entry area is provided with at least one through-hole.
9. Distributor according to any of the preceding claims wherein at least one,
preferably all apertures, exit ports or trough holes in the distributor are
provided with a mesh cover.

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=st2t6dF9op9th6l4aGdNUg==&loc=egcICQiyoj82NGgGrC5ChA==

« Previous Patent

Next Patent »

Patent Number

272983

Indian Patent Application Number

4945/CHENP/2008

PG Journal Number

20/2016

Publication Date

13-May-2016

Grant Date

06-May-2016

Date of Filing

17-Sep-2008

Name of Patentee

ALERIS ALUMINUM KOBLENZ GMBH

Applicant Address

CARL-SPAETER-STRASSE 10, 56070 KOBLENZ,

Inventors:

#	Inventor's Name	Inventor's Address
1	VAN SCHOONEVELDT, HUGO,	MIDDENWEG 13, 1463 HB NOORDBEEMSTER
2	KIEFT, RENE,	WIM SONNEVELDLAAN 22, 1948 AE BEVERWIJIK,
3	BAL, DICO,	KAMPERSINGEL 16 RD, 2012 DK HAARLEM,

PCT International Classification Number

B22D 11/103

PCT International Application Number

PCT/EP07/1229

PCT International Filing date

2007-02-13

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	6075688.9	2006-03-20	EUROPEAN UNION